CN106118463A - A kind of high-quality heat-resisting coating and preparation thereof and application process - Google Patents
A kind of high-quality heat-resisting coating and preparation thereof and application process Download PDFInfo
- Publication number
- CN106118463A CN106118463A CN201610553309.2A CN201610553309A CN106118463A CN 106118463 A CN106118463 A CN 106118463A CN 201610553309 A CN201610553309 A CN 201610553309A CN 106118463 A CN106118463 A CN 106118463A
- Authority
- CN
- China
- Prior art keywords
- quality heat
- resisting coating
- preparation
- resisting
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of high-quality heat-resisting coating and the preparation of this high-quality heat-resisting coating and application process.High-quality heat-resisting coating the most of the present invention, including silester, MTES, triethylamine, ethanol, hydrochloric acid, perfluorinated sulfonic resin, dimethylbenzene, hydroxyethyl cellulose, silicon dioxide, magnesium chloride, china clay in powder, Muscovitum, butyl cellosolve and butanol.High-quality heat-resisting coating of the present invention, its component is reasonable, and product stability is good, and product is corrosion-resistant, heat-resist, and stability is high.The preparation method of high-quality heat-resisting coating of the present invention, simple for process, production efficiency is high, and application cost is low, simple to operate, be easily achieved, the constant product quality of production, has higher application value.
Description
Technical field
The invention belongs to paint production field, in particular it relates to a kind of high-quality heat-resisting coating, and this high-quality heat-resisting
The preparation method and application method of coating.
Background technology
Paint, in general, it is simply that coated article surface can be coated in and the continuous film of firm attachment can be formed
Material, the most traditional coating products with natural materials as raw material, or in modern development to synthesize chemical products
For the coating products of raw material, broadly falling into organic chemical industry's macromolecular material, the film formed belongs to macromolecular compound type, presses
According to the classification of the chemical products that the modern times pass through, coating belongs to fine chemical product, and it is many that modern coating the most progressively becomes a class
Functional engineering material, is an important industry in chemical industry.
For many special equipments or be applied to special harshness hot environment in appliance arrangement, the resistance to height to coating
Gentle decay resistance requires high, it is necessary to use heat-resisting paint.Heat-resisting paint is to prevent iron and steel, cement, chemical industry, electricity
The high temperature corrosions such as plant equipment in the factory such as power, waste incineration, automobile engine, heating system, kitchen utensils and use
Coating.Common coating of the prior art is difficult to meet requirement, general phthalic resin coating, epoxy coating, carbon fluorine tree
Although grease coating material has preferable heat resistance, but is typically only capable to resistance to about 200 DEG C, it is impossible to resistance to higher temperature.At high temperature bar
Under part, the adhesive force of above-mentioned coating is deteriorated, it may appear that dry and cracked and obscission, and the change of color, it is impossible at present should meet
Needs.
Therefore, it is badly in need of wanting a kind of heat-resisting paint, is suitable for the use under hot environment.
Summary of the invention
Goal of the invention: in order to overcome above deficiency, the invention provides a kind of high-quality heat-resisting coating and this high-quality
The preparation of heat-resisting paint and application process.
Technical scheme: in order to overcome the deficiencies in the prior art, the invention provides a kind of high-quality heat-resisting coating,
By weight part, including following components:
Silester 25-45 part
MTES 50-70 part
Triethylamine 10-18 part
Ethanol 80-95 part
Hydrochloric acid 10-20 part
Perfluorinated sulfonic resin 30-50 part
Dimethylbenzene 15-30 part
Hydroxyethyl cellulose 3-8 part
Silicon dioxide 0.2-0.8 part
Magnesium chloride 2-6 part
China clay in powder 0.2-3 part
Muscovitum 10-20 part
Butyl cellosolve 5-12 part
Butanol 12-20 part.
High-quality heat-resisting coating of the present invention, its component is reasonable, and product stability is good, with silicon-type for the most former
Material, wherein silester is as corrosion-resistant, heat resistant composition, also serves as solvent simultaneously, and silicon dioxide and Muscovitum can be further
Coordinate silester, improve heat-resisting, the decay resistance of coating.Heat-resisting paint is high temperature resistant can arrive more than 400 DEG C, at high temperature
Under the conditions of adhesive force good, high temperature will not be caused dry and cracked and obscission, and the color change of coating is little after being heated, and may be used for gold
The brushing of the multiple materials such as genus, glass, is used for preventing the industries such as iron and steel, cement, chemical industry, electric power from running in high-temperature corrosion environment
Plant equipment be corroded.
Further, above-mentioned high-quality heat-resisting coating, described hydrochloric acid is 0.2M hydrochloric acid..Application is convenient, and cost
Low.
