CN106136479A - A kind of self-moistening type resin teeth zipper - Google Patents
A kind of self-moistening type resin teeth zipper Download PDFInfo
- Publication number
- CN106136479A CN106136479A CN201610711724.6A CN201610711724A CN106136479A CN 106136479 A CN106136479 A CN 106136479A CN 201610711724 A CN201610711724 A CN 201610711724A CN 106136479 A CN106136479 A CN 106136479A
- Authority
- CN
- China
- Prior art keywords
- self
- chain
- stop member
- type resin
- teeth zipper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of self-moistening type resin teeth zipper, this slide fastener includes chain, pull head, base band, upper stop member, lower stop member and latch square, described chain is fixedly installed on the inner side edge of base band, described upper stop member is arranged at the opening of chain, lower stop member and latch square are arranged at the closed end of chain, described pull head is set on chain, and the main component of described chain includes: acetal resin, self-lubricity filler and related auxiliaries.Present invention is disclosed a kind of self-moistening type resin teeth zipper, this resin teeth zipper reasonable in design, serviceability is excellent, the one-tenth assignment system that especially chain is unique, it is made in use to possess self-lubricity energy, effectively avoiding slide fastener and in use with medicated clothing, stuck phenomenon occurs, it is the most convenient to provide for daily life.
Description
Technical field
The present invention relates to a kind of resin teeth zipper, particularly relate to a kind of self-moistening type resin teeth zipper, belong to zipper technology field.
Background technology
Slide fastener is dependent on continuously arranged chain tooth, makes article the connector closing or separating, is widely used in clothes now
The fields such as dress, bag and tent.The structure of slide fastener is as follows: mainly include a pair base band, on the opposite side edge of base band respectively
Row are provided with a row chain tooth, and chain tooth is fixing with base band to be connected, and is provided with the pull head making they engagements and separating between two row chain teeth,
It is respectively arranged with upper stop member and lower stop member in the upper and lower end base band of every row chain tooth.Dividing according to the common used material of slide fastener, slide fastener can divide
For nylon zipper, resin teeth zipper and metal zip fastener three major types.
Resin teeth zipper has by force, hardness high, be prone to the advantage such as molding and colouring, preparation technology simplicity, moderate cost, but deposits
Higher in chain tooth surface roughness, the shortcomings such as coefficient of friction is bigger.Therefore, during the use of resin teeth zipper, especially clothing
Slide fastener on clothes is easy to be stuck in clothes, produces the phenomenon that slide fastener is stuck.Running into this situation, people use brute-force mostly
Pull chain, run counter to desire sometimes, make a mess of slide fastener.To this end, people take to smear the mode of paraffin or liquid detergent on slide fastener, profit
Sliding slide fastener, to reduce the frictional force between chain tooth, in order to pull-out slide fastener.Although said method can eliminate the phenomenon that slide fastener is stuck,
But people must lack convenience by foreign object, bring unnecessary trouble to the orthobiosis of people.
Summary of the invention
For the demand, the invention provides a kind of self-moistening type resin teeth zipper, this resin teeth zipper reasonable in design, make
By the unique one-tenth assignment system of function admirable, especially chain so that it is in use possess self-lubricity energy, effectively avoid
Slide fastener in use produces stuck phenomenon with medicated clothing, and it is the most convenient to provide for daily life.
The present invention is a kind of self-moistening type resin teeth zipper, and this slide fastener includes chain, pull head, base band, upper stop member, lower stop member and inserts
Pin square, described chain is fixedly installed on the inner side edge of base band, and described upper stop member is arranged at the opening of chain, the most only
Part and latch square are arranged at the closed end of chain, and described pull head is set on chain, the main component bag of described chain
Include: acetal resin, self-lubricity filler and related auxiliaries.
In a preferred embodiment of the present invention, main component and the percentage composition proportioning thereof of described chain be: polyformaldehyde
Resin 80%-85%, self-lubricity filler 10%-15%, remaining is auxiliary agent.
In a preferred embodiment of the present invention, main component and the percentage composition proportioning thereof of described chain be: polyformaldehyde
Resin 80%-82%, self-lubricity filler 10%-12%, remaining is auxiliary agent.
In a preferred embodiment of the present invention, described self-lubricity filler is the mixed of Nano graphite powder and molybdenum bisuphide micropowder
Closing material, mixed proportion is about 3:1.
In a preferred embodiment of the present invention, described auxiliary agent is by dispersant, heat stabilizer, antioxidant, firming agent, first
Aldehyde absorbent forms.
Present invention is disclosed a kind of self-moistening type resin teeth zipper, this resin teeth zipper reasonable in design, serviceability is excellent, especially
It is the one-tenth assignment system that chain is unique so that it is in use possesses self-lubricity energy, effectively avoids slide fastener and using
With medicated clothing, stuck phenomenon occurring in journey, it is the most convenient to provide for daily life.
Accompanying drawing explanation
The present invention is further detailed explanation with detailed description of the invention below in conjunction with the accompanying drawings:
Fig. 1 is the structural representation of embodiment of the present invention self-moistening type resin teeth zipper.
In accompanying drawing, the labelling of each parts is as follows: 1, chain, and 2, pull head, 3, base band, 4, upper stop member, 5, lower stop member, 6, latch
Square.
Detailed description of the invention
Below in conjunction with the accompanying drawings presently preferred embodiments of the present invention is described in detail, so that advantages and features of the invention energy
It is easier to be readily appreciated by one skilled in the art, thus protection scope of the present invention is made apparent clear and definite defining.
