CN106118405A - A kind of digit printing fabric flame-proof antibiotic coating - Google Patents

A kind of digit printing fabric flame-proof antibiotic coating Download PDF

Info

Publication number
CN106118405A
CN106118405A CN201610616615.6A CN201610616615A CN106118405A CN 106118405 A CN106118405 A CN 106118405A CN 201610616615 A CN201610616615 A CN 201610616615A CN 106118405 A CN106118405 A CN 106118405A
Authority
CN
China
Prior art keywords
parts
powder
oil
essence
digit printing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610616615.6A
Other languages
Chinese (zh)
Inventor
王志英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610616615.6A priority Critical patent/CN106118405A/en
Publication of CN106118405A publication Critical patent/CN106118405A/en
Pending legal-status Critical Current

Abstract

The present invention relates to a kind of digit printing fabric flame-proof antibiotic coating, composed of the following components: acrylic acid modified alkyd resin, a olefin elastomer, acrylate resins, polyether modified silicon oil, essence of Niobe, tricaprylin, phosphate ester, transformer oil, eucalyptus oil, Bravo, cetyl trimethylammonium bromide, tea polyphenols, blanc fixe powder, lead iodate powder, vermiculite power, dolomite powder, sodium iodoacetate, modified attapulgite powder end, pearl essence, silicon powder, IPPP, trichloroethyl phosphate, ammonium polyphosphate, Tissuemat E, nitrocotton, butyl stearate, isopropyl thioxanthone, decahydronaphthalenes, ethyleneglycol dimethyacrylate, alkyl benzene sulphonate.Product of the present invention has the most superior fire-retardant, acid and alkali-resistance, anti-mildew anti-microbial property, improves properties of product.

Description

A kind of digit printing fabric flame-proof antibiotic coating
Technical field
The present invention relates to a kind of digit printing fabric flame-proof antibiotic coating, belong to digital printing technology field.
Background technology
Digit printing, is the stamp carried out by digital technology.Digital printing technology is as computer technology development And gradually form a kind of integrate machinery, the new high-tech product of computer electronic information technology.Going out of this technology Now with the most perfect, bring a completely new concept, the production principle of its advanced person and means to textile printing and dyeing industry, give weaving Printing and dyeing bring a unprecedented opportunity to develop.Digit printing fabric is necessary to suitable mode and is processed, with Just obtaining the preferable function of performance, wherein using suitable coating is exactly one of important mode.
Summary of the invention
It is an object of the invention to provide a kind of digit printing fabric flame-proof antibiotic coating, in order to digital print is better achieved The use function of flower fabric flame-proof antibiotic coating, makes product have fire-retardant, acid and alkali-resistance, anti-mildew anti-microbial property, improves product and make Use performance.
To achieve these goals, technical scheme is as follows.
A kind of digit printing fabric flame-proof antibiotic coating, is made up of the component of following mass fraction: acrylic modified alkyd Resin 10～14 parts, a-olefin elastomer 8～12 parts, acrylate resins 8～12 parts, polyether modified silicon oil 6～10 parts, benzoic acid Methyl ester 8～12 parts, tricaprylin 8～12 parts, phosphate ester 6～10 parts, transformer oil 8～12 parts, eucalyptus oil 8～12 parts, Bravo 6～10 parts, cetyl trimethylammonium bromide 6～10 parts, tea polyphenols 6～10 parts, blanc fixe powder 8～12 parts, Lead iodate powder 6～10 parts, vermiculite power 4～8 parts, dolomite powder 8～12 parts, sodium iodoacetate 6～10 parts, attapulgite modified Powder 4～8 parts, pearl essence 6～10 parts, silicon powder 4～8 parts, IPPP 4～8 parts, trichloroethyl phosphate 6～ 10 parts, ammonium polyphosphate 6～10 parts, Tissuemat E 6～10 parts, nitrocotton 6～10 parts, butyl stearate 6～10 parts, isopropyl Thioxanthone 6～10 parts, decahydronaphthalenes 6～10 parts, ethyleneglycol dimethyacrylate 6～10 parts, alkyl benzene sulphonate 4～8 parts.
