CN106047178A - Infusing paint containing nano molybdenum disilicide and used for clutch facing material - Google Patents
Infusing paint containing nano molybdenum disilicide and used for clutch facing material Download PDFInfo
- Publication number
- CN106047178A CN106047178A CN201610562942.8A CN201610562942A CN106047178A CN 106047178 A CN106047178 A CN 106047178A CN 201610562942 A CN201610562942 A CN 201610562942A CN 106047178 A CN106047178 A CN 106047178A
- Authority
- CN
- China
- Prior art keywords
- parts
- molybdenum disilicide
- nano
- paint
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to infusing paint containing nano molybdenum disilicide and used for a clutch facing material. The paint is characterized by comprising the following components in parts by mass: 80-90 parts of nano liquid resin, 10-20 parts of nano cellulose crystal whiskers, 10-15 parts of sodium polystyrenesulfonate, 5-8 parts of nano molybdenum disilicide, 3-5 parts of feldspar powder, 2-3 parts of sodium bentonite, 1-1.5 parts of molybdenum disulfide, 2-3 parts of yttrium oxide, 2-3 parts of calcium oxide and 1-2 parts of a calcium-zinc stabilizer. The paint is prepared by sequentially mixing and stirring the components. The paint is simple in process and applicable to manufacturing and use of automobile clutch facings, internal structure stability can be effectively ensured, and the use performance can be improved.
Description
Technical field
The present invention relates to Clutch Technology, a kind of clutch surface sheet stock leaching system containing nanometer molybdenum disilicide is coated with
Material.
Background technology
Traditional automobile clutch surface containing nanometer molybdenum disilicide uses riveted type, and dough sheet is riveted on steel disc, bothersome
Taking a lot of work, rivet affects dough sheet service life and uses safety.Existing structure without riveted type, such as Patent No.
A kind of clutch surface containing nanometer molybdenum disilicide disclosed in 201210157147.2, with steel after the employing unordered mixing of multiple material
Sheet sulfuration connects, and the internal structure of its mixing compacting is unstable, affects serviceability.
Summary of the invention
For above-mentioned deficiency without riveted type structure in prior art, the invention provides a kind of technique simple, be suitable to vapour
The car clutch surface manufacture containing nanometer molybdenum disilicide uses, and can effectively guarantee that internal structure is stable, improve containing of serviceability
The clutch surface sheet stock of nanometer molybdenum disilicide is with soaking coating processed.
The technical solution used in the present invention is: a kind of clutch surface sheet stock containing nanometer molybdenum disilicide soaks coating processed, institute
State coating by mass fraction proportioning: liquid nano resin 80-90 part, nano-cellulose whisker 10-20 part, kayexalate
10-15 part, nanometer molybdenum disilicide 5-8 part, feldspar powder 3-5 part, sodium bentonite 2-3 part, molybdenum bisuphide 1-1.5 part, yittrium oxide
2-3 part, calcium oxide 2-3 part, calcium zinc stabilizer 1-2 part, the successively coating of mix and blend.
The clutch surface assembly containing nanometer molybdenum disilicide of the present invention does not damage engine flywheel face and platen face, dough sheet
Without boring, it is not necessary to riveting, service life is long, and its processing technology is simple, prepare in order recombination line, Compound Fabric, coiling lines and
Round shape dough sheet material, effectively guarantees that its internal structure is stable, is conducive to improving usage safety performance and the stability of dough sheet assembly, prolongs
Its service life long.Use liquid nano resin, nano-cellulose whisker, nanometer molybdenum disilicide, feldspar powder, sodium bentonite,
Molybdenum bisuphide, yittrium oxide are blended prepares Wear-resistant, high-temperature resistant coating, is conducive to improving the frictional behaviour of dough sheet structure, extends and use the longevity
Life.
Detailed description of the invention
The invention will be further described below.
Embodiment one
A kind of clutch surface sheet stock containing nanometer molybdenum disilicide soaks coating processed and presses mass fraction proportioning: liquid nano resin 80
Part, nano-cellulose whisker 10 parts, kayexalate 10 parts, nanometer molybdenum disilicide 5 parts, feldspar powder 3 parts, Na-bentonite
2 parts of soil, molybdenum bisuphide 1 part, yittrium oxide 2 parts, calcium oxide 2 parts, calcium zinc stabilizer 1 part, the successively coating of mix and blend.
