CN106116149A - A kind of Spora Lygodii glaze containing shraff and preparation method thereof - Google Patents
A kind of Spora Lygodii glaze containing shraff and preparation method thereof Download PDFInfo
- Publication number
- CN106116149A CN106116149A CN201610461614.9A CN201610461614A CN106116149A CN 106116149 A CN106116149 A CN 106116149A CN 201610461614 A CN201610461614 A CN 201610461614A CN 106116149 A CN106116149 A CN 106116149A
- Authority
- CN
- China
- Prior art keywords
- shraff
- parts
- spora lygodii
- glaze
- bentonite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of Spora Lygodii glaze containing shraff and preparation method thereof, this Spora Lygodii glaze is made up of according to the raw material of weight portion following: potassium feldspar 20 40 parts, calcium carbonate 10 20 parts, Bentonite 15 35 parts, 20 40 parts of quartz, ferrum oxide 10 20 parts, shraff 10 30 parts.Weigh potassium feldspar, calcium carbonate, Bentonite, quartz, ferrum oxide, shraff by weight, grind mix homogeneously after sieving, then mixed material is applied on ceramic body, then insert in electrical kiln, through 1,250 1280 DEG C of high melts 34 hours, i.e. burn till Spora Lygodii glaze.The present invention is coated on base substrate so that base substrate has resistant to elevated temperatures characteristic, has preferable corrosion resistance simultaneously, and glaze is in hot environment, can keep corrosion resistant characteristic for a long time.Spora Lygodii glaze is the invention enables to be combined with base substrate more firm so that adhesion property is more preferable；Also have by clean can the excellent chemical resistance restored, the suitability is wide.
Description
Technical field
The present invention relates to technical field of ceramic material, a kind of Spora Lygodii glaze containing shraff and preparation side thereof
Method.
Background technology
Chinese pottery, since Han dynasty, has just utilized the various plant ashes of the clay containing different elements and heterogeneity to make
For coloring agent decorative porcelain vessel.Spora Lygodii glaze is that the ferrous components with a large amount obtains countless minute metallic at high temperature with burning till under control
Ferrum oxide crystal, these crystal are not the Surface Creations at glaze, and are suspended in glaze layer.Therefore when light irradiates, can be anti-
Penetrate radiance.Very much like with the gold dust of nature, so referred to as Spora Lygodii glaze.Spora Lygodii glaze is more excellent in many aspects,
Such as hardness, weatherability and anti-flammability, but there is also corresponding problem, and i.e. production cost is expensive and Spora Lygodii glaze is easily peeled off, clearly
Wash restoration poor, poor heat resistance.
Summary of the invention
It is an object of the invention to provide a kind of high temperature resistant, corrosion resistance, adhesion property are good, clean that restoration is high, contain
Spora Lygodii glaze of shraff and preparation method thereof, with the problem solving to propose in above-mentioned background technology.
For achieving the above object, the present invention provides following technical scheme:
A kind of Spora Lygodii glaze containing shraff, is made up of according to the raw material of weight portion following:
Potassium feldspar 20-40 part
Calcium carbonate 10-20 part
Bentonite 15-35 part
Quartz 20-40 part
Ferrum oxide 10-20 part
Shraff 10-30 part.
As the further scheme of the present invention: the described Spora Lygodii glaze containing shraff, by following former according to weight portion
Material composition:
Potassium feldspar 25-35 part
Calcium carbonate 12-18 part
Bentonite 20-30 part
Quartz 25-35 part
Ferrum oxide 12-18 part
Shraff 15-25 part.
As the further scheme of the present invention: the described Spora Lygodii glaze containing shraff, by following former according to weight portion
Material composition:
Potassium feldspar 28-32 part
Calcium carbonate 13-17 part
Bentonite 22-18 part
Quartz 28-32 part
Ferrum oxide 13-17 part
Shraff 18-22 part.
