CN106117817A - A kind of rubber buffer for outdoor fitness equipment - Google Patents
A kind of rubber buffer for outdoor fitness equipment Download PDFInfo
- Publication number
- CN106117817A CN106117817A CN201610464801.2A CN201610464801A CN106117817A CN 106117817 A CN106117817 A CN 106117817A CN 201610464801 A CN201610464801 A CN 201610464801A CN 106117817 A CN106117817 A CN 106117817A
- Authority
- CN
- China
- Prior art keywords
- rubber
- minute
- fitness equipment
- rubber buffer
- outdoor fitness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of rubber buffer for outdoor fitness equipment, be made up of following raw material: butadiene rubber, EPDM reclaimed rubber, modified micro-silicon ash, coal gas of converter electro-precipitating dust, tyre talc, montmorillonite powder, ATMP four sodium, zinc naphthenate, dialkyl diphenylamine, soya wax, thiosulfates, diethoxy estersil base ethane, lanolin alcohol.The present invention has the advantage that use reclaimed rubber in the present invention compared to existing technology, contributes to recycling of waste material；Butadiene rubber is used in combination with EPDM reclaimed rubber, it is possible to increase the elasticity of rubber and weatherability；The corresponding different grain diameter of multiple filler, can make raw material be sufficiently mixed, and makes internal structure fine and close, improves the chemical stability of rubber；Rubber buffer elasticity prepared by the present invention is moderate, and anti-impact force is strong, and service life is long, in use will not discharge noxious substance, safety and environmental protection.
Description
Technical field
The invention belongs to outdoor fitness equipment accessory technical field, be specifically related to a kind of rubber for outdoor fitness equipment
Cushion pad.
Background technology
Along with the raising of people's living standard, people increasingly pursue the health of health, and outdoor fitness equipment is extensively applied
In park, square, the public place such as residential quarter, be suitable for men and women, old and young and take exercise, increasing resident joins various open air
In body-building, but being arranged at outdoor for a long time due to body-building apparatus, long-term acceptance is exposed to the sun and rain, if the accessory of body-building apparatus
Poor quality will cause come off or breakage phenomenon occur, accessory can be directly resulted in and scrap, need again to change accessory, or
Person changes body-building apparatus, and wherein, multiple body-building apparatus comprises rubber buffer, protection body-building apparatus and the safety of body builder, and one
Denier is damaged, then may accelerate the damage of equipment, have certain potential safety hazard.
Summary of the invention
It is an object of the invention to for existing problem, it is provided that a kind of rubber buffer for outdoor fitness equipment.
The present invention is achieved by the following technical solutions: a kind of rubber buffer for outdoor fitness equipment, by with
The raw material of lower weight portion is made: butadiene rubber 8-15 part, EPDM reclaimed rubber 28-34 part, modified micro-silicon ash 5-10 part, converter
Coal gas electro-precipitating dust 12-16 part, tyre talc 4-8 part, montmorillonite powder 12-18 part, ATMP four sodium 2-3 part, cycloalkanes
Acid zinc 1-2 part, dialkyl diphenylamine 2-4 part, soya wax 3-5 part, thiosulfates 1-2 part, diethoxy estersil base ethane 2-4
Part, lanolin alcohol 1-2 part；
Wherein, the preparation method of described modification micro-silicon ash is: add the spy being equivalent to its weight portion 1.8-2.2% in SILICA FUME
Butylbenzoic acid, the OPE of 0.5-0.8% and the ammonia spirit of 0.1-0.3%, the mass concentration of ammonia spirit is 20-
28%, under conditions of 65 DEG C, process 20-40 minute in ball mill, to obtain final product.
As further improvement of these options, the water content of described coal gas of converter electro-precipitating dust is 5-8%, particle
Footpath is 60-80nm.
As further improvement of these options, the grain diameter of described modified SILICA FUME is 40-50nm, described tire
The grain diameter of powder is 60-80 μm, and the particle diameter of described montmorillonite powder is 10-20 μm.
A kind of rubber buffer for outdoor fitness equipment, its preparation method comprises the following steps:
(1) butadiene rubber and EPDM reclaimed rubber are put into immersion in mixed solvent, after soaking 40 minutes, use supersonic frequency
30KHz, power 65W to its supersound process 8-12 minute, be then sequentially added into ATMP four sodium, thiosulfates,
Soya wax and lanolin alcohol, be uniformly mixed, and divides its microwave treatment 20-25 at microwave frequency 2560MHz, power 600W
Clock, obtains mixed material I；
(2) modified SILICA FUME, coal gas of converter electro-precipitating dust, tyre talc and montmorillonite powder mix homogeneously, it is heated to 70-80 DEG C,
Insulation mixing 10-15 minute, then proceedes to be heated to 120-150 DEG C, adds zinc naphthenate, dialkyl diphenylamine and diethoxy
Base estersil base ethane, after insulation mixes 20-25 minute, naturally cools to room temperature, obtains mixed material II；
(3) add after mixed material I and mixed material II being sufficiently mixed in banbury, mixing 5-8 under conditions of 150 DEG C
Minute, seal after placing 30-40 minute, obtain semi-finished product；
(4) by semi-finished product by mill mill molding, vulcanize 12-18 minute, by its root under conditions of 200-220 DEG C the most again
Finished product is obtained after repairing according to needs.
