CN106113720B - A kind of Reflection fabric for reflecting seven glories and preparation method thereof - Google Patents
A kind of Reflection fabric for reflecting seven glories and preparation method thereof Download PDFInfo
- Publication number
- CN106113720B CN106113720B CN201610464083.9A CN201610464083A CN106113720B CN 106113720 B CN106113720 B CN 106113720B CN 201610464083 A CN201610464083 A CN 201610464083A CN 106113720 B CN106113720 B CN 106113720B
- Authority
- CN
- China
- Prior art keywords
- film
- layer
- metal oxide
- fabric
- reflecting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to reflectorized material technical field, a kind of Reflection fabric for reflecting seven glories is provided, reflexed light film including fabric and on fabric, reflexed light film include film layer, laminated polyester film, the first PU resin beds, the 2nd PU resin beds, a plurality of glass microballoons and metal oxide reflecting layer；The Reflection fabric preparation method comprises the following steps：（1）Film layer and laminated polyester film is compound；（2）Glass microballoon is uniformly arranged and is implanted in the film layer of composite membrane；（3）Beads formed film is located in film layer with the extruding of the first PU resin beds；（4）The beads formed film for extruding PU resin beds is subjected to metal oxide reflecting layer；（5）The extruding of 2nd PU resin beds is covered on metal oxide reflecting layer；（6）By reflexed light film combination adhesive and fabric assembly.The problems such as the present invention solves existing Reflection fabric low production efficiency, structure is single, reflecting effect is low.
Description
Technical field
The present invention relates to reflectorized material technical field, more particularly to a kind of Reflection fabric for reflecting seven glories and its preparation side
Method.
Background technology
Reflection fabric plays obvious warning function on daytime with its bright colors, in night or the situation of insufficient light
Under, its bright reflecting effect can effectively strengthen the recognition capability of people, see target clearly, arouse vigilance, so as to avoid accident
Occur, reduce casualties, reduce economic loss, turn into the indispensable security guard of road traffic, there is obvious society
Benefit.Reflection fabric product in the market, the reflective membrane on its fabric are produced using screen printing technique, screen printing
Brush production have three it is serious the defects of：First, the thinner thickness that it prints every time, general only 5 μm or so, if to reach
20-30 μm of thickness, it is just very low throughout the above, so its efficiency that it just has to chromatography repeatedly 5；Second, screen printing
Brush is to use version print technology, and it is the printing of one edition one edition, and the slitless connection between version and version can not solve, the 3rd, using silk
The full wafer reflective membrane of wire mark brush is not water-fastness easily to come off；So that the existing staff to be worked on road, uses with it
Reflective clothing retroreflective made of reflective membrane can it is poor, performance is unstable, service life is short, be unfavorable for big rule film popularization and
Use.
The content of the invention
Therefore, for it is above-mentioned the problem of, the present invention proposes a kind of Reflection fabric and preparation method thereof for reflecting seven glories, adopts
With the present invention program can effectively produce good reflecting effect, stable performance, it is comfortable and easy to wear, suitable for a variety of clothes, shoes and hats, skin
Leather etc. can reflect the Reflection fabric of seven glories.
To solve this technical problem, the present invention takes following scheme：A kind of Reflection fabric preparation method for reflecting seven glories,
Comprise the following steps：
（1）Film layer and laminated polyester film adhesive are obtained into composite membrane by the way that dry compound machine is compound；
（2）Glass microballoon is uniformly arranged to the film layer for being implanted in the composite membrane that previous step obtains by fuse machine
On, obtain beads formed film；
（3）The extruding of first PU resin beds is located at polyethylene by the beads formed film that previous step is obtained using upper and lower compression roller
On the groove formed in film layer and between glass microballoon, the beads formed film of PU resin beds was extruded；
（4）The extruding that previous step is obtained PU resin beds beads formed film by vacuum coating equipment in beads formed film away from poly-
Layer of metal oxide reflecting layer is plated in the one side of ester film layer, obtains the beads formed film of metal oxide；
（5）The beads formed film for the metal oxide that previous step is obtained uses upper and lower compression roller by the 2nd PU resins again
Layer extruding is covered on metal oxide reflecting layer and is filled on the groove formed between glass microballoon, obtains reflexed light film；
（6）The reflexed light film that previous step obtains is bonded or passed through with fabric by gravure roll combination adhesive
It is bonded after coating adhesive with fabric, Reflection fabric is made.