Further, above-mentioned digit printing fabric flame-proof antibiotic coating, it is made up of the component of following mass fraction: acrylic acid Modified alkyd resin 10 parts, a-olefin elastomer 8 parts, acrylate resins 8 parts, polyether modified silicon oil 6 parts, essence of Niobe 8 parts, Tricaprylin 8 parts, phosphate ester 6 parts, 8 parts of transformer oil, eucalyptus oil 8 parts, Bravo 6 parts, cetyl trimethyl bromination Ammonium 6 parts, tea polyphenols 6 parts, 8 parts of blanc fixe powder, 6 parts of lead iodate powder, vermiculite power 4 parts, 8 parts of dolomite powder, iodoacetic acid 4 parts of 6 parts of sodium, modified attapulgite powder end, pearl essence 6 parts, silicon powder 4 parts, IPPP 4 parts, tricresyl phosphate chloroethene Ester 6 parts, ammonium polyphosphate 6 parts, Tissuemat E 6 parts, nitrocotton 6 parts, butyl stearate 6 parts, isopropyl thioxanthone 6 parts, ten Hydrogenated naphthalene 6 parts, ethyleneglycol dimethyacrylate 6 parts, alkyl benzene sulphonate 4 parts.
Further, above-mentioned digit printing fabric flame-proof antibiotic coating, it is made up of the component of following mass fraction: acrylic acid Modified alkyd resin 12 parts, a-olefin elastomer 10 parts, acrylate resins 10 parts, polyether modified silicon oil 8 parts, essence of Niobe 10 Part, tricaprylin 10 parts, phosphate ester 8 parts, 10 parts of transformer oil, eucalyptus oil 10 parts, Bravo 8 parts, cetyl front three Base ammonium bromide 8 parts, tea polyphenols 8 parts, 10 parts of blanc fixe powder, 8 parts of lead iodate powder, vermiculite power 6 parts, dolomite powder 10 Part, 6 parts of sodium iodoacetate 8 parts, modified attapulgite powder end, pearl essence 8 parts, silicon powder 6 parts, IPPP 6 parts, phosphorus Acid trichloro ethyl ester 8 parts, ammonium polyphosphate 8 parts, Tissuemat E 8 parts, nitrocotton 8 parts, butyl stearate 8 parts, isopropyl thioxanthone anthracene Ketone 8 parts, decahydronaphthalenes 8 parts, ethyleneglycol dimethyacrylate 8 parts, alkyl benzene sulphonate 6 parts.
Further, above-mentioned digit printing fabric flame-proof antibiotic coating, it is made up of the component of following mass fraction: acrylic acid Modified alkyd resin 14 parts, a-olefin elastomer 12 parts, acrylate resins 12 parts, polyether modified silicon oil 10 parts, essence of Niobe 12 parts, tricaprylin 12 parts, phosphate ester 10 parts, 12 parts of transformer oil, eucalyptus oil 12 parts, Bravo 10 parts, cetyl Trimethylammonium bromide 10 parts, tea polyphenols 10 parts, 12 parts of blanc fixe powder, 10 parts of lead iodate powder, vermiculite power 8 parts, dolomite 8 parts of 12 parts of powder, sodium iodoacetate 10 parts, modified attapulgite powder end, pearl essence 10 parts, silicon powder 8 parts, three cumene of phosphoric acid Ester 8 parts, trichloroethyl phosphate 10 parts, ammonium polyphosphate 10 parts, Tissuemat E 10 parts, nitrocotton 10 parts, butyl stearate 10 parts, Isopropyl thioxanthone 10 parts, decahydronaphthalenes 10 parts, ethyleneglycol dimethyacrylate 10 parts, alkyl benzene sulphonate 8 parts.
