CN106084487A - A kind of weather resistance environmental protection type automobile bumper material - Google Patents
A kind of weather resistance environmental protection type automobile bumper material Download PDFInfo
- Publication number
- CN106084487A CN106084487A CN201610733063.7A CN201610733063A CN106084487A CN 106084487 A CN106084487 A CN 106084487A CN 201610733063 A CN201610733063 A CN 201610733063A CN 106084487 A CN106084487 A CN 106084487A
- Authority
- CN
- China
- Prior art keywords
- parts
- environmental protection
- weather resistance
- protection type
- type automobile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of weather resistance environmental protection type automobile bumper material, component including following mass fraction: modified PC resin 20 45 parts, polyethylene 20 40 parts, titanate coupling agent 10 20 parts, flexible vegetation fiber 45 70 parts, nano titanium oxide 0.2 0.6 parts, dispersibility latex powder 16 parts, thickening agent 24 parts, nano-calcium carbonate 5 10 parts, adipic acid 13 parts, polypropylene 60 75 parts, 0.1 0.5 parts of antioxidant, heat stabilizer 3 15 parts, toughener 26 parts, mica powder 13 parts.The invention provides a kind of weather resistance environmental protection type automobile bumper material, the addition of heat stabilizer is remarkably improved thermostability and the dimensional stability of material, has important effect for automotive material to mould Dai Gang, energy-saving and emission-reduction etc..
Description
Technical field
The invention belongs to automotive material technical field, particularly relate to a kind of weather resistance environmental protection type automobile bumper material.
Background technology
Polypropylene is polymer nontoxic, that odorless, tasteless milky are highly crystalline, density only has 0. 90--" 0. 91g/
Cm3, is one of kind the lightest in current all plastics.It is particularly stable to water, and the water absorption rate in water is only 0. 01%,
Molecular weight about 80,000 one 15 ten thousand.Good moldability, but because shrinkage factor is big (being 1% ~ 2.5%). thick article easily caves in, right
The higher part of some dimensional accuracies, is difficult to reach requirement, product surface good luster, it is easy to coloring.
Temperature and loading speed are the biggest to polyacrylic Toughness.When temperature is higher than vitrification point, impact failure
In ductile rupture, it is brittle fracture less than vitrification point, and impact value significantly declines.Improve loading speed, can make
The temperature that ductile rupture changes to brittle fracture rises.Polypropylene has the flexural fatigue resistance of excellence, and its goods are at normal temperatures
Bent 106 times and do not damage.But under room temperature and low temperature, owing to the molecular structure regularity of itself is high, so shock resistance
Intensity is poor.The most prominent performance of polypropylene is exactly flexural fatigue resistance, is commonly called as polypropylene (PP).
The Main way of existing automotive material technology development is environmental protection and lightweight.Replace metal with plastics, can not only subtract
Light car weight, reduces oil consumption and hydrocarbon emission but also can improve dynamic property, adapts to adverse circumstances, strengthens safety.
Due to plastics recoverable, thus reduce the consumption of resource, be finally that automobile obtains more in safety and cost two aspect
Breakthrough, simultaneously also design, for automobile appearance, the condition of providing convenience.In automotive plastic, the consumption of polypropylene (PP) is
Greatly, growth rate is the fastest.PP has become as the primary raw material of bumper, due to bumper be that a kind of surface area is relatively big, shape relatively
For complicated thin-walled large-sized structural component, can be affected by factors such as impacts during use, therefore bumper material needs higher
Mobility, rigidity, toughness, thermostability etc., also to have good dimensional stability and ageing resistace.But owing to general PP deposits
Big, product size poor stability, easy buckling deformation in shrinkage factor；Low-temperature flexibility brittle failure poor, easy；Heat-resisting, photooxidation aging property is poor
Etc. shortcoming, it is impossible to meet Hyundai Motor, all multi-parts of household electrical appliances, it is therefore necessary to general PP material is modified.
Summary of the invention
Goal of the invention: the present invention is directed to deficiency of the prior art, proposes a kind of weather resistance environmental protection type automobile bumper material,
Meet the demand of mechanical property and processing characteristics the most simultaneously, and intensity high-wear resistance is good.
Technical scheme: a kind of weather resistance environmental protection type automobile bumper material of the present invention, including following mass fraction
Component:
Modified PC resin 20-45 part, polyethylene 20-40 part, titanate coupling agent 10-20 part, flexible vegetation fiber
45-70 part, nano titanium oxide 0.2-0.6 part, dispersibility latex powder 1-6 part, thickening agent 2-4 part, nano-calcium carbonate
Calcium 5-10 part, adipic acid 1-3 part, polypropylene 60-75 part, antioxidant 0.1-0.5 part, heat stabilizer 3-15 part, increasing
Tough dose of 2-6 part, mica powder 1-3 part.