It is further to improve, the step（4）Middle metal oxide reflecting layer includes the section film of a plurality of interconnections
Layer, the thicknesses of layers of the adjacent interval film layer in the metal oxide reflecting layer are different.
It is further to improve, the step（4）The thickness range of each section film layer in middle metal oxide reflecting layer
For 0.3 μm~3 μm.
Further to improve, the metal oxide reflecting layer is alundum (Al2O3) reflecting layer.
It is further to improve, the step（6）In fabric can be any one in cloth, skin, leather.
A kind of Reflection fabric that seven glories of reflection are made using the above method, including fabric and the reflective membrane on fabric
Layer, the reflexed light film include film layer, laminated polyester film, the first PU resin beds, the 2nd PU resin beds, a plurality of glass
Glass microballon and metal oxide reflecting layer, the film layer is located at laminated polyester film upper surface by adhesive, described
Glass microballoon is uniformly planted in one side of the film layer away from laminated polyester film, and the first PU resin beds are set by extruding
In on the groove formed in film layer and between glass microballoon, the metal oxide reflecting layer is micro- located at glass
On pearl and the first one side of the PU resin beds away from film layer, the 2nd PU resin beds are aoxidized by extruding located at metal
On thing reflecting layer and it is filled on the groove formed between glass microballoon.
Further to improve, the fabric is any one in cloth, skin, leather.
Further to improve, the metal oxide reflecting layer includes the section film layer of a plurality of interconnections, the gold
The thicknesses of layers for belonging to the adjacent interval film layer in oxide reflecting layer is different.
Further to improve, the thickness range of each section film layer in the metal oxide reflecting layer is 0.3 μm~3
μm。
Further to improve, the metal oxide reflecting layer is alundum (Al2O3) reflecting layer.
By using preceding solution, the beneficial effects of the invention are as follows：By by film layer, polyester film
Layer, the first PU resin beds, the 2nd PU resin beds, a plurality of glass microballoons and metal oxide reflecting layer are combined reflective membrane
Layer, then reflexed light film is bonded by gravure roll combination adhesive with fabric, you can obtained Reflection fabric, and glass microballoon
By the compounded reflexed light film Stability Analysis of Structures of this method, and the inventive method production reflexed light film speed is fast, is combined to face
The material last time is plastic, and production efficiency is high, greatly reduces the production cost of Reflection fabric, while it uses metal oxide
Reflecting layer so that Reflection fabric produces the reflected light of different colours under different visual angles, forms seven glories, reflecting effect is good, instead
Obvious, comfortable and easy to wear, suitable for clothes, shoes and hats, leather etc. the Reflection fabric of light lines, can wide popularization and application；By entering one
The improvement of step, i.e. metal oxide reflecting layer are formed using a plurality of sections and the thicknesses of layers of adjacent interval film layer is different, are entered
One step enhances the reflecting effect in metal oxide reflecting layer, and different colours can be produced without different visual angles viewing Reflection fabric
Reflected light, further enhancing reflecting effect.
Brief description of the drawings
Fig. 1 is the section mplifying structure schematic diagram of reflexed light film in the embodiment of the present invention.
Embodiment
In conjunction with the drawings and specific embodiments, the present invention is further described.
