CN105969086B - Aqueous anti-stick coating and its application - Google Patents
Aqueous anti-stick coating and its application Download PDFInfo
- Publication number
- CN105969086B CN105969086B CN201610598888.2A CN201610598888A CN105969086B CN 105969086 B CN105969086 B CN 105969086B CN 201610598888 A CN201610598888 A CN 201610598888A CN 105969086 B CN105969086 B CN 105969086B
- Authority
- CN
- China
- Prior art keywords
- stick coating
- parts
- aqueous anti
- titanium
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of coating for preventing from bonding between metal, and in particular to a kind of aqueous anti-stick coating and its application in titanium ingot preparation process.The aqueous anti-stick coating of the present invention, contains following parts by weight ingredient: 50~150 parts of Watery film-fomer, 400~450 parts of Al powder, and Al2O3400~450 parts of powder, 0~50 part of talcum powder.Coating of the present invention can guarantee that titanium tube in 900 DEG C of rollings or perforation procedure, does not occur bonding with steel equipment roll or capstan winch and reacts, and improve the lumber recovery and production efficiency of titanium processing；Simple process, easy to operate, coating is environment friendly and pollution-free, and preparation method is simple.
Description
Technical field
The present invention relates to a kind of coating for preventing from bonding between metal, and in particular to a kind of aqueous anti-stick coating and its in titanium
Application in ingot preparation process.
Background technique
Domestic manufacturer is applied without report using high temperature resistant titanium-steel anti-stick using during titanium ingot round billet production titanium tube at present
Layer；900 DEG C of titanium ingot round billet keeps the temperature 4h or more in heating furnace, could release heating furnace, carries out the rolling work of titanium tube.Due to titanium
And its with steel rolling equipment, roller-way and rolling capstan winch " viscous titanium " phenomenon is occurring for alloy after 900 DEG C of heat preservation 4h of high temperature, this
Titanium tube surface is set " misrun " phenomenon of different depth occur, due to being rotation perforation, rolling when rolling titanium tube, titanium base is in height
Drilling/rolling is carried out in fast rotation process, due to titanium-based titanium alloy high-temperature characteristic effect, is easy to be deposited with iron existing
As notably producing TiFe phase.If titanium tube Surface Creation TiFe, which meets, seriously affects titanium surface mechanical properties and tissue, make
Titanium tube brought in following process and use process various defects, loss, it is not corrosion-resistant the defects of problem；In addition, due to " equipment
Viscous titanium " causes to want first grinding apparatus that could roll subsequent titanium base again in the subsequent operation of rolling.It is unable to continuous rolling titanium tube
Or titanium product, waste a large amount of time and energy consumption；Meanwhile dimension of inner and outer diameters precision and surface quality to guarantee titanium tube, state
Interior producer is all to be carried out machining, lose in this way it is larger, due to titanium ingot be by titanium sponge react make, by titanium tube,
Outer portion machines away, and seriously affects the cost and lumber recovery of titanium, therefore carries out the protection work of high temperature resistant titanium-steel anti-stick coating
It is highly desirable.
The prior art is all to be sprayed on titanium ingot surface before titanium ingot is made annealing treatment, will to each titanium ingot surface
Spray treatment is carried out, along with coating needs certain time dry after spraying, technique, which is prepared, just becomes complicated, preparation time
It is especially long, it is unable to serialization and efficiently produces.And in the operation of rolling of titanium tube, due to the deformation of titanium ingot, sprayed in titanium ingot surface
The coating is ineffective to prevent titanium-steel bonding.If the coating is directly sprayed at rolling capstan winch surface, due to capstan winch and titanium
The material of ingot is different, and film forming and adhesion effect are poor, can not prevent titanium-steel bonding well.
Therefore, to solve the above-mentioned problems, need a kind of simple process, energy conservation and environmental protection, can with serialization, efficiently prepare titanium
Defect loss and production cost is effectively reduced, moreover it is possible to prevent the high temperature resistant anti-stick coating of equipment damage in pipe.
Summary of the invention
Technical problem to be solved by the invention is to provide one kind in the titanium tube operation of rolling, it is possible to reduce titanium tube surface lacks
It falls into, reduces production cost, improve titanium tube surface quality, coating can be bonded with the anti-titanium of the aqueous high-temperature-resistant of continuous production-steel.
