CN106116352A - A kind of low temperature resistant water-repellent paint - Google Patents
A kind of low temperature resistant water-repellent paint Download PDFInfo
- Publication number
- CN106116352A CN106116352A CN201610480568.7A CN201610480568A CN106116352A CN 106116352 A CN106116352 A CN 106116352A CN 201610480568 A CN201610480568 A CN 201610480568A CN 106116352 A CN106116352 A CN 106116352A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- powder
- repellent paint
- mesh
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of low temperature resistant water-repellent paint, including: liquid material and powder；Liquid material includes: acrylic emulsion 87 94 parts, deionized water 24 30 parts, ethyl cellulose 58 parts, triethyl group hexyl phosphoric acid 58 parts, linarin 12 parts, α thujene 1.5 2.5 parts, beta pinene 1.5 2.5 parts, tea polyphenols 24 parts；Described powder includes: portland cement 52 62 parts, 200 300 mesh anion powder 16 24 parts, 20 500 mesh hyperbranched quaternary ammonium salt 11 16 parts, 20 500 mesh isopropyl myristate 24 parts, N phenyl β naphthylamines 0.8 2.2 parts, phenyl salicylate 0.8 1.6 parts, water reducer 2 2.5 parts.Water-repellent paint acid and alkali-resistance of the present invention, salt fog, there is good ageing-resistant performance and decay resistance, ultraviolet is had significant repellence, safety non-toxic, powder and liquid material are mixed to form one layer of fine and close waterproof membrane, water-repellent paint of the present invention can be constructed under the low temperature environment of 5 DEG C, does not still interfere with coating water-proof performance, and PARA FORMALDEHYDE PRILLS(91,95) has good assimilation effect.
Description
Technical field
The present invention relates to building water-proof paint field, be specifically related to a kind of low temperature resistant water-repellent paint.
Background technology
Waterproof material is widely used in building materials protection field, uses water-repellent paint can will build after building is carried out application
Build thing to be isolated with external environment, be therefore prevented from because the dampness in the corrosive liquids such as rainwater, subsoil water and air invades building
The corrosion that thing material causes, extends the service life of construction material.Waterproof material mainly includes water-repellent paint and waterproof roll.Its
In, waterproof roll mainly has asphalt water-proof coiled material, modified asphalt waterproof coiled material, high molecular polymer waterproof roll etc., waterproof volume
Material complicated construction technique, and workmen is required higher, therefore range of application is narrower, the existing waterproof material used mostly is waterproof painting
Material.The construction technology that use water-repellent paint carries out application is relatively simple, only water-repellent paint need to be coated on substrate surface, waterproof painting
Material solidify to form waterproof layer after being applied to substrate surface, and then makes coated object be isolated with water environment, plays protection and makees
With.Existing water-repellent paint mainly includes the polymer waterproof coating material such as water-proof acrylic acid paint and polyurethane water-proof paint.At present
Water-repellent paint weatherability poor, easily bursting by freezing at low temperatures.
Summary of the invention
The technical problem to be solved is to provide a kind of low temperature resistant water-repellent paint, water-repellent paint acid and alkali-resistance, salt
Mist, has good ageing-resistant performance and decay resistance, has significant repellence, safety non-toxic, powder and liquid to ultraviolet
Material is mixed to form one layer of fine and close waterproof membrane, and the waterproof coating surface viscosity after brushing is low, is difficult to covered with dust, and the present invention is waterproof
Coating can be constructed under the low temperature environment of-5 DEG C, does not still interfere with coating water-proof performance, and PARA FORMALDEHYDE PRILLS(91,95) has well suction
Produce effects really.
The technical problem to be solved realizes by the following technical solutions:
A kind of low temperature resistant water-repellent paint, including: liquid material and powder, described liquid material and powder weight ratio be 1:2.44～
2.54；
Described liquid material includes: acrylic emulsion 87-94 part, deionized water 24-30 part, ethyl cellulose 5-8 part, triethyl group
Hexyl phosphoric acid 5-8 part, linarin 1-2 part, α-thujene 1.5-2.5 part, nopinene 1.5-2.5 part, tea polyphenols 2-4 part；
Described powder includes: portland cement 52-62 part, 200-300 mesh anion powder 16-24 part, 20-500 mesh over-expense
Change quaternary ammonium salt 11-16 part, 20-500 mesh isopropyl myristate 2-4 part, N-Phenyl beta naphthylamine 0.8-2.2 part, phenyl salicylate
0.8-1.6 part, water reducer 2-2.5 part.
Described water reducer is sulfonated melamine compound resin.
The preparation method of described liquid material is as follows: first add acrylic emulsion in deionization, after stirring, by mixed liquor
At a temperature of-20 DEG C freezing 20 minutes, re-heat the most again, add ethyl cellulose, triethyl group hexyl phosphoric acid, linarin, α-
Thujene, nopinene, tea polyphenols stir, and obtain liquid material.
