CN106048460B - Dragon's fountain day good fortune sword and its manufacture craft - Google Patents
Dragon's fountain day good fortune sword and its manufacture craft Download PDFInfo
- Publication number
- CN106048460B CN106048460B CN201610553928.1A CN201610553928A CN106048460B CN 106048460 B CN106048460 B CN 106048460B CN 201610553928 A CN201610553928 A CN 201610553928A CN 106048460 B CN106048460 B CN 106048460B
- Authority
- CN
- China
- Prior art keywords
- sword
- temperature
- annealing
- sword body
- dragon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention provides a kind of dragon's fountain day good fortune sword and its manufacture craft, and alloy is made up of the chemical composition of following degree used by the sword body of day Fujian:Mo0.15 ~ 0.25%, V0.1 ~ 0.3%, Mn0.12 ~ 0.20%, Si0.3 ~ 0.5%, C1.4 ~ 1.6%, Cr20.0 ~ 24.0%, Ni0.6 ~ 0.8%, Ca0.2 ~ 0.4%, nanometer Buddha's warrior attendant 0.6 0.9%, remaining is no more than 0.1% impurity for the Fe of surplus and total composition;The invention preparation process comprises the following steps:1)The preparation of sword embryo;2)Water breakthrough;3)See oil;4)Normalizing;5)Annealing;6)Grinding and buffing;7)Salt bath;8)Quenching;9)It is tempered and produces sword body.Sword body of the present invention, which has, forges lines, has that sharp sword knife edge, elastic camber, hardness are superior, and the advantages of be not easy corrosion.
Description
Technical field
The present invention relates to a kind of daggers and swords, and in particular to dragon's fountain day good fortune sword and its manufacture craft.
Technical background
During very long social development, substantially being made using medium carbon steel or high-carbon steel for traditional sword body is raw
The double-edged sword of production gets rusty easily corrosion during using and preserving.The riffled iron forged is exactly folded by hand this similarly be present
The problem of sample.Double-edged sword is during using this is collected, often because playing or being gone to touch the sword body of double-edged sword, sweat on hand with hand
Easily double-edged sword is set to get rusty.Plum rain season is run into use simultaneously and wet weather easily causes sword surface oxidisation.
In addition, existing double-edged sword have one it is obvious the characteristics of, be exactly that its bending resistance is often relatively low when its hardness is very high;And work as
When its flexural strength is very high, its hardness is again relatively low.Such as prior art Authorization Notice No.:CN103741051B Chinese invention
Patent, used by a kind of sword body preparation method sword body of the disclosure of the invention alloy have the chemistry of following degree into
Point:C 1.2-1.4%, Si 0.5-0.7%, Mn 0.10-0.20%, Cr 23.0-24.0%, Ni 0.3-0.5%, Ca 0.30-
0.50%, Mo 0.15-0.25%, V 0.2-0.4%, Nano diamond 0.4-0.6%, remaining for surplus Fe and total composition not
Impurity more than 0.1%.Sword body made of the invention is not easy corrosion, and elastic camber, hardness are more excellent.
The content of the invention
The present invention provides a kind of sword knife edge profit, hardness height, with forging the firm one kind of decorative pattern to solve above-mentioned technical problem
Dragon's fountain day good fortune sword and its manufacture craft.
It is of the invention to be for the taken scheme that solves the above problems:A kind of dragon's fountain day good fortune sword and its manufacture craft, including sword
Body and scabbard, wherein:
Alloy is made up of the chemical composition of following degree used by its Fujian sword body:Mo 0.15 ~ 0.25%, V
0.1 ~ 0.3%, Mn 0.12 ~ 0.20%, Si 0.3 ~ 0.5%, C 1.4 ~ 1.6%, Cr 20.0 ~ 24.0%, Ni 0.6 ~ 0.8%, Ca
0.2 ~ 0.4%, Nano diamond 0.6-0.9%, remaining is no more than 0.1% impurity for the Fe of surplus and total composition.
Nano diamond refers to the diamond particle that average path is 400nm ~ 500nm nanometers.
