CN105969492B - A kind of dedicated mould release of milling train and preparation method thereof - Google Patents
A kind of dedicated mould release of milling train and preparation method thereof Download PDFInfo
- Publication number
- CN105969492B CN105969492B CN201610298416.5A CN201610298416A CN105969492B CN 105969492 B CN105969492 B CN 105969492B CN 201610298416 A CN201610298416 A CN 201610298416A CN 105969492 B CN105969492 B CN 105969492B
- Authority
- CN
- China
- Prior art keywords
- solvent
- added
- mould release
- stirring
- reaction kettle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of dedicated mould release of milling train, the raw material including following mass percent：Aqueous silicon 5~10%, water soluble acrylic acid 6~8%, water-borne wax 10~20%, aqueous polyethylene wax 15~20%, solvent 40~50%, film forming agent 3~9%；After the mould release is applied to roll, so that the adhesiveness of machined material significantly reduces, machined material is not adhered on roll; roll is enabled to keep high-cleanness, high for a long time; the processing quality and machining accuracy for having ensured product, reduce the number of milling train maintenance shut-downs, improve production efficiency；In addition, the mould release is cheap, clean and environmental protection, dosage is few, is added in roll, will not both aoxidize to roll, will not aoxidize to workpiece to be machined, there is no need to clean to workpiece or roll, reduces manufacturing procedure and production cost；In addition, slipping phenomenon will not be generated using the mould release, calendering precision and calendering efficiency, high reliablity have been ensured.
Description
Technical field
The present invention relates to heavy chemicals technical fields more particularly to a kind of dedicated mould release of milling train and preparation method thereof.
Background technique
In the past, when workpieces processing, machined material is easy to be adhered to roll during high temperature process milling train
On.As the material being adhered on roll is more and more, cause the machining accuracy of milling train lower and lower, it is necessary to shut down to roll into
Row cleaning.Therefore, technical staff is added to the lubricating oil of import on the surface of roll to solve the problems, such as roll adhesion material
(because domestic lubricating oil using effect is very poor, seldom milling train be will use).Although the lubricating oil of import solves material
The problem being adhered on roll, but the lubricating oil of import is expensive, greatly improves the use cost of milling train.In addition,
The use of import lubricating oil can aoxidize the surface of workpiece to be machined, the product for causing the quality of product to decline, therefore process
Cleaning agent must be used to be cleaned, increase manufacturing procedure and production cost.In addition, being adhered to the lubricating oil of roller surface
So that the phenomenon that generating skidding between roll and workpiece to be machined, leads to product sideslip, so that calendering precision reduces, seriously
When even can roll and fail, there are improved necessity.
Summary of the invention
The present invention is to overcome drawbacks described above and provide a kind of dedicated mould release of milling train and preparation method thereof, which answers
After roll, so that the adhesiveness of machined material significantly reduces, machined material is not adhered on roll, so that roll
High-cleanness, high can be kept for a long time, ensured the processing quality and machining accuracy of product, reduced the number of milling train maintenance shut-downs,
Improve production efficiency；In addition, the mould release is cheap (only 1/10th or so of import lubricating oil), clean and environmental protection,
Dosage is few, is added in roll, will not both aoxidize to roll, will not aoxidize to workpiece to be machined, there is no need to
Workpiece or roll are cleaned, manufacturing procedure and production cost are reduced；In addition, skidding will not be generated using the mould release
Phenomenon has ensured calendering precision and calendering efficiency, high reliablity；The preparation method simple process of the dedicated mould release of the milling train, behaviour
It is easy, high production efficiency, product qualification rate is high, is suitable for large-scale promotion application.
To achieve the above object, the present invention adopts the following technical scheme that.
A kind of dedicated mould release of milling train, the raw material including following mass percent：
Aqueous silicon, that is, aqueous silica sol.Aqueous silica sol has the characteristics that oiliness, and high brightness, fastness is good, have it is flexible, have anti-
Sliding effect.Aqueous silica sol is the polymer containing the special silicone resin of polyurethane and other auxiliary agents, is the material of one group of self cross-linking type
Material.Aqueous silica sol is commonly applied to production cloth and spins stamp.
Water soluble acrylic acid, characteristic are：It is high glaze, water-fast, oil resistant, heat-resisting.
Water-borne wax has the characteristics that：
Scratch resistance increases sliding or suppression and slides；
It is wear-resisting to undermine scratch-resistant, it prevents adhesion；
Agglomeration resistance, stain resistant, the alcohol of resistance to flaw, the water of resistance to flaw；
Improve hydrophobicity, delustring or raising gloss；
Improve feel, improves the adhesive force of plastic film.
