CN106084269A - A kind of application type polyimides fluorine 46 thin film improving surface quality and preparation method thereof - Google Patents

A kind of application type polyimides fluorine 46 thin film improving surface quality and preparation method thereof Download PDF

Info

Publication number
CN106084269A
CN106084269A CN201610439861.9A CN201610439861A CN106084269A CN 106084269 A CN106084269 A CN 106084269A CN 201610439861 A CN201610439861 A CN 201610439861A CN 106084269 A CN106084269 A CN 106084269A
Authority
CN
China
Prior art keywords
thin film
fluorine
perfluoroethylene
propylene
application type
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201610439861.9A
Other languages
Chinese (zh)
Other versions
CN106084269B (en
Inventor
钱心远
张步峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhuzhou Times Huaxin New Material Technology Co Ltd
Original Assignee
Zhuzhou Times New Material Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhuzhou Times New Material Technology Co Ltd filed Critical Zhuzhou Times New Material Technology Co Ltd
Priority to CN201610439861.9A priority Critical patent/CN106084269B/en
Publication of CN106084269A publication Critical patent/CN106084269A/en
Application granted granted Critical
Publication of CN106084269B publication Critical patent/CN106084269B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

A kind of application type polyimides fluorine 46 thin film improving surface quality, including Kapton matrix and the coat of matrix surface, this coat is to concentrate after dispersion liquid that drying, sintering prepare again by being added with the perfluoroethylene-propylene of surfactant in the coating of the single or double of matrix;This surfactant is soluble in perfluoroethylene-propylene and concentrates dispersion liquid;Its preparation method includes: being added to by surfactant in the gluing machine glue groove concentrating dispersion liquid equipped with perfluoroethylene-propylene, stirring is mixed, and stands;Start gluing machine by Kapton matrix by aforementioned perfluoroethylene-propylene concentration dispersion liquid is coated, then be dried successively, sintering, carry out rolling finally by wrap-up, obtain application type polyimides fluorine 46 thin film.The product apparent mass of the present invention is good, the defect such as the most glue-free trace, microgroove, micelle, and production cost is low, and production efficiency significantly improves.

Description

A kind of application type polyimide-fluorine 46 thin film improving surface quality and preparation thereof Method
Technical field
The present invention relates to a kind of application type Kapton, particularly relate to a kind of polyamides Asia improving surface quality Amine-fluorine 46 thin film and preparation method thereof.
Background technology
Kapton refers on main chain containing a base polymer of imide ring, has the mechanical performance of excellence, resistance to High temperature performance and radiation resistance, and its resistivity is high, dielectric constant is low, thus the widest as protection coverlay and base material General it is applied to the field such as Aero-Space, microelectronic industry.
Body phase character such as mechanical performance, heat resistance and the electric property of polymer is to determine its serviceability and purposes Key factor, polymer surfaces directly contacts with environment in numerous applications, therefore its surface characteristic also plays an important role, and therefore gathers The overall performance of polymer system has substantial connection with its surface or interfacial characteristics.But Kapton smooth surface, chemistry Surface can be relatively low relatively poor with the adhesive property of substrate interface, it is impossible to self is melted and makes it absolutely with other material bonding Application in terms of edge structural material is very restricted.
In order to expand Kapton application in insulant industry, generally in Kapton surface-coated Certain thickness perfluoroethylene-propylene (fluorine 46) concentrates dispersion liquid, and so-called perfluoroethylene-propylene (fluorine 46) concentrates dispersion liquid and refers to In using nonionic surfactant as the aqueous dispersion liquid of stabilizer, politef obtain with polyhexafluoropropylene copolymerization Polymer, it has excellent processing characteristics, electrical insulation properties and hot setting adhesive property.Application type polyamides is sub- Amine-fluorine 46 thin film, is to be concentrated dispersion liquid, through high temperature by Kapton single or double coating perfluoroethylene-propylene (fluorine 46) Sintering forms.It combines the feature of Kapton and fluoroplastics: high temperature resistant and low temperature, can be-80 DEG C~260 DEG C of temperature In the range of life-time service;Electrical insulation properties is good, and insulation grade anti-corrosion is H level;At high temperature can be widely used in from fusible envelope Electromagnetic wire and cable lapped insulation.