A kind of day good fortune sword manufacture craft, comprises the following steps:
The preparation of sword base:Alloy is made up of the chemical composition of following degree used by sword body:Mo 0.15~
0.25%, V 0.1 ~ 0.3%, Mn 0.12 ~ 0.20%, Si 0.3 ~ 0.5%, C 1.4 ~ 1.6%, Cr 20.0 ~ 24.0%, Ni 0.6 ~
0.8%, Ca 0.2 ~ 0.4%, Nano diamond 0.6-0.9%, remaining is no more than 0.1% impurity for the Fe of surplus and total composition,
Crude green body with the much the same shape of sword is made in steel raw material using punch press, then is placed in forge furnace and calcines, calcining heat is 649 DEG C ~
982 DEG C, soften to form sword base;
Water breakthrough:Sword base charge and attack by hand, while flicks sword body repeatedly, sword base is subjected to water breakthrough step after charging and attacking, then
It is repeated 1 times above step and calcines-charge and attack-water breakthrough;
See oil:Calcining heat is calcined-charged and attacked to sword base obtained by upper step process as 649 DEG C ~ 982 DEG C again, carries out seeing oil
Step, sword body is obtained, it is in order that double-edged sword is more flexible to see oil;
Normalizing:Sword body is put into forge furnace and reheats heating, normalizing temperature is 700 DEG C ~ 982 DEG C, is being allowed to cool down, normalizing
Purpose be granulation steel, after sword body is heated to certain temperature, it may occur that austenitizing, can so reduce due to sword body composition
It is irregular caused by stress, and ensure the consistent of whole sword body particle;
Annealing:Sword body obtained by upper step process is made annealing treatment with wrapped with insulation, annealing temperature is 700 DEG C ~
982 DEG C, the purpose of annealing is to allow steel to soften, and is easy to polish and cuts;
Grinding and buffing:Grinding-fine grinding-polishing;
Salt bath:Liquid is dissolved into salt heating, allows sword body to be suspended in 1 ~ 3h in salt bath, the use of salt bath, because of fusion temperature
The salt lower than the temperature of steel fusing, after this temperature, salt will remain in that liquid, thus be provided for blade splendid
" heating bath " condition, heat steel to salt uniform and complete;
Sword body obtained by upper step process is put into quenching tank, the purpose of quenching is that cementite is enclosed in ferrite, system
A kind of stone steel is produced, is called martensite;
It is tempered and produces sword body;
Wherein, during above-mentioned charge and attack, a small amount of alloy should be added on sword sword carry out folding and charge and attack.
The a small amount of alloy added on sword sword by following degree chemical composition:Obsidian 10 ~ 20%, In 0.10 ~
0.25%, Nano diamond 0.6-0.9%, remaining is no more than 0.1% impurity for the Fe of surplus and total composition, and increase sword sword is hard
Spend and allow sword sword sharpness to increase significantly, while surface has lines in layer, turn into that to forge decorative pattern firm, it is very attractive in appearance,
Reserve value is very big.
Normalizing temperature is 720 DEG C ~ 736 DEG C, temperature control, makes sword under austenitizing, with the tissue being stabilized;
Annealing temperature is 723 DEG C ~ 731 DEG C, temperature control, makes sword under austenitizing, with the tissue being stabilized;
Being tempered concrete operations is:Thick clay rib will be covered with whole sword, in the case where temperature is 649 DEG C ~ 727 DEG C, entered
Row tempering, keeps temperature quenching-annealing again for a period of time, repeats 3 ~ 6 times, wrapping portion should be than other portions of sword body
It is point slightly soft, pliability can be increased, and sword sword should then keep hard, repeatedly annealing obtains accurate hardness level, makes steel
Hardness keeps sharp sword sword enough, but hard must can not become fragile, because may so cause tipping or fragmentation.
Compared with prior art, advantage for present invention is:
1st, sword body of the present invention forms and forges riffled iron, has great reserve value.
2nd, sword knife edge of the present invention is sharp, elastic camber, hardness are superior, and is not easy corrosion.