Further, including the component of following mass fraction:
Modified PC resin 30-45 part, polyethylene 30-40 part, titanate coupling agent 15-20 part, flexible vegetation fiber
50-70 part, nano titanium oxide 0.4-0.6 part, dispersibility latex powder 2-6 part, thickening agent 3-4 part, nano-calcium carbonate
Calcium 6-10 part, adipic acid 2-3 part, polypropylene 65-75 part, antioxidant 0.3-0.5 part, heat stabilizer 5-15 part, increasing
Tough dose of 4-6 part, mica powder 2-3 part.
Further, including the component of following mass fraction:
Modified PC resin 35 parts, polyethylene 35 parts, titanate coupling agent 18 parts, flexible vegetation fiber 60 parts, nanometer
Titanium dioxide 0.5 part, dispersibility latex powder 4 parts, thickening agent 3 parts, nano-calcium carbonate 8 parts, adipic acid 2 parts, polypropylene
70 parts, 0.4 part of antioxidant, heat stabilizer 10 parts, toughener 5 parts, mica powder 2 parts.
Further, described thickening agent is non-neighboring benzene dimethyl ester thickening agent.
Further, described flexible vegetation fiber is wood fibre or cotton fiber.
Further, described polypropylene is containing the 20-25 polyacrylic polypropylene miser of weight portion low-shrinkage, should
The melt flow rate (MFR) of polypropylene miser is 10-100g/10min.
Further, stating antioxidant is anti-oxidant DLTP and antioxidant TPP according to compounding mixed of weight ratio 3: 2
Compound.
Further, described heat stabilizer is that thiourea, brucite and zeolite form according to weight ratio 1: 2: 2
Mixture.
Beneficial effect: the invention provides a kind of weather resistance environmental protection type automobile bumper material, the addition of heat stabilizer can show
Write thermostability and the dimensional stability improving material, have important work for automotive material to mould Dai Gang, energy-saving and emission-reduction etc.
With.
Detailed description of the invention
Below in conjunction with specific embodiment, the invention will be further described:
Embodiment 1
A kind of weather resistance environmental protection type automobile bumper material, including the component of following mass fraction:
Modified PC resin 20 parts, polyethylene 20 parts, titanate coupling agent 10 parts, flexible vegetation fiber 45 parts, nano-silica
Change titanium 0.2 part, dispersibility latex powder 1 part, thickening agent 2 parts, nano-calcium carbonate 5 parts, adipic acid 1 part, polypropylene 60
Part, 0.1 part of antioxidant, heat stabilizer 3 parts, toughener 2 parts, mica powder 1 part.
Described thickening agent is non-neighboring benzene dimethyl ester thickening agent.
Described flexible vegetation fiber is wood fibre or cotton fiber.
Described polypropylene is containing the 20 polyacrylic polypropylene misers of weight portion low-shrinkage, this polypropylene miser
Melt flow rate (MFR) be 10-100g/10min.
Described antioxidant is that anti-oxidant DLTP and antioxidant TPP are according to the compounding mixture of weight ratio 3: 2.
Described heat stabilizer is the mixture that thiourea, brucite and zeolite form according to weight ratio 1: 2: 2.
Embodiment 2
A kind of weather resistance environmental protection type automobile bumper material, including the component of following mass fraction:
Modified PC resin 45 parts, polyethylene 40 parts, titanate coupling agent 20 parts, flexible vegetation fiber 70 parts, nanometer
Titanium dioxide 0.6 part, dispersibility latex powder 6 parts, thickening agent 4 parts, nano-calcium carbonate 10 parts, adipic acid 3 parts, poly-
Propylene 75 parts, 0.5 part of antioxidant, heat stabilizer 15 parts, toughener 6 parts, mica powder 3 parts.
Described thickening agent is non-neighboring benzene dimethyl ester thickening agent.
Described flexible vegetation fiber is wood fibre or cotton fiber.
Described polypropylene is containing the 20-25 polyacrylic polypropylene miser of weight portion low-shrinkage, and this polypropylene mixes
The melt flow rate (MFR) of compound is 10-100g/10min.
Described antioxidant is that anti-oxidant DLTP and antioxidant TPP are according to the compounding mixture of weight ratio 3: 2.
Described heat stabilizer is the mixture that thiourea, brucite and zeolite form according to weight ratio 1: 2: 2.