The aqueous anti-stick coating of the present invention, contains following parts by weight ingredient: 50~150 parts of Watery film-fomer, Al powder 400~
450 parts, Al2O3400~450 parts of powder, 0~50 part of talcum powder.
Further, technical solution more preferably, above-mentioned aqueous anti-stick coating, contains following parts by weight ingredient:
50~150 parts of Watery film-fomer, 400~450 parts of Al powder, Al2O3400~450 parts of powder, 10~50 parts of talcum powder；Further preferably
Following parts by weight ingredient: 100 parts of Watery film-fomer, 400 parts of Al powder, Al2O3450 parts of powder, 50 parts of talcum powder.
Further, technical solution more preferably, above-mentioned aqueous anti-stick coating, also containing following parts by weight at
Point: 1~2 part of curing agent, 0.5~1 part of dispersing agent, 1~5 part of water；Further preferably following parts by weight ingredient: 1 part of curing agent, point
0.5 part of powder, 5 parts of water.
Further, technical solution more preferably, above-mentioned aqueous anti-stick coating, preferably by following parts by weight ingredient
Composition: 50~150 parts of Watery film-fomer, 400~450 parts of Al powder, Al2O3350~400 parts of powder, 10~50 parts of talcum powder, solidification
1~2 part of agent, 0.5~1 part of dispersing agent, 1~5 part of water；More preferably it is made of following parts by weight ingredient: 100 parts of Watery film-fomer,
400 parts of Al powder, Al2O3450 parts of powder, 50 parts of talcum powder, 1 part of curing agent, 0.5 part of dispersing agent, 5 parts of water.
Above-mentioned aqueous anti-stick coating, wherein the Watery film-fomer is epoxy resin, aqueous polyurethane paint, aqueous acrylamide
At least one of yogurt shellac varnish, Water-borne alkyd coating.
Above-mentioned aqueous anti-stick coating, wherein the curing agent is SiO2, waterglass, Al2(HPO4)3At least one of,
Preferably SiO2；The dispersing agent is at least one of polyvinyl alcohol, hydrolyzed maleic anhydride, barium stearate, preferably poly- second
Enol.
Further, technical solution more preferably, above-mentioned aqueous anti-stick coating, wherein the aqueous anti-stick applies
The pH value of material is 7.5~9.5；Solid content is 85~90%, preferably 87%.
The present invention also provides a kind of application of aqueous anti-stick coating in titanium tube rolling.
Aqueous anti-stick coating is coated in by application of the above-mentioned aqueous anti-stick coating in titanium tube rolling at room temperature
Steel equipment surface, roller surface or capstan winch surface form the film layer of 0.2~0.4mm thickness；Preferably 0.3mm.
Application of the above-mentioned aqueous anti-stick coating in titanium tube rolling, using pneumatic spraying, airless spraying or manual brush
The mode of painting is coated.
Compared with the prior art, the present invention also has the following beneficial effects:
(1) coating of the present invention can guarantee titanium tube 900 DEG C rolling or perforation procedure in, not with steel equipment roll or capstan winch
Bonding reaction occurs, improves the lumber recovery and production efficiency of titanium processing；
(2) present invention can be set using simple production process, easy to operate equipped with pneumatic spraying, airless spraying and brushing
It is used on standby production line；
(3) this product is aqueous, environmental protective high temperature resistant anti-stick coating, does not contain the nocuousness limited in RoHS mass in coating
Element, meanwhile, this product is volatilized without noxious material in air, does not influence environmentally friendly effect of construction environment etc.；
(4) extemporaneous preparation when the aqueous anti-stick coating of the present invention can be used, prepares period, simple possible；It can also be with
After preparing production, at room temperature, coating stabilization shelf-stability be can reach 6 months or more.
Specific embodiment
The aqueous anti-stick coating of the present invention, contains following parts by weight ingredient: 50~150 parts of Watery film-fomer, Al powder 400~
450 parts, Al2O3400~450 parts of powder, 0~50 part of talcum powder.
