CN106118192A - A kind of luminous reflecting road mark paint containing tripolycyanamide and preparation method thereof - Google Patents
A kind of luminous reflecting road mark paint containing tripolycyanamide and preparation method thereof Download PDFInfo
- Publication number
- CN106118192A CN106118192A CN201610567544.5A CN201610567544A CN106118192A CN 106118192 A CN106118192 A CN 106118192A CN 201610567544 A CN201610567544 A CN 201610567544A CN 106118192 A CN106118192 A CN 106118192A
- Authority
- CN
- China
- Prior art keywords
- solution
- paint containing
- road mark
- emulsion
- gained
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of luminous reflecting road mark paint containing tripolycyanamide and preparation method thereof, be made up of the raw material of following weight portion: melamine solution 12, GdCl313, glass fibre 12, ethylene glycol 6 10, NaF 13, aqueous polyurethane emulsion 40 50, ethyl acrylate 35, carbon fiber 12, citric acid 13, titanium dioxide 10 15, blanc fixe 10 15, glass microballoon 10 15, emulsion acrylic resin is appropriate, and deionized water is appropriate, appropriate amount of ethanol;Aqueous polyurethane coating disclosed by the invention has saving resource, reduces pollution, the feature of low toxic and environment-friendly, utilizes Study of Nanoscale Rare Earth Luminescent Materials to improve aqueous polyurethane coating luminescent properties simultaneously so that it is is more suitable for the section illuminating effect is bad and applies.
Description
Technical field
The present invention relates to a kind of marking paint, belong to paint field, particularly relate to a kind of luminous reflecting containing tripolycyanamide
Road mark paint and preparation method thereof.
Background technology
Roadmarking is used for guiding traffic, is to improve traffic safety, ensure the unimpeded important infrastructure of road traffic.I
State is stepping up traffic infrastructure level, construction of modern road network, simultaneously being continuously increased along with vehicle, road load
Constantly increasing the weight of with graticule abrasion, these all illustrate that Current traffic gage mark coating has huge market demand.
Wherein water paint is a kind of relatively new type coating on Coating Market, and more traditional solvent-based paints coating comes
Saying, water paint is with water as solvent, and the VOC during producing and using is well below solvent-based paints, to human injury
Little, therefore, water paint is more saved resource, is reduced pollution, low toxic and environment-friendly.Progressively replace solvent-based paints to be coated with water paint
Material represents the developing direction of coating industry.
Aqueous polyurethane is the new polyurethane system using water replacement organic solvent as disperse medium, in its molecular structure
Amido-containing acid ester base, urea bond and ionic bond, cohesive energy is high, and cohesive force is strong, and can be short and soft or hard section by changing soft segment length
Proportion adjustment polyurethane performance, so, exploitation aqueous polyurethane marking paint is a good selection.Wu Mingjiang is at the poly-ammonia of aqueous
The development of ester marking paint utilizes the Material synthesis such as waterborne polyurethane resin and blanc fixe a kind of white marking paint, but
Be that reflective function is the most superior, simultaneously do not possess luminescent properties, limit its in dark location, such as freeway tunnel, with evening
The application of up train.
Rare earth element show because of the electronic structure of its uniqueness excellent monochromaticity, anti-light Bleachability, fluorescence lifetime is long
The characteristic such as big with Stocke displacement and have a wide range of applications in fields such as materials.Rare earth luminescent material has other luminous material
Luminosity height, length persistence not available for material, wavelength of transmitted light is adjustable, the radiationless advantage such as pollution-free, should about it
Research receive the extensive concern of people.
Summary of the invention
Based on above thinking, it is an object of the invention to provide a kind of reflective function good, strong with road adhesive force, construction letter
And there is the aqueous polyurethane road mark paint of luminescent properties just,.
The technical problem to be solved uses following technical scheme to realize:
1. the luminous reflecting road mark paint containing tripolycyanamide aqueous, it is characterised in that by the raw material of following weight portion
Make:
Melamine solution 1-2, GdCl31-3, glass fibre 1-2, ethylene glycol 6-10, NaF 1-3, aqueous polyurethane emulsion
40-50, ethyl acrylate 3-5, carbon fiber 1-2, citric acid 1-3, titanium dioxide 10-15, blanc fixe 10-15, glass microballoon
10-15, emulsion acrylic resin is appropriate, and deionized water is appropriate, appropriate amount of ethanol;
The content of described aqueous polyurethane emulsion is 40-50%, and emulsion acrylic resin solid content is 20-40%, and tripolycyanamide is molten
Liquid solvent is methanol, and content is 10-30%.