The application of aqueous polyethylene wax：
1, the ideal surfaced protective agent of water-based gloss oil, water varnish (metallic paint, woodcare paint, plastic paint etc.), it is anti-friction, resist
It scratches, increases slipping and glossiness.Similar functions are also applied in other polish arts such as floor wax；
2, anti-friction scratch resistance is provided in the products such as leather finishing agent, shoes wax water, shoes cream, increases slipping and gloss
Degree improves feel and polishability；
3, fabric softener, smooth agent increase wear-resisting, the resistance to tearing of fabric, increase lubricity when sewing, increase
The flexibility of fabric feeling, and can be applied in concentrator；
4, high-melting-point and the good affinity to plastic film are provided in aqueous adhesive；
5, paper product application of lubricating, remover, sizing agent；
6, water based mold release agent can be used for the fields such as die cast metal；
7, other fields such as the agent of flatting silica surface organic modification, agricultural.
Solvent is that one kind can dissolve solid, and (solvent, solute are all for the liquid (gas or solid) of liquid or gaseous solute
Can be solid, liquid, gas), then become solution.Most common solvent is water in mouth is often lived.And it is so-called organic molten
Agent is the organic compound comprising carbon atom.Solvent usually possesses relatively low boiling point and readily volatilized.Or it can be by steaming
It evaporates to remove, to leave by molten object.Therefore, solvent cannot generate chemical reaction to solute.They are necessary for inertia.Solvent
Soluble compounds can be extracted from mixture, most common example is with brewed in hot water coffee or tea.Solvent is usually transparent, colourless
Liquid, they have unique smell mostly.
All are capable of forming the polymer of continuous film, can be known as film forming agent.Film forming agent is also known as leather binder.
Film forming agent is the important component of finishing agent, is played a decisive role to the performance of finishing agent.Film forming agent be it is a kind of can on leather surface shape
It is sticked together securely at one layer, the material with the continuous uniforms film such as certain flexibility, extensibility and elasticity, rub resistance, water resistance
Material.
Preferably, the dedicated mould release of a kind of milling train, the raw material including following mass percent：
Preferably, the dedicated mould release of a kind of milling train, the raw material including following mass percent：
Wherein, the solvent is pure water.
Wherein, the film forming agent is polyvinyl alcohol.
A kind of preparation method of the dedicated mould release of milling train, including following procedure of processing：
Step A, the material that formula ratio is weighed according to formula, is placed individually into different containers；
Step B, solvent is added in reaction kettle, aqueous polyethylene wax is then added, it is stirring while adding, so that aqueous poly-
Ethylene waxes are evenly spread in solvent；
Step C, water-borne wax is added in reaction kettle, it is stirring while adding, so that water-borne wax is evenly spread in solvent；
Step D, aqueous silicon is added in reaction kettle, it is stirring while adding, so that aqueous silicon is evenly spread in solvent；
Step E, film forming agent is added in reaction kettle, it is stirring while adding, so that film forming agent is evenly spread in solvent；
Step F, water soluble acrylic acid is added in reaction kettle, it is stirring while adding, so that water soluble acrylic acid is evenly spread to
To get finished product in solvent.