The present invention also provides for the preparation method of a kind of high-quality heat-resisting coating, comprises the steps:
(1) silester, MTES and ethanol are mixed, and be heated to 70-90 DEG C;
(2) add hydrochloric acid, under stirring condition, continue insulation continue 10-12h;
(3), after adding triethylamine regulation pH value >=7, after continuing for insulation 2-3 hour, insulation is stopped;
(4) add dimethylbenzene, be uniformly mixed;
(5) perfluorinated sulfonic resin, hydroxyethyl cellulose, silicon dioxide, magnesium chloride, china clay in powder, Muscovitum and butyl cellosolve are added,
It is uniformly mixed;
(6) dripping butanol while stirring, stir to obtain described high-quality heat-resisting coating.
The preparation method of high-quality heat-resisting coating of the present invention, simple for process, production efficiency is high, application cost
Low, simple to operate, be easily achieved, there is higher application value.
Further, the preparation method of above-mentioned high-quality heat-resisting coating, the rotating speed of described stirring is 2500-2800r/
min.The high-speed stirred of 2500-2800r/min is easily achieved, and makes material stirring uniform simultaneously.
Further, the preparation method of above-mentioned high-quality heat-resisting coating, described perfluorinated sulfonic resin, hydroxy ethyl fiber
Through 100-150 mesh sieve after element, silicon dioxide, magnesium chloride, china clay in powder and Muscovitum attrition grinding powdering before use.Ensure system
Standby heat-resisting paint stable performance, quality is high.
Further, the preparation method of above-mentioned high-quality heat-resisting coating, described perfluorinated sulfonic resin, hydroxy ethyl fiber
Element, silicon dioxide, magnesium chloride, china clay in powder and Muscovitum are put in dispersion machine or three-roller and are ground to form powdery.Good crushing effect, effect
Rate is high.
Further, the preparation method of above-mentioned high-quality heat-resisting coating, described sieve is vibrosieve.Carried out by vibrosieve
Sieve process, automaticity height, and filter efficiency height.
The present invention also provides for the application process of a kind of high-quality heat-resisting coating, during application, by described high-quality heat-resisting coating
It is brushed on metal or glass, brushing thickness 23-27 μm, solidifies 15-25min in 220-270 DEG C.Easy to use, both can use
In metal, may be used for again glass, adaptability is good.
Further, the application process of above-mentioned high-quality heat-resisting coating, before described high-quality heat-resisting coating application, by institute
State metal or glass is intended to the place's of brushing surface clean and totally and dries;Repaste after often painting is to be dried after brushing one times and brush one times to described painting
Brush thickness.Laminated coating, it is ensured that brush uniformly and stable performance.
Beneficial effect: compared with prior art, the invention have the advantages that high-quality heat-resisting of the present invention is coated with
Material, its component is reasonable, and product is corrosion-resistant, heat-resist, and stability is high.The system of high-quality heat-resisting coating of the present invention
Preparation Method, simple for process, production efficiency is high, and application cost is low, simple to operate, be easily achieved, and the product quality of production is steady
Fixed, there is higher application value.
Detailed description of the invention
The present invention will be further elucidated with by several specific embodiments below, these embodiments simply to illustrate that problem,
It is not a kind of restriction.
Embodiment 1
A kind of high-quality heat-resisting coating, by weight part, including following components:
Silester 25 parts
MTES 50 parts
Triethylamine 10 parts
Ethanol 80 parts
0.2M hydrochloric acid 10 parts
Perfluorinated sulfonic resin 30 parts
Dimethylbenzene 15 parts
Hydroxyethyl cellulose 3 parts
Silicon dioxide 0.2 part
2 parts of magnesium chloride
China clay in powder 0.2 part
10 parts of Muscovitum
Butyl cellosolve 5 parts
12 parts of butanol.
The preparation method of above-mentioned high-quality heat-resisting coating, comprises the steps:
(1) silester, MTES and ethanol are mixed, and be heated to 70 DEG C;
(2) add hydrochloric acid, under the stirring condition with 2500r/min mixing speed, continue insulation continue 10h;
(3), after adding triethylamine regulation pH value >=7, insulation after continuing for being incubated 2 hours, is stopped;
(4) add dimethylbenzene, be uniformly mixed with the mixing speed of 2500r/min;
(5) addition grinds to form powdery and by the perfluorinated sulfonic resin of 100 mesh vibrosieves, hydroxy ethyl fiber in dispersion machine
Element, silicon dioxide, magnesium chloride, china clay in powder, Muscovitum and butyl cellosolve, be uniformly mixed with the mixing speed of 2500r/min;
(6) dripping butanol while stirring, stir to obtain described high-quality heat-resisting coating.
