CN1060501C - 粘土固化浆液固化剂 - Google Patents

粘土固化浆液固化剂 Download PDF

Info

Publication number
CN1060501C
CN1060501C CN96117823A CN96117823A CN1060501C CN 1060501 C CN1060501 C CN 1060501C CN 96117823 A CN96117823 A CN 96117823A CN 96117823 A CN96117823 A CN 96117823A CN 1060501 C CN1060501 C CN 1060501C
Authority
CN
China
Prior art keywords
slurry
clay
solidifying agent
water
hardening slurry
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN96117823A
Other languages
English (en)
Other versions
CN1184838A (zh
Inventor
王星华
高渠清
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changsha Railway College
Original Assignee
CHANGSHA RAILWAY COLLEGE
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHA RAILWAY COLLEGE filed Critical CHANGSHA RAILWAY COLLEGE
Priority to CN96117823A priority Critical patent/CN1060501C/zh
Publication of CN1184838A publication Critical patent/CN1184838A/zh
Application granted granted Critical
Publication of CN1060501C publication Critical patent/CN1060501C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

在地下水注浆防治施工中因粘土水泥类浆液凝结时间长,浆液结石体早期强度很低,不适应于流动的地下水条件下注浆止水,而粘土固化浆液则能解决在地下水流动状态下注浆时浆液流失量大的问题,其中固化剂则起了主要作用。固化剂主要成分为:铝酸盐30~50%;硫酸盐5~20%;硅酸盐5~15%;氟硅酸盐1~5%;氧化硅1~10%;氧化钙1~10%;氧化铝1~10%。主要用于各种地下工程,堤坝防渗注浆,深基坑注浆止水等注浆施工时粘土固化浆液的配制。

