CN106117991A - 高光泽耐刮擦耐候抗菌聚酯合金树脂 - Google Patents

高光泽耐刮擦耐候抗菌聚酯合金树脂 Download PDF

Info

Publication number
CN106117991A
CN106117991A CN201610517299.7A CN201610517299A CN106117991A CN 106117991 A CN106117991 A CN 106117991A CN 201610517299 A CN201610517299 A CN 201610517299A CN 106117991 A CN106117991 A CN 106117991A
Authority
CN
China
Prior art keywords
polyester alloy
antibacterial
accounts
weather
ester
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610517299.7A
Other languages
English (en)
Inventor
王福海
赵学仕
王建军
褚万丰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuqiao Huike Plastic Material Co Ltd
Original Assignee
Wuqiao Huike Plastic Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuqiao Huike Plastic Material Co Ltd filed Critical Wuqiao Huike Plastic Material Co Ltd
Priority to CN201610517299.7A priority Critical patent/CN106117991A/zh
Publication of CN106117991A publication Critical patent/CN106117991A/zh
Pending legal-status Critical Current

Abstract

高光泽耐刮擦耐候抗菌聚酯合金树脂，由聚酯合金、酯交换抑制剂、增韧剂、耐候剂、抗菌剂、抗氧剂和润滑剂制备而成，其中聚酯合金由聚对苯二甲酸丁二醇酯和聚碳酸酯复配而成，酯交换抑制剂为磷酸二氢钠，增韧剂为丙烯酸酯接枝弹性体，耐候剂为紫外线吸收剂UV 327，抗菌剂为银系无机抗菌剂，抗氧剂为季戊四醇酯和亚磷酸三酯的复混物，润滑剂为季戊四醇硬脂酸酯。本发明采用PBT/PC聚酯合金作为基础树脂，结合增韧剂、耐候剂、抗菌剂、抗氧剂和润滑剂制备而成，具有高抗冲性，抗菌性、耐候性、良好的耐热性、热稳定性和优良的可加工性，可以广泛地应用于卫生洁具，日常用品、电子电器、汽车电器等方面。

