CN106010270A - 热熔胶棒用松香季戊四醇酯的制备方法 - Google Patents

热熔胶棒用松香季戊四醇酯的制备方法 Download PDF

Info

Publication number
CN106010270A
CN106010270A CN201610358233.8A CN201610358233A CN106010270A CN 106010270 A CN106010270 A CN 106010270A CN 201610358233 A CN201610358233 A CN 201610358233A CN 106010270 A CN106010270 A CN 106010270A
Authority
CN
China
Prior art keywords
hot melt
pentalyn
catalyst
colophonium
rubber stick
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610358233.8A
Other languages
English (en)
Inventor
黄桂彬
蒋茵荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangxi Zhongchang Resin Co Ltd
Original Assignee
Guangxi Zhongchang Resin Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangxi Zhongchang Resin Co Ltd filed Critical Guangxi Zhongchang Resin Co Ltd
Priority to CN201610358233.8A priority Critical patent/CN106010270A/zh
Publication of CN106010270A publication Critical patent/CN106010270A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种热熔胶棒用松香季戊四醇酯的制备方法，涉及化工树脂技术领域。本发明热熔胶棒用松香季戊四醇酯的制备方法为：将松香、季戊四醇和硬脂酸加入反应釜中；抽真空减压蒸馏，加热，搅拌均匀；加入催化剂，调节反应釜内温度为160℃～180℃，酯化反应至溶液的色度小于或者等于5.5个加纳色号时，停止反应；过滤，除去催化剂。本发明在松香季戊四醇酯的制备过程中添加了硬脂酸，使得所得产品颜色浅、稳定性较好，初粘性以及抗氧化性能得到明显提高。

Description

热熔胶棒用松香季戊四醇酯的制备方法
技术领域
本发明涉及化工树脂技术领域，尤其是一种热熔胶棒用松香季戊四醇酯的制备方法。
背景技术
热熔胶棒是以乙烯-醋酸乙烯共聚物为主要材料，加入增粘剂与其它成分配合而成的固体型粘合剂，热熔胶棒具有快速粘合、强度高、耐老化、无毒害、热稳定性好等特点、可用于木材、塑料、纤维、织物、金属、家具、灯罩、皮革、工艺品、玩具电子、电器元器件、纸制品、陶瓷、珍珠棉包装等互粘固体。
松香季戊四醇酯是由松香经改性后与季戊四醇酯化合成，通过真空处理后制成不规则透明片状固体，主要用于热熔压敏胶、热熔涂料、酚醛清漆、结构胶、密封胶、复膜胶、油墨等。松香季戊四醇酯应用于热熔胶棒时需要具备良好的储存稳定性、抗热氧化性以及较浅的色泽。
目前松香季戊四醇酯制备方法一般将熔融后的松香加入季戊四醇、催化剂等进行酯化反应，然而这些方法所制备的松香季戊四醇酯的初粘性以及抗热氧化性均待提高。
发明内容
本发明的目的是提供一种热熔胶棒用松香季戊四醇酯的制备方法，这种方法可以解决现有的热熔胶棒用松香季戊四醇酯初粘性以及抗热氧化性能差的问题。
为了解决上述问题，本发明采用的技术方案是：
这种热熔胶棒用松香季戊四醇酯的制备方法包括以下步骤：
A、将松香、季戊四醇和硬脂酸依次加入反应釜中；
B、抽真空减压蒸馏，加热，搅拌均匀；
C、加入催化剂，调节反应釜内温度为160℃～180℃，酯化反应至溶液的色度小于或者等于5.5个加纳色号时，停止反应；
D、过滤，除去催化剂，即得到热熔胶棒用松香季戊四醇酯。
上述技术方案中，更具体的技术方案还可以是：松香、季戊四醇和硬脂酸的质量之比为1：0.3～0.5：0.01～0.02。
进一步的，催化剂为氧化锆，催化剂占松香总重量的0.1％～0.2％。
由于采用了上述技术方案，本发明与现有技术相比具有如下有益效果：
本发明在松香季戊四醇酯的制备过程中添加了硬脂酸，使得所得产品颜色浅、稳定性较好，初粘性以及抗氧化性能得到明显提高。
具体实施方式
下面结合实施例对本发明作进一步详述：
实施例1
本实施例热熔胶棒用松香季戊四醇酯的制备方法为：将松香、季戊四醇和硬脂酸依次加入反应釜中，抽真空减压蒸馏，加热，搅拌均匀；加入氧化锆，调节反应釜内温度为160℃，待酯化反应至溶液的色度为5.5个加纳色号时，停止反应；过滤，除去氧化锆，即得到热熔胶棒用松香季戊四醇酯。
本实施例中松香、季戊四醇和硬脂酸的质量之比为1：0.5：0.01；氧化锆占松香总重量的0.15％。
实施例2
本实施例热熔胶棒用松香季戊四醇酯的制备方法为：将松香、季戊四醇和硬脂酸依次加入反应釜中，抽真空减压蒸馏，加热，搅拌均匀；加入氧化锆，调节反应釜内温度为170℃，待酯化反应至溶液的色度为5个加纳色号时，停止反应；过滤，除去氧化锆，即得到热熔胶棒用松香季戊四醇酯。
本实施例中松香、季戊四醇和硬脂酸的质量之比为1：0.3：0.02；氧化锆占松香总重量的0.1％。
实施例3
本实施例热熔胶棒用松香季戊四醇酯的制备方法为：将松香、季戊四醇和硬脂酸依次加入反应釜中，抽真空减压蒸馏，加热，搅拌均匀；加入氧化锆，调节反应釜内温度为180℃，待酯化反应至溶液的色度为5个加纳色号时，停止反应；过滤，除去氧化锆，即得到热熔胶棒用松香季戊四醇酯。
本实施例中松香、季戊四醇和硬脂酸的质量之比为1：0.4：0.015；氧化锆占松香总重量的0.2％。

Claims (4)

1.一种热熔胶棒用松香季戊四醇酯的制备方法，其特征在于包括以下步骤：
A、将松香、季戊四醇和硬脂酸依次加入反应釜中；
B、抽真空减压蒸馏，加热，搅拌均匀；
C、加入催化剂，调节反应釜内温度为160℃～180℃，酯化反应至溶液的色度小于或者等于5.5个加纳色号时，停止反应；
D、过滤，除去催化剂，即得到热熔胶棒用松香季戊四醇酯。
2.根据权利要求1所述的热熔胶棒用松香季戊四醇酯的制备方法，其特征在于松香、季戊四醇和硬脂酸的质量之比为1：0.3～0.5：0.01～0.02。
3.根据权利要求1或者2所述的热熔胶棒用松香季戊四醇酯的制备方法，其特征在于：所述催化剂为氧化锆，催化剂占松香总重量的0.1％～0.2％。
4.根据权利要求3所述的热熔胶棒用松香季戊四醇酯的制备方法，其特征在于：所述催化剂为氧化锆，催化剂占松香总重量的0.1％～0.2％。
CN201610358233.8A 2016-05-26 2016-05-26 热熔胶棒用松香季戊四醇酯的制备方法 Pending CN106010270A (zh)