2. a kind of luminous reflecting road mark paint containing tripolycyanamide aqueous described in and preparation method thereof, its feature
It is, is made up of following steps:
A. by GdCl3It is dissolved in 3-5 part ethylene glycol solution, stirs to clarify solution;
B. NaF is dissolved in residue ethylene glycol solution, after stirring to clarify solution, mixes with step a gained settled solution rapidly
Close, stir;
C. in step b gained liquid, add sodium lauryl sulphate, move in reactor, put in 150-200 DEG C of baking oven
20-25h。
D. take out reactor after having reacted, be cooled to room temperature, after separating with centrifuge, be filtrated to get precipitation, point
Yong deionized water and washing with alcohol not precipitate 3-5 time;
E. it is dried 20-25h under the conditions of step d gained being deposited in 40-80 DEG C, obtains intermediate;
F. glass fibre, carbon fiber, titanium dioxide, blanc fixe, glass microballoon are put in ball mill ball milling uniformly after, use second
Alcoholic solution ultrasonic disperse, after drying, sprays to its surface with emulsion acrylic resin, after continuously stirred 10-30min, dry
Dry, obtain mixture.
G. hydrotropism's polyaminoester emulsion adds step e gained intermediate, step f gained mixture and ethyl acrylate,
Melamine solution, citric acid, stir.
3. a kind of luminous reflecting road mark paint containing tripolycyanamide aqueous described in and preparation method thereof, its feature
Being, reactor used by step b is polytetrafluoroethyllining lining stainless steel cauldron, and capacity is 15-25mL.
4. a kind of luminous reflecting road mark paint containing tripolycyanamide aqueous described in and preparation method thereof, its feature
It is that centrifuge speed used by step c is 5000-10000r/min, centrifugal 10-15min.
The invention has the beneficial effects as follows: aqueous polyurethane coating disclosed by the invention have saving resource, reduce pollute, low
The feature that poison ring is protected, utilizes Study of Nanoscale Rare Earth Luminescent Materials to improve aqueous polyurethane coating luminescent properties so that it is to be more suitable for simultaneously
In the section application that illuminating effect is bad, reduce road safety hidden danger, ensured pedestrian and vehicle safety, and, add anti-
The glass microballoon that light effect is good, can obtain higher glistening intensity.This coating glue viscosity is good, and ageing resistance is excellent, easy construction,
Less demanding to the cleaning degree of drying on road surface during construction, it is generally applicable to various road surface, there is good promotional value;With third
Olefin(e) acid resin emulsion processes inorganic matter raw material, enhances the mobility between raw material and masking liquid and amalgamation, thus improves painting
The adhesive force of material;Coordinate and with the addition of tripolycyanamide, add stickiness and toughness, the water resistance of coating.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below knot
Close specific embodiment, the present invention is expanded on further.
Embodiment
A kind of luminous reflecting road mark paint containing tripolycyanamide aqueous, it is characterised in that former by following weight portion
Material is made:
Melamine solution 2, GdCl33, glass fibre 2, ethylene glycol 10, NaF 3, aqueous polyurethane emulsion 50, acrylic acid second
Ester 5, carbon fiber 2, citric acid 3, titanium dioxide 15, blanc fixe 15, glass microballoon 15, emulsion acrylic resin is appropriate, deionization
Water is appropriate, appropriate amount of ethanol;
The content of described aqueous polyurethane emulsion is 40-50%, and emulsion acrylic resin solid content is 20-40%, and tripolycyanamide is molten
Liquid solvent is methanol, and content is 10-30%.