Further, above-mentioned digit printing fabric flame-proof antibiotic preparation method for coating step is as follows:
(1) acrylic acid modified alkyd resin of described mass fraction, a-olefin elastomer, acrylate resins, polyethers are changed Property silicone oil, essence of Niobe, tricaprylin, phosphate ester, transformer oil, eucalyptus oil, Bravo, cetyl trimethyl bromine Change ammonium, tea polyphenols, blanc fixe powder, lead iodate powder, vermiculite power, dolomite powder, sodium iodoacetate, modified attapulgite powder End, pearl essence, silicon powder are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 20～40KHz, rate of dispersion 5000～ About 5400r/min, jitter time is 30～60min；
(2) IPPP of described mass fraction, trichloroethyl phosphate, ammonium polyphosphate, polyethylene are added Wax, nitrocotton, ultrasonic high speed dispersion, ultrasonic frequency is 20～35KHz, rate of dispersion 4800～about 5200r/min, dispersion Time is 30～50min；
(3) butyl stearate of described mass fraction, isopropyl thioxanthone, decahydronaphthalenes, methacrylate are added Glycol ester, alkyl benzene sulphonate, ultrasonic high speed dispersion, ultrasonic frequency is 20～30KHz, rate of dispersion 4600～4800r/ About min, jitter time is 20～40min；This product is prepared after mix homogeneously.
This beneficial effect of the invention is: the digit printing fabric flame-proof antibiotic coating in the present invention, by following components group Become: acrylic acid modified alkyd resin, a-olefin elastomer, acrylate resins, polyether modified silicon oil, essence of Niobe, three octanoic acids Glyceride, phosphate ester, transformer oil, eucalyptus oil, Bravo, cetyl trimethylammonium bromide, tea polyphenols, blanc fixe powder End, lead iodate powder, vermiculite power, dolomite powder, sodium iodoacetate, modified attapulgite powder end, pearl essence, silicon powder, phosphoric acid Triisopropyl phenyl ester, trichloroethyl phosphate, ammonium polyphosphate, Tissuemat E, nitrocotton, butyl stearate, isopropyl thioxanthone anthracene Ketone, decahydronaphthalenes, ethyleneglycol dimethyacrylate, alkyl benzene sulphonate.Product of the present invention has the most superior fire-retardant, acidproof Alkali, anti-mildew anti-microbial property, improve properties of product.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is described, in order to be better understood from the present invention.
Embodiment 1
Digit printing fabric flame-proof antibiotic coating in the present embodiment, is made up of the component of following mass fraction: acrylic acid Modified alkyd resin 10 parts, a-olefin elastomer 8 parts, acrylate resins 8 parts, polyether modified silicon oil 6 parts, essence of Niobe 8 parts, Tricaprylin 8 parts, phosphate ester 6 parts, 8 parts of transformer oil, eucalyptus oil 8 parts, Bravo 6 parts, cetyl trimethyl bromination Ammonium 6 parts, tea polyphenols 6 parts, 8 parts of blanc fixe powder, 6 parts of lead iodate powder, vermiculite power 4 parts, 8 parts of dolomite powder, iodoacetic acid 4 parts of 6 parts of sodium, modified attapulgite powder end, pearl essence 6 parts, silicon powder 4 parts, IPPP 4 parts, tricresyl phosphate chloroethene Ester 6 parts, ammonium polyphosphate 6 parts, Tissuemat E 6 parts, nitrocotton 6 parts, butyl stearate 6 parts, isopropyl thioxanthone 6 parts, ten Hydrogenated naphthalene 6 parts, ethyleneglycol dimethyacrylate 6 parts, alkyl benzene sulphonate 4 parts.
Above-mentioned digit printing fabric flame-proof antibiotic preparation method for coating step is as follows:
(1) acrylic acid modified alkyd resin of described mass fraction, a-olefin elastomer, acrylate resins, polyethers are changed Property silicone oil, essence of Niobe, tricaprylin, phosphate ester, transformer oil, eucalyptus oil, Bravo, cetyl trimethyl bromine Change ammonium, tea polyphenols, blanc fixe powder, lead iodate powder, vermiculite power, dolomite powder, sodium iodoacetate, modified attapulgite powder End, pearl essence, silicon powder are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 20kHz, and rate of dispersion 5400r/min is left The right side, jitter time is 60min；
(2) IPPP of described mass fraction, trichloroethyl phosphate, ammonium polyphosphate, polyethylene are added Wax, nitrocotton, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 5200r/min, and jitter time is 50min；
(3) butyl stearate of described mass fraction, isopropyl thioxanthone, decahydronaphthalenes, methacrylate are added Glycol ester, alkyl benzene sulphonate, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 4800r/min, dispersion Time is 40min；This product is prepared after mix homogeneously.