Description

粘土固化浆液固化剂
本发明涉及地下工程的防渗注浆技术领域,特别涉及粘土固化浆液的固化注浆技术领域。
国内粘土类浆液主要为粘土水泥浆或水泥粘土浆液,其主要成分基本上为粘土、水泥,再加上水玻璃等附加剂,而粘土固化浆液主要成分为粘土、水泥、水玻璃、固化剂,其中水玻璃是浆液的一种主要成分,固化剂则是附加剂。我国对水泥粘土浆或粘土水泥浆研究较多,并且有许多注浆成功的例子,而对粘土固化浆液则研究的较少,粘土固化浆液固化剂更加未见报道。英国专利EP428431公开了一种用于管道水力输送的浆液稳定剂;日本专利JP63021248介绍的是钻井泥浆固结剂,用来沉淀泥浆中的固体颗粒,固结剂为水泥、水玻璃和一种水溶性纤维醚;英国专利EP219189所叙为一种石油钻井中所用的防水浆液,主要成分为水膨胀性粘土、非水膨胀填料、水溶性硅酸盐、胶凝剂、高价离子等,其中胶凝剂的成分在该专利中并未说明;日本专利JP52070521为用于固结土壤的土壤固化剂,主要成分为粘土、水玻璃、酸、水和胶凝控制剂;日本专利JP52135512为加固软弱地层的浆液,主要成分为普通硅酸盐水泥、活性粘土、石灰、石膏与硬化剂;另一日本专利JP06041533介绍了另一种地层加固剂的成分,玻璃质细颗粒、氧化钙、氢氧化钠或氢氧化钾、白碳、粘土与石灰等,用来提高软弱地层的承载力,以上国外专利均未涉及到粘土固化浆液与固化剂。
本发明的目的是提供一种粘土固化浆液固化剂,它能有效地加快粘土固化浆液的凝固速度,提高浆液结石体的早期强度。
本发明的目的由以下技术方案实现:在普通的粘土——水泥——水玻璃浆液中加入固化剂,使性能低劣的粘土——水泥——水玻璃浆液成为粘土固化浆液,并具有一些特殊的性能。粘土固化浆液的优越性能全在于所用固化剂在浆液凝固过程中的催化作用,没有固化剂则粘土固化浆液的一切优越性能就完全丧失了,可以说固化剂是粘土固化浆液的核心技术。因此本发明着眼于筛选与优化粘土固化浆液的固化剂的配方,经筛选的粘土固化浆液固化剂组分重量百分比为:铝酸盐30%—50%、硫酸盐5%—20%、硅酸盐5%—15%、氟硅酸盐1%—5%、氧化硅1%—10%、氧化钙1%—10%、氧化铝1%—10%。其中铝酸盐的纯度为85%—95%、硫酸盐的纯度为90%—98%、氟硅酸盐的纯度为90%—98%、氧化铝的纯度为45%—90%。当使用以上纯度的所述组分制成的粘土固化浆液固化剂与30%—50%的粘土、1%—15%的水泥、1%—15%的水玻璃、10—30%的水混合,可以在较短时间内得到强度较高的粘土固化浆液结石体,这里固化剂的使用量在0.05%—10%之间。
本发明与现有技术相比所具有的效果与优点在于:
一、与水泥类浆液相比具有以下优点:
1、良好的抗水稀释性,粘土固化具有能吸收大量的水分而不会发生分层析水,仅是浆液变稀,但仍然能凝固;故能在流动的地下水条件下注浆止水并或成功,此时浆液流失量小,注浆成本低。
2、良好的流变性能,粘土固化浆液流变性较好,并且可以调整其流变参数使其符合设计要求。
3、由于粘土固化浆液采用粘土为基本原料(甚至可以采用施工现场附近的粘土)加上少量水泥、水玻璃与固化剂,因此成本很低,仅为水泥浆的二分之一到三分之一。
4、粘土固化浆液结石体早期强度较低,强度增长时间较长,故粘土固化浆液在注浆几天后仍可进行重复注浆以提高注浆效果。
5、粘土固化浆液初凝时间根据配方不同而不同,从几秒到几十分钟可调。
二、与粘土水泥浆液、粘土—水泥—水玻璃浆液相比具有以下优点:
1、凝结时间大大提高,粘土固化具有加入固化剂之后,由于固化剂的催化作用,使得水泥水化反应加快,同时水泥与水玻璃、与粘土之间的反应也在固化剂的催化作用下加快反应,从而表现出浆液的凝结时间大大缩短(初凝时间从数小时缩短为几秒钟到几十分钟并可调。
2、浆液结石体强度大大提高,粘土固化浆液在固化剂的催化作用下,整个浆液体系反应加快,使得浆液结石体的强度增加,特别是浆液结石体早期强度增加较快(12小时强度可达数百千帕),浆液结石体最终强度可达数兆帕并可调。
本发明的实施例如下:
实例1:
筛选粘土固化浆液固化剂组分重量百分比为:铝酸盐35%、硫酸盐16%、硅酸盐15%、氟硅酸盐4.5%、氧化硅10%、氧化钙9.5%、氧化铝10%。当使用以上纯度的所述组分制成的粘土固化浆液固化剂与30%—50%的粘土、1%—15%的水泥、1%—15%的水玻璃、10—30%的水混合,可以在较短时间内得到强度较高的粘土固化浆液结石体,这里固化剂的使用量在0.05%—10%之间。此时粘土固化浆液的初凝时间为45秒,浆液结石体一小时塑性强度为11.9千帕,四小时为40.0千帕,一天为636.3千帕,二天为1.13兆帕,十六天为1.64兆帕。
实例2:
筛选粘土固化浆液固化剂组分重量百分比为:铝酸盐46%、硫酸盐15%、硅酸盐14%、氟硅酸盐3%、氧化硅9%、氧化钙7.5%、氧化铝5.5%。当使用以上纯度的所述组分制成的粘土固化浆液固化剂与30%—50%的粘土、1%—15%的水泥、1%—15%的水玻璃、10—30%的水混合,可以在较短时间内得到强度较高的粘土固化浆液结石体,这里固化剂的使用量在0.05%—10%之间。此时粘土固化浆液的初凝时间为55秒,浆液结石体一小时塑性强度为7.9千帕,四小时为25.7千帕,一天为520千帕,二天为910.4千帕,十八天为3.5兆帕。
实例3:
筛选粘土固化浆液固化剂组分重量百分比为:铝酸盐42%、硫酸盐20%、硅酸盐11%、氟硅酸盐2.0%、氧化硅8.5%、氧化钙9.0%、氧化铝7.5%。当使用以上纯度的所述组分制成的粘土固化浆液固化剂与30%—50%的粘土、1%—15%的水泥、1%—15%的水玻璃、10—30%的水混合,可以在较短时间内得到强度较高的粘土固化浆液结石体,这里固化剂的使用量在0.05%—10%之间。此时粘土固化浆液的初凝时间为50秒,浆液结石体一小时塑性强度为3.29千帕,四小时为43.0千帕,一天为294千帕,二天为1.94兆帕,十六天为4.4兆帕。
用此固化剂配方配制粘土固化浆液所需的配比(重量%)为:
粘土30~50%;普通水泥1~15%;水玻璃1~15%;水10~30%;固化剂0.05~10%,此时粘土固化浆液初凝时间为50秒,浆液结石体1小时塑性强度为3.29KPa,4小时为43KPa,1天为294KPa,2天为1.94MPa,18天为4.4KPa。

Claims (2)

1、一种粘土固化浆液固化剂,主要由硫酸盐、硅酸盐等盐类和氧化钙等氧化物组成,其特征在于粘土固化浆液固化剂各组分重量百分比为:铝酸盐30%—50%、硫酸盐5%—20%、硅酸盐5%—15%、氟硅酸盐1%—5%、氧化硅1%—10%、氧化钙1%—10%、氧化铝1%—10%。
2、根据权利要求1所述的粘土固化浆液固化剂,其特征在于所述铝酸盐的纯度为85%—95%、硫酸盐的纯度为90%—98%、氟硅酸盐的纯度为90%—98%、氧化铝的纯度为45%—90%。
CN96117823A 1996-12-13 1996-12-13 粘土固化浆液固化剂 Expired - Fee Related CN1060501C (zh)