CN106398647B - A kind of artificial greasy dirt and preparation method thereof of simulation metal cleaning - Google Patents
A kind of artificial greasy dirt and preparation method thereof of simulation metal cleaning Download PDFInfo
- Publication number
- CN106398647B CN106398647B CN201610742682.2A CN201610742682A CN106398647B CN 106398647 B CN106398647 B CN 106398647B CN 201610742682 A CN201610742682 A CN 201610742682A CN 106398647 B CN106398647 B CN 106398647B
- Authority
- CN
- China
- Prior art keywords
- parts
- greasy dirt
- machine oil
- artificial greasy
- metal cleaning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to artificial greasy dirt cleaning technology fields, are specifically related to a kind of artificial greasy dirt and preparation method thereof of simulation metal cleaning.Raw material group becomes barium mahogany sulfonate 1-30 parts, 1-20 parts of 20# machine oil, 1-25 parts of 30# machine oil, 1-20 parts of 32# machine oil, 1-15 parts of 40# machine oil, 1-20 parts of vaseline, 1-12 parts of graphite powder, 5-60 parts of salad oil.Weighing salad oil, barium mahogany sulfonate, machine oil and being mixed keeps it uniformly mixed, obtains a homogeneous mixture；Vaseline is added after heating and is stirred evenly；Graphite powder is added later, is aged to obtain artificial greasy dirt again after stirring.The present invention can be common in true simulation metal cleaning greasy dirt.It can really, objectively reflect the dirt-removing power of different metal cleaners, and can be used for formulating national standard or professional standard.
Description
Technical field
The present invention relates to artificial greasy dirt cleaning technology field, be specifically related to a kind of simulation metal cleaning artificial greasy dirt and
Preparation method.
Background technique
In order to keep the test method of metal cleaner accurate and effective, it is therefore necessary to which developing one kind being capable of true simulation gold
Belong to the artificial greasy dirt of common spot in cleaning.Artificial greasy dirt is consistent with practical greasy dirt, has in test operability, passes through
Metal cleaner washing removal falls off uniformly, and data reproduction and collimation will be got well, the quantitative reaction ability of cleaning greasy dirt of energy.
Summary of the invention
The purpose of the present invention is to provide a kind of artificial greasy dirts and preparation method thereof of simulation metal cleaning, can be truly
Greasy dirt common in metal cleaning is simulated, and can really, objectively reflect the dirt-removing power of different metal cleaners.
To achieve the above object, the invention adopts the following technical scheme:
A kind of artificial greasy dirt of simulation metal cleaning, according to parts by weight meter, raw material composition are as follows:
Preferably, the artificial greasy dirt of simulation metal cleaning, according to parts by weight meter, raw material composition are as follows:
It is further preferred that the artificial greasy dirt of simulation metal cleaning, according to parts by weight meter, raw material composition are as follows:
The preparation method of the artificial greasy dirt of metal cleaning is simulated, steps are as follows:
A. salad oil, barium mahogany sulfonate, 20# machine oil, 30# machine oil, 32# machine oil, the mixing of 40# machine oil are weighed, stirring makes it
It is uniformly mixed, obtains a homogeneous mixture 1；
B. when the homogeneous mixture 1 is heated to 40-60 DEG C, vaseline is added and is simultaneously stirred, until uniform, obtains
To mixture 2；The revolving speed of the stir process is that 1000-1200 turns/min, time 10-30min；
C. graphite powder will be added in obtained mixture 2, is stirred 10-30min, revolving speed be 800-1000 turn/
Min, then carry out ripening for 24 hours, obtain artificial greasy dirt.
Beneficial effects of the present invention are shown:
1, the greasy dirt that the present invention can be common in true simulation metal cleaning.
2, the present invention can really, objectively reflect the dirt-removing power of different metal cleaners, and can be used for formulating
National standard or professional standard.
3, preparation method of the invention is easy to operate, and experimental repeatability and reproducibility are good.
Specific embodiment
Below with reference to embodiment, the present invention is described in detail.But embodiment content is only to this hair
Bright example and explanation, affiliated those skilled in the art do various repair to described specific embodiment
Change or supplement or be substituted in a similar manner, as long as it does not deviate from the concept of invention or surmounts defined in the claims
Range is within the scope of protection of the invention.
Embodiment 1
A kind of artificial greasy dirt of simulation metal cleaning, according to parts by weight meter, raw material composition are as follows:
The preparation method of the artificial greasy dirt of metal cleaning is simulated, steps are as follows:
A. salad oil, barium mahogany sulfonate, 20# machine oil, 30# machine oil, 32# machine oil, the mixing of 40# machine oil are weighed, stirring makes it
It is uniformly mixed, obtains a homogeneous mixture 1；
B. when the homogeneous mixture 1 is heated to 40 DEG C, vaseline is added and is simultaneously stirred, until uniform, obtains
Mixture 2；The revolving speed of the stir process is 1000 turns/min, time 30min；
C. graphite powder being added in obtained mixture 2, is stirred 30min, revolving speed is 1000 turns/min, then into
Row ripening for 24 hours, obtains artificial greasy dirt, refrigerates spare.
