CN106118497A - A kind of photovoltaic storage battery fluid sealant based on ethyl ester and hydroxypropyl acrylate and manufacture method - Google Patents
A kind of photovoltaic storage battery fluid sealant based on ethyl ester and hydroxypropyl acrylate and manufacture method Download PDFInfo
- Publication number
- CN106118497A CN106118497A CN201610486385.6A CN201610486385A CN106118497A CN 106118497 A CN106118497 A CN 106118497A CN 201610486385 A CN201610486385 A CN 201610486385A CN 106118497 A CN106118497 A CN 106118497A
- Authority
- CN
- China
- Prior art keywords
- component
- parts
- ethyl ester
- platinum
- silane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of photovoltaic storage battery fluid sealant based on ethyl ester and hydroxypropyl acrylate and manufacture method, including component A and B component;Described component A is made up of dimethylaminoethyl ethyl ester, ethyl acetate, dioctyl phthalate, fire retardant, silicon powder, antioxidant 1010, heat filling;B component is made up of Hydroxypropyl methacrylate, polyether rubber, N ethyl morpholine, silane crosslinker, platinum or platinum complex, defoamer, silane adhesion promoters;The present invention, by the material in component A and B component is processed production respectively respectively, is processed into by vacuum kneader and reactor.The present invention passes through good fire retardant and heat filling, other materials are utilized to be mutually mixed, in making glue, air bubble content is little, and have that caking property is excellent, high-temp resisting high-humidity resisting excellent performance and flame-retarded heat-conducting and electrical insulating property good, the advantages such as curing rate is fast, easy to operate.
Description
Technical field
The present invention relates to chemical technology field, particularly to accumulator is played the one of sealing function based on ethyl ester and
The photovoltaic storage battery fluid sealant of hydroxypropyl acrylate and manufacture method.
Background technology
In recent years, country built a conservation-minded society in promotion always, advocated energy-saving and emission-reduction, advocated low-carbon environment-friendly, so
Overall situation under, solar energy industry occur to the inexorable trend developed under a kind of policy.Technology disconnected upgrading not also becomes
For the best support of solar energy industry.Solaode is a kind of new technique in solar energy industry, and it utilizes silicon etc. partly to lead
The quantum effect of body, is directly changed into electric energy the visible ray of the sun.The core component of solaode is silicon wafer.For ensureing
The light electrical efficiency of silicon wafer and life-span, industrial meeting is sealed against inside photovoltaic module, and the aluminum frame of assembly, bus bar and
Rosettees etc. are accomplished by with being bonded and sealed that special sealing cement is carried out, it is to avoid in air, water and oxygen etc. enter.
Being currently used for the One component Sealant of photovoltaic module, curing rate is slow, and the curing time of assembly is long, affects efficiency.
Solar energy overhead accumulator requires that fluid sealant should have good resistance to elevated temperatures and good flame-retarded heat-conducting performance, and keeps good
Good electrical insulation capability, and this type of fluid sealant is narrower in research range, it is impossible to meet the market demand.
Summary of the invention
It is an object of the invention to provide one and have that caking property is excellent, high-temp resisting high-humidity resisting excellent performance and flame-retarded heat-conducting and
Electrical insulating property is good, and a kind of based on ethyl ester and hydroxypropyl acrylate the photovoltaic storage battery of the advantages such as curing rate is fast, easy to operate is close
Sealing and manufacture method, solve the use needs of problems of accumulator sealant.
In order to achieve the above object, the present invention provides following technical scheme:
A kind of photovoltaic storage battery fluid sealant based on ethyl ester and hydroxypropyl acrylate, it is characterised in that: include component A and B component;Described
Component A is by dimethylaminoethyl ethyl ester, ethyl acetate, dioctyl phthalate, fire retardant, silicon powder, antioxygen
Agent 1010, heat filling forms;B component is by Hydroxypropyl methacrylate, polyether rubber, N-ethylmorpholine, silane crosslinker, platinum
Or platinum complex, defoamer, silane adhesion promoters forms;In wherein said component A, including: the dimethylaminoethyl acrylate methyl of 40-60 part
Amido ethyl ester, the ethyl acetate of 25-40 part, the dioctyl phthalate of 5-15 part, the fire retardant of 20-35 part, 2-10 part
Silicon powder, the antioxidant 1010 of 2-10 part, 5-15 part heat filling composition;In described B component, including: the first of 60-80 part
Base Hydroxypropyl acrylate, the polyether rubber of 15-25 part, the N-ethylmorpholine of 5-15 part, the silane crosslinker of 3-15 part, 1-8 part
Platinum or platinum complex, the defoamer of 10-15 part, the silane adhesion promoters of 0.1-6 part.