With reference to figure 1, a kind of Reflection fabric preparation method of the glory of reflection seven of the preferable present invention, comprise the following steps：
（1）Film layer and laminated polyester film adhesive are obtained into composite membrane by the way that dry compound machine is compound；
（2）Glass microballoon is uniformly arranged to the film layer for being implanted in the composite membrane that previous step obtains by fuse machine
On, obtain beads formed film；
（3）The extruding of first PU resin beds is located at polyethylene by the beads formed film that previous step is obtained using upper and lower compression roller
On the groove formed in film layer and between glass microballoon, the beads formed film of PU resin beds was extruded；
（4）The extruding that previous step is obtained PU resin beds beads formed film by vacuum coating equipment in beads formed film away from poly-
Layer of metal oxide reflecting layer is plated in the one side of ester film layer, obtains the beads formed film of metal oxide, wherein metal aoxidizes
Thing reflecting layer includes the section film layer of a plurality of interconnections, the film layer of the adjacent interval film layer in the metal oxide reflecting layer
Thickness is different, and thicknesses of layers is completed by adjusting electric current and the evaporating temperature of vacuum coating equipment to control, the metal oxide
Reflecting layer is alundum (Al2O3) reflecting layer, the thickness of each section film layer in metal oxide reflecting layer correspond to respectively 0.5 μm,
One in 0.7 μm, 0.8 μm, 1.0 μm, 1.2 μm, 1.6 μm, 1.8 μm, the thickness of adjacent section film layer is different；
（5）The beads formed film for the metal oxide that previous step is obtained uses upper and lower compression roller by the 2nd PU resins again
Layer extruding is covered on metal oxide reflecting layer and is filled on the groove formed between glass microballoon, obtains reflexed light film；
（6）The reflexed light film that previous step obtains is bonded by gravure roll combination adhesive with fabric, the fabric
For cloth, Reflection fabric is made.
A kind of Reflection fabric that seven glories of reflection are made using the above method, including fabric and the reflective membrane on fabric
Layer, the fabric are cloth, and the reflexed light film includes film layer 1, laminated polyester film 2, the first PU resin beds 3, second
PU resin beds 4, a plurality of glass microballoons 5 and metal oxide reflecting layer 6, the film layer 1 are located at by adhesive
The upper surface of laminated polyester film 2, the glass microballoon 5 are uniformly planted in one side of the film layer 1 away from laminated polyester film 2,
The first PU resin beds 3 are located on the groove formed in film layer 1 and between glass microballoon 5 by extruding,
The metal oxide reflecting layer 6 is in one side of the PU resin beds 3 away from film layer 1 of glass microballoon 5 and the first, institute
The 2nd PU resin beds 4 are stated to be located on metal oxide reflecting layer 6 by extruding and be filled in the groove formed between glass microballoon 5
On, the refractive index of the glass microballoon is 1.91, the 1/4 sphere implantation film layer 1 of the glass microballoon, described first
PU resin layer thickness is 3.1 μm, and the 2nd PU resin layer thickness is 2.8 μm, and the metal oxide reflecting layer 6 includes plural number
The section film layer of individual interconnection, the thicknesses of layers of the adjacent interval film layer in the metal oxide reflecting layer 6 is different, metal oxygen
The thickness of each section film layer in compound reflecting layer correspond to respectively 0.5 μm, 0.7 μm, 0.8 μm, 1.0 μm, 1.2 μm, 1.6 μm,
One in 1.8 μm, the thickness of adjacent section film layer is different, and the metal oxide reflecting layer 6 is reflected for alundum (Al2O3)
Layer.
The thickness of each section film layer in heretofore described metal oxide reflecting layer is preferred with 0.3 μm~3 μm, described
Metal oxide reflecting layer can also be other metal oxide reflecting layer such as alundum (Al2O3) reflecting layer, and reflexed light film may be used also
It is bonded by coating with fabric after adhesive, it can be any one in cloth, skin, leather that Reflection fabric fabric, which is made,；Glass is micro-
The refractive index of pearl is preferred with 1.90~1.93, and the first PU resin layer thickness is preferred with 2.5 μm~3.5 μm, the 2nd PU resin thickness
Degree is preferred with 2.5 μm~3.5 μm.
The present invention is by by film layer, laminated polyester film, the first PU resin beds, the 2nd PU resin beds, a plurality of
Glass microballoon and metal oxide reflecting layer are combined reflexed light film, then reflexed light film is passed through into gravure roll combination gluing
Agent is bonded with fabric, you can Reflection fabric is made, and glass microballoon is by the compounded reflexed light film Stability Analysis of Structures of this method, and
And the inventive method production reflexed light film speed is fast, it is i.e. plastic to be combined to the fabric last time, and production efficiency is high, greatly reduces
The production cost of Reflection fabric, while it uses metal oxide reflecting layer so that Reflection fabric produces not under different visual angles
With the reflected light of color, form seven glories, reflecting effect is good, reflective lines is obvious, it is comfortable and easy to wear, suitable for clothes, shoes and hats, skin
The Reflection fabric of leather etc., can wide popularization and application；By further improving, i.e., metal oxide reflecting layer uses a plurality of areas
Between form and the thicknesses of layers of adjacent interval film layer is different, further enhancing the reflecting effect in metal oxide reflecting layer, nothing
Need different visual angles viewing Reflection fabric to produce the reflected light of different colours, further enhancing reflecting effect.
