CN106009888A - Waste paper deinking agent and application thereof in waste paper deinking - Google Patents
Waste paper deinking agent and application thereof in waste paper deinking Download PDFInfo
- Publication number
- CN106009888A CN106009888A CN201610639398.2A CN201610639398A CN106009888A CN 106009888 A CN106009888 A CN 106009888A CN 201610639398 A CN201610639398 A CN 201610639398A CN 106009888 A CN106009888 A CN 106009888A
- Authority
- CN
- China
- Prior art keywords
- parts
- waste paper
- deinking agent
- deinking
- paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a waste paper deinking agent, and belongs to the technical field of papermaking assistants. The waste paper deinking agent comprises, by weight, 1-10 parts of higher fatty alcohols, 1-10 parts of higher fatty acids, 1-20 parts of fatty alcohol polyoxyethylene ether, 1-20 parts of fatty alcohol polyoxyethylene ether sodium sulfate, 1-20 parts of fatty alcohol polyoxyethylene-polyoxypropylene ether, 1-20 parts of polyoxyethylene-polyoxypropylene ether random polyether, 0-5 parts of sodium silicate, 0-5 parts of sodium hydroxide, 0-5 parts of hydrogen peroxide, 0-5 parts of a chelating agent and 1-20 parts of water. The waste paper deinking agent has the advantages of low viscosity at -10DEG C or above, good fluidity, good deinking effect at a low temperature, small damages to fibers, improvement of the strength of finished pulp and the quality of finished paper, and low cost, and can be used in regeneration of office paper, cultural paper, art paper, white board paper and newsprint.
Description
Technical field
The present invention relates to paper making additive technical field, particularly relate to a kind of waste paper deinking agent.
Background technology
Owing to the eighties resource in last century constantly reduces, environment constantly deteriorates, and sight is turned to useless by people
Paper, if it is possible to utilize regenerated papermaking, will save substantial amounts of timber, water, electricity equal energy source, greatly reduce
Sewage discharge, reduces environmental.Develop through decades, utilize regenerated papermaking to have become as huge
Big industry.Waste paper deinking agent is a kind of to have making of the multiple effects such as infiltration, washing, emulsifying, dispersion
Paper specialty chemicals, are mainly used in the enterprise utilizing waste paper to produce paper pulp or papermaking.China is a money
The country that source is the poorest, therefore country actively promotes regenerated papermaking technology, but due to shortage property
Can excellent papermaking specialty chemicals, many imported units can not give play to due effect, and this becomes system
The about bottleneck problem of regenerated papermaking.
Along with increasing rapidly of waste paper recycling amount, deinking technology faces following problem: due to current print
Updating of brush technology, the composition of ink is also continually changing, along with new printing technology and various difference
The appearance of composition ink, makes the color of print product, glossiness and firm performance all increase, oil supply
The removing of ink adds difficulty, and in printing process, the special handling such as overlay film, finish coatings adds aborning
Sicker and pitch trouble, Zhan Huaiyu discloses work in prior art in " slurrying principle and engineering "
Industry soaps deinking agent needs to dissolve and need isothermal holding can realize weight under the high temperature more than 90 DEG C
The regeneration of applying glue waste paper, pornographic books and magazines brave (" state analysis of sicker under the conditions of different pulpings ", pornographic books and magazines are brave,
China paper industry, 2015,36 (2): 61-63) also disclose that carry out under the high temperature of 80 DEG C pulping process can be real
The removing of sicker in existing waste paper, carries out pulping and processes and return to waste paper waste paper under the high temperature more than 80 DEG C
With causing puzzlement.
The developing direction of novel wastepaper deinking agent requires still have in the case of low temperature, gentleness are discongested well
Deinking efficiency, it is also proposed new challenge to the quality of deinking agent.
Summary of the invention
In view of this, it is an object of the invention to provide the waste paper deinking agent that under a kind of low temperature, deinking efficiency is good,
Regeneration for paper kinds such as chancery paper, Cultural Paper, art paper, white board, newsprints.