Beneficial effects of the present invention are：The dedicated mould release of a kind of milling train of the invention, the original including following mass percent
Material：Aqueous silicon 5~10%, water soluble acrylic acid 6~8%, water-borne wax 10~20%, aqueous polyethylene wax 15~20%, solvent 40
~50%, film forming agent 3~9%；Wherein, aqueous silicon plays lubricating action, and water soluble acrylic acid plays peptizaiton, and water-borne wax plays
Enhanced shine, aqueous polyethylene wax play lubrication enhanced shine, and solvent plays dissolution, and film forming agent plays filming function；It should
After mould release is applied to roll, so that the adhesiveness of machined material significantly reduces, machined material is not adhered on roll,
Enable roll to keep high-cleanness, high for a long time, ensured the processing quality and machining accuracy of product, reduces milling train and shut down dimension
The number of shield, improves production efficiency；In addition, the mould release is cheap (only 1/10th or so of import lubricating oil),
Clean and environmental protection, dosage is few, is added in roll, will not both aoxidize to roll, will not aoxidize to workpiece to be machined,
There is no need to clean to workpiece or roll, reduce manufacturing procedure and production cost；In addition, will not using the mould release
Slipping phenomenon is generated, has ensured calendering precision and calendering efficiency, high reliablity；
A kind of preparation method of the dedicated mould release of milling train of the invention, including following procedure of processing：Step A, according to formula
The material for weighing formula ratio is placed individually into different containers；Step B, solvent is added in reaction kettle, water is then added
Property polyethylene wax, it is stirring while adding, so that aqueous polyethylene wax is evenly spread in solvent；Step C, water-borne wax is added to instead
It answers in kettle, it is stirring while adding, so that water-borne wax is evenly spread in solvent；Step D, aqueous silicon is added in reaction kettle, side
Edged stirring, so that aqueous silicon is evenly spread in solvent；Step E, film forming agent is added in reaction kettle, it is stirring while adding,
So that film forming agent is evenly spread in solvent；Step F, water soluble acrylic acid is added in reaction kettle, it is stirring while adding, so that water
Property acrylic acid is evenly spread in solvent to get finished product；The preparation method simple process of the dedicated mould release of the milling train, operation are held
Easily, high production efficiency, product qualification rate is high, is suitable for large-scale promotion application.
Specific embodiment
Below with reference to embodiment, the present invention is further illustrated, this is presently preferred embodiments of the present invention.
Embodiment 1.
The dedicated mould release of a kind of milling train of the invention, the raw material including following mass percent：
A kind of preparation method of the dedicated mould release of milling train, including following procedure of processing：
Step A, the material that formula ratio is weighed according to formula, is placed individually into different containers；
Step B, solvent is added in reaction kettle, aqueous polyethylene wax is then added, it is stirring while adding, so that aqueous poly-
Ethylene waxes are evenly spread in solvent；
Step C, water-borne wax is added in reaction kettle, it is stirring while adding, so that water-borne wax is evenly spread in solvent；
Step D, aqueous silicon is added in reaction kettle, it is stirring while adding, so that aqueous silicon is evenly spread in solvent；
Step E, film forming agent is added in reaction kettle, it is stirring while adding, so that film forming agent is evenly spread in solvent；
Step F, water soluble acrylic acid is added in reaction kettle, it is stirring while adding, so that water soluble acrylic acid is evenly spread to
To get finished product in solvent.
Embodiment 2.
The dedicated mould release of a kind of milling train of the invention, the raw material including following mass percent：
A kind of preparation method of the dedicated mould release of milling train, including following procedure of processing：
Step A, the material that formula ratio is weighed according to formula, is placed individually into different containers；
Step B, solvent is added in reaction kettle, aqueous polyethylene wax is then added, it is stirring while adding, so that aqueous poly-
Ethylene waxes are evenly spread in solvent；
Step C, water-borne wax is added in reaction kettle, it is stirring while adding, so that water-borne wax is evenly spread in solvent；
Step D, aqueous silicon is added in reaction kettle, it is stirring while adding, so that aqueous silicon is evenly spread in solvent；
Step E, film forming agent is added in reaction kettle, it is stirring while adding, so that film forming agent is evenly spread in solvent；
Step F, water soluble acrylic acid is added in reaction kettle, it is stirring while adding, so that water soluble acrylic acid is evenly spread to
To get finished product in solvent.
Embodiment 3.
The dedicated mould release of a kind of milling train of the invention, the raw material including following mass percent：
A kind of preparation method of the dedicated mould release of milling train, including following procedure of processing：
Step A, the material that formula ratio is weighed according to formula, is placed individually into different containers；
Step B, solvent is added in reaction kettle, aqueous polyethylene wax is then added, it is stirring while adding, so that aqueous poly-
Ethylene waxes are evenly spread in solvent；
Step C, water-borne wax is added in reaction kettle, it is stirring while adding, so that water-borne wax is evenly spread in solvent；
Step D, aqueous silicon is added in reaction kettle, it is stirring while adding, so that aqueous silicon is evenly spread in solvent；
Step E, film forming agent is added in reaction kettle, it is stirring while adding, so that film forming agent is evenly spread in solvent；
Step F, water soluble acrylic acid is added in reaction kettle, it is stirring while adding, so that water soluble acrylic acid is evenly spread to
To get finished product in solvent.
Embodiment 4.