Embodiment 2
Digit printing fabric flame-proof antibiotic coating in the present embodiment, is made up of the component of following mass fraction: acrylic acid Modified alkyd resin 12 parts, a-olefin elastomer 10 parts, acrylate resins 10 parts, polyether modified silicon oil 8 parts, essence of Niobe 10 Part, tricaprylin 10 parts, phosphate ester 8 parts, 10 parts of transformer oil, eucalyptus oil 10 parts, Bravo 8 parts, cetyl front three Base ammonium bromide 8 parts, tea polyphenols 8 parts, 10 parts of blanc fixe powder, 8 parts of lead iodate powder, vermiculite power 6 parts, dolomite powder 10 Part, 6 parts of sodium iodoacetate 8 parts, modified attapulgite powder end, pearl essence 8 parts, silicon powder 6 parts, IPPP 6 parts, phosphorus Acid trichloro ethyl ester 8 parts, ammonium polyphosphate 8 parts, Tissuemat E 8 parts, nitrocotton 8 parts, butyl stearate 8 parts, isopropyl thioxanthone anthracene Ketone 8 parts, decahydronaphthalenes 8 parts, ethyleneglycol dimethyacrylate 8 parts, alkyl benzene sulphonate 6 parts.
Above-mentioned digit printing fabric flame-proof antibiotic preparation method for coating step is as follows:
(1) acrylic acid modified alkyd resin of described mass fraction, a-olefin elastomer, acrylate resins, polyethers are changed Property silicone oil, essence of Niobe, tricaprylin, phosphate ester, transformer oil, eucalyptus oil, Bravo, cetyl trimethyl bromine Change ammonium, tea polyphenols, blanc fixe powder, lead iodate powder, vermiculite power, dolomite powder, sodium iodoacetate, modified attapulgite powder End, pearl essence, silicon powder are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 30kHz, and rate of dispersion 5200r/min is left The right side, jitter time is 45min；
(2) IPPP of described mass fraction, trichloroethyl phosphate, ammonium polyphosphate, polyethylene are added Wax, nitrocotton, ultrasonic high speed dispersion, ultrasonic frequency is 27kHz, rate of dispersion about 5000r/min, and jitter time is 40min；
(3) butyl stearate of described mass fraction, isopropyl thioxanthone, decahydronaphthalenes, methacrylate are added Glycol ester, alkyl benzene sulphonate, ultrasonic high speed dispersion, ultrasonic frequency is 25kHz, rate of dispersion about 4700r/min, dispersion Time is 30min；This product is prepared after mix homogeneously.
Embodiment 3
Digit printing fabric flame-proof antibiotic coating in the present embodiment, is made up of the component of following mass fraction: acrylic acid Modified alkyd resin 14 parts, a-olefin elastomer 12 parts, acrylate resins 12 parts, polyether modified silicon oil 10 parts, essence of Niobe 12 parts, tricaprylin 12 parts, phosphate ester 10 parts, 12 parts of transformer oil, eucalyptus oil 12 parts, Bravo 10 parts, cetyl Trimethylammonium bromide 10 parts, tea polyphenols 10 parts, 12 parts of blanc fixe powder, 10 parts of lead iodate powder, vermiculite power 8 parts, dolomite 8 parts of 12 parts of powder, sodium iodoacetate 10 parts, modified attapulgite powder end, pearl essence 10 parts, silicon powder 8 parts, three cumene of phosphoric acid Ester 8 parts, trichloroethyl phosphate 10 parts, ammonium polyphosphate 10 parts, Tissuemat E 10 parts, nitrocotton 10 parts, butyl stearate 10 parts, Isopropyl thioxanthone 10 parts, decahydronaphthalenes 10 parts, ethyleneglycol dimethyacrylate 10 parts, alkyl benzene sulphonate 8 parts.
