CN106083003A - A kind of boccaro cupping glass and preparation method thereof - Google Patents

A kind of boccaro cupping glass and preparation method thereof Download PDF

Info

Publication number
CN106083003A
CN106083003A CN201610488810.5A CN201610488810A CN106083003A CN 106083003 A CN106083003 A CN 106083003A CN 201610488810 A CN201610488810 A CN 201610488810A CN 106083003 A CN106083003 A CN 106083003A
Authority
CN
China
Prior art keywords
parts
boccaro
cupping glass
trace mineral
mineral supplement
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610488810.5A
Other languages
Chinese (zh)
Inventor
刘海燕
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610488810.5A priority Critical patent/CN106083003A/en
Publication of CN106083003A publication Critical patent/CN106083003A/en
Pending legal-status Critical Current

Abstract

The present invention relates to care appliance technical field, especially a kind of boccaro cupping glass and preparation method thereof；Its mass parts composition is as follows: rod-like aluminum oxide 10 16 parts, CNT 6 10 parts, zinc oxide 58 parts, mullite 2.4 6.4 parts, gull rock 2.4 3.6 parts, calcite in powder 3.6 6.4 parts, camwood knag 2.4 7.2 parts, compound stabilizers 2.4 4.8 parts, Maifanitum 6.4 9.6 parts, trace mineral supplement 0.5 2.4 parts；The boccaro cupping glass of the present invention without the operation such as enamel frit makeing, glazing, it is to avoid secondary enters Bristol glaze and burns, and significantly reduces energy consumption, has significant economic benefit and environmental benefit；Preparation method does not change the production technology of tradition red stoneware ware, beneficially promotion and application；Rationally, compatibility uses the boccaro cupping glass raw material composition of the present invention, changes the medium composition in tank.Be conducive to the maintenance of skin, enhance blood circulation, improve effect and effect of common cupping.