The dedicated mould release of a kind of milling train of the invention, the raw material including following mass percent：
A kind of preparation method of the dedicated mould release of milling train, including following procedure of processing：
Step A, the material that formula ratio is weighed according to formula, is placed individually into different containers；
Step B, solvent is added in reaction kettle, aqueous polyethylene wax is then added, it is stirring while adding, so that aqueous poly-
Ethylene waxes are evenly spread in solvent；
Step C, water-borne wax is added in reaction kettle, it is stirring while adding, so that water-borne wax is evenly spread in solvent；
Step D, aqueous silicon is added in reaction kettle, it is stirring while adding, so that aqueous silicon is evenly spread in solvent；
Step E, film forming agent is added in reaction kettle, it is stirring while adding, so that film forming agent is evenly spread in solvent；
Step F, water soluble acrylic acid is added in reaction kettle, it is stirring while adding, so that water soluble acrylic acid is evenly spread to
To get finished product in solvent.
Embodiment 5.
The dedicated mould release of a kind of milling train of the invention, the raw material including following mass percent：
A kind of preparation method of the dedicated mould release of milling train, including following procedure of processing：
Step A, the material that formula ratio is weighed according to formula, is placed individually into different containers；
Step B, solvent is added in reaction kettle, aqueous polyethylene wax is then added, it is stirring while adding, so that aqueous poly-
Ethylene waxes are evenly spread in solvent；
Step C, water-borne wax is added in reaction kettle, it is stirring while adding, so that water-borne wax is evenly spread in solvent；
Step D, aqueous silicon is added in reaction kettle, it is stirring while adding, so that aqueous silicon is evenly spread in solvent；
Step E, film forming agent is added in reaction kettle, it is stirring while adding, so that film forming agent is evenly spread in solvent；
Step F, water soluble acrylic acid is added in reaction kettle, it is stirring while adding, so that water soluble acrylic acid is evenly spread to
To get finished product in solvent.
Embodiment 6.
The dedicated mould release of a kind of milling train of the invention, the raw material including following mass percent：
A kind of preparation method of the dedicated mould release of milling train, including following procedure of processing：
Step A, the material that formula ratio is weighed according to formula, is placed individually into different containers；
Step B, solvent is added in reaction kettle, aqueous polyethylene wax is then added, it is stirring while adding, so that aqueous poly-
Ethylene waxes are evenly spread in solvent；
Step C, water-borne wax is added in reaction kettle, it is stirring while adding, so that water-borne wax is evenly spread in solvent；
Step D, aqueous silicon is added in reaction kettle, it is stirring while adding, so that aqueous silicon is evenly spread in solvent；
Step E, film forming agent is added in reaction kettle, it is stirring while adding, so that film forming agent is evenly spread in solvent；
Step F, water soluble acrylic acid is added in reaction kettle, it is stirring while adding, so that water soluble acrylic acid is evenly spread to
To get finished product in solvent.
Finally it should be noted that the above embodiments are merely illustrative of the technical solutions of the present invention, rather than the present invention is protected
The limitation of range is protected, although explaining in detail referring to preferred embodiment to the present invention, those skilled in the art are answered
Work as understanding, it can be with modification or equivalent replacement of the technical solution of the present invention are made, without departing from the reality of technical solution of the present invention
Matter and range.
Claims (3)
1. a kind of dedicated mould release of milling train, it is characterised in that：Raw material including following mass percent：
The solvent is pure water；
The film forming agent is polyvinyl alcohol；
Aqueous silicon, that is, the aqueous silica sol is the polymer containing the special silicone resin of polyurethane and other auxiliary agents, is one group and self hands over
The material of connection type；
The preparation method of the mould release, including following procedure of processing：
Step A, the material that formula ratio is weighed according to formula, is placed individually into different containers；
Step B, solvent is added in reaction kettle, aqueous polyethylene wax is then added, it is stirring while adding, so that aqueous polyethylene
Wax is evenly spread in solvent；
Step C, water-borne wax is added in reaction kettle, it is stirring while adding, so that water-borne wax is evenly spread in solvent；
Step D, aqueous silicon is added in reaction kettle, it is stirring while adding, so that aqueous silicon is evenly spread in solvent；
Step E, film forming agent is added in reaction kettle, it is stirring while adding, so that film forming agent is evenly spread in solvent；
Step F, water soluble acrylic acid is added in reaction kettle, it is stirring while adding, so that water soluble acrylic acid evenly spreads to solvent
In to get finished product.
2. the dedicated mould release of a kind of milling train according to claim 1, it is characterised in that：Original including following mass percent
Material：
3. the dedicated mould release of a kind of milling train according to claim 1, it is characterised in that：Original including following mass percent
Material：