Above-mentioned digit printing fabric flame-proof antibiotic preparation method for coating step is as follows:
(1) acrylic acid modified alkyd resin of described mass fraction, a-olefin elastomer, acrylate resins, polyethers are changed Property silicone oil, essence of Niobe, tricaprylin, phosphate ester, transformer oil, eucalyptus oil, Bravo, cetyl trimethyl bromine Change ammonium, tea polyphenols, blanc fixe powder, lead iodate powder, vermiculite power, dolomite powder, sodium iodoacetate, modified attapulgite powder End, pearl essence, silicon powder are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 40kHz, rate of dispersion 5000r/min, point The scattered time is 30min；
(2) IPPP of described mass fraction, trichloroethyl phosphate, ammonium polyphosphate, polyethylene are added Wax, nitrocotton, ultrasonic high speed dispersion, ultrasonic frequency is 35kHz, rate of dispersion 4800r/min, and jitter time is 30min；
(3) butyl stearate of described mass fraction, isopropyl thioxanthone, decahydronaphthalenes, methacrylate are added Glycol ester, alkyl benzene sulphonate, ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion about 4600r/min, dispersion Time is 20min；This product is prepared after mix homogeneously.
Performance measurement is carried out for the product in embodiment 1, embodiment 2 and embodiment 3 and certain commercially available prod, measured Data are as shown in table 1.Fire protection flame retarding level estimate uses UL94 standard.
Table 1 the performance test results
Visible, product of the present invention has the most corrosion-resistant, fire protection flame retarding, anti-mildew, anti-microbial property.
The above is the preferred embodiment of the present invention, it is noted that for those skilled in the art For, under the premise without departing from the principles of the invention, it is also possible to make some improvements and modifications, these improvements and modifications are also considered as Protection scope of the present invention.

Claims (5)

1. a digit printing fabric flame-proof antibiotic coating, it is characterised in that: it is made up of the component of following mass fraction: acrylic acid Modified alkyd resin 10～14 parts, a-olefin elastomer 8～12 parts, acrylate resins 8～12 parts, polyether modified silicon oil 6～10 Part, essence of Niobe 8～12 parts, tricaprylin 8～12 parts, phosphate ester 6～10 parts, transformer oil 8～12 parts, eucalyptus oil 8～12 parts, Bravo 6～10 parts, cetyl trimethylammonium bromide 6～10 parts, tea polyphenols 6～10 parts, blanc fixe powder 8 ～12 parts, lead iodate powder 6～10 parts, vermiculite power 4～8 parts, dolomite powder 8～12 parts, sodium iodoacetate 6～10 parts, modification Attapulgite powder 4～8 parts, pearl essence 6～10 parts, silicon powder 4～8 parts, IPPP 4～8 parts, phosphoric acid trichlorine Ethyl ester 6～10 parts, ammonium polyphosphate 6～10 parts, Tissuemat E 6～10 parts, nitrocotton 6～10 parts, butyl stearate 6～10 Part, isopropyl thioxanthone 6～10 parts, decahydronaphthalenes 6～10 parts, ethyleneglycol dimethyacrylate 6～10 parts, benzene sulfonamide Acid 4～8 parts.
Digit printing fabric flame-proof antibiotic coating the most according to claim 1, it is characterised in that: described digit printing fabric Flame-proof antibiotic coating is made up of the component of following mass fraction: acrylic acid modified alkyd resin 10 parts, a-olefin elastomer 8 parts, Acrylate resins 8 parts, polyether modified silicon oil 6 parts, essence of Niobe 8 parts, tricaprylin 8 parts, phosphate ester 6 parts, transformator Oil 8 parts, eucalyptus oil 8 parts, Bravo 6 parts, cetyl trimethylammonium bromide 6 parts, tea polyphenols 6 parts, 8 parts of blanc fixe powder, 6 parts of lead iodate powder, vermiculite power 4 parts, 8 parts of dolomite powder, sodium iodoacetate 6 parts, modified attapulgite powder end 4 parts, pearl essence 6 Part, silicon powder 4 parts, IPPP 4 parts, trichloroethyl phosphate 6 parts, ammonium polyphosphate 6 parts, Tissuemat E 6 parts, nitre Change cotton 6 parts, butyl stearate 6 parts, isopropyl thioxanthone 6 parts, decahydronaphthalenes 6 parts, ethyleneglycol dimethyacrylate 6 parts, Alkyl benzene sulphonate 4 parts.