In order to realize foregoing invention purpose, the present invention provides techniques below scheme:
The invention provides a kind of waste paper deinking agent, including the component of following weight portion:
High fatty alcohol 1~10 parts, higher fatty acids 1~10 parts, fatty alcohol-polyoxyethylene ether 1~20 parts,
Polyoxyethylenated alcohol sodium sulfate 1~20 parts, aliphatic alcohol polyethenoxy-polyethenoxy ether 1~20 parts, poly-
Oxygen ethylene-polyoxypropylene atactic polyether 1~20 parts, sodium silicate 0~5 parts, sodium hydroxide 0~5 parts, peroxide
Change hydrogen 0~5 parts, chelating agen 0~5 parts and water 1~20 parts.
Preferably, one or more during described high fatty alcohol is tetradecyl alchohol, hexadecanol and octadecanol
Mixture.
Preferably, including the high fatty alcohol of 4~8 parts.
Preferably, described higher fatty acids be stearic acid, oleic acid, palm fibre put the one in acid, linoleic acid or
Several mixture.
Preferably, including the higher fatty acids of 4~8 parts.
Preferably, described chelating agen is ethylenediaminetetraacetic acid or diethylene-triamine pentaacetic acid.
The invention provides the application in deinking of the waste paper deinking agent described in technique scheme, described
Deinking process particularly as follows:
(1) carry out pulping process after being mixed with described waste paper deinking agent by waste paper pulp and obtain pulping mixing
Thing;
(2) the described pulping mixture that step (1) obtains is carried out FLOTATION SEPARATION.
Preferably, in described step (1) consumption is waste paper pulp quality the 0.05~3.0% of waste paper deinking agent.
Preferably, the temperature that in described step (1), pulping processes is 40~50 DEG C.
Preferably, the time that in described step (1), pulping processes is 10~20min.
The invention provides a kind of waste paper deinking agent, have the beneficial effect that:
1, the present invention is with high fatty alcohol potentiation, reduces chemicals usage in waste paper deinking agent, saves
Cost, significantly reduces the COD value of sewage, beneficially environmental conservation, decreases environmental protection treatment expense;
2, the waste paper deinking agent that the present invention provides is relatively low-10 DEG C of viscosity above, has good mobility,
It is easy to dosing pump and adds use continuously, meet the production requirement of continuous deinking, improve production efficiency,
Expand production capacity;
3, the waste paper deinking agent low temperature using effect that the present invention provides is good, and pulping temperature is from about 80-100 DEG C
Dropping to about 40-60 DEG C, pulping time was shortened to less than 20 minutes by 40 minutes, was reducing energy resource consumption
Meanwhile, decrease fibre damage, improve pulping intensity and become paper product matter, being applied to give up by waste paper deinking agent
Paper deinking obtains recycled writing paper, and the whiteness of recycled writing paper is 83%, and paper pulp yield is up to 90%, decreases primary
The dependence of slurry, reduces the papermaking industry destruction to ecological environment, promotes the sustainable development of industry, uses
When waste paper regenerated, remove the printing-ink of absorption on fiber, improve fiber cleaning degree, and the present invention carries
The waste paper deinking agent of confession can prevent while thoroughly removing ink ink redeposition to fiber, flotation
Time ink can be adsorbed in smoothly on bubble and pulp separation, reduce further ink particle content in pulping, will
Waste paper deinking agent is applied to deinking and obtains recycled writing paper, and the whiteness of recycled writing paper is up to 83%, improves pulping white
Degree;
4, the technique taking to relax in deinking process, to reduce fiber destruction, improves pulping intensity and obtains
Rate.
Detailed description of the invention
The invention provides a kind of waste paper deinking agent, including the component of following weight portion:
High fatty alcohol 1~10 parts, higher fatty acids 1~10 parts, fatty alcohol-polyoxyethylene ether 1~20 parts,
Polyoxyethylenated alcohol sodium sulfate 1~20 parts, aliphatic alcohol polyethenoxy-polyethenoxy ether 1~20 parts, poly-
Oxygen ethylene-polyoxypropylene atactic polyether 1~20 parts, sodium silicate 0~5 parts, sodium hydroxide 0~5 parts, peroxide
Change hydrogen 0~5 parts, chelating agen 0~5 parts and water 1~20 parts.