Described fire retardant be basic zinc carbonate, Firebrake ZB, aluminium hydroxide, magnesium hydroxide, iron oxide red, decabromodiphenyl oxide,
At least one in red phosphorus, chlorinated paraffin;Heat filling is nanometer silicon carbide, nano aluminum nitride, nm-class boron nitride, nano silicon nitride
Silicon, high heat conduction composite powder, at least one in nano silicon carbide aluminum;Described defoamer is silicone and polyacrylate apoplexy due to endogenous wind
Any one in BYK-065, BYK-066N, BYK-354, DEUCHEM2700.
In described component A, including: the dimethylaminoethyl ethyl ester of 50 parts, the ethyl acetate of 35 parts, 10 parts
Dioctyl phthalate, the fire retardant of 25 parts, the silicon powder of 5 parts, the antioxidant 1010 of 6 parts, the heat filling composition of 10 parts;
In described B component, including: the Hydroxypropyl methacrylate of 70 parts, the polyether rubber of 20 parts, the N-ethylmorpholine of 10 parts, 8 parts
Silane crosslinker, the platinum of 4 parts or platinum complex, the defoamer of 12 parts, the silane adhesion promoters of 3 parts.
Concretely comprise the following steps:
Component A includes step: by above-mentioned weight, by dimethylaminoethyl ethyl ester, ethyl acetate, adjacent benzene two
Formic acid dioctyl ester adds in vacuum kneader, and temperature controls at 60~100 DEG C, and vacuum is 0.08~0.12MPa, and dehydration is blended
1~6 hour, then move in reactor, start stirring, then put into fire retardant, and silicon powder, antioxidant 1010, heat filling, mixed
Close uniformly, obtain component A;B component includes step: by above-mentioned weight, by Hydroxypropyl methacrylate, and polyether rubber,
N-ethylmorpholine adds in vacuum kneader, and temperature controls at 60~120 DEG C, and vacuum is 0.08~0.12MPa, and dehydration is blended
1~7 hour, then move in reactor, start stirring, put into silane crosslinker, platinum or platinum complex, defoamer, silane increases
Stick, after mix homogeneously, obtains B component.
The rotating speed of described reactor is 50~1000rpm, and the mix and blend time is 15~120 minutes.
Beneficial effects of the present invention: the present invention passes through good fire retardant and heat filling, utilizes other materials the most mixed
Closing, in making glue, air bubble content is little, and has caking property excellence, high-temp resisting high-humidity resisting excellent performance and flame-retarded heat-conducting and electric insulation
Property good, the advantages such as curing rate is fast, easy to operate.
Detailed description of the invention
Below in conjunction with embodiment, technical scheme is clearly and completely described, it is clear that described
Embodiment is only a part of embodiment of the present invention rather than whole embodiments.Based on the embodiment in the present invention, this area
The every other embodiment that those of ordinary skill is obtained under not making creative work premise, broadly falls into present invention protection
Scope.
Embodiment 1:
A kind of photovoltaic storage battery fluid sealant based on ethyl ester and hydroxypropyl acrylate, it is characterised in that: include component A and B component;Described
Component A is by dimethylaminoethyl ethyl ester, ethyl acetate, dioctyl phthalate, fire retardant, silicon powder, antioxygen
Agent 1010, heat filling forms;B component is by Hydroxypropyl methacrylate, polyether rubber, N-ethylmorpholine, silane crosslinker, platinum
Or platinum complex, defoamer, silane adhesion promoters forms;In wherein said component A, including: the dimethylaminoethyl acrylate methyl of 40-60 part
Amido ethyl ester, the ethyl acetate of 25-40 part, the dioctyl phthalate of 5-15 part, the fire retardant of 20-35 part, 2-10 part
Silicon powder, the antioxidant 1010 of 2-10 part, 5-15 part heat filling composition;In described B component, including: the first of 60-80 part
Base Hydroxypropyl acrylate, the polyether rubber of 15-25 part, the N-ethylmorpholine of 5-15 part, the silane crosslinker of 3-15 part, 1-8 part
Platinum or platinum complex, the defoamer of 10-15 part, the silane adhesion promoters of 0.1-6 part.
Described fire retardant be basic zinc carbonate, Firebrake ZB, aluminium hydroxide, magnesium hydroxide, iron oxide red, decabromodiphenyl oxide,
At least one in red phosphorus, chlorinated paraffin;Heat filling is nanometer silicon carbide, nano aluminum nitride, nm-class boron nitride, nano silicon nitride
Silicon, high heat conduction composite powder, at least one in nano silicon carbide aluminum;Described defoamer is silicone and polyacrylate apoplexy due to endogenous wind
Any one in BYK-065, BYK-066N, BYK-354, DEUCHEM2700.