Description

A kind of boccaro cupping glass and preparation method thereof
Technical field
The present invention relates to care appliance technical field, especially a kind of boccaro cupping glass and preparation method thereof.
Background technology
Cup this be a kind of with cup tank make instrument, by means of heating power venting air therein produce negative pressure, make to be attracted in skin, Cause a kind of therapy of stagnation of the blood phenomenon.Ancient medicine is sucked blood evacuation of pus with it when treating skin infection abscess, expands the most again application In the internal disease such as pulmonary tuberculosis, rheumatism.After foundation, owing to updating method, cupping therapy is made to have had new development, further Expand therapeutic domain, become the important therapy of the one in acupuncture and moxibustion therapy.Suction cup feature and principle are that speed suction cup is tradition The innovation of igniting exhaust mode for mechanical, hand-driven vacuum suction mode, safe and reliable, easy to operate, become size according to postural design Different tank bodies, uses more convenient.Solving tradition suction cup easily to scald, cup position is restricted, little the lacking of the scope of application Point.
Traditional cupping uses simple glass to make, and its operation principle is to utilize cylinder body to produce negative pressure, directly acts on Human body, thus reach the therapeutic purposes of relaxing muscles and tendons to promote blood circulation.Owing in using, tank inner air and outer air medium is the same, its function singleness, it is impossible to Preferably play its effect.
Summary of the invention
It is an object of the invention to: overcome deficiency of the prior art, it is provided that the boccaro that a kind of diverse in function, cup are effective Cupping and preparation method thereof.
For solving above-mentioned technical problem, the technical solution used in the present invention is as follows:
A kind of boccaro cupping glass, its mass parts composition is as follows: rod-like aluminum oxide 10-16 part, CNT 6-10 part, zinc oxide 5- 8 parts, mullite 2.4-6.4 part, gull rock 2.4-3.6 part, calcite in powder 3.6-6.4 part, camwood knag 2.4-7.2 part, compounding steady Determine agent 2.4-4.8 part, Maifanitum 6.4-9.6 part, trace mineral supplement 0.5-2.4 part.
Further, described compound stabilizers selects rare-earth stabilizer.
Further, described trace mineral supplement includes lithium, strontium and zinc, and its mass ratio is 1:1.2-1.8:1.5.
Further, lithium, strontium and zinc in described trace mineral supplement, its mass ratio is 1:1.5:1.5.
Further, described boccaro cupping glass mass parts composition as follows: rod-like aluminum oxide 15 parts, CNT 12 parts, Zinc oxide 7 parts, mullite 4 parts, gull rock 3 parts, calcite in powder 4 parts, camwood knag 4.8 parts, compound stabilizers 3.6 parts, Maifanitum 7.2 parts, trace mineral supplement 1.5 parts.
The method preparing boccaro cupping glass, described method is as follows: take rod-like aluminum oxide, CNT, oxidation according to ratio Zinc, mullite, gull rock, calcite in powder, camwood knag, compound stabilizers, Maifanitum, trace mineral supplement, through ball milling, mistake Sieve, size mixing, filter pressing press filt, old pugging, molding, be dried, it is not necessary to again through the operation such as enamel frit makeing, glazing, then directly at 1100- 1250 DEG C are burnt till, are incubated 30min, can be at boccaro carcass surface self-assembling formation glaze layer after cooling.
Technical scheme is used to provide the benefit that:
The boccaro cupping glass of the present invention without the operation such as enamel frit makeing, glazing, it is to avoid secondary enters Bristol glaze and burns, and significantly reduces life Production capacity consumes, and has significant economic benefit and environmental benefit；Preparation method does not change the production technology of tradition red stoneware ware, favorably In promotion and application；
Rationally, compatibility uses the boccaro cupping glass raw material composition of the present invention, changes the medium composition in tank.Be conducive to skin Maintenance, enhances blood circulation, improves effect and effect of common cupping.
Detailed description of the invention
Below in conjunction with detailed description of the invention, the invention will be further described.
Embodiment 1
A kind of boccaro cupping glass, its mass parts composition is as follows: rod-like aluminum oxide 10 parts, CNT 6 parts, zinc oxide 5 parts, Mo Lai 2.4 parts of stone, gull rock 2.4 parts, calcite in powder 3.6 parts, camwood knag 2.4 parts, compound stabilizers 2.4 parts, Maifanitum 6.4 parts, micro- Secondary element additive 0.5 part.
Wherein, compound stabilizers selects rare-earth stabilizer.
Wherein, trace mineral supplement includes lithium, strontium and zinc, and its mass ratio is 1:1.2:1.5.
The method preparing boccaro cupping glass, described method is as follows: take rod-like aluminum oxide, CNT, oxidation according to ratio Zinc, mullite, gull rock, calcite in powder, camwood knag, compound stabilizers, Maifanitum, trace mineral supplement, through ball milling, mistake Sieve, size mixing, filter pressing press filt, old pugging, molding, be dried, it is not necessary to again through the operation such as enamel frit makeing, glazing, then directly at 1100- 1250 DEG C are burnt till, are incubated 30min, can be at boccaro carcass surface self-assembling formation glaze layer after cooling.
Embodiment 2
A kind of boccaro cupping glass, its mass parts composition is as follows: rod-like aluminum oxide 12 parts, CNT 7 parts, zinc oxide 6 parts, Mo Lai 3 parts of stone, gull rock 2.8 parts, calcite in powder 3.8 parts, camwood knag 2.6 parts, compound stabilizers 2.6 parts, Maifanitum 6.8 parts, trace Element additive 0.6 part.
Wherein, compound stabilizers selects rare-earth stabilizer.
Wherein, trace mineral supplement includes lithium, strontium and zinc, and its mass ratio is 1:1.3:1.5.
The method preparing boccaro cupping glass, described method is as follows: take rod-like aluminum oxide, CNT, oxidation according to ratio Zinc, mullite, gull rock, calcite in powder, camwood knag, compound stabilizers, Maifanitum, trace mineral supplement, through ball milling, mistake Sieve, size mixing, filter pressing press filt, old pugging, molding, be dried, it is not necessary to again through the operation such as enamel frit makeing, glazing, then directly at 1100- 1250 DEG C are burnt till, are incubated 30min, can be at boccaro carcass surface self-assembling formation glaze layer after cooling.
Embodiment 3
A kind of boccaro cupping glass, its mass parts composition is as follows: rod-like aluminum oxide 15 parts, CNT 12 parts, zinc oxide 7 parts, not Come 4 parts of stone, gull rock 3 parts, calcite in powder 4 parts, camwood knag 4.8 parts, compound stabilizers 3.6 parts, Maifanitum 7.2 parts, trace unit Element additive 1.5 parts.
Wherein, compound stabilizers selects rare-earth stabilizer.
Wherein, trace mineral supplement includes lithium, strontium and zinc, and its mass ratio is 1:1.5:1.5.
The method preparing boccaro cupping glass, described method is as follows: take rod-like aluminum oxide, CNT, oxidation according to ratio Zinc, mullite, gull rock, calcite in powder, camwood knag, compound stabilizers, Maifanitum, trace mineral supplement, through ball milling, mistake Sieve, size mixing, filter pressing press filt, old pugging, molding, be dried, it is not necessary to again through the operation such as enamel frit makeing, glazing, then directly at 1100- 1250 DEG C are burnt till, are incubated 30min, can be at boccaro carcass surface self-assembling formation glaze layer after cooling.
Embodiment 4
A kind of boccaro cupping glass, its mass parts composition is as follows: rod-like aluminum oxide 15 parts, CNT 9 parts, zinc oxide 7.8 parts, not Come 6 parts of stone, gull rock 3.2 parts, calcite in powder 6 parts, camwood knag 7 parts, compound stabilizers 4.5 parts, Maifanitum 9 parts, trace element Additive 2.1 parts.
Wherein, compound stabilizers selects rare-earth stabilizer.
Wherein, trace mineral supplement includes lithium, strontium and zinc, and its mass ratio is 1:1.6:1.5.
The method preparing boccaro cupping glass, described method is as follows: take rod-like aluminum oxide, CNT, oxidation according to ratio Zinc, mullite, gull rock, calcite in powder, camwood knag, compound stabilizers, Maifanitum, trace mineral supplement, through ball milling, mistake Sieve, size mixing, filter pressing press filt, old pugging, molding, be dried, it is not necessary to again through the operation such as enamel frit makeing, glazing, then directly at 1100- 1250 DEG C are burnt till, are incubated 30min, can be at boccaro carcass surface self-assembling formation glaze layer after cooling.
Embodiment 5
A kind of boccaro cupping glass, its mass parts composition is as follows: rod-like aluminum oxide 16 parts, CNT 10 parts, zinc oxide 8 parts, not Come 6.4 parts of stone, gull rock 2.5 parts, calcite in powder 3.8 parts, camwood knag 2.8 parts, compound stabilizers 2.6 parts, Maifanitum 6.8 parts, Trace mineral supplement 0.8 part.
Wherein, compound stabilizers selects rare-earth stabilizer.
Wherein, trace mineral supplement includes lithium, strontium and zinc, and its mass ratio is 1:1.8:1.5.
The method preparing boccaro cupping glass, described method is as follows: take rod-like aluminum oxide, CNT, oxidation according to ratio Zinc, mullite, gull rock, calcite in powder, camwood knag, compound stabilizers, Maifanitum, trace mineral supplement, through ball milling, mistake Sieve, size mixing, filter pressing press filt, old pugging, molding, be dried, it is not necessary to again through the operation such as enamel frit makeing, glazing, then directly at 1100- 1250 DEG C are burnt till, are incubated 30min, can be at boccaro carcass surface self-assembling formation glaze layer after cooling.
With the above-mentioned desirable embodiment according to the present invention for enlightenment, by above-mentioned description, relevant staff is complete Entirely can carry out various change and amendment in the range of without departing from this invention technological thought.The technology of this invention The content that property scope is not limited in description, it is necessary to determine its technical scope according to right.