Fatty alcohol-polyoxyethylene ether, polyoxyethylenated alcohol sodium sulfate, fatty alcohol polyoxy second in the present invention
Alkene-polyethenoxy ether, PULLRONIC F68 atactic polyether can resin in emulsified ink, chemicals
And dispersion pigment;High fatty alcohol, higher fatty acids play the effect improving deinking efficiency further, make
Resin, chemicals and pigment in ink remove further;Hydrogen peroxide is for bleached fiber and toning,
And the resin in oxidation, destruction ink, promote ink to dissociate, surfactant can be improved further
Performance, preferably separates ink;Sodium silicate can suppress the too quick decomposition of hydrogen peroxide, with heavy metal from
Son forms colloform texture, helps when deinking ink to carry out peptizaiton, stops the suction again of ink particle
Attached, discoloration can be played simultaneously, prevent paper pulp yellowing;The effect of sodium hydroxide is regulation slurry
PH value be alkalescence, saponification and/or hydrolysis ink resin, make fibre swelling, fibrous absorbent and become more
Softness, so that ink particle is attached to the weakened of fiber surface, it helps loosens coating and divides
Split ink, make ink particle become less by mechanism, but will become for the waste paper containing groundwood pulp
Yellow hair is black, so the amount of the sodium hydroxide added is properly better, excess can cause paper pulp to turn yellow or blackening;
The effect of chelating agen is and the complex of heavy metal ion formation solubility, thus stops heavy metal ion to be divided
Xie Bingke prevents adsorbing again of ink particle.The present invention has synergism between each component, accurately controls
The consumption making each component has reached the effect that under low temperature, deinking deinking efficiency is good, reduces pulping temperature
And pulping time, improve the whiteness of recycled writing paper, paper pulp yield simultaneously, can be used for chancery paper, Cultural Paper,
The regeneration of the paper kinds such as art paper, white board, newsprint.
The waste paper deinking agent that the present invention provides includes the high fatty alcohol of 1~10 weight portions, preferably 4~8 parts,
More preferably 5~6 parts.In the present invention, described high fatty alcohol is preferably tetradecyl alchohol, hexadecanol and ten
The alcohol mixture of one or more in eight alcohol;In the present invention, described alcohol mixture preferably includes 14
In alcohol, hexadecanol and octadecanol 2 kinds or 3 kinds, more preferably hexadecanol and octadecanol, tetradecyl alchohol and
Octadecanol.The mass ratio of high fatty alcohol each in alcohol mixture is not limited by the present invention, art technology
Personnel can select the alcohol mixture of the high fatty alcohol of any mass ratio according to actual needs.
The waste paper deinking agent that the present invention provides includes the higher fatty acids of 1~10 part, preferably 4~8 parts, more
It is preferably 5~6 parts.In the present invention, described higher fatty acids preferably stearic acid, oleic acid, palm fibre put acid
With the acid blend of one or more in linoleic acid, described acid blend preferably include stearic acid, oleic acid,
Palm fibre puts 2 kinds in acid and linoleic acid or 3 kinds, more preferably stearic acid and linoleic acid, stearic acid and palm fibre
Put that acid, oleic acid and palm fibre put acid, palm fibre puts acid and linoleic acid.In the present invention, to each senior in acid blend
The mass ratio of fatty acid does not limit, and those skilled in the art can select any mass ratio according to actual needs
The acid blend of higher fatty acids.
The waste paper deinking agent that the present invention provides preferably includes the fatty alcohol-polyoxyethylene ether of 5~15 parts, more preferably
It it is 8~12 parts.
The waste paper deinking agent that the present invention provides preferably includes the polyoxyethylenated alcohol sodium sulfate of 5~15 parts,
More preferably 8~12 parts.
The waste paper deinking agent that the present invention provides preferably includes the aliphatic alcohol polyethenoxy-polyoxypropylene of 8~15 parts
Ether, more preferably 10~12 parts.
The waste paper deinking agent that the present invention provides preferably includes the PULLRONIC F68 of 8~15 parts and randomly gathers
Ether, more preferably includes 10~12 parts.
The waste paper deinking agent that the present invention provides preferably includes the sodium silicate of 2~4 parts.
The waste paper deinking agent that the present invention provides preferably includes the sodium hydroxide of 2~4 parts.For hydrogen peroxide,
Being usually and use the form of hydrogen peroxide to add, in the present invention, the mass percent of hydrogen peroxide is 1~15%,
It is preferably 3~10%.