Fig. 1 is the structural representation of embodiment of the present invention self-moistening type resin teeth zipper；This slide fastener includes chain 1, pull head 2, base
Band 3, upper stop member 4, lower stop member 5 and latch square 6, described chain is fixedly installed on the inner side edge of base band, described upper only
Part 4 is arranged at the opening of chain 1, and lower stop member 5 and latch square 6 are arranged at the closed end of chain 1, and described pull head 2 is sheathed
On chain 1, the main component of described chain 1 includes: acetal resin, self-lubricity filler and related auxiliaries.
In the self-moistening type resin teeth zipper that the present invention mentions, main component and the percentage composition proportioning thereof of chain 1 be: polyformaldehyde
Resin 80%-85%, self-lubricity filler 10%-15%, remaining is auxiliary agent.
Further illustrating, main component and the percentage composition proportioning thereof of chain 1 be: acetal resin 80%-82%, self-lubricity
Filler 10%-12%, remaining is auxiliary agent；Self-lubricity filler is Nano graphite powder and the compound of molybdenum bisuphide micropowder, mixed proportion
It is about 3:1；Auxiliary agent is made up of dispersant, heat stabilizer, antioxidant, firming agent, formaldehyde absorbent.
The concrete preparation process of the self-moistening type resin teeth zipper that the present invention mentions is as follows:
A) selection is got the raw materials ready, and pull head, base band, upper stop member, lower stop member and latch square on slide fastener are outsourcing piece, in addition to base band its
Material is usually engineering plastics or metal, the material terylene of base band, and thickness is 0.3mm；Chain on slide fastener is moulding, and it is main
Composition and the percentage composition proportioning thereof is wanted to be: acetal resin 82%, self-lubricity filler 10%, remaining is auxiliary agent；Self-lubricity filler is
Nano graphite powder and the compound of molybdenum bisuphide micropowder, mixed proportion is about 3:1, by the average particle size after milled processed is
550 mesh；Auxiliary agent by dispersant polyethylene glycol 200, heat stabilizer benzoate, antioxidant tea polyphenols, curing agent ethylene diamine with
And formaldehyde absorbent composition;
B) preparation of raw material, process for preparation is as follows: first, acetal resin, heat stabilizer, antioxidant and formaldehyde absorbent is added
Adding to melt compounding in high temperature batch mixer, batch mixer barrel temperature controls, at 180 DEG C-185 DEG C, fully to merge；Then, to barrel
Middle interpolation self-lubricity filler and dispersant, barrel temperature is promoted to 5 DEG C-7 DEG C, and rotating speed controls at 450r/min；Finally, to barrel
Middle interpolation firming agent, constant temperature is standby after stirring 25 minutes；
C) injection-molded discharge miaow, row microphone machine parameter is provided that screw diameter is chosen to be 20mm, and injection amount controls at 45g, injection pressure
Controlling at 120Mpa, mold clamping force controls at 250KN, and injection temperature controls at 190 DEG C-195 DEG C；The injection mo(u)lding time control of chain
After system processes 35 minutes after 3-4s, chain molding in 60 DEG C of baking ovens, it is cooled to room temperature in atmosphere；
D) chain post processing, aftertreatment technology includes washing and dries, and the deionized water using pressure to be 0.1-0.12Mpa washes away
Chain, takes out the drying in oven at 30 DEG C-35 DEG C after unnecessary powder；
E) assembling detection, assembly technology is included in chain upper end and installs stop member and pull head, and stops under chain lower end is installed
Part and latch square；After assembling, slide fastener is carried out spacing cut-out process；Finally, detect by the way of hand test and draw
The serviceability of chain；After detection, carry out packing and store.
Present invention is disclosed a kind of self-moistening type resin teeth zipper, be characterized in: this resin teeth zipper reasonable in design, usability
Can be excellent, the one-tenth assignment system that especially chain is unique so that it is in use possess self-lubricity energy, effectively avoid slide fastener
In use with medicated clothing, stuck phenomenon occurring, it is the most convenient to provide for daily life.
The above, the only detailed description of the invention of the present invention, but protection scope of the present invention is not limited thereto, and any
Those of ordinary skill in the art in the technical scope that disclosed herein, the change that can expect without creative work or
Replace, all should contain within protection scope of the present invention.Therefore, protection scope of the present invention should be limited with claims
Fixed protection domain is as the criterion.
Claims (5)
1. a self-moistening type resin teeth zipper, it is characterised in that this slide fastener include chain, pull head, base band, upper stop member, lower stop member and
Latch square, described chain is fixedly installed on the inner side edge of base band, and described upper stop member is arranged at the opening of chain, under
Stop member and latch square are arranged at the closed end of chain, and described pull head is set on chain, the main component of described chain
Including: acetal resin, self-lubricity filler and related auxiliaries.
Self-moistening type resin teeth zipper the most according to claim 1, it is characterised in that the main component of described chain and hundred
Point content proportioning is: acetal resin 80%-85%, self-lubricity filler 10%-15%, remaining is auxiliary agent.
Self-moistening type resin teeth zipper the most according to claim 2, it is characterised in that the main component of described chain and hundred
Point content proportioning is: acetal resin 80%-82%, self-lubricity filler 10%-12%, remaining is auxiliary agent.
Self-moistening type resin teeth zipper the most according to claim 1, it is characterised in that described self-lubricity filler is nano-graphite
Powder and the compound of molybdenum bisuphide micropowder, mixed proportion is about 3:1.
Self-moistening type resin teeth zipper the most according to claim 1, it is characterised in that described auxiliary agent is by dispersant, thermally-stabilised
Agent, antioxidant, firming agent, formaldehyde absorbent composition.