CN106045673A - Flower arrangement mud special for cherry flower and production process thereof - Google Patents
Flower arrangement mud special for cherry flower and production process thereof Download PDFInfo
- Publication number
- CN106045673A CN106045673A CN201610369160.2A CN201610369160A CN106045673A CN 106045673 A CN106045673 A CN 106045673A CN 201610369160 A CN201610369160 A CN 201610369160A CN 106045673 A CN106045673 A CN 106045673A
- Authority
- CN
- China
- Prior art keywords
- mud
- parts
- special
- inserting flowers
- oriental cherry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses flower arrangement mud special for cherry flower and a production process thereof. The flower arrangement mud comprises the following components according to parts by weight: 50-80 parts of phenolic plastic, 40-60 parts of clay powder, 15-30 parts of urea, 10-20 parts of ammonium dihydrogen phosphate, 15-25 parts of EVA (ethylene vinyl acetate), 10-15 parts of a water absorber, 10-20 parts of a degrading agent, 1-3 parts of silicone oil and deionized water. The invention has the advantages that elasticity of the flower arrangement mud is optimized through synergy of the components so that the reusable times of the flower arrangement mud can be greatly increased, up to higher than 10; in addition, in the production process of the flower arrangement mud, annealing treatment also plays a key role for the life of the flower arrangement mud; moreover, the flower arrangement mud has good degrading capacity, meets the concept of sustainable development, and has a promising market application prospect.
Description
Technical field
The present invention relates to a kind of mud for inserting flowers and production technology thereof, be specifically related to the special mud for inserting flowers of a kind of oriental cherry and production thereof
Technique.
Background technology
Flower just loses nutrient source after cutting from parent, and in order to keep, flower pattern is bright-coloured, moisturizing is fresh-keeping, need by
Flower cuttage is in mud for inserting flowers.A kind of flower arrangement supplies that the foaming of mud for inserting flowers bakelite is made, for fixing and support flower
Material, various shapes, there are rectangle, square, cylinder, a cone etc., light weight such as foam plastics under normal condition, after water suction again
Weight such as lead, inserts and all be unable to do without it when making the gaily decorated basket and use wide mouth shallow body floral organ.
But, the mud for inserting flowers on market, after using 1-2 time, arises that cuttage hole problem too many, breakable, leads
Cause mud for inserting flowers cannot reuse, and the discarded more difficult natural decomposition of mud for inserting flowers, big for environment pollution, do not meet sustainable development
Environmental protection concept.
Summary of the invention
For solving the deficiencies in the prior art, it is an object of the invention to provide a kind of reusable and there is preferably fall
The mud for inserting flowers of solution ability, also discloses its production technology simultaneously.
In order to realize above-mentioned target, the present invention adopts the following technical scheme that:
The mud for inserting flowers that a kind of oriental cherry is special, including each component of following weight portion: bakelite 50-80 part, clay powder 40-
60 parts, carbamide 15-30 part, potassium dihydrogen phosphate 10-20 part, EVA15-25 part, water absorbing agent 10-15 part, degradation agent 10-20 part, silicon
Oil 1-3 part and deionized water.
Preferably, aforementioned bakelite process through high temperature foaming.
It is highly preferred that blowing temperature is 60-80 DEG C.
More preferably, aforementioned clay powder is attapulgite clay powder.
Preferably, aforementioned water-absorbent agent is cross-linked carboxymethyl cellulose.
It is further preferred that aforementioned degradation agent is gelatinous biodegradation agent.
It is further preferred that aforementioned degradation agent is mixed with benzophenone by starch.
Additionally, the invention also discloses the production technology of the special mud for inserting flowers of foregoing a kind of oriental cherry, including as follows
Step:
S1, by bakelite 50-80 part, clay powder 40-60 part, carbamide 15-30 part, potassium dihydrogen phosphate 10-20 part, EVA
15-25 part, water absorbing agent 10-15 part, degradation agent 10-20 part and silicone oil 1-3 part put into blender and are stirred, and then use deionization
Water regulation denseness, continues stirring 1-3 hour;
Compound is squeezed into lamellar by S2, extruder, naturally dries;
S3, by the mud for inserting flowers naturally dried feeding annealing furnace carry out melting down process.
Preferably, in abovementioned steps S3, annealing temperature is 60-80 DEG C.
It is highly preferred that in abovementioned steps S3, the annealing time is 24-48h.
The invention have benefit that: the mud for inserting flowers of the present invention, by the synergism between each component, optimize flower arrangement
The rebound performance of mud material, so that the reusable number of times of mud for inserting flowers is greatly increased, up to more than 10 times;It addition, inserting
In the production process of flower mud, annealing also life-span to mud for inserting flowers serves vital effect;And, the present invention inserts
Flower mud has good degradation capability, meets the theory of sustainable development, and product has good market application foreground.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention made concrete introduction.