Embodiment 2
A kind of artificial greasy dirt of simulation metal cleaning, according to parts by weight meter, raw material composition are as follows:
The preparation method of the artificial greasy dirt of metal cleaning is simulated, steps are as follows:
A. salad oil, barium mahogany sulfonate, 20# machine oil, 30# machine oil, 32# machine oil, the mixing of 40# machine oil are weighed, stirring makes it
It is uniformly mixed, obtains a homogeneous mixture 1；
B. when the homogeneous mixture 1 is heated to 60 DEG C, vaseline is added and is simultaneously stirred, until uniform, obtains
Mixture 2；The revolving speed of the stir process is 1200 turns/min, time 10min；
C. graphite powder being added in obtained mixture 2, is stirred 10min, revolving speed is 800 turns/min, then into
Row ripening for 24 hours, obtains artificial greasy dirt.
Embodiment 3
A kind of artificial greasy dirt of simulation metal cleaning, according to parts by weight meter, raw material composition are as follows:
The preparation method of the artificial greasy dirt of metal cleaning is simulated, steps are as follows:
A. salad oil, barium mahogany sulfonate, 20# machine oil, 30# machine oil, 32# machine oil, the mixing of 40# machine oil are weighed, stirring makes it
It is uniformly mixed, obtains a homogeneous mixture 1；
B. when the homogeneous mixture 1 is heated to 55 DEG C, vaseline is added and is simultaneously stirred, until uniform, obtains
Mixture 2；The revolving speed of the stir process is 1150 turns/min, time 20min；
C. graphite powder being added in obtained mixture 2, is stirred 20min, revolving speed is 900 turns/min, then into
Row ripening for 24 hours, obtains artificial greasy dirt.
Embodiment 4
A kind of artificial greasy dirt of simulation metal cleaning, according to parts by weight meter, raw material composition are as follows:
The preparation method of the artificial greasy dirt of metal cleaning is simulated, steps are as follows:
A. salad oil, barium mahogany sulfonate, 20# machine oil, 30# machine oil, 32# machine oil, the mixing of 40# machine oil are weighed, stirring makes it
It is uniformly mixed, obtains a homogeneous mixture 1；
B. when the homogeneous mixture 1 is heated to 45 DEG C, vaseline is added and is simultaneously stirred, until uniform, obtains
Mixture 2；The revolving speed of the stir process is 1000 turns/min, time 15min；
C. graphite powder being added in obtained mixture 2, is stirred 15min, revolving speed is 800 turns/min, then into
Row ripening for 24 hours, obtains artificial greasy dirt.
Embodiment 5
A kind of artificial greasy dirt of simulation metal cleaning, according to parts by weight meter, raw material composition are as follows:
The preparation method of the artificial greasy dirt of metal cleaning is simulated, steps are as follows:
A. salad oil, barium mahogany sulfonate, 20# machine oil, 30# machine oil, 32# machine oil, the mixing of 40# machine oil are weighed, stirring makes it
It is uniformly mixed, obtains a homogeneous mixture 1；
B. when the homogeneous mixture 1 is heated to 60 DEG C, vaseline is added and is simultaneously stirred, until uniform, obtains
Mixture 2；The revolving speed of the stir process is 1000 turns/min, time 20min；
C. graphite powder being added in obtained mixture 2, is stirred 20min, revolving speed is 1000 turns/min, then into
Row ripening for 24 hours, obtains artificial greasy dirt.
Claims (1)
1. a kind of preparation method of the artificial greasy dirt of simulation metal cleaning, it is characterised in that steps are as follows:
A. 30-50 parts of salad oil, 5-15 parts of barium mahogany sulfonate, 1-5 parts of 20# machine oil, 1-5 parts of 30# machine oil, 32# machine oil 1-5 are weighed
Part, 1-5 parts of 40# machine oil mixing, stirring are uniformly mixed it, obtain a homogeneous mixture 1；
B. it when the homogeneous mixture 1 is heated to 40-60 DEG C, is added vaseline 5-10 parts and is stirred, until uniform,
Obtain mixture 2；The revolving speed of the stir process is that 1000-1200 turns/min, time 10-30min；
C. graphite powder 3-8 part will be added in obtained mixture 2, be stirred 10-30min, revolving speed is 800-1000 turns/
Min, then carry out ripening for 24 hours, obtain artificial greasy dirt.