Application type polyimide-fluorine 46 thin film, in coat dry run, along with the volatilization of fluorine 46 coating solvents, is being coated with Producing temperature, density and surface tension between clad surface and inside poor, these differences can make coat internal turbulization fortune Dynamic, and then cause coating surface to produce Pericarpium Citri Reticulatae and glue trace, also can produce the Levelling defects such as tiny silking during vertical applications simultaneously. Application type polyimide-fluorine 46 thin film, if there is Levelling defects, not only affects outward appearance, the most also can cause product coat Discontinuously, thickness deviation is big, electromagnetic wire sintering time laminated film adhesion property inconsistent, and then affect the sealing of electromagnetic wire product Effect and electrical insulation properties, reduce the service life of motor.
CN1746248A Chinese patent literature discloses preparation method and the equipment of a kind of polyimide-fluorine 46 adhesive tape, Use scraper to realize the uniformity of coating, but the uniformity using physics mode to improve coating is limited to the precision of cutter Affect Deng many factors, it is impossible to be enough obviously improved the surface quality of coating, it is impossible to what inherently solution was mentioned above asks Topic, and be coated layer can accumulate substantial amounts of micelle along with produce, affect the use of application type product.
Therefore, in order to obtain the best effort characteristic of laminated film, it is necessary to make laminated film have good body phase and table Face overall characteristic.
Summary of the invention
The invention aims to overcome discontinuous, the defect such as thickness deviation is big of coat fluorine 46 in prior art, carry For application type polyimide-fluorine 46 thin film that a kind of surface quality is improved and preparation method thereof.
For solving above-mentioned technical problem, the technical scheme that the present invention proposes is: a kind of application type improving surface quality gathers Acid imide-fluorine 46 thin film, including Kapton matrix and the coat of matrix surface, described coat is by matrix Single or double coating be added with the perfluoroethylene-propylene of surfactant and concentrate after dispersion liquid that drying, sintering are prepared into again Arrive;Described surfactant is soluble in perfluoroethylene-propylene and concentrates dispersion liquid.
In above-mentioned application type polyimide-fluorine 46 thin film, it is preferred that described surfactant is organosiloxane levelling The organosiloxane activating agent of agent or modification.It is furthermore preferred that described organosiloxane levelling agent is selected from polydimethylsiloxane, gathers At least one in methyl phenyl siloxane, the organosiloxane activating agent of described modification selected from alkyl-modified organosiloxane, At least one in organic silicon modified by polyether oxygen alkane, polyester modified organic siloxane.
Through our experimental studies have found that repeatedly, our preferred surfactant have relatively low surface can, and this The surface tension of a little preferred surfactants also can concentrate dispersion liquid system by specific perfluoroethylene-propylene less than in the present invention, this Time, we further find that these preferred surfactants concentrate the limited not phase of dispersion liquid system with perfluoroethylene-propylene Holding, this further results in during follow-up perfluoroethylene-propylene concentration dispersion layer is dried, in surfactant Silicone copolymers can migrate to the interface between coat and air, improves the flow leveling concentrating dispersion liquid, and then serves It is obviously improved the notable technique effect of coat surface quality.
In above-mentioned application type polyimide-fluorine 46 thin film, it is preferred that described perfluoroethylene-propylene concentrates the matter of dispersion liquid Amount mark is 40%~50%, and described surfactant addition in perfluoroethylene-propylene concentrates dispersion liquid is 0.05wt% ~0.5wt%.
In above-mentioned application type polyimide-fluorine 46 thin film, it is preferred that described application type polyimide-fluorine 46 thin film Thickness deviation is ± 1 μm.
As total technology design, the present invention also provides for the system of a kind of above-mentioned application type polyimide-fluorine 46 thin film Preparation Method, comprises the following steps: surfactant adds to the gluing machine glue groove concentrating dispersion liquid equipped with perfluoroethylene-propylene In, stirring, until mix homogeneously, then stands;Start gluing machine, by Kapton matrix by the poly-perfluor after mixing Second propylene concentrates in dispersion liquid and is coated, and the Kapton after having coated is dried through gluing machine drying tunnel, then enters Row sintering, carries out rolling finally by wrap-up, obtains described application type polyimide-fluorine 46 thin film.