As further improvement of these options, described mixed solvent is the mixture of toluene and acetone, mixed weight
Ratio is 1:1.
Modified SILICA FUME improves filler dispersibility in the polymer, and absorption, on rubber particles surface, produces crystallization effect
Really, strengthening adsorption.
The present invention has the advantage that use reclaimed rubber in the present invention compared to existing technology, contributes to the circulation of waste material
Utilize；Butadiene rubber is used in combination with EPDM reclaimed rubber, it is possible to increase the elasticity of rubber and weatherability；Multiple filler is corresponding
Different grain diameters, can make raw material be sufficiently mixed, and makes internal structure fine and close, improves the chemical stability of rubber；Institute of the present invention
The rubber buffer elasticity of preparation is moderate, and anti-impact force is strong, and service life is long, in use will not discharge noxious substance,
Safety and environmental protection.
Detailed description of the invention
Embodiment 1
A kind of rubber buffer for outdoor fitness equipment, is made up of the raw material of following weight portion: butadiene rubber 12 parts, ternary
Second the third reclaimed rubber 32 parts, modified micro-silicon ash 8 parts, coal gas of converter electro-precipitating dust 14 parts, tyre talc 4 parts, montmorillonite powder 14 parts, amino
Three 2 parts of methylenephosphonic acid four sodium, zinc naphthenate 1 part, dialkyl diphenylamine 3 parts, soya wax 4 parts, thiosulfates 2 parts, diethoxy
2 parts of base estersil base ethane, lanolin alcohol 2 parts；
Wherein, the preparation method of described modification micro-silicon ash is: add the tertiary butyl being equivalent to its weight portion 1.8% in SILICA FUME
Benzoic acid, the OPE of 0.7% and the ammonia spirit of 0.2%, the mass concentration of ammonia spirit is 20-28%, at 65 DEG C
Under the conditions of, process 20-40 minute in ball mill, to obtain final product.
Wherein, the water content of described coal gas of converter electro-precipitating dust is 5-8%, and grain diameter is 60-80nm；Described modification is micro-
The grain diameter of silica flour is 40-50nm, and the grain diameter of described tyre talc is 60-80 μm, and the particle diameter of described montmorillonite powder is 10-
20μm。
A kind of rubber buffer for outdoor fitness equipment, its preparation method comprises the following steps:
(1) butadiene rubber and EPDM reclaimed rubber are put into immersion in mixed solvent, after soaking 40 minutes, use supersonic frequency
30KHz, power 65W to its supersound process 8-12 minute, be then sequentially added into ATMP four sodium, thiosulfates,
Soya wax and lanolin alcohol, be uniformly mixed, and divides its microwave treatment 20-25 at microwave frequency 2560MHz, power 600W
Clock, obtains mixed material I；
(2) modified SILICA FUME, coal gas of converter electro-precipitating dust, tyre talc and montmorillonite powder mix homogeneously, it is heated to 70-80 DEG C,
Insulation mixing 10-15 minute, then proceedes to be heated to 120-150 DEG C, adds zinc naphthenate, dialkyl diphenylamine and diethoxy
Base estersil base ethane, after insulation mixes 20-25 minute, naturally cools to room temperature, obtains mixed material II；
(3) add after mixed material I and mixed material II being sufficiently mixed in banbury, mixing 5-8 under conditions of 150 DEG C
Minute, seal after placing 30-40 minute, obtain semi-finished product；
(4) by semi-finished product by mill mill molding, vulcanize 12-18 minute, by its root under conditions of 200-220 DEG C the most again
Finished product is obtained after repairing according to needs.
Embodiment 2
A kind of rubber buffer for outdoor fitness equipment, is made up of the raw material of following weight portion: butadiene rubber 8 parts, ternary
Second the third reclaimed rubber 34 parts, modified micro-silicon ash 10 parts, coal gas of converter electro-precipitating dust 12 parts, tyre talc 5 parts, montmorillonite powder 13 parts, ammonia
3 parts of base three methylenephosphonic acid four sodium, zinc naphthenate 1 part, dialkyl diphenylamine 3 parts, soya wax 4 parts, thiosulfates 2 parts, diethyl
3 parts of epoxide estersil base ethane, lanolin alcohol 2 parts；
Wherein, the preparation method of described modification micro-silicon ash is: add the spy being equivalent to its weight portion 1.8-2.2% in SILICA FUME
Butylbenzoic acid, the OPE of 0.5-0.8% and the ammonia spirit of 0.1-0.3%, the mass concentration of ammonia spirit is 20-
28%, under conditions of 65 DEG C, process 20-40 minute in ball mill, to obtain final product.