In described component A, including: the dimethylaminoethyl ethyl ester of 50 parts, the ethyl acetate of 35 parts, 10 parts
Dioctyl phthalate, the fire retardant of 25 parts, the silicon powder of 5 parts, the antioxidant 1010 of 6 parts, the heat filling composition of 10 parts;
In described B component, including: the Hydroxypropyl methacrylate of 70 parts, the polyether rubber of 20 parts, the N-ethylmorpholine of 10 parts, 8 parts
Silane crosslinker, the platinum of 4 parts or platinum complex, the defoamer of 12 parts, the silane adhesion promoters of 3 parts.
Concretely comprise the following steps:
Component A includes step: by above-mentioned weight, by dimethylaminoethyl ethyl ester, ethyl acetate, adjacent benzene two
Formic acid dioctyl ester adds in vacuum kneader, and temperature controls at 60~100 DEG C, and vacuum is 0.08~0.12MPa, and dehydration is blended
1~6 hour, then move in reactor, start stirring, then put into fire retardant, and silicon powder, antioxidant 1010, heat filling, mixed
Close uniformly, obtain component A;B component includes step: by above-mentioned weight, by Hydroxypropyl methacrylate, and polyether rubber,
N-ethylmorpholine adds in vacuum kneader, and temperature controls at 60~120 DEG C, and vacuum is 0.08~0.12MPa, and dehydration is blended
1~7 hour, then move in reactor, start stirring, put into silane crosslinker, platinum or platinum complex, defoamer, silane increases
Stick, after mix homogeneously, obtains B component.
The rotating speed of described reactor is 50~1000rpm, and the mix and blend time is 15~120 minutes.
Embodiment 2:
In described component A, including: the dimethylaminoethyl ethyl ester of 40-60 part, the ethyl acetate of 25-40 part, 5-15
The dioctyl phthalate of part, the fire retardant of 20-35 part, the silicon powder of 2-10 part, the antioxidant 1010 of 2-10 part, 5-15 part
Heat filling composition;In described B component, including: the Hydroxypropyl methacrylate of 60-80 part, the polyether rubber of 15-25 part,
The N-ethylmorpholine of 5-15 part, the silane crosslinker of 3-15 part, the platinum of 1-8 part or platinum complex, the defoamer of 10-15 part,
The silane adhesion promoters of 0.1-6 part.
Concrete production and processing step is:
Component A includes step: by above-mentioned weight, by dimethylaminoethyl ethyl ester, ethyl acetate, adjacent benzene two
Formic acid dioctyl ester adds in vacuum kneader, and temperature controls at 60~100 DEG C, and vacuum is 0.08~0.12MPa, and dehydration is blended
1~6 hour, then move in reactor, start stirring, then put into fire retardant, and silicon powder, antioxidant 1010, heat filling, mixed
Close uniformly, obtain component A;B component includes step: by above-mentioned weight, by Hydroxypropyl methacrylate, and polyether rubber,
N-ethylmorpholine adds in vacuum kneader, and temperature controls at 60~120 DEG C, and vacuum is 0.08~0.12MPa, and dehydration is blended
1~7 hour, then move in reactor, start stirring, put into silane crosslinker, platinum or platinum complex, defoamer, silane increases
Stick, after mix homogeneously, obtains B component.
Component A, B component stand subpackage respectively, during use directly by component A, B component according to weight ratio mix homogeneously after
Potting operation can be carried out.
Embodiment 3:
In described component A, including: the dimethylaminoethyl ethyl ester of 50 parts, the ethyl acetate of 35 parts, the adjacent benzene of 10 parts
Dioctyl phthalate dioctyl ester, the fire retardant of 25 parts, the silicon powder of 5 parts, the antioxidant 1010 of 6 parts, the heat filling composition of 10 parts;Described
In B component, including: the Hydroxypropyl methacrylate of 70 parts, the polyether rubber of 20 parts, the N-ethylmorpholine of 10 parts, the silane of 8 parts
Cross-linking agent, the platinum of 4 parts or platinum complex, the defoamer of 12 parts, the silane adhesion promoters of 3 parts.
Concrete production and processing step is:
Component A includes step: by above-mentioned weight, by dimethylaminoethyl ethyl ester, ethyl acetate, adjacent benzene two
Formic acid dioctyl ester adds in vacuum kneader, and temperature controls at 60~100 DEG C, and vacuum is 0.08~0.12MPa, and dehydration is blended
1~6 hour, then move in reactor, start stirring, then put into fire retardant, and silicon powder, antioxidant 1010, heat filling, mixed
Close uniformly, obtain component A;B component includes step: by above-mentioned weight, by Hydroxypropyl methacrylate, and polyether rubber,
N-ethylmorpholine adds in vacuum kneader, and temperature controls at 60~120 DEG C, and vacuum is 0.08~0.12MPa, and dehydration is blended
1~7 hour, then move in reactor, start stirring, put into silane crosslinker, platinum or platinum complex, defoamer, silane increases
Stick, after mix homogeneously, obtains B component.