As the further scheme of the present invention: the described Spora Lygodii glaze containing shraff, by following former according to weight portion
Material composition:
Potassium feldspar 30 parts
Calcium carbonate 15 parts
Bentonite 25 parts
30 parts of quartz
Ferrum oxide 15 parts
Shraff 20 parts.
The preparation method of the described Spora Lygodii glaze containing shraff, weighs potassium feldspar, calcium carbonate, Bentonite, stone by weight
English, ferrum oxide, shraff, ground mix homogeneously after 200 mesh sieves, then be applied on ceramic body by mixed material, so
After insert in electrical kiln, through 1250-1280 DEG C of high melt 3-4 hour, i.e. burn till Spora Lygodii glaze.
Compared with prior art, the invention has the beneficial effects as follows:
Spora Lygodii glaze of the present invention is coated on base substrate so that base substrate has resistant to elevated temperatures characteristic, has the most corrosion-resistant simultaneously
Property, glaze is in hot environment, can keep corrosion resistant characteristic for a long time.Spora Lygodii glaze of the present invention uses potassium feldspar, carbonic acid
It is more firm that calcium, Bentonite etc. make Spora Lygodii glaze be combined with base substrate with the mixing of ferrum oxide so that adhesion property is more preferable；In addition this
Bright also have by clean can the excellent chemical resistance restored, there is wide applicability.
Detailed description of the invention
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only a part of embodiment of the present invention rather than whole embodiments.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under not making creative work premise, all
Belong to the scope of protection of the invention.
Embodiment 1
In the embodiment of the present invention, a kind of Spora Lygodii glaze containing shraff, it is made up of according to the raw material of weight portion following:
Potassium feldspar 20 parts
Calcium carbonate 10 parts
Bentonite 15 parts
20 parts of quartz
Ferrum oxide 10 parts
Shraff 10 parts.
The preparation method of the described Spora Lygodii glaze containing shraff, weighs potassium feldspar, calcium carbonate, Bentonite, stone by weight
English, ferrum oxide, shraff, ground mix homogeneously after 200 mesh sieves, then be applied on ceramic body by mixed material, so
After insert in electrical kiln, through 1250 DEG C of high melts 3 hours, i.e. burn till the Spora Lygodii glaze containing shraff.
Embodiment 2
In the embodiment of the present invention, a kind of Spora Lygodii glaze containing shraff, it is made up of according to the raw material of weight portion following:
Potassium feldspar 40 parts
Calcium carbonate 20 parts
Bentonite 35 parts
40 parts of quartz
Ferrum oxide 20 parts
Shraff 30 parts.
The preparation method of the described Spora Lygodii glaze containing shraff, weighs potassium feldspar, calcium carbonate, Bentonite, stone by weight
English, ferrum oxide, shraff, ground mix homogeneously after 200 mesh sieves, then be applied on ceramic body by mixed material, so
After insert in electrical kiln, through 1280 DEG C of high melts 4 hours, i.e. burn till the Spora Lygodii glaze containing shraff.
Embodiment 3
In the embodiment of the present invention, a kind of Spora Lygodii glaze containing shraff, it is made up of according to the raw material of weight portion following:
Potassium feldspar 25 parts
Calcium carbonate 12 parts
Bentonite 20 parts
25 parts of quartz
Ferrum oxide 12 parts
Shraff 15 parts.
The preparation method of the described Spora Lygodii glaze containing shraff, weighs potassium feldspar, calcium carbonate, Bentonite, stone by weight
English, ferrum oxide, shraff, ground mix homogeneously after 200 mesh sieves, then be applied on ceramic body by mixed material, so
After insert in electrical kiln, through 1260 DEG C of high melts 3.2 hours, i.e. burn till the Spora Lygodii glaze containing shraff.
Embodiment 4
In the embodiment of the present invention, a kind of Spora Lygodii glaze containing shraff, it is made up of according to the raw material of weight portion following:
Potassium feldspar 35 parts
Calcium carbonate 18 parts
Bentonite 30 parts
35 parts of quartz
Ferrum oxide 18 parts
Shraff 25 parts.
