CN106012145A - Glove yarn and manufacturing method and application thereof - Google Patents
Glove yarn and manufacturing method and application thereof Download PDFInfo
- Publication number
- CN106012145A CN106012145A CN201610374674.7A CN201610374674A CN106012145A CN 106012145 A CN106012145 A CN 106012145A CN 201610374674 A CN201610374674 A CN 201610374674A CN 106012145 A CN106012145 A CN 106012145A
- Authority
- CN
- China
- Prior art keywords
- yarn
- crude oil
- glove
- carbon fiber
- cashmere
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a glove yarn which contains, by weight, 65-75% of cashmere, 24-32% of bamboo carbon fiber and 1-3% of chinlon. The invention further discloses a manufacturing method and application of the yarn. A glove woven by the yarn has both heat retention property and breathability, is antibacterial and capable of removing odor, and has no foreign taste.
Description
Technical field
The present invention relates to field of textiles, in particular to a kind of glove yarn and preparation method thereof and purposes.
Background technology
Glove are conventional articles for use in people's daily life, have protection, the function such as warming.Glove can be by cotton thread, hair
Line, cashmere line etc. are made into, although cashmere glove good warmth retention effect, but poor air permeability, and hands can not be arranged after perspiring in time
Going out, make to become damp inside glove, of long duration also have abnormal flavour.Seldom have at present the yarn having warmth retention property and breathability concurrently for
Make glove.
Bamboo carbon fiber is that to take Phyllostachys pubescens Mazei ex H.de Lebaie be raw material, have employed pure oxygen high temperature and nitrogen intercepts the calcine technology of time delay so that bamboo charcoal
The micropore innately having more refines and honeycomb, cuts into slices molten with the polyester modification with honeycomb microporous structure trend the most again
Melt spinning and make.It is thin, soft that bamboo carbon fiber has unit G fineness;Whiteness is good, color is beautiful;Toughness and resistance to
Mill property is strong, has the resilience of uniqueness;Having stronger vertical and horizontal intensity, and stable uniform, drapability is good;Soft sliding
Feel well and do not prick body, softer than cotton, there is distinctive velvet sense.Bamboo carbon fiber cross section has been covered with the hole of big and small ellipse
Gap, can be with transient absorption and evaporate substantial amounts of moisture.The hygroscopicity of bamboo carbon fiber, wet putting, breathability occupy each big weaving
First of fiber.Bamboo carbon fiber textile uses summer and autumn, makes people feel the most nice and cool, ventilative;Winter-spring season uses fluffy
Comfortable can get rid of again internal unnecessary steam and moisture content, not get angry, do not send out dry.Bamboo carbon fiber can bacteriostasis antibiosis, antibacterial
Rate 94.5%, same amount of antibacterial examines under a microscope, and antibacterial can multiply in cotton, wood fiber goods in a large number, and
Antibacterial then reduced 94.5% on bamboo charcoal bamboo fibre fabric after 24 hours.Bamboo carbon fiber is the green refining out from former bamboo
Environment-friendly materials, it has the natural anti-demodicid mite of bamboo, deodorant, insect protected and generation anion characteristic.Prove after testing, bamboo charcoal
Fabric is almost nil to the ultraviolet ray transmissivity of 200-400nm, and the ultraviolet of this wavelength is to the injury of human body
Greatly, thus bamboo carbon fiber have protection human body not by the effect of uv damage.Though bamboo carbon fiber has above-mentioned advantage, but
There is presently no and be well used in gloving.
Summary of the invention
It is an object of the invention to provide a kind of glove yarn, the glove prevented with this yarn have warmth retention property and breathability concurrently, anti-
Bacterium deodorization, does not has abnormal flavour.
To achieve these goals, the present invention adopts the following technical scheme that:
A kind of glove yarn, it is characterised in that contain cashmere 65~75%, bamboo carbon fiber 24~32 in this yarn by weight percentage
%, chinlon 1~3%.
Preferably, this yarn contains cashmere 70%, bamboo carbon fiber 28%, chinlon 2% by weight percentage.
