CN106113809A - A kind of composite wood-plastic sheet material and production technology thereof - Google Patents
A kind of composite wood-plastic sheet material and production technology thereof Download PDFInfo
- Publication number
- CN106113809A CN106113809A CN201610623534.9A CN201610623534A CN106113809A CN 106113809 A CN106113809 A CN 106113809A CN 201610623534 A CN201610623534 A CN 201610623534A CN 106113809 A CN106113809 A CN 106113809A
- Authority
- CN
- China
- Prior art keywords
- woven fabrics
- attached
- veneer
- sheet material
- plastic sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of composite wood-plastic sheet material and production technology thereof, relate to wood-plastic board production technical field, including substrate, non-woven fabrics, veneer, color paper and abrasion-proof paper, described non-woven fabrics is attached to the surface of substrate, described veneer is attached to the upside of non-woven fabrics, described color paper is attached to the upside of veneer, and described abrasion-proof paper is attached to the upside of color paper.Comprise the following steps, 1), non-woven fabrics is shakeout, then the thermosetting cement after heating is poured into the inside of non-woven fabrics, then non-woven fabrics is attached to the surface of substrate；2), before the uncolled sizing of thermosetting cement, veneer is fitted on non-woven fabrics, then cooling and shaping；3), color paper and abrasion-proof paper pass sequentially through binding agent the most again attach.Production cost of the present invention is low, and intensity is high, and wearability is good, resistance to tears, and environment-friendly waterproof is effective.
Description
Technical field:
The present invention relates to wood-plastic board production technical field, specifically a kind of composite wood-plastic sheet material and production technology thereof.
Background technology:
Wood-plastic composite panel is a kind of mainly high with thermoplasticity by material based on timber (lignose, plant cellulose)
Molecular material (plastics) and processing aid etc., the high-tech made through die apparatus heating extrusion molding again after mix homogeneously is green
Colour circle protects new decorative material, has timber and the performance of plastics and feature concurrently, is the NEW TYPE OF COMPOSITE material that can substitute timber and plastics
Material.Wood-plastic board so that exterior appearance and increase service life, typically can attach one layer of color paper and wear-resisting in outside
Paper, color paper and abrasion-proof paper can not directly be attached in wood-plastic board, are typically all the graft material in the middle of needing, existing skill
Art generally uses the kraft paper graft material as centre, but kraft paper is expensive, therefore can cause wood-plastic board
Relatively costly, and the thickness of kraft paper is fixed, and is being typically to also need to use substantial amounts of glue to carry out as middle graft material
Thicken, also result in cost and raise.
Summary of the invention:
The technical problem to be solved is to provide a kind of production cost low, and intensity is high, and environment-friendly waterproof is effective
Composite wood-plastic sheet material and production technology.
Solve the technical problem that used following technical scheme:
A kind of composite wood-plastic sheet material, it is characterised in that: include substrate, non-woven fabrics, veneer, color paper and abrasion-proof paper, described
Non-woven fabrics be attached to the surface of substrate, described veneer is attached to the upside of non-woven fabrics, and described color paper is attached to veneer
Upside, described abrasion-proof paper is attached to the upside of color paper.
Also include that freezing plastic, described freezing plastic are immersed in the inside of non-woven fabrics.
A kind of production technology of composite wood-plastic sheet material, it is characterised in that: comprise the following steps,
1), non-woven fabrics is shakeout, then the thermosetting cement after heating is poured into the inside of non-woven fabrics, then non-woven fabrics is pasted
Surface at substrate；
2), before the uncolled sizing of thermosetting cement, veneer is fitted on non-woven fabrics, then cooling and shaping；
3), color paper and abrasion-proof paper pass sequentially through binding agent the most again attach.
Described veneer is Recombinant Wood.
Described non-woven fabrics thickeies thickness by being folded into multilamellar.
Described freezing plastic is PUR.
The present invention is to use non-woven fabrics and veneer to coordinate combining freezing plastic, and the production technology of uniqueness, shape
One-tenth can substitute kraft paper as middle graft material, well can adhere to substrate and color paper simultaneously, play very
Good grafting, can be substantially reduced the cost of traditional mode of production simultaneously, and wearability of the present invention is good, resistance to tears, good water-proof effect,
Less than 50 DEG C indeformable features.
The invention has the beneficial effects as follows: production cost of the present invention is low, intensity is high, and wearability is good, resistance to tears, environment-friendly waterproof effect
Good.
Detailed description of the invention:
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below knot
Close instantiation, the present invention is expanded on further.
A kind of composite wood-plastic sheet material, including substrate, non-woven fabrics, veneer, color paper and abrasion-proof paper, non-woven fabrics is attached to substrate
Surface, veneer is attached to the upside of non-woven fabrics, and color paper is attached to the upside of veneer, and abrasion-proof paper is attached to the upper of color paper
Side.
Also include that freezing plastic, described freezing plastic are immersed in the inside of non-woven fabrics.
The production technology of a kind of composite wood-plastic sheet material, comprises the following steps,
1), non-woven fabrics is shakeout, then the thermosetting cement after heating is poured into the inside of non-woven fabrics, then non-woven fabrics is pasted
Surface at substrate；
2), before the uncolled sizing of thermosetting cement, veneer is fitted on non-woven fabrics, then cooling and shaping；
3), color paper and abrasion-proof paper pass sequentially through binding agent the most again attach.
Veneer is Recombinant Wood.
Non-woven fabrics thickeies thickness by being folded into multilamellar.
Freezing plastic is PUR.
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.The technology of the industry
Personnel, it should be appreciated that the present invention is not restricted to the described embodiments, simply illustrating this described in above-described embodiment and description
The principle of invention, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, and these become
Change and improvement both falls within scope of the claimed invention.Claimed scope by appending claims and
Equivalent defines.
Claims (6)
1. a composite wood-plastic sheet material, it is characterised in that: include substrate, non-woven fabrics, veneer, color paper and abrasion-proof paper, described
Non-woven fabrics is attached to the surface of substrate, and described veneer is attached to the upside of non-woven fabrics, and described color paper is attached to veneer
Upside, described abrasion-proof paper is attached to the upside of color paper.
A kind of composite wood-plastic sheet material the most according to claim 1, it is characterised in that: also include freezing plastic, described solidification
Glue is immersed in the inside of non-woven fabrics.
The production technology of a kind of composite wood-plastic sheet material the most according to claim 1, it is characterised in that: comprise the following steps,
1), non-woven fabrics is shakeout, then the thermosetting cement after heating is poured into the inside of non-woven fabrics, then non-woven fabrics is attached to base
The surface of plate；
2), before the uncolled sizing of thermosetting cement, veneer is fitted on non-woven fabrics, then cooling and shaping；
3), color paper and abrasion-proof paper pass sequentially through binding agent the most again attach.
A kind of composite wood-plastic sheet material the most according to claim 1, it is characterised in that: described veneer is Recombinant Wood.
The production technology of a kind of composite wood-plastic sheet material the most according to claim 2, it is characterised in that: described non-woven fabrics leads to
Cross and be folded into multilamellar to thicken thickness.
The production technology of a kind of composite wood-plastic sheet material the most according to claim 2, it is characterised in that: described freezing plastic is
PUR.