CN106009214A - Heat-resistant aging-resistant insulation material for coal mine - Google Patents
Heat-resistant aging-resistant insulation material for coal mine Download PDFInfo
- Publication number
- CN106009214A CN106009214A CN201610387747.6A CN201610387747A CN106009214A CN 106009214 A CN106009214 A CN 106009214A CN 201610387747 A CN201610387747 A CN 201610387747A CN 106009214 A CN106009214 A CN 106009214A
- Authority
- CN
- China
- Prior art keywords
- parts
- resisting
- insulation material
- heat
- colliery
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a heat-resistant aging-resistant insulation material for a coal mine, wherein the insulation material comprises the raw materials in parts by weight: 15-35 parts of low-density polyethylene, 20-40 parts of EVA resin, 0.8-1.5 parts of dibutyltin dilaurate, 1-2 parts of N-isopropyl-N'-phenyl-p-phenylenediamine, 0.8-1.6 parts of triallyl cyanurate, 0.5-1.2 parts of 3-aminopropyl methyl dimethoxy silane, 0.4-1 part of a vinyl chloride-vinyl acetate copolymer, 0.4-1 part of diethylenetriamine, 0.5-1.5 parts of dicumyl peroxide, 0.4-1 part of polydimethylsiloxane with vinyl as an end group, 20-35 parts of a modified plant protein, 1-2 parts of tall oil, 0.4-0.9 part of polytetrafluoroethylene, 0.5-1 part of a graphite powder, and 1-3 parts of paraffin oil. The insulation material has the advantages of good thermal stability, good mechanical property and excellent aging resistance.
Description
Technical field
The present invention relates to CABLE MATERIALS technical field, particularly relate to a kind of heat-resisting ageing-resisting colliery Insulation Material.
Background technology
In recent years, along with the fast development of China market economy, coal industry was as world today's main energy sources
One of basic industries obtain and develop rapidly, the nervous contradiction of energy supply is more and more prominent, for meeting this
Demand, each big Coal Exploitation powerful coal excavation apparatus raising production capacity, and the cable of matched transmission electric power
Requirement improve constantly, due to underground work bad environments, mine in the serious threat that occurs of various accidents
Safety and the life of miner, the heat stability of matched cable, mechanical property and resistance to ag(e)ing are increasingly
Cause the concern of people.
Summary of the invention
The technical problem existed based on background technology, the present invention proposes the insulation of a kind of heat-resisting ageing-resisting colliery
Material, Heat stability is good, mechanical property is good, and ageing-resistant performance is excellent.
A kind of heat-resisting ageing-resisting colliery Insulation Material that the present invention proposes, its raw material includes by weight: low close
Degree polyethylene 15-35 part, EVA resin 20-40 part, dibutyl tin laurate 0.8-1.5 part, N-is different
Propyl group-N '-diphenyl-para-phenylene diamine 1-2 part, triallyl cyanurate 0.8-1.6 part, 3-aminopropyltriethoxy
Dimethoxysilane 0.5-1.2 part, vinyl chloride-vinyl acetate resin 0.4-1 part, diethylenetriamines 0.4-1 part, peroxide
Changing diisopropylbenzene (DIPB) 0.5-1.5 part, end group is polydimethylsiloxane 0.4-1 part of vinyl, improved plant
Protein 20-35 parts, tall oil 1-2 part, politef 0.4-0.9 part, graphite powder 0.5-1 part, stone
Wax oil 1-3 part.
Preferably, modified vegetable protein use following technique prepare: by weight by 10-30 part zein,
10-20 part soybean protein, 60-100 part water mix homogeneously, be warming up to 85-95 DEG C of homogeneous milled processed, filters,
Addition 80-120 part water, 10-30 part dehydrated alcohol, 1-3 part PVP stir, microwave
Process 10-20min, microwave power is 400-500W, add 30-50 part lactalbumin, 40-60 part in
Property phosphate buffer mixed at room temperature stirring 4-5h, 60-80 DEG C of stirring in water bath 20-30min, regulation system
PH to 7.2-7.4, adds 1-2 part oleic acid, 0.5-2 part sorbitol, 0.5-1.5 part galactose mix and blend
20-50min, whipping temp is 40-60 DEG C, adds 0.1-0.15 part T-5398 at 40-46 DEG C of water
Bath concussion 1-2h, inactivation, regulation system pH, to neutral, adds 30-50 part polyethylene, 10-20 under stirring
Part calcium carbonate, 5-15 part nano silicon, 1-2 part age resistor, continue after adding completely to stir 15-35min,
Obtain modified vegetable protein.