The preparation method of the described Spora Lygodii glaze containing shraff, weighs potassium feldspar, calcium carbonate, Bentonite, stone by weight
English, ferrum oxide, shraff, ground mix homogeneously after 200 mesh sieves, then be applied on ceramic body by mixed material, so
After insert in electrical kiln, through 1270 DEG C of high melts 3.8 hours, i.e. burn till the Spora Lygodii glaze containing shraff.
Embodiment 5
In the embodiment of the present invention, a kind of Spora Lygodii glaze containing shraff, it is made up of according to the raw material of weight portion following:
Potassium feldspar 28 parts
Calcium carbonate 13 parts
Bentonite 22 parts
28 parts of quartz
Ferrum oxide 13 parts
Shraff 18 parts.
The preparation method of the described Spora Lygodii glaze containing shraff, weighs potassium feldspar, calcium carbonate, Bentonite, stone by weight
English, ferrum oxide, shraff, ground mix homogeneously after 200 mesh sieves, then be applied on ceramic body by mixed material, so
After insert in electrical kiln, through 1250 DEG C of high melts 3.4 hours, i.e. burn till the Spora Lygodii glaze containing shraff.
Embodiment 6
In the embodiment of the present invention, a kind of Spora Lygodii glaze containing shraff, it is made up of according to the raw material of weight portion following:
Potassium feldspar 32 parts
Calcium carbonate 17 parts
Bentonite 18 parts
32 parts of quartz
Ferrum oxide 17 parts
Shraff 22 parts.
The preparation method of the described Spora Lygodii glaze containing shraff, weighs potassium feldspar, calcium carbonate, Bentonite, stone by weight
English, ferrum oxide, shraff, ground mix homogeneously after 200 mesh sieves, then be applied on ceramic body by mixed material, so
After insert in electrical kiln, through 1280 DEG C of high melts 3.6 hours, i.e. burn till the Spora Lygodii glaze containing shraff.
Embodiment 7
In the embodiment of the present invention, a kind of Spora Lygodii glaze containing shraff, it is made up of according to the raw material of weight portion following:
Potassium feldspar 30 parts
Calcium carbonate 15 parts
Bentonite 25 parts
30 parts of quartz
Ferrum oxide 15 parts
Shraff 20 parts.
The preparation method of the described Spora Lygodii glaze containing shraff, weighs potassium feldspar, calcium carbonate, Bentonite, stone by weight
English, ferrum oxide, shraff, ground mix homogeneously after 200 mesh sieves, then be applied on ceramic body by mixed material, so
After insert in electrical kiln, through 1270 DEG C of high melts 3.5 hours, i.e. burn till the Spora Lygodii glaze containing shraff.
Embodiment 8
In the embodiment of the present invention, a kind of Spora Lygodii glaze containing shraff, it is made up of according to the raw material of weight portion following:
Potassium feldspar 22 parts
Calcium carbonate 11 parts
Bentonite 18 parts
20 parts of quartz
Ferrum oxide 11 parts
Shraff 20 parts.
The preparation method of the described Spora Lygodii glaze containing shraff, weighs potassium feldspar, calcium carbonate, Bentonite, stone by weight
English, ferrum oxide, shraff, ground mix homogeneously after 200 mesh sieves, then be applied on ceramic body by mixed material, so
After insert in electrical kiln, through 1250 DEG C of high melts 3.1 hours, i.e. burn till the Spora Lygodii glaze containing shraff.
Embodiment 9
In the embodiment of the present invention, a kind of Spora Lygodii glaze containing shraff, it is made up of according to the raw material of weight portion following:
Potassium feldspar 38 parts
Calcium carbonate 19 parts
Bentonite 32 parts
40 parts of quartz
Ferrum oxide 19 parts
Shraff 20 parts.
The preparation method of the described Spora Lygodii glaze containing shraff, weighs potassium feldspar, calcium carbonate, Bentonite, stone by weight
English, ferrum oxide, shraff, ground mix homogeneously after 200 mesh sieves, then be applied on ceramic body by mixed material, so
After insert in electrical kiln, through 1280 DEG C of high melt .3.9 hours, i.e. burn till the Spora Lygodii glaze containing shraff.