Described a kind of luminous reflecting road mark paint containing tripolycyanamide aqueous and preparation method thereof, its feature exists
In, it is made up of following steps:
A. by GdCl3It is dissolved in 3-5 part ethylene glycol solution, stirs to clarify solution;
B. NaF is dissolved in residue ethylene glycol solution, after stirring to clarify solution, mixes with step a gained settled solution rapidly
Close, stir;
C. in step b gained liquid, add sodium lauryl sulphate, move in reactor, put in 150-200 DEG C of baking oven
20-25h。
D. take out reactor after having reacted, be cooled to room temperature, after separating with centrifuge, be filtrated to get precipitation, point
Yong deionized water and washing with alcohol not precipitate 3-5 time;
E. it is dried 20-25h under the conditions of step d gained being deposited in 40-80 DEG C, obtains intermediate;
F. glass fibre, carbon fiber, titanium dioxide, blanc fixe, glass microballoon are put in ball mill ball milling uniformly after, use second
Alcoholic solution ultrasonic disperse, after drying, sprays to its surface with emulsion acrylic resin, after continuously stirred 10-30min, dry
Dry, obtain mixture.
G. hydrotropism's polyaminoester emulsion adds step e gained intermediate, step f gained mixture and ethyl acrylate,
Melamine solution, citric acid, stir.
Described a kind of luminous reflecting road mark paint containing tripolycyanamide aqueous and preparation method thereof, its feature exists
In, reactor used by step b is polytetrafluoroethyllining lining stainless steel cauldron, and capacity is 15-25mL.
Described a kind of luminous reflecting road mark paint containing tripolycyanamide aqueous and preparation method thereof, it is characterised in that
Centrifuge speed used by step c is 5000-10000r/min, centrifugal 10-15min.
This coating property:
Outward appearance: do not lump, it is easy to stirring;
Workability: good;
Do not glue tire drying time :≤15min.
Claims (4)
1. the luminous reflecting road mark paint containing tripolycyanamide aqueous, it is characterised in that by the raw material of following weight portion
Make:
Melamine solution 1-2, GdCl31-3, glass fibre 1-2, ethylene glycol 6-10, NaF 1-3, aqueous polyurethane emulsion 40-
50, ethyl acrylate 3-5, carbon fiber 1-2, citric acid 1-3, titanium dioxide 10-15, blanc fixe 10-15, glass microballoon 10-
15, emulsion acrylic resin is appropriate, and deionized water is appropriate, appropriate amount of ethanol;
The content of described aqueous polyurethane emulsion is 40-50%, and emulsion acrylic resin solid content is 20-40%, and tripolycyanamide is molten
Liquid solvent is methanol, and content is 10-30%.
A kind of luminous reflecting road mark paint containing tripolycyanamide aqueous the most according to claim 1 and preparation side thereof
Method, it is characterised in that be made up of following steps:
A. by GdCl3It is dissolved in 3-5 part ethylene glycol solution, stirs to clarify solution;
B. NaF is dissolved in residue ethylene glycol solution, after stirring to clarify solution, mixes with step a gained settled solution rapidly
Close, stir;
C. in step b gained liquid, add sodium lauryl sulphate, move in reactor, put in 150-200 DEG C of baking oven
20-25h;
D. take out reactor after having reacted, be cooled to room temperature, after separating with centrifuge, be filtrated to get precipitation, use respectively
Deionized water and washing with alcohol precipitate 3-5 time;
E. it is dried 20-25h under the conditions of step d gained being deposited in 40-80 DEG C, obtains intermediate;
F. glass fibre, carbon fiber, titanium dioxide, blanc fixe, glass microballoon are put in ball mill ball milling uniformly after, use second
Alcoholic solution ultrasonic disperse, after drying, sprays to its surface with emulsion acrylic resin, after continuously stirred 10-30min, dry
Dry, obtain mixture;
G., hydrotropism's polyaminoester emulsion adds step e gained intermediate, step f gained mixture and ethyl acrylate, trimerization
Cyanamide solution, citric acid, stir.
A kind of luminous reflecting road mark paint containing tripolycyanamide aqueous the most according to claim 2 and preparation side thereof
Method, it is characterised in that reactor used by step b is polytetrafluoroethyllining lining stainless steel cauldron, capacity is 15-25mL.
A kind of luminous reflecting road mark paint containing tripolycyanamide aqueous the most according to claim 2 and preparation side thereof
Method, it is characterised in that centrifuge speed used by step c is 5000-10000r/min, centrifugal 10-15min.