In above-mentioned preparation method, it is preferred that described mixing time is 10~30 minutes, time of repose is 10~30 points Clock.
In above-mentioned preparation method, it is preferred that described Kapton matrix is with the speed of 1.5~2.5 ms/min Concentrated in dispersion liquid by the perfluoroethylene-propylene after mixing and be coated.This preferred version makes by adding surfactant Under higher coating speed, polyimide-fluorine 46 thin film that above-mentioned preparation method prepares still is able to obtain good painting Covering quality, the coating efficiency of equipment can improve 2~3 times.
In above-mentioned preparation method, it is preferred that described dry temperature is 230 DEG C~270 DEG C, and drying time is 2~6 points Clock;The temperature of described sintering is 310 DEG C~350 DEG C, and sintering time is 2~4 minutes.
Compared with prior art, the beneficial effects of the present invention is:
(1) present invention adds surfactant by concentrating to perfluoroethylene-propylene in dispersion liquid so that the painting prepared Cover type polyimide-fluorine 46 thin film apparent mass good, without defects such as any glue trace, microgroove, micelles;And the thin film obtained is coated with Coating thickness is homogeneous, can be reduced to ± 1 μm during thickness deviation optimum by ± 3 μm.
(2) surface of the main chain of currently preferred organosiloxane class surfactant can be low, with the heat of matrix emulsion Mechanical compatibility is poor, and during perfluoroethylene-propylene concentration dispersion layer is dried, silicone copolymers can migrate to Interface between coat and air, to improve the flow leveling of perfluoroethylene-propylene concentration dispersion liquid, thus improves coat table Face quality.
(3) preparation method of the present invention is simple to operate, it is only necessary to add minimal amount of surfactant when emulsion is prepared Can, the addition in preferred version is only 0.05wt%~0.5wt% of emulsion weight, and addition is few, does not affect dispersion liquid And the overall performance of thin film.
(4) preparation method of the present invention can make Kapton coating speed by 0.8 m/min the highest bring up to 2.5 meters/ Point, production capacity can improve nearly 212%, thus drastically increases production efficiency, reduces production cost.
Detailed description of the invention
For the ease of understanding the present invention, below in conjunction with specific embodiment, the present invention is made more comprehensively, describes meticulously, But protection scope of the present invention is not limited to below example.
Embodiment 1:
Application type polyimide-fluorine 46 thin film of a kind of the present embodiment, including Kapton matrix and matrix surface Coat, coat is to be added with the perfluoroethylene of organic silicon modified by polyether oxygen alkane activating agent by the coating of one side on matrix After propylene concentration dispersion liquid, drying, sintering prepare again, the thickness deviation of application type polyimide-fluorine 46 thin film obtained For ± 1 μm.
The preparation method of application type polyimide-fluorine 46 thin film of the present embodiment is as follows: by 10g organic silicon modified by polyether oxygen Alkane activating agent (preferably Silok2243 Si Luoke Chemical Co., Ltd., lower with, but be not limited to this) add to equipped with the poly-perfluor of 20Kg Second propylene concentrates in the gluing machine glue groove of dispersion liquid (mass fraction is 50%), stirs 10 minutes mix homogeneously, then stands 10 Minute;Starting gluing machine, arranging gluing machine speed is 0.8 m/min, by Kapton matrix by the poly-perfluor after mixing Second propylene concentrates in dispersion liquid and carries out one side coating, the Kapton after having coated through gluing machine drying tunnel at 230 DEG C Being dried 6 minutes, then sinter 4 minutes at 310 DEG C, carry out rolling finally by wrap-up, the application type obtaining the present invention gathers Acid imide-fluorine 46 thin film.