The preparation method of described powder is as follows: by hyperbranched to portland cement, 200-300 mesh anion powder, 20-500 mesh
Quaternary ammonium salt, 20-500 mesh isopropyl myristate, N-Phenyl beta naphthylamine, phenyl salicylate, water reducer mixing and stirring, i.e.
Obtain powder.
The using method of a kind of low temperature resistant water-repellent paint, comprises the steps:
(1) powder in the water-repellent paint described in Claims 1-4 any one is slowly added in liquid material the most constantly
Stirring, until stirring into homogeneous paste and i.e. obtaining rubber cement without small particles or bubble；
(2) directly step (1) gained rubber cement is uniformly painted on basal plane with hairbrush or round brush, constantly stirs in smearing
Glue mixing is starched.
The invention has the beneficial effects as follows: water-repellent paint acid and alkali-resistance of the present invention, salt fog that there is good ageing-resistant performance and resistance to
Corrosive nature, has significant repellence, safety non-toxic, powder and liquid material to be mixed to form one layer of fine and close waterproof membrane to ultraviolet,
Waterproof coating surface viscosity after brushing is low, is difficult to covered with dust, and water-repellent paint of the present invention can be executed under the low temperature environment of-5 DEG C
Work, does not still interfere with coating water-proof performance, and PARA FORMALDEHYDE PRILLS(91,95) has good assimilation effect.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below knot
Close specific embodiment, the present invention is expanded on further.
Embodiment 1
A kind of low temperature resistant water-repellent paint, including: liquid material and powder, described liquid material and powder weight ratio are 1:2.5；
Described liquid material includes: acrylic emulsion 90kg, deionized water 27kg, ethyl cellulose 6kg, triethyl group hexyl phosphoric acid
6kg, linarin 1kg, α-thujene 2kg, nopinene 2kg, tea polyphenols 3kg；
Described powder includes: portland cement 57kg, 200-300 mesh anion powder hyperbranched quaternary ammonium of 20kg, 20-500 mesh
Salt 14kg, 20-500 mesh isopropyl myristate 3kg, N-Phenyl beta naphthylamine 1.5kg, phenyl salicylate 1.2kg, water reducer
2.2kg。
Described water reducer is sulfonated melamine compound resin.
The preparation method of described liquid material is as follows: first add acrylic emulsion in deionization, after stirring, by mixed liquor
At a temperature of-20 DEG C freezing 20 minutes, re-heat the most again, add ethyl cellulose, triethyl group hexyl phosphoric acid, linarin, α-
Thujene, nopinene, tea polyphenols stir, and obtain liquid material.
The preparation method of described powder is as follows: by hyperbranched to portland cement, 200-300 mesh anion powder, 20-500 mesh
Quaternary ammonium salt, 20-500 mesh isopropyl myristate, N-Phenyl beta naphthylamine, phenyl salicylate, water reducer mixing and stirring, i.e.
Obtain powder.
The using method of a kind of low temperature resistant water-repellent paint, comprises the steps:
(1) powder in the water-repellent paint described in Claims 1-4 any one is slowly added in liquid material the most constantly
Stirring, until stirring into homogeneous paste and i.e. obtaining rubber cement without small particles or bubble；
(2) directly step (1) gained rubber cement is uniformly painted on basal plane with hairbrush or round brush, constantly stirs in smearing
Glue mixing is starched.
Embodiment 2
A kind of low temperature resistant water-repellent paint, including: liquid material and powder, described liquid material and powder weight ratio are 1:2.44；
Described liquid material includes: acrylic emulsion 87kg, deionized water 24kg, ethyl cellulose 5kg, triethyl group hexyl phosphoric acid
5kg, linarin 1kg, α-thujene 1.5kg, nopinene 1.5kg, tea polyphenols 2kg；
Described powder includes: portland cement 52kg, 200-300 mesh anion powder hyperbranched quaternary ammonium of 16kg, 20-500 mesh
Salt 11kg, 20-500 mesh isopropyl myristate 2kg, N-Phenyl beta naphthylamine 0.8kg, phenyl salicylate 0.8kg, water reducer
2kg。
Described water reducer is sulfonated melamine compound resin.
The preparation method of described liquid material is as follows: first add acrylic emulsion in deionization, after stirring, by mixed liquor
At a temperature of-20 DEG C freezing 20 minutes, re-heat the most again, add ethyl cellulose, triethyl group hexyl phosphoric acid, linarin, α-
Thujene, nopinene, tea polyphenols stir, and obtain liquid material.
The preparation method of described powder is as follows: by hyperbranched to portland cement, 200-300 mesh anion powder, 20-500 mesh
Quaternary ammonium salt, 20-500 mesh isopropyl myristate, N-Phenyl beta naphthylamine, phenyl salicylate, water reducer mixing and stirring, i.e.
Obtain powder.