The waste paper deinking agent that the present invention provides preferably includes the chelating agen of 2~4 parts.In the present invention, described
Chelating agen is ethylenediaminetetraacetic acid or diethylene-triamine pentaacetic acid.
The waste paper deinking agent that the present invention provides preferably includes the water of 1~15 part, more preferably 8~12 parts.
The present invention does not has special restriction to the preparation method of described waste paper deinking agent, uses art technology
Technical scheme prepared by the compositions known to personnel.In the present invention, the system of described waste paper deinking agent
Preparation Method preferably includes following steps:
By each component mixing homogenizing described in technique scheme, obtain waste paper deinking agent.
In the present invention, the temperature of described homogenizing is preferably 50~60 DEG C, and the time of described homogenizing is preferably
30~50min.The present invention does not has special restriction to the equipment of described homogenizing, uses those skilled in the art
Known to homogenizer.
Present invention also offers the application in deinking of the waste paper deinking agent described in technique scheme, institute
State deinking process particularly as follows:
(1) carry out pulping process after being mixed with described waste paper deinking agent by waste paper pulp, obtain pulping mixing
Thing;
(2) the described pulping mixture that step (1) obtains is carried out FLOTATION SEPARATION.
The present invention does not has special restriction to the source of described waste paper pulp, uses those skilled in the art ripe
The paper pulp that the waste and old raw material in field of papermaking employing known obtains;Concrete, in the present invention, institute
State waste paper pulp be waste and old chancery paper, waste and old Cultural Paper, waste and old art paper, waste and old white board, waste and old newly
Hear the paper pulp that the mixture of one or more in the waste paper kinds such as paper obtains.
The present invention mixes, with described waste paper deinking agent, the mode used to described waste paper pulp does not has special limit
System, uses hybrid mode well known to those skilled in the art;In an embodiment of the present invention, preferably
Use mechanical agitation mode to mix, alr mode is not had particular/special requirement, known to those skilled in the art
Technological means be stirred.In the present invention, to waste paper pulp described in step (1) and described waste paper
The charging sequence of deinking agent does not has any restriction.
In the present invention, in described step (1), the Functionality, quality and appealing design of waste paper deinking agent elects waste paper pulp quality as
0.05~3.0%, more preferably 2.00~2.50%.
In the present invention, the temperature that in described step (1), pulping processes is preferably 40~50 DEG C, more preferably
It it is 44~46 DEG C.In the present invention, the time that in described step (1), pulping processes is preferably 10~20min,
More preferably 13~16min.
After obtaining pulping mixture, described pulping mixture is carried out FLOTATION SEPARATION by the present invention.The present invention couple
The mode of the employing of FLOTATION SEPARATION described in step (2) does not has special restriction, uses people in the art
FLOTATION SEPARATION mode known to Yuan, FLOTATION SEPARATION i.e. completes deinking and processes.
The invention provides a kind of waste paper deinking agent, with polyethers as host, with higher fatty acids, senior fat
Fat alcohol potentiation, reduces chemicals usage in waste paper deinking agent, has saved cost, significantly reduce sewage
COD value, beneficially environmental conservation, decrease environmental protection treatment expense;It is relatively low-10 DEG C of viscosity above,
There is good mobility, it is simple to dosing pump adds use continuously, meet the production requirement of continuous deinking,
Improve production efficiency, expand production capacity;The waste paper deinking agent low temperature using effect that the present invention provides is good,
Pulping temperature drops to about 40-60 DEG C from about 80-100 DEG C, and pulping time was shortened to 20 minutes by 40 minutes
Hereinafter, while reducing energy resource consumption, decrease fibre damage, improve pulping intensity and become paper product matter,
Waste paper deinking agent being applied to deinking and obtains recycled writing paper, the whiteness of recycled writing paper is 83%, and paper pulp yield is high
Reach 90%, decrease the dependence to primary slurry, reduce the papermaking industry destruction to ecological environment, promote row
The sustainable development of industry, removes the printing-ink of absorption on fiber when waste paper regenerated, improves fiber
Cleannes, and the waste paper deinking agent of present invention offer can prevent ink while thoroughly removing ink
Being re-depositing on fiber, during flotation, ink can be adsorbed on bubble and pulp separation smoothly, reduces further
Ink particle content in pulping, improves into pulp brightness, waste paper deinking agent is applied to deinking and is regenerated
Paper, the whiteness of recycled writing paper is up to 83%;The technique taking to relax in deinking process, to reduce fiber destruction,
Improve pulping intensity and yield.