Embodiment 2
Application type polyimide-fluorine 46 thin film of a kind of the present embodiment, including Kapton matrix and matrix surface Coat, coat is to be added with the perfluoroethylene-propylene of polydimethylsiloxane activating agent by the coating of one side on matrix Concentrate after dispersion liquid drying, sintering again to prepare, the thickness deviation of application type polyimide-fluorine 46 thin film obtained for ± 1μm。
The preparation method of application type polyimide-fluorine 46 thin film of the present embodiment is as follows: lived by 20g polydimethylsiloxane Property agent add to equipped with 20Kg perfluoroethylene-propylene concentrate dispersion liquid (mass fraction is 50%) gluing machine glue groove in, stir 15 Minute mix homogeneously, then stands 10 minutes;Starting gluing machine, arranging gluing machine speed is 1.5 ms/min, and polyimides is thin Film matrix is concentrated in dispersion liquid by the perfluoroethylene-propylene after mixing and carries out one side coating, and the polyimides after having coated is thin Film is dried 6 minutes at 245 DEG C through gluing machine drying tunnel, then sinters 2 minutes at 330 DEG C, receives finally by wrap-up Volume, obtains application type polyimide-fluorine 46 thin film of the present invention.
Embodiment 3
Application type polyimide-fluorine 46 thin film of a kind of the present embodiment, including Kapton matrix and matrix surface Coat, coat be by one side on matrix coating add PSI activating agent perfluoroethylene-propylene Concentrate after dispersion liquid drying, sintering again to prepare, the thickness deviation of application type polyimide-fluorine 46 thin film obtained for ± 1μm。
The preparation method of application type polyimide-fluorine 46 thin film of the present embodiment is as follows: by 100g polymethyl-benzene base silica Alkane activating agent adds in the gluing machine glue groove concentrating dispersion liquid (mass fraction is 50%) equipped with 20Kg perfluoroethylene-propylene, stirs Mix 30 minutes mix homogeneously, then stand 30 minutes;Starting gluing machine, arranging gluing machine speed is 2 ms/min, by polyimides Film matrix is concentrated in dispersion liquid by the perfluoroethylene-propylene after mixing and carries out one side coating, the polyimides after having coated Thin film is dried 2.5 minutes at 260 DEG C through gluing machine drying tunnel, then sinters 1.5 minutes at 340 DEG C, finally by wrap-up Carry out rolling, obtain application type polyimide-fluorine 46 thin film of the present invention.
Embodiment 4
Application type polyimide-fluorine 46 thin film of a kind of the present embodiment, including Kapton matrix and matrix surface Coat, coat is to be added with the perfluoroethylene of alkyl-modified organosiloxane activating agent by the coating of one side on matrix After propylene concentration dispersion liquid, drying, sintering prepare again, the thickness deviation of application type polyimide-fluorine 46 thin film obtained For ± 1 μm.
The preparation method of application type polyimide-fluorine 46 thin film of the present embodiment is as follows: by alkyl-modified for 100g organosilicon Oxygen alkane activating agent adds in the gluing machine glue groove concentrating dispersion liquid (mass fraction is 50%) equipped with 20Kg perfluoroethylene-propylene, Stir 30 minutes mix homogeneously, then stand 30 minutes;Starting gluing machine, arranging gluing machine speed is 2.5 ms/min, by polyamides Imines film matrix is concentrated in dispersion liquid by the perfluoroethylene-propylene after mixing and carries out one side coating, the polyamides after having coated Imines thin film is dried 2 minutes at 270 DEG C through gluing machine drying tunnel, then sinters 1.2 minutes at 350 DEG C, fills finally by rolling Put and carry out rolling, obtain application type polyimide-fluorine 46 thin film of the present invention.
Embodiment 5
Application type polyimide-fluorine 46 thin film of a kind of the present embodiment, including Kapton matrix and matrix surface Coat, coat is the perfluoroethylene being added with polyester modified organic siloxane activating agent by dual coating on matrix After propylene concentration dispersion liquid, drying, sintering prepare again, the thickness deviation of application type polyimide-fluorine 46 thin film obtained For ± 1 μm.
The preparation method of application type polyimide-fluorine 46 thin film of the present embodiment is as follows: by 10g polyester resin change properties of organic silicon oxygen Alkane activating agent (preferably BD-3310, Bao Er get organosilicon company limited, lower with, but be not limited to this) add to equipped with 20Kg poly-complete Fluoro ethyl propene concentrates in the gluing machine glue groove of dispersion liquid (mass fraction is 50%), stirs 10 minutes mix homogeneously, then stands 10 minutes;Starting gluing machine, arranging gluing machine speed is 1.0 ms/min, by Kapton matrix by gathering entirely after mixing Fluoro ethyl propene concentrates in dispersion liquid and carries out dual coating, the Kapton after having coated through gluing machine drying tunnel at 230 DEG C Under be dried 6 minutes, then at 310 DEG C sinter 4 minutes, carry out rolling finally by wrap-up, obtain the application type of the present invention Polyimide-fluorine 46 thin film.
