CN106079622A - 一种抗紫外线防雾霾纱网 - Google Patents
一种抗紫外线防雾霾纱网 Download PDFInfo
- Publication number
- CN106079622A CN106079622A CN201610414315.XA CN201610414315A CN106079622A CN 106079622 A CN106079622 A CN 106079622A CN 201610414315 A CN201610414315 A CN 201610414315A CN 106079622 A CN106079622 A CN 106079622A
- Authority
- CN
- China
- Prior art keywords
- parts
- uvioresistant
- gauze
- additive
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种抗紫外线防雾霾纱网，所述抗紫外线防雾霾纱网包括三层，第一层和第三层均为纱网层，中间层为薄膜层，薄膜层粘附在纱网层上；其中，薄膜层是由涂料加工成膜得到，所述涂料的原料按重量份包括：硅胶乳液60‑80份，水性聚氨酯乳液20‑40份，聚乙二醇200 3‑4份，轻质碳酸钙10‑15份，竹炭粉5‑6份，负离子粉8‑12份，十二烷基硫酸钠1‑2份，乳化硅油0.1‑0.3份，添加剂4‑6份，羧甲基纤维素钠0.2‑0.3份，水10‑15份。本发明抗紫外线性能好，防雾霾性能高，抗菌性能好。
Description
技术领域
本发明涉及防雾霾纱网技术领域，尤其涉及一种抗紫外线防雾霾纱网。
背景技术
目前，雾霾污染越来越严重，对大气环境、交通安全和人们的身体健康的威胁越来越大，市面上出现了各种各样的防雾霾纱网，这些防雾霾纱网，由于长期暴露在空气和阳光下中，长期受到紫外线照射容易老化，长期接触灰尘、雾霾、潮湿气体，容易滋生细菌，因此需要提供一种新的防雾霾的纱网。
发明内容
基本背景技术存在的技术问题，本发明提出了一种抗紫外线防雾霾纱网，本发明抗紫外线性能好，防雾霾性能高，抗菌性能好。
本发明提出的一种抗紫外线防雾霾纱网，所述抗紫外线防雾霾纱网包括三层，第一层和第三层均为纱网层，中间层为薄膜层，薄膜层粘附在纱网层上；
其中，薄膜层是由涂料加工成膜得到，所述涂料的原料按重量份包括：硅胶乳液60-80份，水性聚氨酯乳液20-40份，聚乙二醇200 3-4份，轻质碳酸钙10-15份，竹炭粉5-6份，负离子粉8-12份，十二烷基硫酸钠1-2份，乳化硅油0.1-0.3份，添加剂4-6份，羧甲基纤维素钠0.2-0.3份，水10-15份。
优选地，纱网层的孔径为300-500μm，薄膜层上带有小孔，其中，薄膜层上的孔径为30-50μm。
优选地，硅胶乳液中固含量为30-50wt％。
优选地，水性聚氨酯乳液中固含量为30-40wt％。
优选地，在添加剂的制备过程中，将壳聚糖溶液加入海藻酸钠溶液中，搅拌得到混合液；将混合液滴加至氯化钙水溶液中，搅拌，过滤，用水洗涤滤饼，真空干燥得到物料A；将物料A加入纳米二氧化钛水分散液中，升温，搅拌，过滤，真空干燥得到添加剂。
优选地，在添加剂的制备过程中，将壳聚糖溶液加入海藻酸钠溶液中，以200-400r/min的速度搅拌5-6h得到混合液；将混合液滴加至质量分数为3-5wt％氯化钙水溶液中，搅拌5-6h，过滤，用水洗涤滤饼，真空干燥得到物料A；将物料A加入纳米二氧化钛水分散液中，升温至50-70℃，以600-800r/min的速度搅拌10-15h，过滤，真空干燥得到添加剂。
优选地，在添加剂的制备过程中，壳聚糖溶液和海藻酸钠溶液的溶剂均为pH＝3.5的醋酸-醋酸钠缓冲液，壳聚糖溶液和海藻酸钠溶液的质量分数均为3-5wt％。