Claims (6)

1. a boccaro cupping glass, it is characterised in that its mass parts composition is as follows: rod-like aluminum oxide 10-16 part, CNT 6- 10 parts, zinc oxide 5-8 part, mullite 2.4-6.4 part, gull rock 2.4-3.6 part, calcite in powder 3.6-6.4 part, camwood knag 2.4- 7.2 parts, compound stabilizers 2.4-4.8 part, Maifanitum 6.4-9.6 part, trace mineral supplement 0.5-2.4 part.
A kind of boccaro cupping glass the most according to claim 1, it is characterised in that described compound stabilizers is selected rare earth-stabilized Agent.
A kind of boccaro cupping glass the most according to claim 1, it is characterised in that: described trace mineral supplement include lithium, Strontium and zinc, its mass ratio is 1:1.2-1.8:1.5.
A kind of boccaro cupping glass the most according to claim 3, it is characterised in that: lithium, strontium in described trace mineral supplement And zinc, its mass ratio is 1:1.5:1.5.
A kind of boccaro cupping glass the most according to claim 1, it is characterised in that the mass parts composition of described boccaro cupping glass As follows: rod-like aluminum oxide 15 parts, CNT 12 parts, zinc oxide 7 parts, mullite 4 parts, gull rock 3 parts, calcite in powder 4 parts, purple Knaur 4.8 parts, compound stabilizers 3.6 parts, Maifanitum 7.2 parts, trace mineral supplement 1.5 parts.
6. the method for preparation boccaro cupping glass as according to any one of claim 1-5, it is characterised in that described method is such as Under: take rod-like aluminum oxide, CNT, zinc oxide, mullite, gull rock, calcite in powder, camwood knag according to ratio, compound surely Determine agent, Maifanitum, trace mineral supplement, through ball milling, sieve, size mixing, filter pressing press filt, old pugging, molding, be dried, it is not necessary to Again through the operation such as enamel frit makeing, glazing, then directly burn till at 1100-1250 DEG C, be incubated 30min, can be at boccaro carcass after cooling Surface self-assembling formation glaze layer.
CN201610488810.5A 2016-06-29 2016-06-29 A kind of boccaro cupping glass and preparation method thereof Pending CN106083003A (en)