The application process of above-mentioned high-quality heat-resisting coating, before application brushing, is intended to brush place's surface clean clean also by metal
Dry, then by described high-quality heat-resisting coating application to metal, brushing thickness 23 μm, in 220 DEG C of solidification 15min, described height
Quality heat-resisting paint be often coated with the most to be dried after brushing one times after repaste and brush one times to described brushing thickness.
Embodiment 2
A kind of high-quality heat-resisting coating, by weight part, including following components:
Silester 45 parts
MTES 70 parts
Triethylamine 18 parts
Alcohol 95 part
0.2M hydrochloric acid 20 parts
Perfluorinated sulfonic resin 50 parts
Dimethylbenzene 30 parts
Hydroxyethyl cellulose 8 parts
Silicon dioxide 0.8 part
6 parts of magnesium chloride
China clay in powder 3 parts
20 parts of Muscovitum
Butyl cellosolve 12 parts
20 parts of butanol.
The preparation method of above-mentioned high-quality heat-resisting coating, comprises the steps:
(1) silester, MTES and ethanol are mixed, and be heated to 90 DEG C;
(2) add hydrochloric acid, under the stirring condition with 2800r/min mixing speed, continue insulation continue 12h;
(3), after adding triethylamine regulation pH value >=7, insulation after continuing for being incubated 3 hours, is stopped;
(4) add dimethylbenzene, be uniformly mixed with the mixing speed of 2800r/min;
(5) addition grinds to form powdery and by the perfluorinated sulfonic resin of 150 mesh vibrosieves, hydroxy ethyl fiber in three-roller
Element, silicon dioxide, magnesium chloride, china clay in powder, Muscovitum and butyl cellosolve, be uniformly mixed with the mixing speed of 2800r/min;
(6) dripping butanol while stirring, stir to obtain described high-quality heat-resisting coating.
The application process of above-mentioned high-quality heat-resisting coating, before application brushing, is intended to brush place's surface clean clean also by glass
Dry, then by described high-quality heat-resisting coating application to glass, brushing thickness 27 μm, in 270 DEG C of solidification 25min, described height
Quality heat-resisting paint be often coated with the most to be dried after brushing one times after repaste and brush one times to described brushing thickness.
Embodiment 3
A kind of high-quality heat-resisting coating, by weight part, including following components:
Silester 30 parts
MTES 55 parts
Triethylamine 12 parts
Ethanol 85 parts
0.2M hydrochloric acid 18 parts
Perfluorinated sulfonic resin 40 parts
Dimethylbenzene 18 parts
Hydroxyethyl cellulose 5 parts
Silicon dioxide 0.6 part
4 parts of magnesium chloride
China clay in powder 0.8 part
15 parts of Muscovitum
Butyl cellosolve 9 parts
18 parts of butanol.
The preparation method of above-mentioned high-quality heat-resisting coating, comprises the steps:
(1) silester, MTES and ethanol are mixed, and be heated to 80 DEG C;
(2) add hydrochloric acid, under the stirring condition with 2700r/min mixing speed, continue insulation continue 11h;
(3), after adding triethylamine regulation pH value >=7, insulation after continuing for being incubated 2.5 hours, is stopped;
(4) add dimethylbenzene, be uniformly mixed with the mixing speed of 2700r/min;
(5) addition grinds to form powdery and by the perfluorinated sulfonic resin of 120 mesh vibrosieves, hydroxy ethyl fiber in dispersion machine
Element, silicon dioxide, magnesium chloride, china clay in powder, Muscovitum and butyl cellosolve, be uniformly mixed with the mixing speed of 2700r/min;
(6) dripping butanol while stirring, stir to obtain described high-quality heat-resisting coating.
The application process of above-mentioned high-quality heat-resisting coating, before application brushing, is intended to brush place's surface clean clean also by glass
Dry, then by described high-quality heat-resisting coating application to glass, brushing thickness 25 μm, in 250 DEG C of solidification 20min, described height
Quality heat-resisting paint be often coated with the most to be dried after brushing one times after repaste and brush one times to described brushing thickness.
Embodiment 4
A kind of high-quality heat-resisting coating, by weight part, including following components:
Silester 25 parts
MTES 50 parts
Triethylamine 18 parts
Alcohol 95 part
0.2M hydrochloric acid 15 parts
Perfluorinated sulfonic resin 35 parts
Dimethylbenzene 15 parts
Hydroxyethyl cellulose 8 parts
Silicon dioxide 0.58 part
6 parts of magnesium chloride
China clay in powder 1 part
16 parts of Muscovitum
Butyl cellosolve 10 parts
16 parts of butanol.