优选地，在添加剂的制备过程中，壳聚糖和海藻酸钠的摩尔比为1：0.8-1.2。
优选地，在添加剂的制备过程中，混合液和氯化钙水溶液的重量比为1：5-10。
优选地，在添加剂的制备过程中，物料A和纳米二氧化钛的重量比为3-5：1-2。
上述水均为去离子水。
上述添加剂的制备过程中，纳米二氧化钛水分散液中，水的作用是使纳米二氧化钛分散均匀，不规定水的用量，根据具体操作确定其用量。
上述硅胶、水性聚氨酯、聚乙二醇200、轻质碳酸钙、竹炭粉、十二烷基硫酸钠、乳化硅油、羧甲基纤维素钠均为食品级。
本发明的制备方法为：将涂料涂覆在硅胶模具表面成膜，脱模得到薄膜层；将薄膜层置于两层纱网中间，热压复合，激光打孔得到抗紫外线防雾霾纱网。
本发明选用壳聚糖和海藻酸钠反应，壳聚糖上的羟基、氨基与海藻酸钠上的羧基发生键合，使得海藻酸钠接枝到壳聚糖上，大大增加壳聚糖在水中的溶解性和分散性；使得壳聚糖与纳米二氧化钛能均匀分散，壳聚糖上剩余的羟基、氨基与纳米二氧化钛表面大量的羟基发生键合，使得壳聚糖、海藻酸钠和纳米二氧化钛包覆在一起，从而大大增加了纳米二氧化钛在硅胶乳液和水性聚氨酯乳液中的分散性，使三者均匀分散，同时避免了纳米二氧化钛团聚的问题，从而大大增加了本发明的抗紫外线作用和杀菌作用；壳聚糖没有毒性，并且具有良好的杀菌性，负离子粉也具有杀菌作用，纳米二氧化钛和壳聚糖、负离子粉相互配合，可以大大增加本发明的抗菌性；海藻酸钠内部具有多孔结构，配合竹炭粉，可以大大增加本发明对灰尘和雾霾的吸附性能，负离子粉具有良好的净化空气的能力，负离子粉和竹炭粉、添加剂中的海藻酸钠相互配合，吸附和净化两种作用相互配合，从而大大增加本发明的防雾霾性能；轻质碳酸钙、竹炭粉、负离子粉、添加剂可以增加本发明的机械性能；硅胶乳液和水性聚氨酯乳液相互配合可以增加本发明的机械性能和耐高温性能。
具体实施方式
下面，通过具体实施例对本发明的技术方案进行详细说明。
实施例1
一种抗紫外线防雾霾纱网，所述抗紫外线防雾霾纱网包括三层，第一层和第三层均为纱网层，中间层为薄膜层，薄膜层粘附在纱网层上；
其中，薄膜层是由涂料加工成膜得到，所述涂料的原料按重量份包括：硅胶乳液70份，水性聚氨酯乳液30份，聚乙二醇200 3.5份，轻质碳酸钙13份，竹炭粉5.5份，负离子粉10份，十二烷基硫酸钠1.5份，乳化硅油0.2份，添加剂5份，羧甲基纤维素钠0.25份，水13份；
在添加剂的制备过程中，将壳聚糖溶液加入海藻酸钠溶液中，搅拌得到混合液；将混合液滴加至氯化钙水溶液中，搅拌，过滤，用水洗涤滤饼，真空干燥得到物料A；将物料A加入纳米二氧化钛水分散液中，升温，搅拌，过滤，真空干燥得到添加剂。
实施例2
一种抗紫外线防雾霾纱网，所述抗紫外线防雾霾纱网包括三层，第一层和第三层均为纱网层，中间层为薄膜层，薄膜层粘附在纱网层上；
其中，薄膜层是由涂料加工成膜得到，所述涂料的原料按重量份包括：固含量为30wt％硅胶乳液80份，固含量为30wt％水性聚氨酯乳液40份，聚乙二醇200 3份，轻质碳酸钙15份，竹炭粉5份，负离子粉12份，十二烷基硫酸钠1份，乳化硅油0.3份，添加剂4份，羧甲基纤维素钠0.3份，水10份；
在添加剂的制备过程中，将质量分数为5wt％壳聚糖溶液加入质量分数为5wt％海藻酸钠溶液中，以200r/min的速度搅拌6h得到混合液，其中，壳聚糖溶液和海藻酸钠溶液的溶剂均为pH＝3.5的醋酸-醋酸钠缓冲液，壳聚糖和海藻酸钠的摩尔比为1：0.8；将混合液滴加至质量分数为5wt％氯化钙水溶液中，搅拌5h，过滤，用水洗涤滤饼，真空干燥得到物料A，其中，混合液和氯化钙水溶液的重量比为1：10；将物料A加入纳米二氧化钛水分散液中，升温至50℃，以800r/min的速度搅拌10h，过滤，真空干燥得到添加剂，其中，物料A和纳米二氧化钛的重量比为5：1。
