CN106010218A - Waterproof floor and preparation method thereof - Google Patents
Waterproof floor and preparation method thereof Download PDFInfo
- Publication number
- CN106010218A CN106010218A CN201610456650.6A CN201610456650A CN106010218A CN 106010218 A CN106010218 A CN 106010218A CN 201610456650 A CN201610456650 A CN 201610456650A CN 106010218 A CN106010218 A CN 106010218A
- Authority
- CN
- China
- Prior art keywords
- parts
- coupling agent
- floor
- acrylic resin
- kieselguhr
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a waterproof floor and a preparation method thereof. The waterproof floor comprises raw materials in parts by weight as follows: 50-80 parts of waterborne polyaniline emulsion, 40-70 parts of acrylic resin, 25-45 parts of kieselguhr, 13-18 parts of wood fiber powder, 3-5 parts of sodium percarbonate, 2-4 parts of sodium polyacrylate, 4-6 parts of soybean meal, 10-15 parts of a titanate coupling agent, 4-6 parts of maleic anhydride, 2-4 parts of a camphor tree leaf extract, 15-20 parts of ricinoleic acid and 10-12 parts of a silane coupling agent KH550. The waterproof floor has good infiltration, combination performance and good thermal insulation effect, and is anti-aging and environment-friendly; phenomena such as wire skipping, cracking, burr occurrence and the like can be avoided, the floor quality is improved greatly, the main materials including the waterborne polyaniline emulsion and the acrylic resin are matched and cooperate with various auxiliaries and filler, so that the floor has very high water absorption, the stability and water resistance are improved greatly, and the service life of the floor is prolonged accordingly.
Description
Technical field
The present invention relates to a kind of Environmental protection floor material, be specifically related to a kind of water-proof floor and preparation method thereof.
Background technology
Floor is the wide variety of a kind of product of modern society, as the finishing in the rooms such as house, office, trade company, can beautify space, can keep again indoor clean hygiene, simple floor typically wood materials is made, rough surface, and easily the moisture absorption is rotted, service life is short, and therefore, plank coatings is used for solving the problems referred to above, it is possible not only to prevent plank from rotting, make smooth surface, it is also possible to increase the service life, beautify space；At present, there are some defects in traditional plank coatings, aliquation as inadequate in paint adhesion, easy, comes off, flame retardant effect difference etc..
Summary of the invention
It is an object of the invention to provide a kind of water-proof floor and preparation method thereof.
To achieve these goals, the present invention adopts the following technical scheme that
Water-proof floor, the weight portion of its constitutive material is, aqueous polyanion emulsion 50-80, acrylic resin 40-70, kieselguhr 25-45, wood fiber powder 13-18, SODIUM PERCARBONATE 3-5, sodium polyacrylate 2-4, analysis for soybean powder 4-6, titanate coupling agent 10-15, maleic anhydride 4-6, camphor leaf extract 2-4, castor oil acid 15-20, Silane coupling agent KH550 10-12.
Water-proof floor, the weight portion of its constitutive material is, aqueous polyanion emulsion 70, acrylic resin 50, kieselguhr 35, wood fiber powder 15, SODIUM PERCARBONATE 4, sodium polyacrylate 3, analysis for soybean powder 5, titanate coupling agent 12, maleic anhydride 5, camphor leaf extract 3, castor oil acid 18, Silane coupling agent KH550 11.
The manufacture method of water-proof floor, including herein below:
(1) weigh aqueous polyanion emulsion, acrylic resin by the weight portion of constitutive material, add mixer, be warming up to 80-90 DEG C, be sufficiently stirred for mixing, standby；
(2) weigh kieselguhr by weight, be placed in roasting kiln roasting 1-2 hour, control temperature 550-600 DEG C, cool down after roasting, and be placed in dehydrated alcohol grinding with wood fiber powder, analysis for soybean powder one, grind 20-25 hour, prepare slurry；
(3) step (2) slurry is added in the compound of above-mentioned steps (1), fully after mixing, it is added thereto to other residue constitutive materials such as SODIUM PERCARBONATE, sodium polyacrylate, titanate coupling agent, maleic anhydride, camphor leaf extract, castor oil acid, Silane coupling agent KH550 again, disperse 50-60 minute then at 800-1200r/min low speed, finally put in extruder, temperature be 180-195 DEG C, screw speed be 15-20rpm forming machine in extrude through mould, prepare ground board finished product after sizing.
