CN105925032A - High-adhesion road marking paint and preparation method thereof - Google Patents
High-adhesion road marking paint and preparation method thereof Download PDFInfo
- Publication number
- CN105925032A CN105925032A CN201610528667.8A CN201610528667A CN105925032A CN 105925032 A CN105925032 A CN 105925032A CN 201610528667 A CN201610528667 A CN 201610528667A CN 105925032 A CN105925032 A CN 105925032A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- preparation
- good
- gained
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-adhesion road marking paint and a preparation method thereof. The invention is characterized in that the high-adhesion road marking paint is prepared from the following raw materials in parts by weight: 1-3 parts of aluminum oxide, 1-3 parts of GdCl3, 6-10 parts of ethanediol, 1-2 parts of zirconium oxide, 1-3 parts of NaF, 40-50 parts of water-based polyurethane emulsion, 3-5 parts of ethyl acrylate, 1-2 parts of corundum, 1-3 parts of citric acid, 10-15 parts of titanium white, 10-15 parts of barite powder, 10-15 parts of glass microballoon, a right amount of deionized water and a right amount of ethanol. The water-based polyurethane paint disclosed by the invention has the characteristics of resource saving, lower pollution, low toxicity and environment friendliness. The rare-earth nano luminescent material is utilized to improve the luminescence of the water-based polyurethane paint, so that the water-based polyurethane paint is more suitable for use on roads with poor illuminating effect, thereby lowering the road potential safety hazard. The aluminum oxide and corundum are matched and added to enhance the adhesion strength and mechanical strength of the paint.
Description
Technical field
The present invention relates to a kind of marking paint, belong to paint field, particularly relate to good road mark paint of a kind of cohesiveness and preparation method thereof.
Background technology
Roadmarking is used for guiding traffic, is to improve traffic safety, ensure the unimpeded important infrastructure of road traffic.China is stepping up traffic infrastructure level, construction of modern road network, simultaneously being continuously increased along with vehicle, road load and graticule abrasion and is constantly increasing the weight of, and these all illustrate that Current traffic gage mark coating has huge market demand.
Wherein water paint is a kind of relatively new type coating on Coating Market, and for more traditional solvent-based paints coating, water paint is with water as solvent, during producing and using
VOC is well below solvent-based paints, little to human injury, and therefore, water paint is more saved resource, reduced pollution, low toxic and environment-friendly.Progressively replace solvent-based paints coating to represent the developing direction of coating industry with water paint.
Aqueous polyurethane is to replace organic solvent as the new polyurethane system of decentralized medium using water, amido-containing acid ester base, urea bond and ionic bond in its molecular structure, cohesive energy is high, cohesive force is strong, and can be by changing the short proportion adjustment polyurethane performance with soft or hard section of soft segment length, so, exploitation aqueous polyurethane marking paint is a good selection.Wu Mingjiang utilizes the Material synthesis such as waterborne polyurethane resin and blanc fixe a kind of white marking paint in the development of aqueous polyurethane marking paint, but reflective function is the most superior, do not possesses luminescent properties simultaneously, limit it in dark location, such as freeway tunnel, and the application of driving in evening.
Rare earth element show because of the electronic structure of its uniqueness excellent monochromaticjty, anti-light Bleachability, fluorescence lifetime length and
The characteristics such as Stocke displacement is big and have a wide range of applications in fields such as materials.Rare earth luminescent material has luminosity height, length persistence not available for other luminescent material, wavelength of transmitted light is adjustable, the radiationless advantage such as pollution-free, receives the extensive concern of people about its research applied.
Summary of the invention
Based on above thinking, it is an object of the invention to provide a kind of reflective function good, strong with road adhesive force, easy construction, and there is the aqueous polyurethane road mark paint of luminescent properties.
The technical problem to be solved uses following technical scheme to realize:
1. the road mark paint that a cohesiveness is good, it is characterised in that be made up of the raw material of following weight portion:
Alundum (Al2O3) 1-3, GdCl3
1-3, ethylene glycol 6-10, zirconium oxide 1-2, NaF 1-3, aqueous polyurethane emulsion 40-50, ethyl acrylate 3-5, diamond dust 1-2, citric acid 1-3, titanium dioxide 10-15, blanc fixe 10-15, glass microballoon 10-15, deionized water is appropriate, appropriate amount of ethanol;
The content of described aqueous polyurethane emulsion is 40-50%.
2. road mark paint that a kind of cohesiveness described in is good and preparation method thereof, it is characterised in that be made up of following steps:
a.
By GdCl3It is dissolved in 3-5 part ethylene glycol solution, stirs to clarify solution;
B. NaF is dissolved in residue ethylene glycol solution, after stirring to clarify solution, mixes with step a gained settled solution rapidly, stir;
c.
In step b gained liquid, add lauryl sodium sulfate, move in reactor, put into 20-25h in 150-200 DEG C of baking oven.
d.
Take out reactor after having reacted, be cooled to room temperature, after separating with centrifuge, be filtrated to get precipitation, precipitate 3-5 time with deionized water and ethanol washing respectively;
e.
It is dried 20-25h under the conditions of step d gained is deposited in 40-80 DEG C, obtains intermediate;
F. alundum (Al2O3), titanium dioxide, zirconium oxide, blanc fixe, diamond dust, glass microballoon are put in ball mill ball milling uniformly after, use ethanol solution ultrasonic disperse, be dried, obtain mixture.
G., hydrotropism's polyaminoester emulsion adds step e gained intermediate, step f gained mixture and ethyl acrylate, citric acid, stirs.