Embodiment 10
In the embodiment of the present invention, a kind of Spora Lygodii glaze containing shraff, it is made up of according to the raw material of weight portion following:
Potassium feldspar 27 parts
Calcium carbonate 14 parts
Bentonite 24 parts
29 parts of quartz
Ferrum oxide 14 parts
Shraff 20 parts.
The preparation method of the described Spora Lygodii glaze containing shraff, weighs potassium feldspar, calcium carbonate, Bentonite, stone by weight
English, ferrum oxide, shraff, ground mix homogeneously after 200 mesh sieves, then be applied on ceramic body by mixed material, so
After insert in electrical kiln, through 1260 DEG C of high melts 3.3 hours, i.e. burn till the Spora Lygodii glaze containing shraff.
Embodiment 11
In the embodiment of the present invention, a kind of Spora Lygodii glaze containing shraff, it is made up of according to the raw material of weight portion following:
Potassium feldspar 33 parts
Calcium carbonate 16 parts
Bentonite 27 parts
31 parts of quartz
Ferrum oxide 16 parts
Shraff 20 parts.
The preparation method of the described Spora Lygodii glaze containing shraff, weighs potassium feldspar, calcium carbonate, Bentonite, stone by weight
English, ferrum oxide, shraff, ground mix homogeneously after 200 mesh sieves, then be applied on ceramic body by mixed material, so
After insert in electrical kiln, through 1270 DEG C of high melts 3.7 hours, i.e. burn till the Spora Lygodii glaze containing shraff.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of the spirit or essential attributes of the present invention, it is possible to realize the present invention in other specific forms.Therefore, no matter
From the point of view of which point, all should regard embodiment as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit requires rather than described above limits, it is intended that all by fall in the implication of equivalency and scope of claim
Change is included in the present invention.
Although moreover, it will be appreciated that this specification is been described by according to embodiment, but the most each embodiment only wraps
Containing an independent technical scheme, this narrating mode of description is only that for clarity sake those skilled in the art should
Description can also be formed those skilled in the art through appropriately combined as an entirety, the technical scheme in each embodiment
May be appreciated other embodiments.
Claims (5)
1. the Spora Lygodii glaze containing shraff, it is characterised in that be made up of according to the raw material of weight portion following:
Potassium feldspar 20-40 part
Calcium carbonate 10-20 part
Bentonite 15-35 part
Quartz 20-40 part
Ferrum oxide 10-20 part
Shraff 10-30 part.
Spora Lygodii glaze containing shraff the most according to claim 1, it is characterised in that by following former according to weight portion
Material composition:
Potassium feldspar 25-35 part
Calcium carbonate 12-18 part
Bentonite 20-30 part
Quartz 25-35 part
Ferrum oxide 12-18 part
Shraff 15-25 part.
Spora Lygodii glaze containing shraff the most according to claim 1, it is characterised in that by following former according to weight portion
Material composition:
Potassium feldspar 28-32 part
Calcium carbonate 13-17 part
Bentonite 22-18 part
Quartz 28-32 part
Ferrum oxide 13-17 part
Shraff 18-22 part.
Spora Lygodii glaze containing shraff the most according to claim 1, it is characterised in that by following former according to weight portion
Material composition:
Potassium feldspar 30 parts
Calcium carbonate 15 parts
Bentonite 25 parts
30 parts of quartz
Ferrum oxide 15 parts
Shraff 20 parts.
5. the preparation method of the Spora Lygodii glaze containing shraff as described in claim 1-4 is arbitrary, it is characterised in that press
Weight portion weighs potassium feldspar, calcium carbonate, Bentonite, quartz, ferrum oxide, shraff, and after grinding 200 mesh sieves, mixing was all
Even, then mixed material is applied on ceramic body, then insert in electrical kiln, through 1250-1280 DEG C of high melt 3-4 hour,
I.e. burn till Spora Lygodii glaze.