CN105985747A - Transparent back glue used for double-face color development hot stamping foil - Google Patents
Transparent back glue used for double-face color development hot stamping foil Download PDFInfo
- Publication number
- CN105985747A CN105985747A CN201510041551.7A CN201510041551A CN105985747A CN 105985747 A CN105985747 A CN 105985747A CN 201510041551 A CN201510041551 A CN 201510041551A CN 105985747 A CN105985747 A CN 105985747A
- Authority
- CN
- China
- Prior art keywords
- parts
- colour developing
- water
- back glue
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to transparent back glue used for a double-face color development hot stamping foil and solves a problem of influence on color development on the last one coating due to poor transparency of a coated back glue layer in the prior art. The transparent back glue includes, by weight, 5-18 parts of aqueous polyurethane resin, 5-10 parts of aqueous rosin-modified phenolic resin, 0-10 parts of aqueous amino resin, 0.1-0.5 parts of a defoamer, 0.5-2 parts of a film-forming aid, 0-2 parts of a wetting agent, and 60-120 parts of deionized water. The transparent back glue is free of addition of fumed silica powder into the glue material during usage, and has high transparency and good cutting property.
Description
Technical field
The present invention relates to a kind of speciality polymer material, particularly a kind of use process is without adding gas phase two
Silica powder, possesses the two-sided transparent gum of colour developing alumite thermoprinting foil that transparency is high, cutting property is good.
Background technology
Two-sided colour developing alumite thermoprinting foil can show as pattern positive and negative after thermoprint a in alumite thermoprinting foil
The product of different (or identical) colors, it is widely used in all kinds of transparent substrate surface thermoprint, can enrich thermoprint
The color effects of pattern, promotes aesthetics.But routine alumite thermoprinting foil gum is due to production technology and technology
Restriction, backing material transparency relative deviation, use process need add aerosil powder, make reverse side
Chromatograph cannot normally develop the color, and manufacture and popularization to two-sided colour developing alumite thermoprinting foil bring the biggest difficulty.
Summary of the invention
In order to overcome the defect of prior art, the present invention provides a kind of use process without adding gas phase titanium dioxide
Silicon, possesses the two-sided transparent gum of colour developing alumite thermoprinting foil that transparency is high, cutting property is good.
To achieve these goals, the technical solution used in the present invention is as follows: a kind of two-sided colour developing electrochemical aluminium thermoprinting
The transparent gum of paper tinsel, its composition and weight proportion be: waterborne polyurethane resin 5～18 parts, water-soluble rosin change
Property phenolic resin 5～10 parts, water-compatible amino resin 0～10 parts, defoamer 0.1～0.5 part, coalescents 0.5～2
Part, wetting agent 0～2 parts, deionized water 60～120 parts.
Described defoamer is polysiloxanes.
Described coalescents is propylene glycol methyl ether acetate.
Described wetting agent is polyoxyethylene aliphatic alcohol ether.
The method preparing the transparent gum of above-mentioned two-sided colour developing alumite thermoprinting foil, its method step is:
1), by described recipe requirements, whole deionized waters are put in container, under stirring at low speed, make from
Sub-coolant-temperature gage is maintained at 15 DEG C～25 DEG C；
2), under stirring at low speed state, by described waterborne polyurethane resin, water-soluble rosin modified phenolic resin
Fat, water-compatible amino resin, defoamer, coalescents, wetting agent put in container the most in proportion, first low speed
Stir 20～30 minutes, then high-speed stirred 5～10 minutes；
3), stop stirring, temperature in container is controlled at 20～25 DEG C, keep 30 minutes；
4), pour into after last strainer filtering standby.
