CN106119479A - 一种提高13Cr9Mo2Co1NiVNbNB晶粒度的退火方法 - Google Patents

一种提高13Cr9Mo2Co1NiVNbNB晶粒度的退火方法 Download PDF

Info

Publication number
CN106119479A
CN106119479A CN201610788494.3A CN201610788494A CN106119479A CN 106119479 A CN106119479 A CN 106119479A CN 201610788494 A CN201610788494 A CN 201610788494A CN 106119479 A CN106119479 A CN 106119479A
Authority
CN
China
Prior art keywords
annealing
grain size
forging
furnace
present
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610788494.3A
Other languages
English (en)
Inventor
许亮
刘智
陈翠
王骏
李姚君
丁佐军
郑卓
郜均虎
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuxi Parker New Materials Polytron Technologies Inc
Original Assignee
Wuxi Parker New Materials Polytron Technologies Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuxi Parker New Materials Polytron Technologies Inc filed Critical Wuxi Parker New Materials Polytron Technologies Inc
Priority to CN201610788494.3A priority Critical patent/CN106119479A/zh
Publication of CN106119479A publication Critical patent/CN106119479A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种提高13Cr9Mo2Co1NiVNbNB晶粒度的退火方法，锻件经锻造后，退火时，将其置入炉温为850‑1000℃的退火炉中，保温8‑40h后，退火炉缓冷至700‑780℃，保温8‑40h后空冷至室温。本发明的退火方法，用于13Cr9Mo2Co1NiVNbNB材质的锻件退火，退火后其晶粒度得到有效提高，得到晶粒较细的组织，组织均匀。

Description

一种提高13Cr9Mo2Co1NiVNbNB晶粒度的退火方法
技术领域
本发明涉及金属加工的热处理工艺。
背景技术
现有技术中，对13Cr9Mo2Co1NiVNbNB材料，采用普通的退火方法，其晶粒度较低，组织不均匀。
发明内容
针对现有技术存在的上述问题，申请人提供一种提高13Cr9Mo2Co1NiVNbNB晶粒度的退火方法。
为了解决上述问题，本发明采用如下方案：
一种提高13Cr9Mo2Co1NiVNbNB晶粒度的退火方法，材料为13Cr9Mo2Co1NiVNbNB的锻件经锻造后，退火时，将其置入炉温为850-1000℃的退火炉中，保温8-40h后，退火炉缓冷至700-780℃，保温8-40h后空冷至室温。
作为上述技术方案的进一步改进：
将所述锻件置入880-980℃的退火炉中，保温10h后，退火炉缓冷至750-780℃，保温12h后空冷至室温。
本发明的技术效果在于：
本发明的退火方法，用于13Cr9Mo2Co1NiVNbNB材质的锻件退火，退火后其晶粒度得到有效提高，得到晶粒较细的组织，组织均匀。
具体实施方式
下面结合对本发明的具体实施方式作进一步说明。
本实施例的提高13Cr9Mo2Co1NiVNbNB晶粒度的退火方法，材料为13Cr9Mo2Co1NiVNbNB的锻件经锻造后，退火时，将其置入炉温为850-1000℃的退火炉中，保温8-40h后，退火炉缓冷至700-780℃，保温8-40h后空冷至室温。
以外形尺寸为Φ700/Φ550*100的锻件为例，锻造成形后将锻件置入880-980℃的退火炉中，保温10h后，退火炉缓冷至750-780℃，保温12h后空冷至室温。
通过上述退火处理，可得到均匀、晶粒较细的组织。
以上所举实施例为本发明的较佳实施方式，仅用来方便说明本发明，并非对本发明作任何形式上的限制，任何所属技术领域中具有通常知识者，若在不脱离本发明所提技术特征的范围内，利用本发明所揭示技术内容所作出局部改动或修饰的等效实施例，并且未脱离本发明的技术特征内容，均仍属于本发明技术特征的范围内。

Claims (2)

1.一种提高13Cr9Mo2Co1NiVNbNB晶粒度的退火方法，材料为13Cr9Mo2Co1NiVNbNB的锻件经锻造后，退火时，将其置入炉温为850-1000℃的退火炉中，保温8-40h后，退火炉缓冷至700-780℃，保温8-40h后空冷至室温。
2.根据权利要求1所述的提高13Cr9Mo2Co1NiVNbNB晶粒度的退火方法，其特征在于：将所述锻件置入880-980℃的退火炉中，保温10h后，退火炉缓冷至750-780℃，保温12h后空冷至室温。
CN201610788494.3A 2016-08-31 2016-08-31 一种提高13Cr9Mo2Co1NiVNbNB晶粒度的退火方法 Pending CN106119479A (zh)