Although specifically showing and describing the present invention with reference to preferred embodiment, those skilled in the art should be bright
In vain, do not departing from the spirit and scope of the present invention that appended claims are limited, in the form and details can be right
The present invention makes a variety of changes, and is protection scope of the present invention.
Claims (10)
- A kind of 1. Reflection fabric preparation method for reflecting seven glories, it is characterised in that：Comprise the following steps：（1）Film layer and laminated polyester film adhesive are obtained into composite membrane by the way that dry compound machine is compound；（2）Glass microballoon is uniformly arranged by fuse machine and is implanted in the film layer for the composite membrane that previous step obtains, Obtain beads formed film；（3）The extruding of first PU resin beds is located at polyethylene film by the beads formed film that previous step is obtained using upper and lower compression roller On the groove formed on layer and between glass microballoon, the beads formed film of PU resin beds was extruded；（4）The extruding that previous step is obtained PU resin beds beads formed film by vacuum coating equipment in beads formed film away from polyester Layer of metal oxide reflecting layer is plated in the one side of film layer, obtains the beads formed film of metal oxide；（5）The beads formed film for the metal oxide that previous step is obtained again is squeezed the 2nd PU resin beds using upper and lower compression roller Gland is on metal oxide reflecting layer and is filled on the groove formed between glass microballoon, obtains reflexed light film；（6）The reflexed light film that previous step obtains is bonded or passed through coating by gravure roll combination adhesive with fabric It is bonded after adhesive with fabric, Reflection fabric is made.
- A kind of 2. Reflection fabric preparation method for reflecting seven glories according to claim 1, it is characterised in that：The step （4）Middle metal oxide reflecting layer includes the section film layer of a plurality of interconnections, the metal oxide reflecting layer it is adjacent The thicknesses of layers of section film layer is different.
- A kind of 3. Reflection fabric preparation method for reflecting seven glories according to claim 2, it is characterised in that：The step （4）The thickness range of each section film layer in middle metal oxide reflecting layer is 0.3 μm~3 μm.
- A kind of 4. Reflection fabric preparation method of the glory of reflection seven according to claim 1 or 2 or 3, it is characterised in that：Institute It is alundum (Al2O3) reflecting layer to state metal oxide reflecting layer.
- A kind of 5. Reflection fabric preparation method for reflecting seven glories according to claim 1, it is characterised in that：The step （6）In fabric can be any one in cloth, skin, leather.
- A kind of 6. Reflection fabric according to any one method of claim 1-5 seven glories of obtained reflection, it is characterised in that：Including Fabric and the reflexed light film on fabric, the reflexed light film include film layer, laminated polyester film, the first PU resins Layer, the 2nd PU resin beds, a plurality of glass microballoons and metal oxide reflecting layer, the film layer are set by adhesive In laminated polyester film upper surface, the glass microballoon is uniformly planted in one side of the film layer away from laminated polyester film, institute The first PU resin beds are stated by extruding on the groove formed in film layer and between glass microballoon, the gold Belong to oxide reflecting layer on glass microballoon and the first one side of the PU resin beds away from film layer, the 2nd PU trees Lipid layer on metal oxide reflecting layer and is filled on the groove formed between glass microballoon by extruding.
- A kind of 7. Reflection fabric for reflecting seven glories according to claim 6, it is characterised in that：The fabric be cloth, skin, Any one in leather.
- A kind of 8. Reflection fabric for reflecting seven glories according to claim 6, it is characterised in that：The metal oxide is anti- Penetrating layer includes the section film layer of a plurality of interconnections, the thicknesses of layers of the adjacent interval film layer in the metal oxide reflecting layer It is different.
- A kind of 9. Reflection fabric for reflecting seven glories according to claim 8, it is characterised in that：The metal oxide is anti- The thickness range for penetrating each section film layer of layer is 0.3 μm~3 μm.
- A kind of 10. Reflection fabric of the glory of reflection seven according to claim 6 or 8 or 9, it is characterised in that：The metal Oxide reflecting layer is alundum (Al2O3) reflecting layer.