The waste paper deinking agent and the application that there is provided the present invention below in conjunction with embodiment are described in detail, but
It is they can not to be interpreted as limiting the scope of the present invention.
Embodiment 1
By hexadecanol 5kg, stearic acid 6kg, fatty alcohol-polyoxyethylene ether 1kg, fatty alcohol-polyoxyethylene ether
Sodium sulfate 1kg, aliphatic alcohol polyethenoxy-polyethenoxy ether 1kg, PULLRONIC F68 atactic polyether
1kg, water 5kg weigh needed raw material, and each raw material is mixed to join discharging after stirring in homogenizer,
I.e. obtain waste paper deinking agent.
The waste paper deinking agent obtained is applied to deinking, and waste paper pulp mass concentration is 50g/L, will be useless
The waste paper deinking agent of old pulp quality 0.5% joins mix homogeneously in waste paper pulp, at 40 DEG C at pulping
Reason 10min, obtains pulping mixture, carries out FLOTATION SEPARATION the most again, obtain recycled writing paper.
Whiteness and the paper pulp yield of the present invention recycled writing paper to obtaining are analyzed, and the whiteness of recycled writing paper is
58%, paper pulp yield is 77%.
Embodiment 2
By tetradecyl alchohol 5kg, linoleic acid 6kg, fatty alcohol-polyoxyethylene ether 1kg, fatty alcohol-polyoxyethylene ether
Sodium sulfate 1kg, aliphatic alcohol polyethenoxy-polyethenoxy ether 1kg, PULLRONIC F68 atactic polyether
1kg, sodium silicate 2kg, sodium hydroxide 3kg, hydrogen peroxide 2kg, ethylenediaminetetraacetic acid 2kg, water 8kg
Weigh needed raw material, each raw material is mixed to join discharging after stirring in homogenizer, i.e. obtains waste paper
Deinking agent.
The waste paper deinking agent obtained is applied to deinking, and waste paper pulp mass concentration is 50g/L, will be useless
The waste paper deinking agent of old pulp quality 0.5% joins mix homogeneously in waste paper pulp, at 40 DEG C at pulping
Reason 12min, obtains pulping mixture, carries out FLOTATION SEPARATION the most again, obtain recycled writing paper, to obtaining again
Whiteness and the paper pulp yield of raw paper are analyzed, and the whiteness of recycled writing paper is 61%, and paper pulp yield is 79%.
Embodiment 3
By tetradecyl alchohol 3kg, octadecanol 3kg, stearic acid 3kg, Palmic acid 3kg, aliphatic alcohol polyethenoxy
Ether 12kg, polyoxyethylenated alcohol sodium sulfate 8kg, aliphatic alcohol polyethenoxy-polyethenoxy ether 12kg,
PULLRONIC F68 atactic polyether 12kg, sodium silicate 2kg, sodium hydroxide 3kg, hydrogen peroxide 2kg,
Ethylenediaminetetraacetic acid 2kg, water 12kg weigh needed raw material, are mixed to join in homogenizer by each raw material and stir
Discharging after mixing uniformly, i.e. obtains waste paper deinking agent.
The waste paper deinking agent obtained is applied to deinking, and waste paper pulp mass concentration is 50g/L, will be useless
The waste paper deinking agent of old pulp quality 1.0% joins mix homogeneously in waste paper pulp, carries out pulping process,
At 44 DEG C, pulping processes 13min, obtains pulping mixture, carries out FLOTATION SEPARATION the most again, obtain
Giving birth to paper, whiteness and paper pulp yield to the recycled writing paper obtained are analyzed, and the whiteness of recycled writing paper is 68%,
Paper pulp yield is 81%.
Embodiment 4
Acid 4kg, linoleic acid 5kg, aliphatic alcohol polyethenoxy is put by hexadecanol 4kg, octadecanol 4kg, palm fibre
Ether 8kg, polyoxyethylenated alcohol sodium sulfate 12kg, aliphatic alcohol polyethenoxy-polyethenoxy ether 10kg,
PULLRONIC F68 atactic polyether 10kg, sodium silicate 4kg, sodium hydroxide 4kg, hydrogen peroxide 4kg,
Diethylene-triamine pentaacetic acid 2kg, water 15kg weigh needed raw material, and each raw material is mixed to join homogenizer
In stir after discharging, i.e. obtain waste paper deinking agent.