Embodiment
It is described in further detail with reference to embodiments:
Embodiment 1:
A kind of day good fortune sword and its manufacture craft, including sword body and scabbard, wherein:
Alloy is made up of the chemical composition of following degree used by its Fujian sword body:Mo 0.15 ~ 0.25%, V
0.1 ~ 0.3%, Mn 0.12 ~ 0.20%, Si 0.3 ~ 0.5%, C 1.4 ~ 1.6%, Cr 20.0 ~ 24.0%, Ni 0.6 ~ 0.8%, Ca
0.2 ~ 0.4%, Nano diamond 0.6-0.9%, remaining is no more than 0.1% impurity for the Fe of surplus and total composition.
Nano diamond refers to the diamond particle that average path is 400nm ~ 500nm nanometers.
A kind of day good fortune sword manufacture craft, comprises the following steps:
The preparation of sword base:Alloy is made up of the chemical composition of following degree used by sword body:Mo 0.15~
0.25%, V 0.1 ~ 0.3%, Mn 0.12 ~ 0.20%, Si 0.3 ~ 0.5%, C 1.4 ~ 1.6%, Cr 20.0 ~ 24.0%, Ni 0.6 ~
0.8%, Ca 0.2 ~ 0.4%, Nano diamond 0.6-0.9%, remaining is no more than 0.1% impurity for the Fe of surplus and total composition,
Crude green body with the much the same shape of sword is made in steel raw material using punch press, then is placed in forge furnace and calcines, calcining heat is 649 DEG C ~
982 DEG C, soften to form sword base;
Water breakthrough:Sword base charge and attack by hand, while flicks sword body repeatedly, sword base is subjected to water breakthrough step after charging and attacking, then
It is repeated 1 times above step and calcines-charge and attack-water breakthrough;
See oil:Calcining heat is calcined-charged and attacked to sword base obtained by upper step process as 649 DEG C ~ 982 DEG C again, carries out seeing oil
Step, sword body is obtained, it is in order that double-edged sword is more flexible to see oil;
Normalizing:Sword body is put into forge furnace and reheats heating, normalizing temperature is 700 DEG C ~ 982 DEG C, is being allowed to cool down, normalizing
Purpose be granulation steel, after sword body is heated to certain temperature, it may occur that austenitizing, can so reduce due to sword body composition
It is irregular caused by stress, and ensure the consistent of whole sword body particle;
Annealing:Sword body obtained by upper step process is made annealing treatment with wrapped with insulation, annealing temperature is 700 DEG C ~
982 DEG C, the purpose of annealing is to allow steel to soften, and is easy to polish and cuts;
Grinding and buffing:Grinding-fine grinding-polishing;
Salt bath:Liquid is dissolved into salt heating, allows sword body to be suspended in 1 ~ 3h in salt bath, the use of salt bath, because of fusion temperature
The salt lower than the temperature of steel fusing, after this temperature, salt will remain in that liquid, thus be provided for blade splendid
" heating bath " condition, heat steel to salt uniform and complete;
Sword body obtained by upper step process is put into quenching tank, the purpose of quenching is that cementite is enclosed in ferrite, system
A kind of stone steel is produced, is called martensite;
It is tempered and produces sword body;
Wherein, during above-mentioned charge and attack, a small amount of alloy should be added on sword sword carry out folding and charge and attack.
The a small amount of alloy added on sword sword by following degree chemical composition:Obsidian 10 ~ 20%, In 0.10 ~
0.25%, Nano diamond 0.6-0.9%, remaining is no more than 0.1% impurity for the Fe of surplus and total composition, and increase sword sword is hard
Spend and allow sword sword sharpness to increase significantly, while surface has lines in layer, turn into that to forge decorative pattern firm, it is very attractive in appearance,
Reserve value is very big.