实施例3
一种抗紫外线防雾霾纱网，所述抗紫外线防雾霾纱网包括三层，第一层和第三层均为纱网层，中间层为薄膜层，薄膜层粘附在纱网层上；
其中，薄膜层是由涂料加工成膜得到，所述涂料的原料按重量份包括：固含量为50wt％硅胶乳液60份，固含量为40wt％水性聚氨酯乳液20份，聚乙二醇200 4份，轻质碳酸钙10份，竹炭粉6份，负离子粉8份，十二烷基硫酸钠2份，乳化硅油0.1份，添加剂6份，羧甲基纤维素钠0.2份，水15份；
在添加剂的制备过程中，将质量分数为3wt％壳聚糖溶液加入质量分数为3wt％海藻酸钠溶液中，以400r/min的速度搅拌5h得到混合液，其中，壳聚糖溶液和海藻酸钠溶液的溶剂均为pH＝3.5的醋酸-醋酸钠缓冲液，壳聚糖和海藻酸钠的摩尔比为1：1.2；将混合液滴加至质量分数为3wt％氯化钙水溶液中，搅拌6h，过滤，用水洗涤滤饼，真空干燥得到物料A，其中，混合液和氯化钙水溶液的重量比为1：5；将物料A加入纳米二氧化钛水分散液中，升温至70℃，以600r/min的速度搅拌15h，过滤，真空干燥得到添加剂，其中，物料A和纳米二氧化钛的重量比为3：2。
实施例4
一种抗紫外线防雾霾纱网，所述抗紫外线防雾霾纱网包括三层，第一层和第三层均为纱网层，中间层为薄膜层，薄膜层粘附在纱网层上；
其中，纱网层的孔径为300μm，薄膜层上带有小孔，其中，薄膜层上的孔径为50μm；
薄膜层是由涂料加工成膜得到，所述涂料的原料按重量份包括：固含量为35wt％硅胶乳液75份，固含量为32wt％水性聚氨酯乳液35份，聚乙二醇200 3.3份，轻质碳酸钙14份，竹炭粉5.2份，负离子粉11份，十二烷基硫酸钠1.3份，乳化硅油0.25份，添加剂4.5份，羧甲基纤维素钠0.28份，水12份；
在添加剂的制备过程中，将质量分数为4.5wt％壳聚糖溶液加入质量分数为4.5wt％海藻酸钠溶液中，以250r/min的速度搅拌5.8h得到混合液，其中，壳聚糖溶液和海藻酸钠溶液的溶剂均为pH＝3.5的醋酸-醋酸钠缓冲液，壳聚糖和海藻酸钠的摩尔比为1：0.9；将混合液滴加至质量分数为4.5wt％氯化钙水溶液中，搅拌5.3h，过滤，用水洗涤滤饼，真空干燥得到物料A，其中，混合液和氯化钙水溶液的重量比为1：8；将物料A加入纳米二氧化钛水分散液中，升温至55℃，以750r/min的速度搅拌11h，过滤，真空干燥得到添加剂，其中，物料A和纳米二氧化钛的重量比为4.5：1.2。
实施例5
一种抗紫外线防雾霾纱网，所述抗紫外线防雾霾纱网包括三层，第一层和第三层均为纱网层，中间层为薄膜层，薄膜层粘附在纱网层上；
其中，纱网层的孔径为500μm，薄膜层上带有小孔，其中，薄膜层上的孔径为30μm；
薄膜层是由涂料加工成膜得到，所述涂料的原料按重量份包括：固含量为45wt％硅胶乳液65份，固含量为38wt％水性聚氨酯乳液25份，聚乙二醇200 3.7份，轻质碳酸钙12份，竹炭粉5.8份，负离子粉9份，十二烷基硫酸钠1.7份，乳化硅油0.15份，添加剂5.5份，羧甲基纤维素钠0.22份，水14份；
在添加剂的制备过程中，将质量分数为3.5wt％壳聚糖溶液加入质量分数为3.5wt％海藻酸钠溶液中，以350r/min的速度搅拌5.2h得到混合液，其中，壳聚糖溶液和海藻酸钠溶液的溶剂均为pH＝3.5的醋酸-醋酸钠缓冲液，壳聚糖和海藻酸钠的摩尔比为1：1.1；将混合液滴加至质量分数为3.5wt％氯化钙水溶液中，搅拌5.7h，过滤，用水洗涤滤饼，真空干燥得到物料A，其中，混合液和氯化钙水溶液的重量比为1：6；将物料A加入纳米二氧化钛水分散液中，升温至65℃，以650r/min的速度搅拌13h，过滤，真空干燥得到添加剂，其中，物料A和纳米二氧化钛的重量比为3.5：1.8。
实施例6
