CN106084651A - A kind of sports buildings floor glue and preparation method and application - Google Patents
A kind of sports buildings floor glue and preparation method and application Download PDFInfo
- Publication number
- CN106084651A CN106084651A CN201610617491.3A CN201610617491A CN106084651A CN 106084651 A CN106084651 A CN 106084651A CN 201610617491 A CN201610617491 A CN 201610617491A CN 106084651 A CN106084651 A CN 106084651A
- Authority
- CN
- China
- Prior art keywords
- floor glue
- sports buildings
- buildings floor
- parts
- sports
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to high-molecular organic material field, specifically provide a kind of sports buildings floor glue.The raw material of described sports buildings floor glue includes the composition of following mass parts: melamine resin 10～30 parts；Elastomer 10～30 parts；Chlorine partial emulsion 5～15 parts；Sodium carboxymethyl cellulose 0.5～1.5 parts；Wear-resistant material 20～40 parts；Filler 5～15 parts.The sports buildings floor glue that the present invention provides, do not fire, nontoxic, good springiness, wear-resisting, anti-skidding, non-reflective, do not chap, ageing-resistant, water-fast, adhesive force is strong.High temperature resistant more than 600 DEG C, low temperature resistant less than 40 DEG C, closed cell foam, firm but gentle.Can be widely applied to the ground such as stadiums, school, recreation ground, park, space for activities, residential quarter, for-all health security, kindergarten.
Description
Technical field
The present invention relates to high-molecular organic material field, specifically, relate to a kind of sports buildings floor glue.
Background technology
The floor glue continued to use at present is inflammable, dangerous, containing formaldehyde, how Anhui, Henan, Shanghai, Shenzhen in 2015 etc. are learned
There is poison runway events in school, Xinhua the reporter discovered that some schools's runway raw material is three-without-product, and formaldehyde, dimethylbenzene exceed standard
139 times, becoming the poisonous runway of plastic cement, product of the present invention does not contains formaldehyde, nonpoisonous and tasteless, is a kind of fully natural green product.
Summary of the invention
In order to solve problems of the prior art, it is an object of the invention to provide a kind of low temperature resistant, extensibility is strong
Sports buildings floor glue.
In order to realize the object of the invention, technical scheme is as follows:
Present invention firstly provides a kind of sports buildings floor glue, the raw material of described sports buildings floor glue includes following matter
The composition of amount part:
Wherein, described elastomer is selected from acrylic emulsion, IPDI (isophorone diisocyanate) or NDI (1,5-naphthalene two
Isocyanates) in one or more.One or more in glass microballoon, silica flour or calcium carbonate of described wear-resistant material.
One or more in titanium dioxide, White Carbon black or Kaolin of described filler.
As preferably, the raw material of described sports buildings floor glue includes the composition of following mass parts:
More preferably, the raw material of described sports buildings floor glue includes the composition of following mass parts:
In the above-mentioned technical scheme being more highly preferred to, the present invention still further preferably elastomer, wear-resistant material and filler
Concrete composition, the raw material of the most described sports buildings floor glue includes the composition of following mass parts:
In one particular embodiment of the present invention, above-mentioned sports buildings floor glue has at aspect elastic, wear-resisting, ageing-resistant
There is more preferably excellent performance.
Second aspect, present invention also offers the preparation method of aforementioned movement venue floor glue, particularly as follows: by tripolycyanamide
Formaldehyde resin, elastomer, chlorine partial emulsion and sodium carboxymethyl cellulose stir, then add wear-resistant material and filler stirs i.e.
Can.
According to actual needs, also while adding wear-resistant material and filler or afterwards can add pigment 1～10 parts, be stirred for
Uniformly.Optionally, described pigment can be chrome green or iron oxide red etc..
The third aspect, the invention provides the application in paving sports field of the aforementioned movement venue floor glue.
The ground of athletic ground or venue can be applied to, play its good springiness, wear-resisting, do not fire, ageing-resistant, attachment
The advantages such as power is strong, nontoxic.
The beneficial effects of the present invention is:
The sports buildings floor glue that the present invention provides, do not fire, nontoxic, good springiness, wear-resisting, anti-skidding, non-reflective, do not chap,
Ageing-resistant, water-fast, adhesive force is strong.High temperature resistant more than 600 DEG C, low temperature resistant less than 40 DEG C, closed cell foam, firm but gentle.Can be extensive
It is applied to the ground such as stadiums, school, recreation ground, park, space for activities, residential quarter, for-all health security, kindergarten.
Detailed description of the invention
Below in conjunction with embodiment, embodiment of the present invention are described in detail, but those skilled in the art will
Understanding, the following example is merely to illustrate the present invention, and should not be taken as limiting the scope of the invention.In embodiment unreceipted specifically
Condition person, the condition advised according to normal condition or manufacturer is carried out.Agents useful for same or instrument unreceipted production firm person, be
Can by city available from conventional products.