Preferably, Low Density Polyethylene, EVA resin, the weight ratio of modified vegetable protein are 25-30:30-35:
32-34。
Preferably, diethylenetriamines, cumyl peroxide, end group are the polydimethylsiloxanes of vinyl
The weight ratio of alkane is 0.6-0.8:1.2-1.4:0.6-0.8.
Preferably, dibutyl tin laurate, N-isopropyl-N '-diphenyl-para-phenylene diamine, cyanuric acid three
Allyl ester, 3-aminopropyltriethoxy dimethoxysilane, vinyl chloride-vinyl acetate resin, the weight ratio of modified vegetable protein are
1-1.2:1.5-1.8:1-1.3:0.6-1:0.8-0.86:32-34.
Preferably, N-isopropyl-N '-diphenyl-para-phenylene diamine, 3-aminopropyltriethoxy dimethoxysilane, chlorine
Vinegar resin, politef, graphite powder, the weight ratio of paraffin oil are 1.5-1.8:0.6-1:0.8-0.86:
0.5-0.8:0.6-0.8:1.5-2.2.
Preferably, the weight ratio of modified vegetable protein, tall oil, politef, graphite powder, paraffin oil
For 32-34:1.5-1.8:0.5-0.8:0.6-0.8:1.5-2.2.
Preferably, described heat-resisting ageing-resisting colliery Insulation Material, its raw material includes by weight: low-density
Polyethylene 25-30 part, EVA resin 30-35 part, dibutyl tin laurate 1-1.2 part, N-isopropyl
-N '-diphenyl-para-phenylene diamine 1.5-1.8 part, triallyl cyanurate 1-1.3 part, 3-aminopropyltriethoxy two
Methoxy silane 0.6-1 part, vinyl chloride-vinyl acetate resin 0.8-0.86 part, diethylenetriamines 0.6-0.8 part, peroxide
Changing diisopropylbenzene (DIPB) 1.2-1.4 part, end group is polydimethylsiloxane 0.6-0.8 part of vinyl, and modification is planted
Thing protein 32-34 parts, tall oil 1.5-1.8 part, politef 0.5-0.8 part, graphite powder 0.6-0.8
Part, paraffin oil 1.5-2.2 part.
In the present invention, EVA resin, Low Density Polyethylene, modified vegetable protein is used to be used as base material,
Cumyl peroxide, end group are that the polydimethylsiloxane of vinyl, diethylenetriamines are as sulfuration body
System, goods heat stability, mechanical property are good, and ageing-resistant performance is excellent, wherein, the improved plant egg of addition
Bai Zhong, deforms after zein, soybean protein high-temperature process, micro-at dehydrated alcohol, PVP
Ripple helps after melting process, with the lactalbumin added under oleic acid, sorbitol, galactose effect, not only fine and close
Property high, and toughness is fabulous with stretch-proof performance, further under transglutamin-ase 9 enzyme catalysis, unmodified protein
Amino in matter is combined with hydroxyl amide groups, Heat stability is good, with zinc sulfate, calcium carbonate, nano silicon,
Age resistor dispersion is high, the compatibility, Heat stability is good, and ageing-resistant performance is fabulous, and mechanical property is fabulous, and
Modified vegetable protein and end group are the polydimethylsiloxane effect of vinyl, can effectively reduce improved plant egg
White internal flaw and the formation in cavity, heat stability, ageing-resistant further enhance with mechanical property, N-isopropyl
Base-N '-diphenyl-para-phenylene diamine, vinyl chloride-vinyl acetate resin, 3-aminopropyltriethoxy dimethoxysilane and tall oil, paraffin
Oil, politef, graphite powder synergism, not only can effectively slow down goods aging speed, and goods
Elongation at break is higher, and mechanical property is good, and service life is long.The present invention, thermally-stabilised good, mechanical property is good,
Service life is long.