3. according to the digit printing fabric flame-proof antibiotic coating described in claim 1 to 2, it is characterised in that: described digit printing Fabric flame-proof antibiotic coating is made up of the component of following mass fraction: acrylic acid modified alkyd resin 12 parts, a-olefin elastomer 10 parts, acrylate resins 10 parts, polyether modified silicon oil 8 parts, essence of Niobe 10 parts, tricaprylin 10 parts, phosphate ester 8 Part, 10 parts of transformer oil, eucalyptus oil 10 parts, Bravo 8 parts, cetyl trimethylammonium bromide 8 parts, tea polyphenols 8 parts, barite 10 parts of powder powder, 8 parts of lead iodate powder, vermiculite power 6 parts, 10 parts of dolomite powder, sodium iodoacetate 8 parts, modified attapulgite powder End 6 parts, pearl essence 8 parts, silicon powder 6 parts, IPPP 6 parts, trichloroethyl phosphate 8 parts, ammonium polyphosphate 8 parts, Tissuemat E 8 parts, nitrocotton 8 parts, butyl stearate 8 parts, isopropyl thioxanthone 8 parts, decahydronaphthalenes 8 parts, double metering system Acid glycol ester 8 parts, alkyl benzene sulphonate 6 parts.
4. according to the digit printing fabric flame-proof antibiotic coating described in claims 1 to 3, it is characterised in that: described digit printing Fabric flame-proof antibiotic coating is made up of the component of following mass fraction: acrylic acid modified alkyd resin 14 parts, a-olefin elastomer 12 parts, acrylate resins 12 parts, polyether modified silicon oil 10 parts, essence of Niobe 12 parts, tricaprylin 12 parts, phosphate ester 10 Part, 12 parts of transformer oil, eucalyptus oil 12 parts, Bravo 10 parts, cetyl trimethylammonium bromide 10 parts, tea polyphenols 10 parts, weight 12 parts of spar powder powder, 10 parts of lead iodate powder, vermiculite power 8 parts, 12 parts of dolomite powder, sodium iodoacetate 10 parts, modified concavo-convex Rod soil 8 parts of powder, pearl essence 10 parts, silicon powder 8 parts, IPPP 8 parts, trichloroethyl phosphate 10 parts, poly phosphorus Acid ammonium 10 parts, Tissuemat E 10 parts, nitrocotton 10 parts, butyl stearate 10 parts, isopropyl thioxanthone 10 parts, decahydronaphthalenes 10 Part, ethyleneglycol dimethyacrylate 10 parts, alkyl benzene sulphonate 8 parts.
Digit printing fabric flame-proof antibiotic coating the most according to claim 1, it is characterised in that: described digit printing fabric Flame-proof antibiotic preparation method for coating step is as follows:
(1) by the acrylic acid modified alkyd resin of described mass fraction, a-olefin elastomer, acrylate resins, polyether-modified silicon Oil, essence of Niobe, tricaprylin, phosphate ester, transformer oil, eucalyptus oil, Bravo, cetyl trimethyl bromination Ammonium, tea polyphenols, blanc fixe powder, lead iodate powder, vermiculite power, dolomite powder, sodium iodoacetate, modified attapulgite powder End, pearl essence, silicon powder are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 20～40KHz, rate of dispersion about 5000～ 5400r/min, jitter time is 30～about 60min；
(2) IPPP of described mass fraction, trichloroethyl phosphate, ammonium polyphosphate, Tissuemat E, nitre are added Changing cotton, ultrasonic high speed dispersion, ultrasonic frequency is 20～35KHz, and rate of dispersion is about 4800～5200r/min, jitter time It is 30～about 50min；
(3) butyl stearate of described mass fraction, isopropyl thioxanthone, decahydronaphthalenes, methacrylate second two are added Alcohol ester, alkyl benzene sulphonate, ultrasonic high speed dispersion, ultrasonic frequency is 20～30KHz, and rate of dispersion is about 4600～4800r/ Min, jitter time is 20～about 40min；This product is prepared after mix homogeneously.
CN201610616615.6A 2016-07-29 2016-07-29 A kind of digit printing fabric flame-proof antibiotic coating Pending CN106118405A (en)