Above-mentioned glove yarn can make by the following method:
A cashmere, bamboo carbon fiber, chinlon are weighed by () by described weight proportion, be then stirred being mixed to get mixture
Material;
B mixed material is added fans entrance by () successively, through blower fan blowout in proportioning room space, and treat that it lands shape
Become the material bed of 1~2 cm thicks;
C () carries out moistening to material bed upper sprinkling and crude oil, then place and within 2 hours, obtain moistening material for the first time, used
With 30~50% that the amount of crude oil is material bed gross weight;
D (), again to material bed sprinkling and crude oil and place 2 hours to obtain second time moistening material, used and crude oil amount is step
Suddenly (c) neutralizes the 50~60% of crude oil amount;
E (), with second time moistening material for raw material spun yarn, fineness of yarn is 16~18.
Preferably, and crude oil uses Guangzhou Tao Shi Chemical Co., Ltd. AL-106 type and crude oil.
Present invention also offers the application in making glove of the above-mentioned yarn.
The invention has the beneficial effects as follows, bamboo carbon fiber has stronger adsorption-decomposition function ability, can resist with hygroscopic desiccation, smelly eliminating
Bacterium, also has the performances such as anion penetrates, and cashmere, bamboo carbon fiber, chinlon is mixed with special ratios, it is possible to make to be spun into
Yarn have breathability, warmth retention property and use intensity and toughness concurrently, make wearing comfort after glove, perspire and do not become damp, do not have
There is abnormal flavour.The manufacture method of the present invention, it is possible to effectively by three kinds of raw material mixing, so that yarn property is excellent.
Detailed description of the invention
Below by specific embodiment, the present invention is described in detail.
Embodiment 1
Cashmere 65%, bamboo carbon fiber 32%, chinlon 3%.
Embodiment 2
Cashmere 75%, bamboo carbon fiber 24%, chinlon 1%.
Embodiment 3
Cashmere 70%, bamboo carbon fiber 28%, chinlon 2%.
The manufacture method of embodiment 4 glove yarn, comprises the steps:
A cashmere, bamboo carbon fiber, chinlon are weighed by () by described weight proportion, be then stirred being mixed to get mixture
Material;
B mixed material is added fans entrance by () successively, through blower fan blowout in proportioning room space, and treat that it lands shape
Become the material bed of 1~2 cm thicks;
C () carries out moistening to material bed upper sprinkling and crude oil, then place and within 2 hours, obtain moistening material for the first time, used
With 30~50% that the amount of crude oil is material bed gross weight, and crude oil uses Guangzhou Tao Shi Chemical Co., Ltd. AL-106 type and hair
Oil;
D (), again to material bed sprinkling and crude oil and place 2 hours to obtain second time moistening material, used and crude oil amount is step
Suddenly (c) neutralizes the 50~60% of crude oil amount, and crude oil uses Guangzhou Tao Shi Chemical Co., Ltd. AL-106 type and crude oil;
E (), with second time moistening material for raw material spun yarn, fineness of yarn is 16~18.
Embodiment 5
Making glove with the yarn of embodiment 3, compared with cashmere glove, warmth retention property is good, and outside permeable gas is good, more resistance to
Mill breakage-proof.
Claims (5)
1. a glove yarn, it is characterised in that contain cashmere 65~75%, bamboo carbon fiber 24 in this yarn by weight percentage
~32%, chinlon 1~3%.
2. glove yarn as claimed in claim 1, it is characterised in that contain cashmere 70% in this yarn by weight percentage,
Bamboo carbon fiber 28%, chinlon 2%.
3. the manufacture method of glove yarn as claimed in claim 1 or 2, it is characterised in that comprise the steps:
A cashmere, bamboo carbon fiber, chinlon are weighed by () by described weight proportion, be then stirred being mixed to get mixture
Material;
B mixed material is added fans entrance by () successively, through blower fan blowout in proportioning room space, and treat that it lands shape
Become the material bed of 1~2 cm thicks;
C () carries out moistening to material bed upper sprinkling and crude oil, then place and within 2 hours, obtain moistening material for the first time, used
With 30~50% that the amount of crude oil is material bed gross weight;
D (), again to material bed sprinkling and crude oil and place 2 hours to obtain second time moistening material, used and crude oil amount is step
Suddenly (c) neutralizes the 50~60% of crude oil amount;
E (), with second time moistening material for raw material spun yarn, fineness of yarn is 16~18.
4. the manufacture method of glove yarn as claimed in claim 3, it is characterised in that described and crude oil uses Guangzhou pottery
Family name Chemical Co., Ltd. AL-106 type and crude oil.
5. the yarn as claimed in claim 1 or 2 application in making glove.