Detailed description of the invention
Embodiment 1
A kind of heat-resisting ageing-resisting colliery Insulation Material, its raw material includes by weight: Low Density Polyethylene 15 parts,
EVA resin 40 parts, dibutyl tin laurate 0.8 part, N-isopropyl-N '-diphenyl-para-phenylene diamine 2 parts,
Triallyl cyanurate 0.8 part, 3-aminopropyltriethoxy dimethoxysilane 1.2 parts, vinyl chloride-vinyl acetate resin 0.4
Part, diethylenetriamines 1 part, cumyl peroxide 0.5 part, end group is the poly dimethyl silicon of vinyl
1 part of oxygen alkane, modified vegetable protein 20 parts, tall oil 2 parts, politef 0.4 part, graphite powder 1 part,
Paraffin oil 1 part.
Embodiment 2
A kind of heat-resisting ageing-resisting colliery Insulation Material, its raw material includes by weight: Low Density Polyethylene 35 parts,
EVA resin 20 parts, dibutyl tin laurate 1.5 parts, N-isopropyl-N '-diphenyl-para-phenylene diamine 1 part,
Triallyl cyanurate 1.6 parts, 3-aminopropyltriethoxy dimethoxysilane 0.5 part, vinyl chloride-vinyl acetate resin 1 part,
Diethylenetriamines 0.4 part, cumyl peroxide 1.5 parts, end group is the polydimethylsiloxanes of vinyl
0.4 part of alkane, modified vegetable protein 35 parts, tall oil 1 part, politef 0.9 part, graphite powder 0.5
Part, paraffin oil 3 parts.
Embodiment 3
A kind of heat-resisting ageing-resisting colliery Insulation Material, its raw material includes by weight: Low Density Polyethylene 25 parts,
EVA resin 35 parts, dibutyl tin laurate 1 part, N-isopropyl-N '-diphenyl-para-phenylene diamine 1.8 parts,
Triallyl cyanurate 1 part, 3-aminopropyltriethoxy dimethoxysilane 1 part, vinyl chloride-vinyl acetate resin 0.8 part,
Diethylenetriamines 0.8 part, cumyl peroxide 1.2 parts, end group is the polydimethylsiloxanes of vinyl
0.8 part of alkane, modified vegetable protein 32 parts, tall oil 1.8 parts, politef 0.5 part, graphite powder 0.8
Part, paraffin oil 1.5 parts.
Modified vegetable protein uses following technique to prepare: by weight by 30 parts of zeins, 10 portions of Semen sojae atricolor eggs
In vain, 100 parts of water mix homogeneously, be warming up to 85 DEG C of homogeneous milled processed, filter, add 120 parts of water, 10
Part dehydrated alcohol, 3 parts of PVPs stir, microwave treatment 10min, and microwave power is 500W,
Add 30 parts of lactalbumins, 60 parts of phosphate buffer mixed at room temperature stirring 4h in neutrality, 80 DEG C of water-baths
Stirring 20min, regulation system pH to 7.4, adds 1 part of oleic acid, 2 parts of sorbitol, 0.5 portion of galactose mixed
Closing stirring 50min, whipping temp is 40 DEG C, adds 0.15 part of T-5398 and shakes 40 DEG C of water-baths
2h, inactivation, regulation system pH to neutral, add under stirring 30 parts of polyethylene, 20 parts of calcium carbonate, 5
Part nano silicon, 2 parts of age resistor, continue after adding completely to stir 15min, obtain modified vegetable protein.
Embodiment 4
A kind of heat-resisting ageing-resisting colliery Insulation Material, its raw material includes by weight: Low Density Polyethylene 30 parts,
EVA resin 30 parts, dibutyl tin laurate 1.2 parts, N-isopropyl-N '-diphenyl-para-phenylene diamine 1.5
Part, triallyl cyanurate 1.3 parts, 3-aminopropyltriethoxy dimethoxysilane 0.6 part, vinyl chloride-vinyl acetate resin
0.86 part, diethylenetriamines 0.6 part, cumyl peroxide 1.4 parts, end group is poly-the two of vinyl
Methylsiloxane 0.6 part, modified vegetable protein 34 parts, tall oil 1.5 parts, politef 0.8 part,
Graphite powder 0.6 part, paraffin oil 2.2 parts.