Normalizing temperature is 720 DEG C ~ 736 DEG C, temperature control, makes sword under austenitizing, with the tissue being stabilized;
Annealing temperature is 723 DEG C ~ 731 DEG C, temperature control, makes sword under austenitizing, with the tissue being stabilized;
Being tempered concrete operations is:Thick clay rib will be covered with whole sword, in the case where temperature is 649 DEG C ~ 727 DEG C, entered
Row tempering, keeps temperature quenching-annealing again for a period of time, repeats 3 ~ 6 times, wrapping portion should be than other portions of sword body
It is point slightly soft, pliability can be increased, and sword sword should then keep hard, repeatedly annealing obtains accurate hardness level, makes steel
Hardness keeps sharp sword sword enough, but hard must can not become fragile, because may so cause tipping or fragmentation.
Contrast experiment:
Embodiment group:Sword body alloy is formed with the chemical composition by following degree:Mo 0.15 ~ 0.25%, V 0.1
~ 0.3%, Mn 0.12 ~ 0.20%, Si 0.3 ~ 0.5%, C 1.4 ~ 1.6%, Cr 20.0 ~ 24.0%, Ni 0.6 ~ 0.8%, Ca 0.2 ~
0.4%, Nano diamond 0.6-0.9%, remaining is no more than 0.1% impurity for the Fe of surplus and total composition;The preparation of sword body:
1)The preparation of sword base:Crude green body with the much the same shape of sword is made in steel raw material using punch press, then is placed in forge furnace and calcines, is calcined
Temperature is 649 DEG C ~ 982 DEG C, softens to form sword base;2)Water breakthrough:Sword base charge and attack by hand, while flicks sword repeatedly
Body, sword base is subjected to water breakthrough step after charging and attacking, 1 above step is repeated and calcines-charge and attack-water breakthrough;3)See oil:At upper step
Calcining heat is calcined-charged and attacked to reason gained sword base as 649 DEG C ~ 982 DEG C again, carries out seeing oily step, obtains sword body;4)Normalizing:By sword
Body is put into forge furnace and reheats heating, and normalizing temperature is 700 DEG C ~ 982 DEG C, is being allowed to cool down;5)Annealing:By upper step process institute
Obtain sword body to be made annealing treatment with wrapped with insulation, annealing temperature is 700 DEG C ~ 982 DEG C;6)Grinding and buffing:Grinding-essence
Mill-polishing;7)Salt bath:Liquid is dissolved into salt heating, allows sword body to be suspended in 1 ~ 3h in salt bath;8)Quenching:By upper step process
Gained sword body is put into quenching tank;9)It is tempered and produces sword body;During charging and attacking, a small amount of alloy added on sword sword is by following percentage
Than the chemical composition of content:Obsidian 10 ~ 20%, In 0.10 ~ 0.25%, Nano diamond 0.6-0.9%, remaining is the Fe of surplus
And total composition is no more than 0.1% impurity.
Control group:Embodiment group:Sword body alloy is formed with the chemical composition by following degree:Mo 0.15~
0.25%, V 0.1 ~ 0.3%, Mn 0.12 ~ 0.20%, Si 0.3 ~ 0.5%, C 1.4 ~ 1.6%, Cr 20.0 ~ 24.0%, Ni 0.6 ~
0.8%, Ca 0.2 ~ 0.4%, Nano diamond 0.6-0.9%, remaining is no more than 0.1% impurity for the Fe of surplus and total composition;
The preparation of sword body:1)The preparation of sword base:Crude green body with the much the same shape of sword is made in steel raw material using punch press, then is placed on forge furnace
Middle calcining, calcining heat are 649 DEG C ~ 982 DEG C, soften to form sword base;2)Water breakthrough:Sword base charge and attack by hand, simultaneously
Sword body is flicked repeatedly, and sword base is subjected to water breakthrough step after charging and attacking, 1 above step is repeated and calcines-charge and attack-water breakthrough;3)See oil:
Calcining heat is calcined-charged and attacked to sword base obtained by upper step process as 649 DEG C ~ 982 DEG C again, carries out seeing oily step, obtains sword body;4)
Normalizing:Sword body is put into forge furnace and reheats heating, normalizing temperature is 700 DEG C ~ 982 DEG C, is being allowed to cool down;5)Annealing:Will be upper
Sword body obtained by step process is made annealing treatment with wrapped with insulation, and annealing temperature is 700 DEG C ~ 982 DEG C;6)Polishing and throwing
Light:Grinding-fine grinding-polishing;7)Salt bath:Liquid is dissolved into salt heating, allows sword body to be suspended in 1 ~ 3h in salt bath;8)Quenching:Will
Sword body obtained by upper step process is put into quenching tank;9)It is tempered and produces sword body;Sword obtained by two groups of experiments is subjected to contrast test, as a result
Such as table 1 below:
The comparative test result of table 1
Forge riffled iron | Hardness | Anti- rust corrosion | It is sharp | |
Embodiment group | Have | It is good | It is good | It is excellent |
Control group | Nothing | It is good | It is good | It is good |
As can be seen from the above table, embodiment group has natural lines, and formation forges riffled iron, in hardness and sword knife edge profit journey
It is better than control group on degree.