Embodiment 6
Application type polyimide-fluorine 46 thin film of a kind of the present embodiment, including Kapton matrix and matrix surface Coat, coat is to be added with organic silicon modified by polyether oxygen alkane activating agent and polyester modification by dual coating on matrix After the perfluoroethylene-propylene concentration dispersion liquid of organosiloxane activating agent, drying, sintering prepare again, the application type obtained The thickness deviation of polyimide-fluorine 46 thin film is ± 1 μm.
The preparation method of application type polyimide-fluorine 46 thin film of the present embodiment is as follows: by 15g organic silicon modified by polyether oxygen Alkane activating agent and 15g polyester modified organic siloxane activating agent add to equipped with 20Kg perfluoroethylene-propylene concentration dispersion liquid (matter Amount mark is 50%) gluing machine glue groove in, stir 20 minutes mix homogeneously, then standing 20 minutes;Start gluing machine, arrange Gluing machine speed is 1.5 ms/min, concentrates in dispersion liquid by the perfluoroethylene-propylene after mixing by Kapton matrix Row one side coats, and the Kapton after having coated is dried 3 minutes at 245 DEG C through gluing machine drying tunnel, then at 330 DEG C Sinter 2 minutes, carry out rolling finally by wrap-up, obtain application type polyimide-fluorine 46 thin film of the present invention.
Embodiment 7
Application type polyimide-fluorine 46 thin film of a kind of the present embodiment, including Kapton matrix and matrix surface Coat, coat is to be added with polydimethylsiloxane and PSI by dual coating on matrix to live Property agent perfluoroethylene-propylene concentrate after dispersion liquid drying, sintering again and prepare, the application type polyimide-fluorine 46 obtained The thickness deviation of thin film is ± 1 μm.
The preparation method of application type polyimide-fluorine 46 thin film of the present embodiment is as follows: lived by 50g polydimethylsiloxane Property agent and 50g PSI activating agent add to equipped with 20Kg perfluoroethylene-propylene concentrate dispersion liquid (mass fraction Be 50%) gluing machine glue groove in, stir 30 minutes mix homogeneously, then stand 30 minutes;Start gluing machine, gluing machine is set Speed is 2.5 ms/min, and Kapton matrix is two-sided by carrying out in the perfluoroethylene-propylene concentration dispersion liquid after mixing Coating, the Kapton after having coated is dried 2 minutes at 270 DEG C through gluing machine drying tunnel, then sinters at 350 DEG C 1.2 minutes, carry out rolling finally by wrap-up, obtain application type polyimide-fluorine 46 thin film of the present invention.
Comparative example 1
The preparation method of application type polyimide-fluorine 46 thin film is as follows: takes 20Kg perfluoroethylene-propylene and concentrates dispersion liquid (matter Amount mark is 50%) it is placed in gluing machine glue groove, start gluing machine, arranging gluing machine speed is 0.8 m/min, and polyamides is sub- Amine thin film (thickness deviation is ± 1 μm) is concentrated in dispersion liquid by perfluoroethylene-propylene and carries out one side coating, after having coated Kapton is dried 6 minutes at 230 DEG C through gluing machine drying tunnel, then sinters 4 minutes at 310 DEG C, finally by rolling Device carries out rolling, obtains application type polyimide-fluorine 46 thin film.
Comparative example 2
The preparation method of application type polyimide-fluorine 46 thin film is as follows: takes 20Kg perfluoroethylene-propylene and concentrates dispersion liquid (matter Amount mark is 50%) it is placed in gluing machine glue groove, start gluing machine, arranging gluing machine speed is 0.8 m/min, and polyamides is sub- Amine thin film (thickness deviation is ± 1 μm) is concentrated in dispersion liquid by perfluoroethylene-propylene and carries out dual coating, after having coated Kapton is dried 6 minutes at 230 DEG C through gluing machine drying tunnel, then sinters 4 minutes at 310 DEG C, finally by rolling Device carries out rolling, obtains application type polyimide-fluorine 46 thin film.