Embodiment 3
A kind of weather resistance environmental protection type automobile bumper material, including the component of following mass fraction:
Modified PC resin 35 parts, polyethylene 35 parts, titanate coupling agent 18 parts, flexible vegetation fiber 60 parts, nanometer
Titanium dioxide 0.5 part, dispersibility latex powder 4 parts, thickening agent 3 parts, nano-calcium carbonate 8 parts, adipic acid 2 parts, polypropylene
70 parts, 0.4 part of antioxidant, heat stabilizer 10 parts, toughener 5 parts, mica powder 2 parts.
Described thickening agent is non-neighboring benzene dimethyl ester thickening agent.
Described flexible vegetation fiber is wood fibre or cotton fiber.
Described polypropylene is containing the 20-25 polyacrylic polypropylene miser of weight portion low-shrinkage, and this polypropylene mixes
The melt flow rate (MFR) of compound is 10-100g/10min.
Described antioxidant is that anti-oxidant DLTP and antioxidant TPP are according to the compounding mixture of weight ratio 3: 2.
Described heat stabilizer is the mixture that thiourea, brucite and zeolite form according to weight ratio 1: 2: 2.
The above, be only presently preferred embodiments of the present invention, and the present invention not makees any pro forma restriction, though
So the present invention is disclosed above with preferred embodiment, but is not limited to the present invention, any technology people being familiar with this specialty
Member, in the range of without departing from technical solution of the present invention, when the technology contents of available the disclosure above makes a little change or modification
For the Equivalent embodiments of equivalent variations, as long as being the content without departing from technical solution of the present invention, the technical spirit of the foundation present invention
Any simple modification, equivalent variations and the modification being made above example, all still falls within the range of technical solution of the present invention.
Claims (8)
1. a weather resistance environmental protection type automobile bumper material, it is characterised in that: include the component of following mass fraction:
Modified PC resin 20-45 part, polyethylene 20-40 part, titanate coupling agent 10-20 part, flexible vegetation fiber
45-70 part, nano titanium oxide 0.2-0.6 part, dispersibility latex powder 1-6 part, thickening agent 2-4 part, nano-calcium carbonate
Calcium 5-10 part, adipic acid 1-3 part, polypropylene 60-75 part, antioxidant 0.1-0.5 part, heat stabilizer 3-15 part, increasing
Tough dose of 2-6 part, mica powder 1-3 part.
A kind of weather resistance environmental protection type automobile bumper material the most according to claim 1, it is characterised in that: include following quality
The component of number:
Modified PC resin 30-45 part, polyethylene 30-40 part, titanate coupling agent 15-20 part, flexible vegetation fiber
50-70 part, nano titanium oxide 0.4-0.6 part, dispersibility latex powder 2-6 part, thickening agent 3-4 part, nano-calcium carbonate
Calcium 6-10 part, adipic acid 2-3 part, polypropylene 65-75 part, antioxidant 0.3-0.5 part, heat stabilizer 5-15 part, increasing
Tough dose of 4-6 part, mica powder 2-3 part.
A kind of weather resistance environmental protection type automobile bumper material the most according to claim 1, it is characterised in that: include following quality
The component of number:
Modified PC resin 35 parts, polyethylene 35 parts, titanate coupling agent 18 parts, flexible vegetation fiber 60 parts, nanometer
Titanium dioxide 0.5 part, dispersibility latex powder 4 parts, thickening agent 3 parts, nano-calcium carbonate 8 parts, adipic acid 2 parts, polypropylene
70 parts, 0.4 part of antioxidant, heat stabilizer 10 parts, toughener 5 parts, mica powder 2 parts.
A kind of weather resistance environmental protection type automobile bumper material the most according to claim 1, it is characterised in that: described thickening agent is
Non-neighboring benzene dimethyl ester thickening agent.
A kind of weather resistance environmental protection type automobile bumper material the most according to claim 1, it is characterised in that: described flexible vegetation
Fiber is wood fibre or cotton fiber.
A kind of weather resistance environmental protection type automobile bumper material the most according to claim 1, it is characterised in that: described polypropylene is
Containing the 20-25 polyacrylic polypropylene miser of weight portion low-shrinkage, the melt flow rate (MFR) of this polypropylene miser is
10-100g/10min。
A kind of weather resistance environmental protection type automobile bumper material the most according to claim 1, it is characterised in that: described antioxidant is
Anti-oxidant DLTP and antioxidant TPP are according to the compounding mixture of weight ratio 3: 2.
A kind of weather resistance environmental protection type automobile bumper material the most according to claim 1, it is characterised in that: described is thermally-stabilised
Agent is the mixture that thiourea, brucite and zeolite form according to weight ratio 1: 2: 2.