Embodiment 1
1, composition
2, preparation method:
Melamine resin, elastomer, chlorine partial emulsion and sodium carboxymethyl cellulose are stirred, then adds wear-resistant material
Stir with filler and i.e. obtain described sports buildings floor glue.
Embodiment 2
The present embodiment is with the difference of embodiment 1: described acrylic emulsion is replaced with IPDI.
Embodiment 3
The present embodiment is with the difference of embodiment 1: described acrylic emulsion is replaced with NDI.
Embodiment 4
The present embodiment is with the difference of embodiment 1: described titanium dioxide is replaced with Kaolin.
Embodiment 5
The present embodiment is with the difference of embodiment 1: described glass microballoon is replaced with silica flour.
Embodiment 6
The present embodiment is from the difference of embodiment 1: form different, as follows:
Embodiment 7
The present embodiment is from the difference of embodiment 1: form different, as follows:
Embodiment 8
The present embodiment is from the difference of embodiment 1: form different, as follows:
Embodiment 9
The present embodiment is from the difference of embodiment 1: form different, as follows:
Experimental example 1 abrasion test
Sports buildings floor glue described in embodiment 1～9 is taked the method for international practice DIN carry out detecting wearability
Can, testing result is shown in Table 1.The abrasion DIN index of general sizing material is≤200cm3, particular/special requirement for abrasion DIN index be≤
150cm3。
Table 1 abrasion resistance test results
| Test group | DIN index (cm<sup>3</sup>) |
| Embodiment 1 | 60 |
| Embodiment 2 | 68 |
| Embodiment 3 | 68 |
| Embodiment 4 | 66 |
| Embodiment 5 | 66 |
| Embodiment 6 | 89 |
| Embodiment 7 | 95 |
| Embodiment 8 | 115 |
| Embodiment 9 | 107 |
Experimental example 2 fire resistance test
The fire resistance of detection sports buildings floor glue described in embodiment 1～9, respectively to its impose naked light, cigarette end with
Electric wire break spark is tested, result display sports buildings floor glue described in embodiment 1～9 in above test the most not
Combustion, i.e. fire resistance are high, safe and reliable.
Experimental example 3 is heat-resisting, ageing-resistant performance test
Sports buildings floor glue described in embodiment 1～9 is applied to surface area respectively is 1m2(plank, sandstone, cement
Deng) in plane, skimulated motion space enrironment, and it is placed on high-temperature baking 10 times/day at 180 DEG C, each 4 minutes, enter continuously
Row test 3 months, found that there is not seminess, does not has catabiosis yet.
Experimental example 4 elasticity test
Sports buildings floor glue described in embodiment 1～9 is carried out flexibility test (GB/T6670-at ambient temperature
2008), compare that it is elastic, the results are shown in Table 2:
Table 2 elasticity test
| Test group | Elastic behavior |
| Embodiment 1 | Excellent |
| Embodiment 2 | Excellent |
| Embodiment 3 | Excellent |
| Embodiment 4 | Excellent |
| Embodiment 5 | Excellent |
| Embodiment 6 | Excellent |
| Embodiment 7 | Excellent |
| Embodiment 8 | Typically |
| Embodiment 9 | Typically |
Although, the present invention is described in detail the most with a general description of the specific embodiments, but
On the basis of the present invention, can make some modifications or improvements it, this will be apparent to those skilled in the art.Cause
This, these modifications or improvements without departing from theon the basis of the spirit of the present invention, belong to the scope of protection of present invention.
Claims (10)
1. a sports buildings floor glue, it is characterised in that the raw material of described sports buildings floor glue includes following mass parts
Composition:
Sports buildings floor glue the most according to claim 1, it is characterised in that the raw material bag of described sports buildings floor glue
Include the composition of following mass parts:
Sports buildings floor glue the most according to claim 2, it is characterised in that the raw material bag of described sports buildings floor glue
Include the composition of following mass parts:
Sports buildings floor glue the most according to claims 1 to 3, it is characterised in that described elastomer is selected from propylene yogurt
One or more in liquid, IPDI or NDI.
Sports buildings floor glue the most according to claim 4, it is characterised in that described wear-resistant material is selected from glass microballoon, stone
One or more in English powder or calcium carbonate.
Sports buildings floor glue the most according to claim 5, it is characterised in that described filler is selected from titanium dioxide, White Carbon black
Or one or more in Kaolin.
Sports buildings floor glue the most according to claim 6, it is characterised in that the raw material bag of described sports buildings floor glue
Include the composition of following mass parts:
8. the preparation method of the sports buildings floor glue described in any one of claim 1～7, it is characterised in that by tripolycyanamide
Formaldehyde resin, elastomer, chlorine partial emulsion and sodium carboxymethyl cellulose stir, then add wear-resistant material and filler stirs i.e.
Can.
Preparation method the most according to claim 8, it is characterised in that while adding wear-resistant material and filler or afterwards, also may be used
Add pigment 1～10 parts, stir.
10. the application in paving sports field of the sports buildings floor glue described in any one of claim 1～7.