CN106118191A - A kind of anticracking antiknock car clutch face sheet material is with soaking coating processed - Google Patents
A kind of anticracking antiknock car clutch face sheet material is with soaking coating processed Download PDFInfo
- Publication number
- CN106118191A CN106118191A CN201610562592.5A CN201610562592A CN106118191A CN 106118191 A CN106118191 A CN 106118191A CN 201610562592 A CN201610562592 A CN 201610562592A CN 106118191 A CN106118191 A CN 106118191A
- Authority
- CN
- China
- Prior art keywords
- parts
- face sheet
- sheet material
- clutch face
- anticracking
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of anticracking antiknock car clutch face sheet material and soak coating processed, it is characterized in that: described coating is by mass fraction proportioning: high temperature resistant 472 DEG C of liquid nano resins 80 90 parts, vinyltrimethoxy silane 10 20 parts, isopropanol 10 15 parts, maleic anhydride grafting EVA5 8 parts, white alundum powder 35 parts, prodan 23 parts, molybdenum bisuphide 1 1.5 parts, manganous acid lithium 23 parts, calcium oxide 23 parts, calcium zinc stabilizer 12 parts, the successively coating of mix and blend.Its technique is simple, is suitable to car clutch face sheet manufacture and uses, and can effectively guarantee that internal structure is stable, improve serviceability.
Description
Technical field
The present invention relates to Clutch Technology, a kind of anticracking antiknock car clutch face sheet material is with soaking coating processed.
Background technology
Traditional car clutch face sheet uses riveted type, and dough sheet is riveted on steel disc, bothersome takes a lot of work, and rivet affects
Dough sheet service life and use safety.Existing structure without riveted type, a kind of as disclosed in Patent No. 201210157147.2
Anticracking antiknock car clutch face sheet, is connected with steel disc sulfuration after using the unordered mixing of multiple material, the inside of its mixing compacting
Structural instability, affects serviceability.
Summary of the invention
For above-mentioned deficiency without riveted type structure in prior art, the invention provides a kind of technique simple, be suitable to vapour
Car clutch surface manufacture uses, and can effectively guarantee that internal structure is stable, improve the anticracking antiknock automobile clutch of serviceability
Dough sheet material is with soaking coating processed.
The technical solution used in the present invention is: a kind of anticracking antiknock car clutch face sheet material soaks coating processed, described painting
Mass fraction proportioning pressed by material: high temperature resistant 472 DEG C of liquid nano resin 80-90 parts, vinyltrimethoxy silane 10-20 part, different
Propanol 10-15 part, maleic anhydride grafting EVA5-8 part, white alundum powder 3-5 part, prodan 2-3 part, molybdenum bisuphide 1-1.5
Part, manganous acid lithium 2-3 part, calcium oxide 2-3 part, calcium zinc stabilizer 1-2 part, the successively coating of mix and blend.
The anticracking antiknock car clutch face sheet assembly of the present invention does not damage engine flywheel face and platen face, dough sheet without
Boring, it is not necessary to riveting, service life is long, and its processing technology is simple, prepares recombination line, Compound Fabric, coiling lines and round shape in order
Dough sheet material, effectively guarantees that its internal structure is stable, is conducive to improving usage safety performance and the stability of dough sheet assembly, extends it
Service life.High temperature resistant 472 DEG C of liquid nano resins, vinyltrimethoxy silane, maleic anhydride is used to be grafted EVA, Bai Gang
Beautiful powder, prodan, molybdenum bisuphide, manganous acid lithium are blended prepares Wear-resistant, high-temperature resistant coating, is conducive to improving rubbing of dough sheet structure
Wipe performance, increase the service life.
Detailed description of the invention
The invention will be further described below.
Embodiment one
Mass fraction proportioning pressed by a kind of anticracking antiknock car clutch face sheet material leaching coating processed: high temperature resistant 472 DEG C of liquid nanos
Resin 80 parts, vinyltrimethoxy silane 10 parts, isopropanol 10 parts, maleic anhydride grafting EVA5 part, white alundum powder 3 parts, fluorine
Sodium silicate 2 parts, molybdenum bisuphide 1 part, manganous acid lithium 2 parts, calcium oxide 2 parts, calcium zinc stabilizer 1 part, the successively coating of mix and blend.