Although the present invention is disclosed as above with embodiment, it is not limited to protection scope of the present invention, any ripe
Those skilled in the art is known, in the change and retouching done without departing from the spirit and scope of the invention, this hair all should be belonged to
The protection domain of bright appended claims.
Claims (3)
1. dragon's fountain day good fortune sword manufacture craft, it is characterised in that following steps:
1)The preparation of sword base:Alloy is made up of the chemical composition of following degree used by sword body:Mo 0.15~
0.25%, V 0.1 ~ 0.3%, Mn 0.12 ~ 0.20%, Si 0.3 ~ 0.5%, C 1.4 ~ 1.6%, Cr 20.0 ~ 24.0%, Ni 0.6 ~
0.8%, Ca 0.2 ~ 0.4%, Nano diamond 0.6-0.9%, remaining is no more than 0.1% impurity for the Fe of surplus and total composition,
Crude green body with the much the same shape of sword is made in steel raw material using punch press, then is placed in forge furnace and calcines, calcining heat is 649 DEG C ~
982 DEG C, soften to form sword base;
2)Water breakthrough:Sword base charge and attack by hand, while flicks sword body repeatedly, sword base is subjected to water breakthrough step after charging and attacking, then weigh
- water breakthrough is calcined-charged and attacked to multiple 1 above step;
3)See oil:Calcining heat is calcined-charged and attacked to sword base obtained by upper step process as 649 DEG C ~ 982 DEG C again, carries out seeing oily step
Suddenly, sword body is obtained;
4)Normalizing:Sword body is put into forge furnace and reheats heating, normalizing temperature is 700 DEG C ~ 982 DEG C, is being allowed to cool down;
5)Annealing:Sword body obtained by upper step process is made annealing treatment with wrapped with insulation, annealing temperature is 700 DEG C ~ 982
℃;
6)Grinding and buffing:Grinding-fine grinding-polishing;
7)Salt bath:Liquid is dissolved into salt heating, allows sword body to be suspended in 1 ~ 3h in salt bath;
8)Quenching:Sword body obtained by upper step process is put into quenching tank;
9)It is tempered and produces sword body;
Wherein, during above-mentioned charge and attack, a small amount of alloy should be added on sword sword and is charged and attacked;During described charge and attack, sword
The a small amount of alloy added on sword by following degree chemical composition:Obsidian 10 ~ 20%, In 0.10 ~ 0.25%, nanometer
Diamond 0.6-0.9%, remaining is no more than 0.1% impurity for the Fe of surplus and total composition.
2. good fortune sword manufacture craft in dragon's fountain day according to claim 1, it is characterised in that:
The step 4)In normalizing temperature be 720 DEG C ~ 736 DEG C;
The step 5)In annealing temperature be 723 DEG C ~ 731 DEG C.
3. good fortune sword manufacture craft in dragon's fountain day according to claim 1, it is characterised in that:The step 9)In tempering it is specific
Operate and be:Thick clay rib will be covered with whole sword, in the case where temperature is 649 DEG C ~ 727 DEG C, be tempered, keep tempering temperature
Degree a period of time quenching-annealing again, is repeated 3 ~ 6 times.