CN106009123A - Automobile tire and manufacturing method thereof - Google Patents
Automobile tire and manufacturing method thereof Download PDFInfo
- Publication number
- CN106009123A CN106009123A CN201610598783.7A CN201610598783A CN106009123A CN 106009123 A CN106009123 A CN 106009123A CN 201610598783 A CN201610598783 A CN 201610598783A CN 106009123 A CN106009123 A CN 106009123A
- Authority
- CN
- China
- Prior art keywords
- parts
- tire
- rubber
- automobile tire
- calcium carbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an automobile tire and a manufacturing method thereof. The automobile tire is prepared from the following raw materials in parts by weight: 20 to 30 parts of butylbenzene rubber, 20 to 30 parts of butyl bromide rubber, 5 to 8 parts of calcium carbonate, 7 to 10 parts of stearic acid, 3 to 7 parts of nano-crystalline cellulose crystal whiskers, 5 to 7 parts of polyester fiber, 1 to 3 parts of nylon short fiber, 5 to 9 parts of medium ultra-wear-resistant carbon black and 1 to 3 parts of sulphur powder. The automobile tire has the beneficial effects that the air tightness of an air-tight layer of the tire material manufactured by the material according to the manufacturing method is improved, so that the service life of the tire is prolonged; a series of good properties are brought.
Description
Technical field
The present invention relates to automotive field, be specifically related to a kind of automobile tire and preparation method thereof.
Background technology
Tire is the safety member of automobile, as the medium of automobile Yu road surface, its performance power to automobile
Property, fuel economy, braking, control stability, ride comfort and cross-country ability etc. suffer from direct shadow
Ring.The correct selection of tire can ensure that automobile has optimal serviceability.It is total that our times tire develops
Trend is attributed to " three change one ", the i.e. meridian of tire, flattening and tubeless, and often exists
Embody on same tire, be ensure that the air-tightness of tire by some peculiar industry, material technology.
It is well known that the height air-tightness of tire almost has a desirable influence to its all serviceabilities:
Safety, cornering ability and the comfortableness travelled can be improved.Owing to distance travelled improves, tread wear
Improve, maintain meridian section configuration and the raising of revision rate in traveling, extend the use of tire
Life-span;Owing to reducing resistance to rolling, decrease the consumption of fuel, it is simple to Motor Maintenance (decreases inspection
Tire pressure and the number of times of inflation);Owing to reducing oil consumption, decrease CO2Discharge capacity;Owing to improve
In the service life of tire, decrease damaged tire quantity to be processed, thus improve ecological environment, therefore,
Excellent bubble-tight tire material becomes the urgent need of current tyre industry.
Summary of the invention
In sum, in order to overcome the deficiencies in the prior art, the technical problem to be solved is to carry
For a kind of automobile tire and preparation method thereof.
The technical scheme is that a kind of automobile tire, by following weight
The raw material of number prepares: butylbenzene rubber 20-30 part glue, brombutyl 20-30 part, calcium carbonate 5-8
Part, stearic acid 7-10 part, nano-cellulose whisker 3-7 part, polyester fiber 5-7 part, nylon staple
Dimension 1-3 part, intermediate super abrasion furnace black 5-9 part and Cosan 1-3 part.
The manufacture method of a kind of automobile tire, is completed by the steps:
(1) each component of following parts by weight is obtained respectively: butylbenzene rubber 20-30 part glue, butyl rubber bromide
Glue 20-30 part, calcium carbonate 5-8 part, stearic acid 7-10 part, nano-cellulose whisker 3-7 part, poly-
Ester fiber 5-7 part, nylon short fibre 1-3 part, intermediate super abrasion furnace black 5-9 part and Cosan 1-3 part;
(2) butylbenzene rubber step (1) weighed and brombutyl mix homogeneously;
(3) addition step (1) weighs calcium carbonate, stearic acid and the stirring of nano-cellulose whisker are mixed
Close adjuvant;
(4) again polyester fiber and nylon short fibre are put in banbury mixing uniformly, melting temperature is
80-100 DEG C, banbury rotating speed is 60rpm, when temperature of charge is increased to 100 DEG C, super resistance in addition
Mill white carbon black is mixing, and temperature is to binder removal when 120-130 DEG C, slice;
(5) adding Cosan mixing 10-15min, reaction temperature is 200-300 DEG C, and discharge obtains wear-resisting
Tire rubber material.
Further, the mixing speed of step (3) is 50-60rpm.
Further, the mixing time of step (3) is 20min.
The invention has the beneficial effects as follows: the tire material prepared by this material and manufacture method improves gas
The air-tightness of close layer, thus extend the service life of tire and bring a series of premium properties.
Detailed description of the invention
Being described principle and the feature of the present invention below in conjunction with instantiation, example is served only for solving
Release the present invention, be not intended to limit the scope of the present invention.