A kind of anticracking antiknock car clutch face sheet assembly manufacture method, comprises the following steps:
A. raw material is chosen: FKF compound mineral fiber 22Kg, high-carbon steel wire 8Kg, aromatic polyamide fibre 15Kg, polyacrylonitrile
Fiber 15Kg, resistance to high mill brass wire 5Kg, sepiolite fibre 20Kg and glass fibre 15Kg are woven into the high-strength composite of 4mm
Line, then this line is made into 100Kg, 1 meter of wide Compound Fabric；
B. by above-mentioned 1 meter of wide Compound Fabric coating above-mentioned coating, air-dry to tack-free；
C. with cutter, 1 meter of wide Compound Fabric is cut into every wide for 10mm dough sheet materials, use wrapping machine to be coiled into round shape dough sheet
Material；
D. round shape dough sheet material is put into lower mold, put into steel disc, steel disc positive and negative brushing FH11-128 rubber cement；
E. on steel disc, place into round shape dough sheet material, pressing mold；
F. electric heating warming is to 175 DEG C, opens press, pressure to 30MPa, and insulation, pressurize depanning in 40 minutes, sulfidization molding must be without riveting
Connect examination car clutch face sheet.
Embodiment two
Mass fraction proportioning pressed by a kind of anticracking antiknock car clutch face sheet material leaching coating processed: high temperature resistant 472 DEG C of liquid nanos
Resin 90 parts, vinyltrimethoxy silane 20 parts, isopropanol 15 parts, maleic anhydride grafting EVA8 part, white alundum powder 5 parts, fluorine
Sodium silicate 3 parts, molybdenum bisuphide 1.5 parts, manganous acid lithium 3 parts, calcium oxide 3 parts, calcium zinc stabilizer 2 parts, the successively painting of mix and blend
Material.
A kind of anticracking antiknock car clutch face sheet assembly manufacture method, comprises the following steps:
G. raw material is chosen: FKF compound mineral fiber 22Kg, high-carbon steel wire 8Kg, aromatic polyamide fibre 15Kg, polyacrylonitrile
Fiber 15Kg, resistance to high mill brass wire 5Kg, sepiolite fibre 20Kg and glass fibre 15Kg are woven into the high-strength composite of 4mm
Line, then this line is made into 100Kg, 1 meter of wide Compound Fabric；
A. by above-mentioned 1 meter of wide Compound Fabric coating above-mentioned coating, air-dry to tack-free；
B. with cutter, 1 meter of wide Compound Fabric is cut into every wide for 10mm dough sheet materials, use wrapping machine to be coiled into round shape dough sheet
Material；
C. round shape dough sheet material is put into lower mold, put into steel disc, steel disc positive and negative brushing FH11-128 rubber cement；
D. on steel disc, place into round shape dough sheet material, pressing mold；
E. electric heating warming is to 180 DEG C, opens press, pressure to 35MPa, and insulation, pressurize depanning in 45 minutes, sulfidization molding must be without riveting
Connect examination car clutch face sheet.
Embodiment three
Mass fraction proportioning pressed by a kind of anticracking antiknock car clutch face sheet material leaching coating processed: high temperature resistant 472 DEG C of liquid nanos
Resin 85 parts, vinyltrimethoxy silane 15 parts, isopropanol 12 parts, maleic anhydride grafting EVA6 part, white alundum powder 4 parts, fluorine
Sodium silicate 2.5 parts, molybdenum bisuphide 1.2 parts, manganous acid lithium 2.3 parts, calcium oxide 2.5 parts, calcium zinc stabilizer 1.5 parts, mix successively
The coating of stirring.
A kind of anticracking antiknock car clutch face sheet assembly manufacture method, comprises the following steps:
A. raw material is chosen: FKF compound mineral fiber 22Kg, high-carbon steel wire 8Kg, aromatic polyamide fibre 15Kg, polyacrylonitrile
Fiber 15Kg, resistance to high mill brass wire 5Kg, sepiolite fibre 20Kg and glass fibre 15Kg are woven into the high-strength composite of 4mm
Line, then this line is made into 100Kg, 1 meter of wide Compound Fabric；
B. by above-mentioned 1 meter of wide Compound Fabric coating above-mentioned coating, air-dry to tack-free；
C. with cutter, 1 meter of wide Compound Fabric is cut into every wide for 10mm dough sheet materials, use wrapping machine to be coiled into round shape dough sheet
Material；
D. round shape dough sheet material is put into lower mold, put into steel disc, steel disc positive and negative brushing FH11-128 rubber cement；
E. on steel disc, place into round shape dough sheet material, pressing mold；
F. electric heating warming is to 178 DEG C, opens press, pressure to 32MPa, and insulation, pressurize depanning in 44 minutes, sulfidization molding must be without riveting
Connect examination car clutch face sheet.
Claims (1)
1. an anticracking antiknock car clutch face sheet material is with soaking coating processed, it is characterised in that: described coating is joined by mass fraction
Ratio: high temperature resistant 472 DEG C of liquid nano resin 80-90 parts, vinyltrimethoxy silane 10-20 part, isopropanol 10-15 part, horses
Maleic anhydride grafted EVA5-8 part, white alundum powder 3-5 part, prodan 2-3 part, molybdenum bisuphide 1-1.5 part, manganous acid lithium 2-3
Part, calcium oxide 2-3 part, calcium zinc stabilizer 1-2 part, the successively coating of mix and blend.