Modified vegetable protein uses following technique to prepare: by weight by 10 parts of zeins, 20 portions of Semen sojae atricolor eggs
In vain, 60 parts of water mix homogeneously, be warming up to 95 DEG C of homogeneous milled processed, filter, add 80 parts of water, 30 parts
Dehydrated alcohol, 1 part of PVP stir, microwave treatment 20min, and microwave power is 400W,
Add 50 parts of lactalbumins, 40 parts of phosphate buffer mixed at room temperature stirring 5h in neutrality, 60 DEG C of water-baths
Stirring 30min, regulation system pH to 7.2, add 2 parts of oleic acid, 0.5 portion of sorbitol, 1.5 portions of galactose
Mix and blend 20min, whipping temp is 60 DEG C, adds 0.1 part of T-5398 and shakes 46 DEG C of water-baths
1h, inactivation, regulation system pH to neutral, add under stirring 50 parts of polyethylene, 10 parts of calcium carbonate,
15 parts of nano silicons, 1 part of age resistor, continue stirring 35min, obtain improved plant egg after adding completely
In vain.
Embodiment 5
A kind of heat-resisting ageing-resisting colliery Insulation Material, its raw material includes by weight: Low Density Polyethylene 28 parts,
EVA resin 33 parts, dibutyl tin laurate 1.1 parts, N-isopropyl-N '-diphenyl-para-phenylene diamine 1.6
Part, triallyl cyanurate 1.2 parts, 3-aminopropyltriethoxy dimethoxysilane 0.8 part, vinyl chloride-vinyl acetate resin
0.83 part, diethylenetriamines 0.7 part, cumyl peroxide 1.3 parts, end group is poly-the two of vinyl
Methylsiloxane 0.7 part, modified vegetable protein 33 parts, tall oil 1.6 parts, politef 0.6 part,
Graphite powder 0.75 part, paraffin oil 2.15 parts.
Modified vegetable protein uses following technique to prepare: by weight by 22 parts of zeins, 16 portions of Semen sojae atricolor eggs
In vain, 85 parts of water mix homogeneously, be warming up to 92 DEG C of homogeneous milled processed, filter, add 100 parts of water, 16 parts
Dehydrated alcohol, 2 parts of PVPs stir, microwave treatment 16min, and microwave power is 450W,
Add 46 parts of lactalbumins, 50 parts of phosphate buffer mixed at room temperature stirring 4.5h in neutrality, 72 DEG C of water
Bath stirring 25min, regulation system pH to 7.3, add 1.6 parts of oleic acid, 1.2 parts of sorbitol, 1.2 part half
Lactose mix and blend 40min, whipping temp is 50 DEG C, adds 0.12 part of T-5398 43 DEG C of water-baths
Concussion 1.5h, inactivation, regulation system pH, to neutral, adds 42 parts of polyethylene, 16 parts of carbon under stirring
Acid calcium, 12 parts of nano silicons, 1.6 parts of age resistor, continue stirring 22min, changed after adding completely
Property vegetable protein.
The above, the only present invention preferably detailed description of the invention, but protection scope of the present invention not office
Being limited to this, any those familiar with the art is in the technical scope that the invention discloses, according to this
The technical scheme of invention and inventive concept thereof in addition equivalent or change, all should contain the protection in the present invention
Within the scope of.
Claims (8)
1. a heat-resisting ageing-resisting colliery Insulation Material, it is characterised in that its raw material includes by weight: low
Density polyethylene 15-35 part, EVA resin 20-40 part, dibutyl tin laurate 0.8-1.5 part, N-
Isopropyl-N '-diphenyl-para-phenylene diamine 1-2 part, triallyl cyanurate 0.8-1.6 part, 3-aminopropyl first
Base dimethoxysilane 0.5-1.2 part, vinyl chloride-vinyl acetate resin 0.4-1 part, diethylenetriamines 0.4-1 part, mistake
Oxidation diisopropylbenzene (DIPB) 0.5-1.5 part, end group is polydimethylsiloxane 0.4-1 part of vinyl, and modification is planted
Thing protein 20-35 parts, tall oil 1-2 part, politef 0.4-0.9 part, graphite powder 0.5-1 part,
Paraffin oil 1-3 part.