Description

高光泽耐刮擦耐候抗菌聚酯合金树脂
技术领域
本发明涉及卫生洁具用高分子复合材料技术领域，具体涉及一种高光泽耐刮擦耐候抗菌聚酯合金树脂。
背景技术
卫生洁具是现代建筑中室内配套不可缺少的组成部分。目前卫生洁具根据材质配方主要分为两种，一种为无机材料卫生洁具，包括陶瓷、木材和玻璃等卫生洁具，这种卫生洁具在色彩层次上都较为单一，这种卫生洁具都适应不了高温酸碱环境，外形单一、艺术观赏价值低，手感也不理想；第二种为高分子材料卫生洁具，高分子卫生洁具目前有聚丙烯材料、脲醛塑料、亚克力材料和ABS材料等等，聚丙烯材料耐刮擦性不好，耐候性不好，因此，仅用聚丙烯树很难获得良好的耐刮擦性、耐候性和高强度；脲醛塑料硬度高却脆性大，并且不环保；亚克力材料的卫浴一般都不具备抗菌功能，长期使用后会滋生有害细菌，影响人身健康，为减少有害细菌对我们生活的危害；ABS材料虽然具有良好韧性和耐水性，但是由于收缩率小，并且耐候性差不能符合要求。
发明内容
本发明针对现有技术存在的不足，提供了一种高光泽耐刮擦耐候抗菌聚酯合金树脂。
本发明解决其技术问题所采用的技术方案是：
一种高光泽耐刮擦耐候抗菌聚酯合金树脂，由聚酯合金、酯交换抑制剂、增韧剂、耐候剂、抗菌剂、抗氧剂和润滑剂制备而成，其中聚酯合金由聚对苯二甲酸丁二醇酯和聚碳酸酯复配而成，酯交换抑制剂为磷酸二氢钠，增韧剂为丙烯酸酯接枝弹性体，耐候剂为紫外线吸收剂UV 327，抗菌剂为银系无机抗菌剂，抗氧剂为季戊四醇酯和亚磷酸三酯的复混物，润滑剂为季戊四醇硬脂酸酯。
上述聚酯合金中聚对苯二甲酸丁二醇酯占聚酯合金质量的50%-95%；聚碳酸酯占聚酯合金质量的5%-50％。
上述聚酯合金占整个配方质量75-95％；酯交换抑制剂占整个配方质量0.1-0.5%；增韧剂丙烯酸酯接枝弹性体占整个配方质量3-15％；耐候剂紫外线吸收剂UV 327占整个配方质量0.2-0.5%；银系无机抗菌剂占整个配方质量0.1-0.5％；抗氧剂占整个配方质量0.1-0.3%；润滑剂季戊四醇硬脂酸酯占整个配方质量0.2-0.6%。
本发明配方中PBT/PC聚酯合金组分相容性好，光泽度高，韧性好，强度高、耐刮擦；酯交换抑制剂可有效防止聚酯合金中聚对苯二甲酸丁二醇酯和聚碳酸酯发生酯交换反应形成副产物；增韧剂丙烯酸酯接枝弹性体与PBT/PC聚酯合金相容性好，能进一步提高材料韧性，同时提升材料的收缩率，改善加工性；耐候剂和抗氧剂的加入提升配方的使用时间，原PP材料使用时间为6个月-12个月，改进后的材料可以使用3年-5年甚至更长；抗菌剂目的是为了提升卫浴材料的方便清洗性，以及提升材料的健康使用特点；润滑剂目的是为了改善加工性，减少物性损失。
本发明采用PBT/PC聚酯合金作为基础树脂，结合酯交换抑制剂、增韧剂、耐候剂、抗菌剂、抗氧剂和润滑剂制备而成，具有高抗冲性，抗菌性、耐候性、良好的耐热性、热稳定性和优良的可加工性，可以广泛地应用于卫生洁具，日常用品、电子电器、汽车电器等方面。
具体实施方式
一种高光泽耐刮擦耐候抗菌聚酯合金树脂，由聚酯合金、酯交换抑制剂、增韧剂、耐候剂、抗菌剂、抗氧剂和润滑剂制备而成，其中聚酯合金由聚对苯二甲酸丁二醇酯和聚碳酸酯复配而成，酯交换抑制剂为磷酸二氢钠，增韧剂为丙烯酸酯接枝弹性体，耐候剂为紫外线吸收剂UV 327，抗菌剂为银系无机抗菌剂，抗氧剂为季戊四醇酯和亚磷酸三酯的复混物，润滑剂为季戊四醇硬脂酸酯。
上述聚酯合金中聚对苯二甲酸丁二醇酯占聚酯合金质量的50%-95%；聚碳酸酯占聚酯合金质量的5%-50％。
上述聚酯合金占整个配方质量75-95％；酯交换抑制剂占整个配方质量0.1-0.5%；增韧剂丙烯酸酯接枝弹性体占整个配方质量3-15％；耐候剂紫外线吸收剂UV 327占整个配方质量0.2-0.5%；银系无机抗菌剂占整个配方质量0.1-0.5％；抗氧剂占整个配方质量0.1-0.3%；润滑剂季戊四醇硬脂酸酯占整个配方质量0.2-0.6%。
本发明配方中PBT/PC聚酯合金组分相容性好，光泽度高，韧性好，强度高、耐刮擦；酯交换抑制剂可有效防止聚酯合金中聚对苯二甲酸丁二醇酯和聚碳酸酯发生酯交换反应形成副产物；增韧剂丙烯酸酯接枝弹性体与PBT/PC聚酯合金相容性好，能进一步提高材料韧性，同时提升材料的收缩率，改善加工性；耐候剂和抗氧剂的加入提升配方的使用时间，原PP材料使用时间为6个月-12个月，改进后的材料可以使用3年-5年甚至更长；抗菌剂目的是为了提升卫浴材料的方便清洗性，以及提升材料的健康使用特点；润滑剂目的是为了改善加工性，减少物性损失。

Claims (3)

1. 一种高光泽耐刮擦耐候抗菌聚酯合金树脂，其特征是由聚酯合金、酯交换抑制剂、增韧剂、耐候剂、抗菌剂、抗氧剂和润滑剂制备而成，其中聚酯合金由聚对苯二甲酸丁二醇酯和聚碳酸酯复配而成，酯交换抑制剂为磷酸二氢钠，增韧剂为丙烯酸酯接枝弹性体，耐候剂为紫外线吸收剂UV 327，抗菌剂为银系无机抗菌剂，抗氧剂为季戊四醇酯和亚磷酸三酯的复混物，润滑剂为季戊四醇硬脂酸酯。
2.根据权利要求1所述的高光泽耐刮擦耐候抗菌聚酯合金树脂，其特征是聚酯合金中聚对苯二甲酸丁二醇酯占聚酯合金质量的50%-95%；聚碳酸酯占聚酯合金质量的5%-50％。
3.根据权利要求1所述的高光泽耐刮擦耐候抗菌聚酯合金树脂，其特征是聚酯合金占整个配方质量75-95％；酯交换抑制剂占整个配方质量0.1-0.5%；增韧剂丙烯酸酯接枝弹性体占整个配方质量3-15％；耐候剂紫外线吸收剂UV 327占整个配方质量0.2-0.5%；银系无机抗菌剂占整个配方质量0.1-0.5％；抗氧剂占整个配方质量0.1-0.3%；润滑剂季戊四醇硬脂酸酯占整个配方质量0.2-0.6%。
CN201610517299.7A 2016-07-05 2016-07-05 高光泽耐刮擦耐候抗菌聚酯合金树脂 Pending CN106117991A (zh)