Its preparation method is identical with embodiment.
Embodiment 3
A kind of rubber buffer for outdoor fitness equipment, is made up of the raw material of following weight portion: butadiene rubber 13 parts, ternary
Second the third reclaimed rubber 30 parts, modified micro-silicon ash 6 parts, coal gas of converter electro-precipitating dust 12 parts, tyre talc 8 parts, montmorillonite powder 16 parts, amino
Three 3 parts of methylenephosphonic acid four sodium, zinc naphthenate 2 parts, dialkyl diphenylamine 2 parts, soya wax 3 parts, thiosulfates 2 parts, diethoxy
2 parts of base estersil base ethane, lanolin alcohol 1 part；
Wherein, the preparation method of described modification micro-silicon ash is: add the spy being equivalent to its weight portion 1.8-2.2% in SILICA FUME
Butylbenzoic acid, the OPE of 0.5-0.8% and the ammonia spirit of 0.1-0.3%, the mass concentration of ammonia spirit is 20-
28%, under conditions of 65 DEG C, process 20-40 minute in ball mill, to obtain final product.
Its preparation method is identical with embodiment.
In the present invention, prepared gained rubber buffer is for outdoor fitness equipment, elastic preferable, clashes into without bright for a long time
Aobvious damage, useful life reaches about 5 years, in the case of high light prolonged exposure, discharge without noxious substance, safety and environmental protection, resistance to
Strong by property.
Claims (5)
1. the rubber buffer for outdoor fitness equipment, it is characterised in that be made up of the raw material of following weight portion: along fourth
Rubber 8-15 part, EPDM reclaimed rubber 28-34 part, modified micro-silicon ash 5-10 part, coal gas of converter electro-precipitating dust 12-16 part, wheel
Tire powder 4-8 part, montmorillonite powder 12-18 part, ATMP four sodium 2-3 part, zinc naphthenate 1-2 part, dialkyl diphenylamine
2-4 part, soya wax 3-5 part, thiosulfates 1-2 part, diethoxy estersil base ethane 2-4 part, lanolin alcohol 1-2 part；
Wherein, the preparation method of described modification micro-silicon ash is: add the spy being equivalent to its weight portion 1.8-2.2% in SILICA FUME
Butylbenzoic acid, the OPE of 0.5-0.8% and the ammonia spirit of 0.1-0.3%, the mass concentration of ammonia spirit is 20-
28%, under conditions of 65 DEG C, process 20-40 minute in ball mill, to obtain final product.
A kind of rubber buffer for outdoor fitness equipment, it is characterised in that described coal gas of converter
The water content of electro-precipitating dust is 5-8%, and grain diameter is 60-80nm.
A kind of rubber buffer for outdoor fitness equipment, it is characterised in that the described micro-silicon of modification
The grain diameter of powder is 40-50nm, and the grain diameter of described tyre talc is 60-80 μm, and the particle diameter of described montmorillonite powder is 10-20
μm。
A kind of rubber buffer for outdoor fitness equipment, it is characterised in that its preparation method bag
Include following steps:
(1) butadiene rubber and EPDM reclaimed rubber are put into immersion in mixed solvent, after soaking 40 minutes, use supersonic frequency
30KHz, power 65W to its supersound process 8-12 minute, be then sequentially added into ATMP four sodium, thiosulfates,
Soya wax and lanolin alcohol, be uniformly mixed, and divides its microwave treatment 20-25 at microwave frequency 2560MHz, power 600W
Clock, obtains mixed material I；
(2) modified SILICA FUME, coal gas of converter electro-precipitating dust, tyre talc and montmorillonite powder mix homogeneously, it is heated to 70-80 DEG C,
Insulation mixing 10-15 minute, then proceedes to be heated to 120-150 DEG C, adds zinc naphthenate, dialkyl diphenylamine and diethoxy
Base estersil base ethane, after insulation mixes 20-25 minute, naturally cools to room temperature, obtains mixed material II；
(3) add after mixed material I and mixed material II being sufficiently mixed in banbury, mixing 5-8 under conditions of 150 DEG C
Minute, seal after placing 30-40 minute, obtain semi-finished product；
(4) by semi-finished product by mill mill molding, vulcanize 12-18 minute, by its root under conditions of 200-220 DEG C the most again
Finished product is obtained after repairing according to needs.
A kind of rubber buffer for outdoor fitness equipment, it is characterised in that described mixed solvent
For toluene and the mixture of acetone, mixed weight is than for 1:1.