The waste paper deinking agent obtained is applied to deinking, and waste paper pulp mass concentration is 50g/L, will be useless
The waste paper deinking agent of old pulp quality 0.05% joins mix homogeneously in waste paper pulp, pulping at 46 DEG C
Process 16min, obtain pulping mixture, carry out FLOTATION SEPARATION the most again, obtain recycled writing paper, to obtain
Whiteness and the paper pulp yield of recycled writing paper are analyzed, and the whiteness of recycled writing paper is 73%, and paper pulp yield is 84%.
Embodiment 5
By hexadecanol 2kg, octadecanol 3kg, stearic acid 4kg, linoleic acid 4kg, aliphatic alcohol polyethenoxy
Ether 5kg, polyoxyethylenated alcohol sodium sulfate 5kg, aliphatic alcohol polyethenoxy-polyethenoxy ether 5kg, poly-
Oxygen ethylene-polyoxypropylene atactic polyether 5kg, sodium silicate 5kg, sodium hydroxide 5kg, hydrogen peroxide 5kg,
Diethylene-triamine pentaacetic acid 5kg, water 18kg weigh needed raw material, and each raw material is mixed to join homogenizer
In stir after discharging, i.e. obtain waste paper deinking agent.
The waste paper deinking agent obtained is applied to deinking, and waste paper pulp mass concentration is 50g/L, will be useless
The waste paper deinking agent of old pulp quality 3.0% joins mix homogeneously in waste paper pulp, at 48 DEG C at pulping
Reason 18min, obtains pulping mixture, carries out FLOTATION SEPARATION the most again, obtain recycled writing paper, to obtaining again
Whiteness and the paper pulp yield of raw paper are analyzed, and the whiteness of recycled writing paper is 76%, and paper pulp yield is 87%.
Embodiment 6
By tetradecyl alchohol 2kg, octadecanol 3kg, stearic acid 3kg, linoleic acid 3kg, aliphatic alcohol polyethenoxy
Ether 8kg, polyoxyethylenated alcohol sodium sulfate 12kg, aliphatic alcohol polyethenoxy-polyethenoxy ether 15kg,
PULLRONIC F68 atactic polyether 15kg, sodium silicate 5kg, sodium hydroxide 5kg, hydrogen peroxide 5kg,
Ethylenediaminetetraacetic acid 5kg, water 20kg weigh needed raw material, are mixed to join in homogenizer by each raw material and stir
Discharging after mixing uniformly, i.e. obtains waste paper deinking agent.
The waste paper deinking agent obtained is applied to deinking, and waste paper pulp mass concentration is 50g/L, will be useless
The waste paper deinking agent of old pulp quality 5.0% joins mix homogeneously in waste paper pulp, at 50 DEG C at pulping
Reason 20min, obtains pulping mixture, carries out FLOTATION SEPARATION the most again, obtain recycled writing paper, to obtaining again
Whiteness and the paper pulp yield of raw paper are analyzed, and the whiteness of recycled writing paper is 83%, and paper pulp yield is 90%.
Comparative example 1
The graceful efficient deinking auxiliary agent-BRD of commercially available Bark is used to carry out being applied to deinking, waste paper pulp matter
Amount concentration is 50g/L, is joined by the waste paper deinking agent of waste paper pulp quality 5.0% in waste paper pulp and mixes
Uniformly, at 80 DEG C, pulping processes 60min, obtains pulping mixture, carries out FLOTATION SEPARATION the most again,
Obtaining recycled writing paper, whiteness and paper pulp yield to the recycled writing paper obtained are analyzed, and the whiteness of recycled writing paper is
64%, paper pulp yield is 70%.
By whiteness and the paper pulp yield of embodiment 6 with the recycled writing paper of comparative example 1 are compared, make
In the case of the deinking agent of equal in quality, the present invention provide deinking agent not only reduce pulping temperature and
Pulping time, while reducing energy resource consumption, decreases fibre damage, improves pulping intensity and become
Paper product matter, improves fiber cleaning degree, prevents ink redeposition to fiber while thoroughly removing ink
On, during flotation, ink can be adsorbed on bubble and pulp separation smoothly, reduces residual oil in pulping further
Mo Liang, improves into pulp brightness, and reduces the production cost of deinking agent, the deinking agent that the present invention provides
Cost is only 1/2nd of the commercially available graceful efficient deinking auxiliary agent-BRD cost of Bark.