Embodiment 1
The mud for inserting flowers that the oriental cherry of the present invention is special, including each component of following weight portion: 50 parts of bakelite, clay powder 40
Part, 15 parts of carbamide, potassium dihydrogen phosphate 10 parts, EVA 15 parts, water absorbing agent 10 parts, degradation agent 10 parts, silicone oil 1 part and deionized water.
Wherein, bakelite process through 60-80 DEG C of high temperature foaming;Clay powder is attapulgite clay powder;Water absorbing agent is for handing over
Connection carboxymethyl cellulose;Degradation agent is gelatinous biodegradation agent, starch mix with benzophenone.
Production technology is as follows: by bakelite, clay powder, carbamide, potassium dihydrogen phosphate, EVA, water absorbing agent, degradation agent and silicon
Oil puts into blender by weight and is stirred, and then regulates denseness with deionized water, continues stirring 1-3 hour;Extruder will
Compound is squeezed into lamellar, naturally dries;Naturally the mud for inserting flowers dried feeding annealing furnace is carried out melting down process, annealing temperature
Degree is 60 DEG C, and the annealing time is 48h.
Embodiment 2
The difference of the present embodiment and embodiment 1 is weight portion and the annealing condition of each component, specific as follows:
The mud for inserting flowers that the oriental cherry of the present invention is special, including each component of following weight portion: 60 parts of bakelite, clay powder 50
Part, 20 parts of carbamide, potassium dihydrogen phosphate 15 parts, EVA 20 parts, water absorbing agent 12 parts, degradation agent 15 parts, silicone oil 2 parts and deionized water.
Production technology is as follows: by bakelite, clay powder, carbamide, potassium dihydrogen phosphate, EVA, water absorbing agent, degradation agent and silicon
Oil puts into blender by weight and is stirred, and then regulates denseness with deionized water, continues stirring 1-3 hour;Extruder will
Compound is squeezed into lamellar, naturally dries;Naturally the mud for inserting flowers dried feeding annealing furnace is carried out melting down process, annealing temperature
Degree is 70 DEG C, and the annealing time is 36h.
Embodiment 3
The difference of the present embodiment and embodiment 1 is weight portion and the annealing condition of each component, specific as follows:
The mud for inserting flowers that the oriental cherry of the present invention is special, including each component of following weight portion: 80 parts of bakelite, clay powder 60
Part, 30 parts of carbamide, potassium dihydrogen phosphate 20 parts, EVA25 part, water absorbing agent 15 parts, degradation agent 20 parts, silicone oil 3 parts and deionized water.
Production technology is as follows: by bakelite, clay powder, carbamide, potassium dihydrogen phosphate, EVA, water absorbing agent, degradation agent and silicon
Oil puts into blender by weight and is stirred, and then regulates denseness with deionized water, continues stirring 1-3 hour;Extruder will
Compound is squeezed into lamellar, naturally dries;Naturally the mud for inserting flowers dried feeding annealing furnace is carried out melting down process, annealing temperature
Degree is 80 DEG C, and the annealing time is 24h.
Comparative example 1
This comparative example is with the difference of embodiment 2: not silicate-containing oil in component.
The mud for inserting flowers that the oriental cherry of the present invention is special, including each component of following weight portion: 60 parts of bakelite, clay powder 50
Part, 20 parts of carbamide, potassium dihydrogen phosphate 15 parts, EVA 20 parts, water absorbing agent 12 parts, degradation agent 15 parts and deionized water.
Production technology is as follows: by bakelite, clay powder, carbamide, potassium dihydrogen phosphate, EVA, water absorbing agent and degradation agent by weight
Amount part puts into blender and is stirred, and then regulates denseness with deionized water, continues stirring 1-3 hour;Extruder is by compound
It is squeezed into lamellar, naturally dries;Carrying out melting down process by the mud for inserting flowers naturally dried feeding annealing furnace, annealing temperature is 70
DEG C, the annealing time is 36h.
Comparative example 2
This comparative example is with the difference of embodiment 2: without EVA and silicone oil in component.
The mud for inserting flowers that the oriental cherry of the present invention is special, including each component of following weight portion: 60 parts of bakelite, clay powder 50
Part, 20 parts of carbamide, potassium dihydrogen phosphate 15 parts, water absorbing agent 12 parts, degradation agent 15 parts and deionized water.