一种抗紫外线防雾霾纱网，所述抗紫外线防雾霾纱网包括三层，第一层和第三层均为纱网层，中间层为薄膜层，薄膜层粘附在纱网层上；
其中，纱网层的孔径为400μm，薄膜层上带有小孔，其中，薄膜层上的孔径为40μm；
薄膜层是由涂料加工成膜得到，所述涂料的原料按重量份包括：固含量为40wt％硅胶乳液70份，固含量为35wt％水性聚氨酯乳液30份，聚乙二醇200 3.5份，轻质碳酸钙13份，竹炭粉5.5份，负离子粉10份，十二烷基硫酸钠1.5份，乳化硅油0.2份，添加剂5份，羧甲基纤维素钠0.25份，水13份；
在添加剂的制备过程中，将质量分数为4wt％壳聚糖溶液加入质量分数为4wt％海藻酸钠溶液中，以300r/min的速度搅拌5.5h得到混合液，其中，壳聚糖溶液和海藻酸钠溶液的溶剂均为pH＝3.5的醋酸-醋酸钠缓冲液，壳聚糖和海藻酸钠的摩尔比为1：1；将混合液滴加至质量分数为4wt％氯化钙水溶液中，搅拌5.5h，过滤，用水洗涤滤饼，真空干燥得到物料A，其中，混合液和氯化钙水溶液的重量比为1：7；将物料A加入纳米二氧化钛水分散液中，升温至60℃，以700r/min的速度搅拌12h，过滤，真空干燥得到添加剂，其中，物料A和纳米二氧化钛的重量比为4：1.5。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。
Claims (10)
1.一种抗紫外线防雾霾纱网，其特征在于，所述抗紫外线防雾霾纱网包括三层，第一层和第三层均为纱网层，中间层为薄膜层，薄膜层粘附在纱网层上；
其中，薄膜层是由涂料加工成膜得到，所述涂料的原料按重量份包括：硅胶乳液60-80份，水性聚氨酯乳液20-40份，聚乙二醇200 3-4份，轻质碳酸钙10-15份，竹炭粉5-6份，负离子粉8-12份，十二烷基硫酸钠1-2份，乳化硅油0.1-0.3份，添加剂4-6份，羧甲基纤维素钠0.2-0.3份，水10-15份。
2.根据权利要求1所述抗紫外线防雾霾纱网，其特征在于，纱网层的孔径为300-500μm，薄膜层上带有小孔，其中，薄膜层上的孔径为30-50μm。
3.根据权利要求1或2所述抗紫外线防雾霾纱网，其特征在于，硅胶乳液中固含量为30-50wt％。
4.根据权利要求1-3任一项所述抗紫外线防雾霾纱网，其特征在于，水性聚氨酯乳液中固含量为30-40wt％。
5.根据权利要求1-4任一项所述抗紫外线防雾霾纱网，其特征在于，在添加剂的制备过程中，将壳聚糖溶液加入海藻酸钠溶液中，搅拌得到混合液；将混合液滴加至氯化钙水溶液中，搅拌，过滤，用水洗涤滤饼，真空干燥得到物料A；将物料A加入纳米二氧化钛水分散液中，升温，搅拌，过滤，真空干燥得到添加剂。
6.根据权利要求5所述抗紫外线防雾霾纱网，其特征在于，在添加剂的制备过程中，将壳聚糖溶液加入海藻酸钠溶液中，以200-400r/min的速度搅拌5-6h得到混合液；将混合液滴加至质量分数为3-5wt％氯化钙水溶液中，搅拌5-6h，过滤，用水洗涤滤饼，真空干燥得到物料A；将物料A加入纳米二氧化钛水分散液中，升温至50-70℃，以600-800r/min的速度搅拌10-15h，过滤，真空干燥得到添加剂。
7.根据权利要求5所述抗紫外线防雾霾纱网，其特征在于，在添加剂的制备过程中，壳聚糖溶液和海藻酸钠溶液的溶剂均为pH＝3.5的醋酸-醋酸钠缓冲液，壳聚糖溶液和海藻酸钠溶液的质量分数均为3-5wt％。
8.根据权利要求5所述抗紫外线防雾霾纱网，其特征在于，在添加剂的制备过程中，壳聚糖和海藻酸钠的摩尔比为1：0.8-1.2。
9.根据权利要求5所述抗紫外线防雾霾纱网，其特征在于，在添加剂的制备过程中，混合液和氯化钙水溶液的重量比为1：5-10。
10.根据权利要求5所述抗紫外线防雾霾纱网，其特征在于，在添加剂的制备过程中，物料A和纳米二氧化钛的重量比为3-5：1-2。