Observe embodiment 1~7 and polyimide-fluorine 46 film surface for preparing of comparative example 1~2, testing film Transverse gage deviation, the method for testing of transverse gage deviation is as follows: the longitudinal direction along thin film takes the batten that 20mm is wide, along horizontal To the thickness every 20mm testing film, the difference between measured value and desired value is transverse gage deviation, and the data of gained are such as Shown in table 1.
Table 1 polyimide-fluorine 46 film surface quality and transverse gage deviation log
From the results shown in Table 1, in the case of gluing machine speed is relatively low, with the addition of the poly-of organosiloxane activating agent The polyimide-fluorine 46 film surface quality that perfluoroethylene-propylene (copolymer) concentration dispersion liquid prepares is good, and the homogeneous deviation of thickness is little, does not has Occur the Levelling defects such as glue trace, microgroove;Then there is levelling in polyimide-fluorine 46 film surface that customary preparation methods obtains Defect, thickness deviation is big, and flatness is low.Additionally, in the case of gluing machine speed is higher, with the addition of organosiloxane activating agent Perfluoroethylene-propylene concentrate dispersion liquid preparation-obtained polyimide-fluorine 46 thin film remain to obtain good surface quality, The coating efficiency of equipment can improve 2~3 times, thus improves production efficiency.

Claims (9)

1. improve application type polyimide-fluorine 46 thin film for surface quality, including Kapton matrix and matrix table The coat in face, it is characterised in that described coat is by being added with surfactant in the coating of the single or double of matrix Perfluoroethylene-propylene concentrate after dispersion liquid that drying, sintering prepare again;Described surfactant is soluble in perfluoroethylene Propylene concentrates dispersion liquid.
Application type polyimide-fluorine 46 thin film the most according to claim 1, it is characterised in that described surfactant is The organosiloxane activating agent of organosiloxane levelling agent or modification.
Application type polyimide-fluorine 46 thin film the most according to claim 2, it is characterised in that described organosiloxane stream At least one in polydimethylsiloxane, PSI of flat agent, the organosiloxane activity of described modification At least one in alkyl-modified organosiloxane, organic silicon modified by polyether oxygen alkane, polyester modified organic siloxane of agent.
4. according to application type polyimide-fluorine 46 thin film according to any one of claims 1 to 3, it is characterised in that described poly- It is 40%~50% that perfluoroethylene-propylene (copolymer) concentrates the mass fraction of dispersion liquid, and described surfactant concentrates at perfluoroethylene-propylene and divides The addition dissipated in liquid is 0.05wt%~0.5wt%.
5. according to application type polyimide-fluorine 46 thin film according to any one of claims 1 to 3, it is characterised in that described painting The thickness deviation covering type polyimide-fluorine 46 thin film is ± 1 μm.
6. a preparation method for application type polyimide-fluorine 46 thin film as according to any one of Claims 1 to 4, including Following steps: surfactant is added to equipped with perfluoroethylene-propylene concentrate dispersion liquid gluing machine glue groove in, stirring until Mix homogeneously, then stands;Start gluing machine, Kapton matrix is concentrated by the perfluoroethylene-propylene after mixing and divides Dissipating in liquid and be coated, the Kapton after having coated is dried through gluing machine drying tunnel, then is sintered, and finally leads to Cross wrap-up and carry out rolling, obtain application type polyimide-fluorine 46 thin film.
Preparation method the most according to claim 6, it is characterised in that described mixing time is 10~30 minutes, during standing Between be 10~30 minutes.
Preparation method the most according to claim 6, it is characterised in that described Kapton matrix is with 1.5~2.5 M/min speed concentrated in dispersion liquid by the perfluoroethylene-propylene after mixing and be coated.
9. according to the preparation method described in claim 6,7 or 8, it is characterised in that described dry temperature is 230 DEG C~270 DEG C, drying time is 2~6 minutes;The temperature of described sintering is 310 DEG C~350 DEG C, and sintering time is 2~4 minutes.
CN201610439861.9A 2016-06-20 2016-06-20 A kind of 46 film of application type polyimide-fluorine and preparation method thereof improving surface quality Active CN106084269B (en)