Component A, B component stand subpackage respectively, during use directly by component A, B component according to weight ratio mix homogeneously after
Potting operation can be carried out.
The above, the only detailed description of the invention of the present invention, but protection scope of the present invention is not limited thereto, and any
Those familiar with the art, in the technical scope that the invention discloses, can readily occur in change or replace, should contain
Cover within protection scope of the present invention.Therefore, protection scope of the present invention should described be as the criterion with scope of the claims.
Claims (5)
1. a photovoltaic storage battery fluid sealant based on ethyl ester and hydroxypropyl acrylate, it is characterised in that: include component A and B component;Institute
State component A by dimethylaminoethyl ethyl ester, ethyl acetate, dioctyl phthalate, fire retardant, silicon powder, anti-
Oxygen agent 1010, heat filling forms;B component by Hydroxypropyl methacrylate, polyether rubber, N-ethylmorpholine, silane crosslinker,
Platinum or platinum complex, defoamer, silane adhesion promoters forms;In wherein said component A, including: the methacrylic acid two of 40-60 part
Methylamino ethyl ester, the ethyl acetate of 25-40 part, the dioctyl phthalate of 5-15 part, the fire retardant of 20-35 part, 2-10
The silicon powder of part, the antioxidant 1010 of 2-10 part, the heat filling composition of 5-15 part;In described B component, including: 60-80 part
Hydroxypropyl methacrylate, the polyether rubber of 15-25 part, the N-ethylmorpholine of 5-15 part, the silane crosslinker of 3-15 part, 1-8
The platinum of part or platinum complex, the defoamer of 10-15 part, the silane adhesion promoters of 0.1-6 part.
A kind of photovoltaic storage battery fluid sealant based on ethyl ester and hydroxypropyl acrylate the most according to claim 1, it is characterised in that:
Described fire retardant is basic zinc carbonate, Firebrake ZB, aluminium hydroxide, magnesium hydroxide, iron oxide red, decabromodiphenyl oxide, red phosphorus, chlorination
At least one in paraffin;Heat filling is nanometer silicon carbide, nano aluminum nitride, nm-class boron nitride, nano-silicon nitride, high heat conduction
Composite powder, at least one in nano silicon carbide aluminum;Described defoamer be silicone and polyacrylate apoplexy due to endogenous wind BYK-065,
Any one in BYK-066N, BYK-354, DEUCHEM2700.
A kind of photovoltaic storage battery fluid sealant based on ethyl ester and hydroxypropyl acrylate the most according to claim 1, it is characterised in that:
In described component A, including: the dimethylaminoethyl ethyl ester of 50 parts, the ethyl acetate of 35 parts, the O-phthalic of 10 parts
Dioctyl phthalate, the fire retardant of 25 parts, the silicon powder of 5 parts, the antioxidant 1010 of 6 parts, the heat filling composition of 10 parts;Described B group
In Fen, including: the Hydroxypropyl methacrylate of 70 parts, the polyether rubber of 20 parts, the N-ethylmorpholine of 10 parts, the crosslinkable silane of 8 parts
Connection agent, the platinum of 4 parts or platinum complex, the defoamer of 12 parts, the silane adhesion promoters of 3 parts.
4. according to a kind of based on ethyl ester and hydroxypropyl acrylate the photovoltaic storage battery fluid sealant according to any one of claim 1-3
Manufacture method, it is characterised in that: concretely comprise the following steps:
Component A includes step: by above-mentioned weight, by dimethylaminoethyl ethyl ester, ethyl acetate, adjacent benzene two
Formic acid dioctyl ester adds in vacuum kneader, and temperature controls at 60~100 DEG C, and vacuum is 0.08~0.12MPa, and dehydration is blended
1~6 hour, then move in reactor, start stirring, then put into fire retardant, and silicon powder, antioxidant 1010, heat filling, mixed
Close uniformly, obtain component A;B component includes step: by above-mentioned weight, by Hydroxypropyl methacrylate, and polyether rubber,
N-ethylmorpholine adds in vacuum kneader, and temperature controls at 60~120 DEG C, and vacuum is 0.08~0.12MPa, and dehydration is blended
1~7 hour, then move in reactor, start stirring, put into silane crosslinker, platinum or platinum complex, defoamer, silane increases
Stick, after mix homogeneously, obtains B component.
5. according to the making side of a kind of based on ethyl ester and hydroxypropyl acrylate the photovoltaic storage battery fluid sealant described in claim 4
Method, it is characterised in that: the rotating speed of described reactor is 50~1000rpm, and the mix and blend time is 15~120 minutes.