Comparative example 2
The graceful efficient deinking auxiliary agent-BRD of commercially available Bark is used to carry out being applied to deinking, waste paper pulp matter
Amount concentration is 50g/L, is joined by the waste paper deinking agent of waste paper pulp quality 0.5% in waste paper pulp and mixes
Uniformly, at 50 DEG C, pulping processes 20min, obtains pulping mixture, carries out FLOTATION SEPARATION the most again,
Obtaining recycled writing paper, whiteness and paper pulp yield to the recycled writing paper obtained are analyzed, and the whiteness of recycled writing paper is
45%, paper pulp yield is 56%.
By whiteness and the paper pulp yield of embodiment 1 with the recycled writing paper of comparative example 2 are compared, make
In the case of the deinking agent of equal in quality, the present invention provide deinking agent not only reduce pulping temperature and
Pulping time, while reducing energy resource consumption, decreases fibre damage, improves pulping intensity and become
Paper product matter, improves fiber cleaning degree, prevents ink redeposition to fiber while thoroughly removing ink
On, during flotation, ink can be adsorbed on bubble and pulp separation smoothly, reduces residual oil in pulping further
Mo Liang, improves into pulp brightness, and reduces the production cost of deinking agent, the deinking agent that the present invention provides
Cost is only 1/2nd of the commercially available graceful efficient deinking auxiliary agent-BRD cost of Bark.
The above is only the preferred embodiment of the present invention, it is noted that general for the art
For logical technical staff, under the premise without departing from the principles of the invention, it is also possible to make some improvement and profit
Decorations, these improvements and modifications also should be regarded as protection scope of the present invention.
Claims (10)
1. a waste paper deinking agent, it is characterised in that include the component of following weight portion:
High fatty alcohol 1~10 parts, higher fatty acids 1~10 parts, fatty alcohol-polyoxyethylene ether 1~20 parts,
Polyoxyethylenated alcohol sodium sulfate 1~20 parts, aliphatic alcohol polyethenoxy-polyethenoxy ether 1~20 parts, poly-
Oxygen ethylene-polyoxypropylene atactic polyether 1~20 parts, sodium silicate 0~5 parts, sodium hydroxide 0~5 parts, peroxide
Change hydrogen 0~5 parts, chelating agen 0~5 parts and water 1~20 parts.
Waste paper deinking agent the most according to claim 1, it is characterised in that described high fatty alcohol is
The mixture of one or more in tetradecyl alchohol, hexadecanol and octadecanol.
Waste paper deinking agent the most according to claim 1 and 2, it is characterised in that include 4~8 parts
High fatty alcohol.
Waste paper deinking agent the most according to claim 1, it is characterised in that described higher fatty acids is
Stearic acid, oleic acid, palm fibre put the mixture of one or more in acid, linoleic acid.
5. according to the waste paper deinking agent described in claim 1 or 4, it is characterised in that include 4~8 parts
Higher fatty acids.
Waste paper deinking agent the most according to claim 1, it is characterised in that described chelating agen is second two
Amine tetraacethyl or diethylene-triamine pentaacetic acid.
7. the application in deinking of the waste paper deinking agent described in claim 1~6 any one, it is special
Levy and be, described deinking process particularly as follows:
(1) carry out pulping process after being mixed with described waste paper deinking agent by waste paper pulp, obtain pulping mixing
Thing;
(2) the pulping mixture that described step (1) obtains is carried out FLOTATION SEPARATION.
The deinking agent the most according to claim 7 application in deinking, it is characterised in that institute
State in step (1) consumption is waste paper pulp quality the 0.05~3.0% of waste paper deinking agent.
The deinking agent the most according to claim 7 application in deinking, it is characterised in that institute
Stating the temperature that in step (1), pulping processes is 40~50 DEG C.
The deinking agent the most according to claim 7 application in deinking, it is characterised in that
The time that in described step (1), pulping processes is 10~20min.