The preparation method of above-mentioned high-quality heat-resisting coating, comprises the steps:
(1) silester, MTES and ethanol are mixed, and be heated to 80 DEG C;
(2) add hydrochloric acid, under the stirring condition with 2800r/min mixing speed, continue insulation continue 10h;
(3), after adding triethylamine regulation pH value >=7, insulation after continuing for being incubated 2 hours, is stopped;
(4) add dimethylbenzene, be uniformly mixed with the mixing speed of 2800r/min;
(5) addition grinds to form powdery and by the perfluorinated sulfonic resin of 100 mesh vibrosieves, hydroxy ethyl fiber in three-roller
Element, silicon dioxide, magnesium chloride, china clay in powder, Muscovitum and butyl cellosolve, be uniformly mixed with the mixing speed of 2800r/min;
(6) dripping butanol while stirring, stir to obtain described high-quality heat-resisting coating.
The application process of above-mentioned high-quality heat-resisting coating, before application brushing, is intended to the place's of brushing surface clean by described metal and does
Clean and dry, then by described high-quality heat-resisting coating application to metal, brushing thickness 27 μm, solidify 20min, institute in 250 DEG C
State high-quality heat-resisting coating be often coated with brush one times after the most to be dried after repaste and brush one times to described brushing thickness.
The above is only several embodiments of invention, it is noted that for those skilled in the art
For, on the premise of without departing from inventive principle, it is also possible to make some improvement, these improve the protection that also should be regarded as the present invention
Scope.
Claims (9)
1. a high-quality heat-resisting coating, it is characterised in that: by weight part, including following components:
Silester 25-45 part
MTES 50-70 part
Triethylamine 10-18 part
Ethanol 80-95 part
Hydrochloric acid 10-20 part
Perfluorinated sulfonic resin 30-50 part
Dimethylbenzene 15-30 part
Hydroxyethyl cellulose 3-8 part
Silicon dioxide 0.2-0.8 part
Magnesium chloride 2-6 part
China clay in powder 0.2-3 part
Muscovitum 10-20 part
Butyl cellosolve 5-12 part
Butanol 12-20 part.
High-quality heat-resisting coating the most according to claim 1, it is characterised in that: described hydrochloric acid is 0.2M hydrochloric acid.
3. the preparation method of a high-quality heat-resisting coating as claimed in claim 1 or 2, it is characterised in that: include walking as follows
Rapid:
(1) silester, MTES and ethanol are mixed, and be heated to 70-90 DEG C;
(2) add hydrochloric acid, under stirring condition, continue insulation continue 10-12h;
(3), after adding triethylamine regulation pH value >=7, after continuing for insulation 2-3 hour, insulation is stopped;
(4) add dimethylbenzene, be uniformly mixed;
(5) perfluorinated sulfonic resin, hydroxyethyl cellulose, silicon dioxide, magnesium chloride, china clay in powder, Muscovitum and butyl cellosolve are added,
It is uniformly mixed;
(6) dripping butanol while stirring, stir to obtain described high-quality heat-resisting coating.
The preparation method of high-quality heat-resisting coating the most according to claim 3, it is characterised in that: the rotating speed of described stirring is
2500-2800r/min。
The preparation method of high-quality heat-resisting coating the most according to claim 3, it is characterised in that: described perfluorinated sulfonic acid tree
Through 100-after fat, hydroxyethyl cellulose, silicon dioxide, magnesium chloride, china clay in powder and Muscovitum attrition grinding powdering before use
150 mesh sieves.
The preparation method of high-quality heat-resisting coating the most according to claim 5, it is characterised in that: described perfluorinated sulfonic acid tree
Fat, hydroxyethyl cellulose, silicon dioxide, magnesium chloride, china clay in powder and Muscovitum are put in dispersion machine or three-roller and are ground to form powdery.
The preparation method of high-quality heat-resisting coating the most according to claim 5, it is characterised in that: described sieve is vibrosieve.
8. the application process of the high-quality heat-resisting coating as described in claim 1 or 3, it is characterised in that: during application, by institute
State high-quality heat-resisting coating application to metal or glass, brushing thickness 23-27 μm, solidify 15-25min in 220-270 DEG C.
The application process of high-quality heat-resisting coating the most according to claim 8, it is characterised in that: described high-quality heat-resisting is coated with
Before material brushing, described metal or glass are intended to the place's of brushing surface clean and totally and dry;Repaste after often painting is to be dried after brushing one times
Brush one times to described brushing thickness.