Production technology is as follows: by bakelite, clay powder, carbamide, potassium dihydrogen phosphate, water absorbing agent and degradation agent by weight
Input blender is stirred, and then regulates denseness with deionized water, continues stirring 1-3 hour;Compound is extruded by extruder
Slabbing, dries naturally;Carrying out melting down process by the mud for inserting flowers naturally dried feeding annealing furnace, annealing temperature is 70 DEG C,
The annealing time is 36h.
Comparative example 3
This comparative example is with the difference of embodiment 2: is provided without annealing in production technology and melts down process.
The mud for inserting flowers that the oriental cherry of the present invention is special, including each component of following weight portion: 60 parts of bakelite, clay powder 50
Part, 20 parts of carbamide, potassium dihydrogen phosphate 15 parts, EVA 20 parts, water absorbing agent 12 parts, degradation agent 15 parts, silicone oil 2 parts and deionized water.
Production technology is as follows: by bakelite, clay powder, carbamide, potassium dihydrogen phosphate, EVA, water absorbing agent, degradation agent and silicon
Oil puts into blender by weight and is stirred, and then regulates denseness with deionized water, continues stirring 1-3 hour;Extruder will
Compound is squeezed into lamellar, naturally dries.
Performance detects
Embodiment 1-3 and the service life of comparative example 1-3 and degradation capability carry out detection contrast, and result is as follows:
Sequence number | Reusable number of times | Degradation property |
Embodiment 1 | > 10 times | Excellent |
Embodiment 2 | > 10 times | Excellent |
Embodiment 3 | > 10 times | Excellent |
Comparative example 1 | 7-9 time | Excellent |
Comparative example 2 | 2-3 time | Excellent |
Comparative example 3 | 5-8 time | Excellent |
Table 1 embodiment 1-3 and comparative example 1-3 performance comparison
Therefore, in the present invention, the rebound performance of mud for inserting flowers material can be optimized by adding EVA component, so that
The reusable number of times of mud for inserting flowers is greatly increased, and silicone oil can occur synergism with EVA, makes the repeatable of mud for inserting flowers make
It is up to more than 10 times with number of times;It addition, in the production process of mud for inserting flowers, annealing also life-span to mud for inserting flowers serve to
Close important effect.
The ultimate principle of the present invention, principal character and advantage have more than been shown and described.The technical staff of the industry should
Understanding, above-described embodiment limits the present invention the most in any form, and the mode of all employing equivalents or equivalent transformation is obtained
Technical scheme, all falls within protection scope of the present invention.
Claims (10)
1. the mud for inserting flowers that an oriental cherry is special, it is characterised in that include each component of following weight portion: bakelite 50-80 part,
Clay powder 40-60 part, carbamide 15-30 part, potassium dihydrogen phosphate 10-20 part, EVA 15-25 part, water absorbing agent 10-15 part, degradation agent
10-20 part, silicone oil 1-3 part and deionized water.
The mud for inserting flowers that a kind of oriental cherry the most according to claim 1 is special, it is characterised in that described bakelite are through high temperature
Foaming processes.
The mud for inserting flowers that a kind of oriental cherry the most according to claim 2 is special, it is characterised in that blowing temperature is 60-80 DEG C.
The mud for inserting flowers that a kind of oriental cherry the most according to claim 1 is special, it is characterised in that described clay powder is that attapulgite glues
Soil powder.
The mud for inserting flowers that a kind of oriental cherry the most according to claim 1 is special, it is characterised in that described water absorbing agent is crosslinking carboxylic first
Base cellulose.
The mud for inserting flowers that a kind of oriental cherry the most according to claim 1 is special, it is characterised in that described degradation agent is gelatinous
Biodegradation agent.
The mud for inserting flowers that a kind of oriental cherry the most according to claim 6 is special, it is characterised in that described degradation agent is by starch and benzene
Ketone mixes.
8. the production technology of the mud for inserting flowers that a kind of oriental cherry as described in any one of claim 1-7 is special, it is characterised in that include
Following steps:
S1, by bakelite 50-80 part, clay powder 40-60 part, carbamide 15-30 part, potassium dihydrogen phosphate 10-20 part, EVA 15-
25 parts, water absorbing agent 10-15 part, degradation agent 10-20 part and silicone oil 1-3 part put into blender and are stirred, and then use deionized water
Regulation denseness, continues stirring 1-3 hour;
Compound is squeezed into lamellar by S2, extruder, naturally dries;
S3, by the mud for inserting flowers naturally dried feeding annealing furnace carry out melting down process.
The production technology of the mud for inserting flowers that a kind of oriental cherry the most according to claim 8 is special, it is characterised in that described step S3
In, annealing temperature is 60-80 DEG C.
The production technology of the mud for inserting flowers that a kind of oriental cherry the most according to claim 9 is special, it is characterised in that described step
In S3, the annealing time is 24-48h.