3. road mark paint that a kind of cohesiveness described in is good and preparation method thereof, it is characterised in that reactor used by step b is polytetrafluoroethyllining lining stainless steel cauldron, and capacity is 15-25mL.
4. road mark paint that a kind of cohesiveness described in is good and preparation method thereof, it is characterised in that centrifuge speed used by step c is 5000-10000r/min, centrifugal 10-15min.
The invention has the beneficial effects as follows:Aqueous polyurethane coating disclosed by the invention has saving resource, reduces pollution, the feature of low toxic and environment-friendly, utilize Study of Nanoscale Rare Earth Luminescent Materials to improve aqueous polyurethane coating luminescent properties simultaneously, its section being more suitable for illuminating effect is bad is made to apply, reduce road safety hidden danger, pedestrian and vehicle safety are ensured, further, add the glass microballoon that reflecting effect is good, higher glistening intensity can be obtained.This coating glue viscosity is good, and ageing resistance is excellent, easy construction, less demanding to the cleaning degree of drying on road surface during construction, is generally applicable to various road surface, has good promotional value;Coordinate and with the addition of alundum (Al2O3) and diamond dust, add bond strength and the mechanical strength of coating.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below in conjunction with specific embodiment, the present invention is expanded on further.
Embodiment
The road mark paint that a kind of cohesiveness is good, it is characterised in that be made up of the raw material of following weight portion:
Alundum (Al2O3) 3, GdCl3
3, ethylene glycol 10, zirconium oxide 2, NaF 3, aqueous polyurethane emulsion 50, ethyl acrylate 5, diamond dust 2, citric acid 3, titanium dioxide 15, blanc fixe 15, glass microballoon 15, deionized water is appropriate, appropriate amount of ethanol;
The content of described aqueous polyurethane emulsion is 40-50%.
Road mark paint that described a kind of cohesiveness is good and preparation method thereof, it is characterised in that be made up of following steps:
a.
By GdCl3It is dissolved in 3-5 part ethylene glycol solution, stirs to clarify solution;
B. NaF is dissolved in residue ethylene glycol solution, after stirring to clarify solution, mixes with step a gained settled solution rapidly, stir;
c.
In step b gained liquid, add lauryl sodium sulfate, move in reactor, put into 20-25h in 150-200 DEG C of baking oven.
d.
Take out reactor after having reacted, be cooled to room temperature, after separating with centrifuge, be filtrated to get precipitation, precipitate 3-5 time with deionized water and ethanol washing respectively;
e.
It is dried 20-25h under the conditions of step d gained is deposited in 40-80 DEG C, obtains intermediate;
F. alundum (Al2O3), titanium dioxide, zirconium oxide, blanc fixe, diamond dust, glass microballoon are put in ball mill ball milling uniformly after, use ethanol solution ultrasonic disperse, be dried, obtain mixture.
G., hydrotropism's polyaminoester emulsion adds step e gained intermediate, step f gained mixture and ethyl acrylate, citric acid, stirs.
Road mark paint that described a kind of cohesiveness is good and preparation method thereof, it is characterised in that reactor used by step b is polytetrafluoroethyllining lining stainless steel cauldron, capacity is 15-25mL.
Road mark paint that described a kind of cohesiveness is good and preparation method thereof, it is characterised in that centrifuge speed used by step c is 5000-10000r/min, centrifugal 10-15min.
This coating property:
Outward appearance: do not lump, it is easy to stirring;
Workability: good;
Do not glue tire drying time :≤15min.
Claims (4)
1. the road mark paint that a cohesiveness is good, it is characterised in that be made up of the raw material of following weight portion:
Alundum (Al2O3) 1-3, GdCl31-3, ethylene glycol 6-10, zirconium oxide 1-2, NaF 1-3, aqueous polyurethane emulsion 40-50, ethyl acrylate 3-5, diamond dust 1-2, citric acid 1-3, titanium dioxide 10-15, blanc fixe 10-15, glass microballoon 10-15, deionized water is appropriate, appropriate amount of ethanol;
The content of described aqueous polyurethane emulsion is 40-50%.
Road mark paint that a kind of cohesiveness the most according to claim 1 is good and preparation method thereof, it is characterised in that be made up of following steps:
a.
By GdCl3It is dissolved in 3-5 part ethylene glycol solution, stirs to clarify solution;
B. NaF is dissolved in residue ethylene glycol solution, after stirring to clarify solution, mixes with step a gained settled solution rapidly, stir;
c.
In step b gained liquid, add lauryl sodium sulfate, move in reactor, put into 20-25h in 150-200 DEG C of baking oven;
d.
Take out reactor after having reacted, be cooled to room temperature, after separating with centrifuge, be filtrated to get precipitation, precipitate 3-5 time with deionized water and ethanol washing respectively;
e.
It is dried 20-25h under the conditions of step d gained is deposited in 40-80 DEG C, obtains intermediate;
F. alundum (Al2O3), titanium dioxide, zirconium oxide, blanc fixe, diamond dust, glass microballoon are put in ball mill ball milling uniformly after, use ethanol solution ultrasonic disperse, be dried, obtain mixture;
G., hydrotropism's polyaminoester emulsion adds step e gained intermediate, step f gained mixture and ethyl acrylate, citric acid, stirs.
Road mark paint that a kind of cohesiveness the most according to claim 2 is good and preparation method thereof, it is characterised in that reactor used by step b is polytetrafluoroethyllining lining stainless steel cauldron, capacity is 15-25mL.
Road mark paint that a kind of cohesiveness the most according to claim 2 is good and preparation method thereof, it is characterised in that centrifuge speed used by step c is 5000-10000r/min, centrifugal 10-15min.