A kind of clutch surface assembly manufacture method containing nanometer molybdenum disilicide, comprises the following steps:
A. raw material is chosen: FKF compound mineral fiber 22Kg, ceramic fibre 8Kg, aromatic polyamide fibre 15Kg, polyacrylonitrile
Fiber 15Kg, resistance to high mill brass wire 5Kg, sepiolite fibre 20Kg and nylon wire 15Kg are woven into the high-strength complex zygonema of 4mm,
This line is made into 100Kg, 1 meter of wide Compound Fabric again;
B. by above-mentioned 1 meter of wide Compound Fabric coating above-mentioned coating, air-dry to tack-free;
C. with cutter, 1 meter of wide Compound Fabric is cut into every wide for 10mm dough sheet materials, use wrapping machine to be coiled into round shape dough sheet
Material;
D. round shape dough sheet material is put into lower mold, put into steel disc, steel disc positive and negative brushing FH11-128 rubber cement;
E. on steel disc, place into round shape dough sheet material, pressing mold;
F. electric heating warming is to 175 DEG C, opens press, pressure to 30MPa, and insulation, pressurize depanning in 40 minutes, sulfidization molding must be without riveting
Connect the examination automobile clutch surface containing nanometer molybdenum disilicide.
Embodiment two
A kind of clutch surface sheet stock containing nanometer molybdenum disilicide soaks coating processed and presses mass fraction proportioning: liquid nano resin 90
Part, nano-cellulose whisker 20 parts, kayexalate 15 parts, nanometer molybdenum disilicide 8 parts, feldspar powder 5 parts, Na-bentonite
3 parts of soil, molybdenum bisuphide 1.5 parts, yittrium oxide 3 parts, calcium oxide 3 parts, calcium zinc stabilizer 2 parts, the successively coating of mix and blend.
A kind of clutch surface assembly manufacture method containing nanometer molybdenum disilicide, comprises the following steps:
A. raw material is chosen: FKF compound mineral fiber 22Kg, ceramic fibre 8Kg, aromatic polyamide fibre 15Kg, polyacrylonitrile
Fiber 15Kg, resistance to high mill brass wire 5Kg, sepiolite fibre 20Kg and nylon wire 15Kg are woven into the high-strength complex zygonema of 4mm,
This line is made into 100Kg, 1 meter of wide Compound Fabric again;
B. by above-mentioned 1 meter of wide Compound Fabric coating above-mentioned coating, air-dry to tack-free;
C. with cutter, 1 meter of wide Compound Fabric is cut into every wide for 10mm dough sheet materials, use wrapping machine to be coiled into round shape dough sheet
Material;
D. round shape dough sheet material is put into lower mold, put into steel disc, steel disc positive and negative brushing FH11-128 rubber cement;
E. on steel disc, place into round shape dough sheet material, pressing mold;
F. electric heating warming is to 180 DEG C, opens press, pressure to 35MPa, and insulation, pressurize depanning in 45 minutes, sulfidization molding must be without riveting
Connect the examination automobile clutch surface containing nanometer molybdenum disilicide.
Embodiment three
A kind of clutch surface sheet stock containing nanometer molybdenum disilicide soaks coating processed and presses mass fraction proportioning: liquid nano resin 85
Part, nano-cellulose whisker 15 parts, kayexalate 12 parts, nanometer molybdenum disilicide 6 parts, feldspar powder 4 parts, Na-bentonite
2.5 parts of soil, molybdenum bisuphide 1.2 parts, yittrium oxide 2.3 parts, calcium oxide 2.5 parts, calcium zinc stabilizer 1.5 parts, successively mix and blend
Coating.
A kind of clutch surface assembly manufacture method containing nanometer molybdenum disilicide, comprises the following steps:
A. raw material is chosen: FKF compound mineral fiber 22Kg, ceramic fibre 8Kg, aromatic polyamide fibre 15Kg, polyacrylonitrile
Fiber 15Kg, resistance to high mill brass wire 5Kg, sepiolite fibre 20Kg and nylon wire 15Kg are woven into the high-strength complex zygonema of 4mm,
This line is made into 100Kg, 1 meter of wide Compound Fabric again;
B. by above-mentioned 1 meter of wide Compound Fabric coating above-mentioned coating, air-dry to tack-free;
C. with cutter, 1 meter of wide Compound Fabric is cut into every wide for 10mm dough sheet materials, use wrapping machine to be coiled into round shape dough sheet
Material;
D. round shape dough sheet material is put into lower mold, put into steel disc, steel disc positive and negative brushing FH11-128 rubber cement;
E. on steel disc, place into round shape dough sheet material, pressing mold;
F. electric heating warming is to 178 DEG C, opens press, pressure to 32MPa, and insulation, pressurize depanning in 44 minutes, sulfidization molding must be without riveting
Connect the examination automobile clutch surface containing nanometer molybdenum disilicide.
Claims (1)
1. the clutch surface sheet stock containing nanometer molybdenum disilicide is with soaking coating processed, it is characterised in that: described coating is divided by quality
Number proportioning: liquid nano resin 80-90 part, nano-cellulose whisker 10-20 part, kayexalate 10-15 part, nanometer two
Molybdenum silicide 5-8 part, feldspar powder 3-5 part, sodium bentonite 2-3 part, molybdenum bisuphide 1-1.5 part, yittrium oxide 2-3 part, calcium oxide 2-
3 parts, calcium zinc stabilizer 1-2 part, the successively coating of mix and blend.