The using method of a kind of low temperature resistant water-repellent paint, comprises the steps:
(1) powder in the water-repellent paint described in Claims 1-4 any one is slowly added in liquid material the most constantly
Stirring, until stirring into homogeneous paste and i.e. obtaining rubber cement without small particles or bubble；
(2) directly step (1) gained rubber cement is uniformly painted on basal plane with hairbrush or round brush, constantly stirs in smearing
Glue mixing is starched.
Embodiment 3
A kind of low temperature resistant water-repellent paint, including: liquid material and powder, described liquid material and powder weight ratio are 1:2.54；
Described liquid material includes: acrylic emulsion 94kg, deionized water 30kg, ethyl cellulose 8kg, triethyl group hexyl phosphoric acid
8kg, linarin 2kg, α-thujene 2.5kg, nopinene 2.5kg, tea polyphenols 4kg；
Described powder includes: portland cement 62kg, 200-300 mesh anion powder hyperbranched quaternary ammonium of 24kg, 20-500 mesh
Salt 16kg, 20-500 mesh isopropyl myristate 4kg, N-Phenyl beta naphthylamine 2.2kg, phenyl salicylate 1.6kg, water reducer
2.5kg。
Described water reducer is sulfonated melamine compound resin.
The preparation method of described liquid material is as follows: first add acrylic emulsion in deionization, after stirring, by mixed liquor
At a temperature of-20 DEG C freezing 20 minutes, re-heat the most again, add ethyl cellulose, triethyl group hexyl phosphoric acid, linarin, α-
Thujene, nopinene, tea polyphenols stir, and obtain liquid material.
The preparation method of described powder is as follows: by hyperbranched to portland cement, 200-300 mesh anion powder, 20-500 mesh
Quaternary ammonium salt, 20-500 mesh isopropyl myristate, N-Phenyl beta naphthylamine, phenyl salicylate, water reducer mixing and stirring, i.e.
Obtain powder.
The using method of a kind of low temperature resistant water-repellent paint, comprises the steps:
(1) powder in the water-repellent paint described in Claims 1-4 any one is slowly added in liquid material the most constantly
Stirring, until stirring into homogeneous paste and i.e. obtaining rubber cement without small particles or bubble；
(2) directly step (1) gained rubber cement is uniformly painted on basal plane with hairbrush or round brush, constantly stirs in smearing
Glue mixing is starched.
Test
The common coating of coating and market that the embodiment of the present invention 1,2,3 prepares carries out using test, test result such as following table
Shown in:
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.The technology of the industry
Personnel, it should be appreciated that the present invention is not restricted to the described embodiments, simply illustrating this described in above-described embodiment and description
The principle of invention, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, and these become
Change and improvement both falls within scope of the claimed invention.Claimed scope by appending claims and
Equivalent defines.
Claims (5)
1. a low temperature resistant water-repellent paint, it is characterised in that including: liquid material and powder, described liquid material and powder weight ratio are 1:
2.44～2.54；
Described liquid material includes: acrylic emulsion 87-94 part, deionized water 24-30 part, ethyl cellulose 5-8 part, triethyl group hexyl
Phosphoric acid 5-8 part, linarin 1-2 part, α-thujene 1.5-2.5 part, nopinene 1.5-2.5 part, tea polyphenols 2-4 part；
Described powder includes: portland cement 52-62 part, 200-300 mesh anion powder 16-24 part, 20-500 mesh hyperbranched season
Ammonium salt 11-16 part, 20-500 mesh isopropyl myristate 2-4 part, N-Phenyl beta naphthylamine 0.8-2.2 part, phenyl salicylate 0.8-
1.6 parts, water reducer 2-2.5 part.
A kind of low temperature resistant water-repellent paint the most as claimed in claim 1, it is characterised in that described water reducer is sulfonated melamine
Formaldehyde resin.
A kind of low temperature resistant water-repellent paint the most as claimed in claim 1, it is characterised in that the preparation method of described liquid material is as follows:
In deionization, first add acrylic emulsion, after stirring, by mixed liquor freezing 20 minutes at a temperature of-20 DEG C, the most again
Re-heat, adds ethyl cellulose, triethyl group hexyl phosphoric acid, linarin, α-thujene, nopinene, tea polyphenols are sufficiently stirred for all
Even, obtain liquid material.
A kind of low temperature resistant water-repellent paint the most as claimed in claim 1, it is characterised in that the preparation method of described powder is as follows:
By portland cement, 200-300 mesh anion powder, 20-500 mesh hyperbranched quaternary ammonium salt, 20-500 mesh isopropyl myristate, N-
Phenyl beta naphthylamine, phenyl salicylate, water reducer mixing and stirring, obtain powder.
5. the using method of a low temperature resistant water-repellent paint, it is characterised in that comprise the steps:
(1) powder in the water-repellent paint described in Claims 1-4 any one is slowly added in liquid material and constantly stirs
Mix, until stirring into homogeneous paste and i.e. obtaining rubber cement without small particles or bubble；
(2) directly step (1) gained rubber cement is uniformly painted on basal plane with hairbrush or round brush, in smearing, is stirred continuously glue
Slurry.