Embodiment 1
The manufacture method of a kind of automobile tire, is completed by the steps:
(1) each component of following parts by weight is obtained respectively: 20 parts of glue of butylbenzene rubber, brombutyl 20
Part, calcium carbonate 5 parts, stearic acid 7 parts, nano-cellulose whisker 3 parts, 5 parts of polyester fiber, nylon
Chopped fiber 1 part, intermediate super abrasion furnace black 5 parts and Cosan 1 part;
(2) butylbenzene rubber step (1) weighed and brombutyl mix homogeneously;
(3) calcium carbonate, stearic acid and the nano-cellulose whisker that addition step (1) weighs is with 50rpm's
Rotating speed stirring 20min obtains mixed accessories;
(4) again polyester fiber and nylon short fibre are put in banbury mixing uniformly, melting temperature is
80 DEG C, banbury rotating speed is 60rpm, when temperature of charge is increased to 100 DEG C, and super abrasive charcoal in addition
Black mixing, binder removal during temperature to 120 DEG C, slice;
(5) adding Cosan mixing 10min, reaction temperature is 200 DEG C, and discharge obtains wear-resistant tyre rubber
Glue material.
Embodiment 2
The manufacture method of a kind of automobile tire, is completed by the steps:
(1) each component of following parts by weight is obtained respectively: 25 parts of glue of butylbenzene rubber, brombutyl 25
Part, calcium carbonate 7 parts, stearic acid 8 parts, nano-cellulose whisker 5 parts, 6 parts of polyester fiber, nylon
Chopped fiber 2 parts, intermediate super abrasion furnace black 7 parts and Cosan 2 parts;
(2) butylbenzene rubber step (1) weighed and brombutyl mix homogeneously;
(3) calcium carbonate, stearic acid and the nano-cellulose whisker that addition step (1) weighs is with 55rpm's
Rotating speed stirring 20min obtains mixed accessories;
(4) again polyester fiber and nylon short fibre are put in banbury mixing uniformly, melting temperature is
90 DEG C, banbury rotating speed is 60rpm, when temperature of charge is increased to 100 DEG C, and super abrasive charcoal in addition
Black mixing, binder removal during temperature to 110 DEG C, slice;
(5) adding Cosan mixing 12min, reaction temperature is 250 DEG C, and discharge obtains wear-resistant tyre rubber
Material.
Embodiment 3
The manufacture method of a kind of automobile tire, is completed by the steps:
(1) each component of following parts by weight is obtained respectively: 30 parts of glue of butylbenzene rubber, brombutyl 30
Part, calcium carbonate 8 parts, stearic acid 10 parts, nano-cellulose whisker 7 parts, 7 parts of polyester fiber, Buddhist nun
Dragon chopped fiber 3 parts, intermediate super abrasion furnace black 9 parts and Cosan 3 parts;
(2) butylbenzene rubber step (1) weighed and brombutyl mix homogeneously;
(3) calcium carbonate, stearic acid and the nano-cellulose whisker that addition step (1) weighs is with 60rpm's
Rotating speed stirring 20min obtains mixed accessories;
(4) again polyester fiber and nylon short fibre are put in banbury mixing uniformly, melting temperature is
100 DEG C, banbury rotating speed is 60rpm, when temperature of charge is increased to 100 DEG C, and super abrasive charcoal in addition
Black mixing, binder removal during temperature to 130 DEG C, slice;
(5) adding Cosan mixing 15min, reaction temperature is 300 DEG C, and discharge obtains wear-resistant tyre rubber
Material.
The foregoing is only presently preferred embodiments of the present invention, not in order to limit the present invention, all in the present invention
Spirit and principle within, any modification, equivalent substitution and improvement etc. made, should be included in this
Within bright protection domain.
Claims (4)
1. an automobile tire, it is characterised in that prepared by the raw material of following parts by weight: butylbenzene rubber
20-30 part glue, brombutyl 20-30 part, calcium carbonate 5-8 part, stearic acid 7-10 part, nanometer
Cellulose whiskers 3-7 part, polyester fiber 5-7 part, nylon short fibre 1-3 part, intermediate super abrasion furnace black 5-9
Part and Cosan 1-3 part.
2. the manufacture method of an automobile tire, it is characterised in that completed by the steps:
(1) each component of following parts by weight is obtained respectively: butylbenzene rubber 20-30 part glue, butyl rubber bromide
Glue 20-30 part, calcium carbonate 5-8 part, stearic acid 7-10 part, nano-cellulose whisker 3-7 part, poly-
Ester fiber 5-7 part, nylon short fibre 1-3 part, intermediate super abrasion furnace black 5-9 part and Cosan 1-3 part;
(2) butylbenzene rubber step (1) weighed and brombutyl mix homogeneously;
(3) addition step (1) weighs calcium carbonate, stearic acid and the stirring of nano-cellulose whisker are mixed
Close adjuvant;
(4) again polyester fiber and nylon short fibre are put in banbury mixing uniformly, melting temperature is
80-100 DEG C, banbury rotating speed is 60rpm, when temperature of charge is increased to 100 DEG C, super resistance in addition
Mill white carbon black is mixing, and temperature is to binder removal when 120-130 DEG C, slice;
(5) adding Cosan mixing 10-15min, reaction temperature is 200-300 DEG C, and discharge obtains wear-resisting
Tire rubber material.
Manufacture method the most according to claim 2, it is characterised in that the mixing speed of step (3)
For 50-60rpm.
4. according to the manufacture method described in Claims 2 or 3, it is characterised in that the stirring of step (3)
Time is 20min.