CN105969367B - 一种预拌高强度水泥土 - Google Patents

一种预拌高强度水泥土 Download PDF

Info

Publication number
CN105969367B
CN105969367B CN201610314044.0A CN201610314044A CN105969367B CN 105969367 B CN105969367 B CN 105969367B CN 201610314044 A CN201610314044 A CN 201610314044A CN 105969367 B CN105969367 B CN 105969367B
Authority
CN
China
Prior art keywords
soil
cement
sand
mix
high strength
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610314044.0A
Other languages
English (en)
Other versions
CN105969367A (zh
Inventor
王继忠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BEIJING PUISSANT GEOTECHNICAL ENGINEERING Co Ltd
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610314044.0A priority Critical patent/CN105969367B/zh
Publication of CN105969367A publication Critical patent/CN105969367A/zh
Priority to PCT/CN2017/000291 priority patent/WO2017193607A1/zh
Application granted granted Critical
Publication of CN105969367B publication Critical patent/CN105969367B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本申请涉及一种预拌高强度水泥土。其通过在施工现场，将土体取出并掺入水泥、粉煤灰、砂和适量的水，利用机械充分拌合均匀，得到具有可泵送的流动性的高强度水泥土。该水泥土具有高强度和适于泵送施工的流动性，不仅施工速度快，而且形成的水泥土强度高，质量可控，成本低，适用范围广泛，环境友好，是一种非常好的施工材料。

Description

一种预拌高强度水泥土
技术领域
本发明涉及一种预拌高强度水泥土。
背景技术
在各类工程施工过程中，往往会遇到改良土体，加固土体或者针对特定部位土体进行施工作业。如何最有效的改善土体性能以满足施工需要是当前岩土工程领域面临的重大课题。从业者进行了多方的尝试，其思路往往是通过混凝土等材料替换土体，造成施工成本高，施工速度慢；或者在土体中掺加入水泥等固化剂，通过在原位处的搅拌使其与土体结合以提高强度。但是，这种原位拌合往往由于缺乏流动空间，或者机械设备等原因拌合不均匀，而导致水泥土强度较低。
发明内容
为解决上述问题，本申请发明一种预拌高强度水泥土，其通过在施工现场，将土体取出并掺入水泥、粉煤灰、砂和适量的水，利用机械充分拌合均匀，得到具有可泵送的流动性的高强度水泥土。其中，土、水泥、粉煤灰、砂的重量比为3～8∶1∶1～2∶1～3。拌合均匀后的水泥土塌落度为8～20cm。水泥土硬化后强度为2～10MPa。其中的水泥能够以粘土固化剂代替。在砂土当中可以减少甚至不加砂。拌合时根据土质和设计要求加入混凝土外加剂。
该水泥土具有高强度和适于泵送施工的流动性，不仅施工速度快，而且形成的水泥土强度高，质量可控，成本低，适用范围广泛，环境友好，是一种非常好的施工材料。
具体实施方式
在淤泥土现场进行水泥土拌合，按照淤泥土、水泥、粉煤灰、砂的重量比为4.5：1：1.2：2的比例配置水泥土，并向其中加入适量水，使得最终拌合均匀的水泥土的塌落度为15cm，水泥土中水泥标号为42.5，水泥土硬化后的强度为4.2MPa。
在粉质土现场进行水泥土拌合，按照粉土、水泥、粉煤灰、砂的重量比为5：1：1.5：2.5的比例配置水泥土，并向其中加入适量水，使得最终拌合均匀的水泥土的塌落度为10cm，水泥土中水泥标号为 42.5，水泥土硬化后的强度为5.5MPa。
在黏土现场进行水泥土拌合，按照黏土、水泥、粉煤灰、砂的重量比为4：1：1.8：3的比例配置水泥土，并向其中加入适量水，使得最终拌合均匀的水泥土的塌落度为8cm，水泥土中水泥标号为 32.5，水泥土硬化后的强度为5.1MPa。
在砂土现场进行水泥土拌合，按照砂土、水泥、粉煤灰的重量比为5：1：1的比例配置水泥土，并向其中加入适量水，使得最终拌合均匀的水泥土的塌落度为16cm，水泥土中水泥标号为 42.5，水泥土硬化后的强度为6.9MPa。

Claims (5)

1.一种预拌高强度水泥土，其特征在于，通过在施工现场，将土体掺入水泥、粉煤灰、砂和适量的水，利用机械充分拌合均匀，得到具有流动性的高强度水泥土，拌合均匀后的水泥土的塌落度为8～20cm。
2.如权利要求1所述的水泥土，其特征在于，拌合时土、水泥、粉煤灰、砂的重量比为3～8∶1∶1～2∶1～3。
3.如权利要求1或2所述的水泥土，其特征在于，水泥土硬化后的强度为2～10MPa。
4.如权利要求1～3之一所述的水泥土，其特征在于，其中的水泥能够以粘土固化剂代替，当土为砂土时，拌合时少加砂或者不加砂。
5.如权利要求1所述的水泥土，其特征在于，拌合时根据土质和设计要求加入混凝土外加剂。
CN201610314044.0A 2016-05-13 2016-05-13 一种预拌高强度水泥土 Active CN105969367B (zh)