The present invention compared with prior art, has use process without adding aerosil powder, possesses transparent
Degree is high, cutting property is good, the advantage that the gum layer after coating does not affect a coating colour developing.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention will be described in detail: one of the present invention two-sided colour developing electricity
Changing the transparent gum of aluminum stamping systems, its composition and weight proportion be: waterborne polyurethane resin 5～18 parts, water-soluble
Property rosin modified phenolic resin 5～10 parts, water-compatible amino resin 0～10 parts, defoamer 0.1～0.5 part, film forming
Auxiliary agent 0.5～2 parts, wetting agent 0～2 parts, deionized water 60～120 parts.
Other embodiments of the invention combination in any can be constituted in the range of said ratio, it is not limited to following
Specifically disclosed embodiment.
Embodiment 1
A kind of two-sided colour developing alumite thermoprinting foil transparent gum and preparation method thereof, including following methods step:
1), first 120 parts of deionized waters put in container, under stirring at low speed, make deionized water temperature keep
At 15 DEG C～25 DEG C；
2), under stirring at low speed state, by 13 parts of waterborne polyurethane resins, 6 parts of water-soluble rosin modification phenol
Urea formaldehyde, 5 parts of water-compatible amino resins, 0.5 part of defoamer, 1.2 parts of coalescents, 1.6 parts of wetting agent are successively
Put in proportion in container, first stirring at low speed 20～30 minutes, then high-speed stirred 5～10 minutes；
3), stop stirring, temperature in container is controlled at 20～25 DEG C, keep 30 minutes；
4), pour into after last strainer filtering standby.
Embodiment 2
A kind of two-sided colour developing alumite thermoprinting foil transparent gum and preparation method thereof, including following methods step:
1), first 100 parts of deionized waters put in container, under stirring at low speed, make deionized water temperature keep
At 15 DEG C～25 DEG C；
2), under stirring at low speed state, by 6 parts of waterborne polyurethane resins, 10 parts of water-soluble rosin modification phenol
Urea formaldehyde, 7 parts of water-compatible amino resins, 0.3 part of defoamer, 0.7 part of coalescents, 1 part of wetting agent are pressed successively
Ratio puts in container, first stirring at low speed 20～30 minutes, then high-speed stirred 5～10 minutes；
3), stop stirring, temperature in container is controlled at 20～25 DEG C, keep 30 minutes；
4), pour into after last strainer filtering standby.
Claims (5)
1. the two-sided transparent gum of colour developing alumite thermoprinting foil, it is characterised in that composition and weight proportion be:
Waterborne polyurethane resin 5～18 parts, water-soluble rosin phenol-formaldehyde resin modified 5～10 parts, water-compatible amino resin 0～10
Part, defoamer 0.1～0.5 part, coalescents 0.5～2 parts, wetting agent 0～2 parts, deionized water 60～120 parts.
A kind of two-sided transparent gum of colour developing alumite thermoprinting foil the most as claimed in claim 1, its feature exists
In, described defoamer is polysiloxanes.
A kind of two-sided transparent gum of colour developing alumite thermoprinting foil the most as claimed in claim 1, it is characterised in that
Described coalescents is propylene glycol methyl ether acetate.
A kind of two-sided transparent gum of colour developing alumite thermoprinting foil the most as claimed in claim 1, its feature exists
In, described wetting agent is polyoxyethylene aliphatic alcohol ether.
5. the method preparing the transparent gum of a kind of two-sided colour developing alumite thermoprinting foil as claimed in claim 1,
It is characterized in that, method step is:
1), by described recipe requirements, whole deionized waters are put in container, under stirring at low speed, make from
Sub-coolant-temperature gage is maintained at 15 DEG C～25 DEG C；
2), under stirring at low speed state, by described waterborne polyurethane resin, water-soluble rosin modified phenolic resin
Fat, water-compatible amino resin, defoamer, coalescents, wetting agent put in container the most in proportion, first low speed
Stir 20～30 minutes, then high-speed stirred 5～10 minutes；
3), stop stirring, temperature in container is controlled at 20～25 DEG C, keep 30 minutes；
4), pour into after last strainer filtering standby.