Heat-resisting ageing-resisting colliery the most according to claim 1 Insulation Material, it is characterised in that modification is planted
Thing albumen use following technique prepare: by weight by 10-30 part zein, 10-20 part soybean protein,
60-100 part water mix homogeneously, is warming up to 85-95 DEG C of homogeneous milled processed, filters, addition 80-120 part water,
10-30 part dehydrated alcohol, 1-3 part PVP stir, and microwave treatment 10-20min is micro-
Wave power is 400-500W, adds 30-50 part lactalbumin, 40-60 part in neutral phosphate buffer
Mixed at room temperature stirring 4-5h, 60-80 DEG C of stirring in water bath 20-30min, regulation system pH to 7.2-7.4, add
Enter 1-2 part oleic acid, 0.5-2 part sorbitol, 0.5-1.5 part galactose mix and blend 20-50min, stirring
Temperature is 40-60 DEG C, adds 0.1-0.15 part T-5398 and shakes 1-2h 40-46 DEG C of water-bath, goes out
Live, regulation system pH to neutral, add under stirring 30-50 part polyethylene, 10-20 part calcium carbonate,
5-15 part nano silicon, 1-2 part age resistor, continue stirring 15-35min, changed after adding completely
Property vegetable protein.
Heat-resisting ageing-resisting colliery the most according to claim 1 and 2 Insulation Material, it is characterised in that low
Density polyethylene, EVA resin, the weight ratio of modified vegetable protein are 25-30:30-35:32-34.
4. according to the heat-resisting ageing-resisting colliery Insulation Material described in any one of claim 1-3, it is characterised in that
Diethylenetriamines, cumyl peroxide, end group are that the weight ratio of the polydimethylsiloxane of vinyl is
0.6-0.8:1.2-1.4:0.6-0.8.
5. according to the heat-resisting ageing-resisting colliery Insulation Material described in any one of claim 1-4, it is characterised in that
Dibutyl tin laurate, N-isopropyl-N '-diphenyl-para-phenylene diamine, triallyl cyanurate, 3-ammonia
Hydroxypropyl methyl dimethoxysilane, vinyl chloride-vinyl acetate resin, the weight ratio of modified vegetable protein are 1-1.2:1.5-1.8:
1-1.3:0.6-1:0.8-0.86:32-34.
6. according to the heat-resisting ageing-resisting colliery Insulation Material described in any one of claim 1-5, it is characterised in that
N-isopropyl-N '-diphenyl-para-phenylene diamine, 3-aminopropyltriethoxy dimethoxysilane, vinyl chloride-vinyl acetate resin, poly-four
Fluorothene, graphite powder, the weight ratio of paraffin oil are 1.5-1.8:0.6-1:0.8-0.86:0.5-0.8:
0.6-0.8:1.5-2.2.
7. according to the heat-resisting ageing-resisting colliery Insulation Material described in any one of claim 1-6, it is characterised in that
Modified vegetable protein, tall oil, politef, graphite powder, the weight ratio of paraffin oil are 32-34:1.5-1.8:
0.5-0.8:0.6-0.8:1.5-2.2.
8. according to the heat-resisting ageing-resisting colliery Insulation Material described in any one of claim 1-7, it is characterised in that
Its raw material includes by weight: Low Density Polyethylene 25-30 part, EVA resin 30-35 part, tin dilaurate
Dibutyl tin 1-1.2 part, N-isopropyl-N '-diphenyl-para-phenylene diamine 1.5-1.8 part, cyanuric acid triolefin
Propyl ester 1-1.3 part, 3-aminopropyltriethoxy dimethoxysilane 0.6-1 part, vinyl chloride-vinyl acetate resin 0.8-0.86 part,
Diethylenetriamines 0.6-0.8 part, cumyl peroxide 1.2-1.4 part, end group is poly-the two of vinyl
Methylsiloxane 0.6-0.8 part, modified vegetable protein 32-34 part, tall oil 1.5-1.8 part, polytetrafluoro
Ethylene 0.5-0.8 part, graphite powder 0.6-0.8 part, paraffin oil 1.5-2.2 part.