Beneficial effects of the present invention:
The water-proof floor of the present invention has good infiltration and associativity, good heat insulating, aging resistance, environmental protection；It can be avoided that occur jumping the phenomenons such as silk, cracking, burr, substantially increase the quality on floor, its aqueous polyanion emulsion, acrylic resin major ingredient, arrange in pairs or groups multiple auxiliary agent and filler synergism, there is the strongest water absorption, stability and resistance to water are greatly improved, thus extend the service life on floor.
Detailed description of the invention
Embodiment: water-proof floor, the weight (kg) of its constitutive material is, aqueous polyanion emulsion 70, acrylic resin 50, kieselguhr 35, wood fiber powder 15, SODIUM PERCARBONATE 4, sodium polyacrylate 3, analysis for soybean powder 5, titanate coupling agent 12, maleic anhydride 5, camphor leaf extract 3, castor oil acid 18, Silane coupling agent KH550 11.
The manufacture method of water-proof floor, including herein below:
(1) weigh aqueous polyanion emulsion, acrylic resin by the weight portion of constitutive material, add mixer, be warming up to 80-90 DEG C, be sufficiently stirred for mixing, standby；
(2) weigh kieselguhr by weight, be placed in roasting kiln roasting 1.5 hours, control temperature 580 DEG C, cool down after roasting, and be placed in dehydrated alcohol grinding with wood fiber powder, analysis for soybean powder one, grind 20-25 hour, prepare slurry；
(3) step (2) slurry is added in the compound of above-mentioned steps (1), fully after mixing, it is added thereto to other residue constitutive materials such as SODIUM PERCARBONATE, sodium polyacrylate, titanate coupling agent, maleic anhydride, camphor leaf extract, castor oil acid, Silane coupling agent KH550 again, disperse 55 minutes then at 1000r/min low speed, finally put in extruder, temperature be 190 DEG C, screw speed be 15-20rpm forming machine in extrude through mould, prepare ground board finished product after sizing.
Claims (3)
1. a water-proof floor, it is characterized in that, the weight portion of its constitutive material is, aqueous polyanion emulsion 50-80, acrylic resin 40-70, kieselguhr 25-45, wood fiber powder 13-18, SODIUM PERCARBONATE 3-5, sodium polyacrylate 2-4, analysis for soybean powder 4-6, titanate coupling agent 10-15, maleic anhydride 4-6, camphor leaf extract 2-4, castor oil acid 15-20, Silane coupling agent KH550 10-12.
Water-proof floor the most according to claim 1, it is characterized in that, the weight portion of its constitutive material is, aqueous polyanion emulsion 70, acrylic resin 50, kieselguhr 35, wood fiber powder 15, SODIUM PERCARBONATE 4, sodium polyacrylate 3, analysis for soybean powder 5, titanate coupling agent 12, maleic anhydride 5, camphor leaf extract 3, castor oil acid 18, Silane coupling agent KH550 11.
3. the manufacture method of a water-proof floor as claimed in claim 1, it is characterised in that include herein below:
(1) weigh aqueous polyanion emulsion, acrylic resin by the weight portion of constitutive material, add mixer, be warming up to 80-90 DEG C, be sufficiently stirred for mixing, standby；
(2) weigh kieselguhr by weight, be placed in roasting kiln roasting 1-2 hour, control temperature 550-600 DEG C, cool down after roasting, and be placed in dehydrated alcohol grinding with wood fiber powder, analysis for soybean powder one, grind 20-25 hour, prepare slurry；
(3) step (2) slurry is added in the compound of above-mentioned steps (1), fully after mixing, it is added thereto to other residue constitutive materials such as SODIUM PERCARBONATE, sodium polyacrylate, titanate coupling agent, maleic anhydride, camphor leaf extract, castor oil acid, Silane coupling agent KH550 again, disperse 50-60 minute then at 800-1200r/min low speed, finally put in extruder, temperature be 180-195 DEG C, screw speed be 15-20rpm forming machine in extrude through mould, prepare ground board finished product after sizing.