Further, technical solution more preferably, above-mentioned aqueous anti-stick coating, contains following parts by weight ingredient:
50~150 parts of Watery film-fomer, 400~450 parts of Al powder, Al2O3400~450 parts of powder, 10~50 parts of talcum powder；Further preferably
Following parts by weight ingredient: 100 parts of Watery film-fomer, 400 parts of Al powder, Al2O3450 parts of powder, 50 parts of talcum powder.
Further, technical solution more preferably, above-mentioned aqueous anti-stick coating, also containing following parts by weight at
Point: 1~2 part of curing agent, 0.5~1 part of dispersing agent, 1~5 part of water；Further preferably following parts by weight ingredient: 1 part of curing agent, point
0.5 part of powder, 5 parts of water.
Further, technical solution more preferably, above-mentioned aqueous anti-stick coating, preferably by following parts by weight ingredient
Composition: 50~150 parts of Watery film-fomer, 400~450 parts of Al powder, Al2O3350~400 parts of powder, 10~50 parts of talcum powder, solidification
1~2 part of agent, 0.5~1 part of dispersing agent, 1~5 part of water；More preferably it is made of following parts by weight ingredient: 100 parts of Watery film-fomer,
400 parts of Al powder, Al2O3450 parts of powder, 50 parts of talcum powder, 1 part of curing agent, 0.5 part of dispersing agent, 5 parts of water.
Above-mentioned aqueous anti-stick coating, wherein the Watery film-fomer is epoxy resin, aqueous polyurethane paint, aqueous acrylamide
At least one of yogurt shellac varnish, Water-borne alkyd coating.
Above-mentioned aqueous anti-stick coating, wherein the curing agent is SiO2, waterglass, Al2(HPO4)3At least one of,
Preferably SiO2；The dispersing agent is at least one of polyvinyl alcohol, hydrolyzed maleic anhydride, barium stearate, preferably poly- second
Enol.
Further, technical solution more preferably, above-mentioned aqueous anti-stick coating, wherein the aqueous anti-stick applies
The pH value of material is 7.5~9.5；Solid content is 85~90%, preferably 87%, can guarantee that rolling equipment surface is formed uniformly in this way
High-temperature adhesion resistant knot protective film layer.
The present invention also provides a kind of application of aqueous anti-stick coating in titanium tube rolling.
Aqueous anti-stick coating is coated in by application of the above-mentioned aqueous anti-stick coating in titanium tube rolling at room temperature
Steel equipment surface, roller surface or capstan winch surface form the film layer of 0.2~0.4mm thickness；Preferably 0.3mm.When film layer is adhered to
When amount is less than 0.20mm, in rolling or perforation procedure, the rotation of titanium ingot pastes and coating adhesion amount thickness is caused to gradually decrease, institute
It to guarantee to have enough coating layer thicknesses, prevents from all being sticked out by titanium tube, cannot get sufficient high temperature oxidation resisting protection.If film layer
When adhesion amount is more than 0.40mm, cost is increased.
Application of the above-mentioned aqueous anti-stick coating in titanium tube rolling, using pneumatic spraying, airless spraying or manual brush
The mode of painting carry out be coated in steel equipment surface, roller surface or capstan winch surface after, the film layer of formation at room temperature, 5~
Rapid curing in 10min；Since solid part is high, phenomena such as being not in film layer trickling, sagging, coating adhesion is very good, nothing
By being under wet film or when dry film, coating adhesion can meet the needs of titanium ingot roller-way bobbing machine friction, be not in apply
Layer scaling or picking phenomenon；Coating method, drying means etc. are not particularly limited, coating method can be according to live practical
Situation needs to carry out corresponding form of construction work.
The preparation method of the aqueous anti-stick coating of the present invention can use various sides commonly used in the art without particular/special requirement
Method can matching while using as long as each component is uniformly mixed.But the present inventor has found under study for action, it is preferred to use
Following method prepares aqueous anti-stick coating, and each component can be made to mix more evenly.Method particularly includes: first by aqueous at
Film is mixed with water and is diluted, and then under stiring, is slowly added to aluminium powder, iron powder, ferric oxide powder and aluminum oxide
Then powder adds curing agent, stir evenly, and adds dispersing agent, stirring is in uniform and stable phase.
In solidification process, it is only necessary to the moisture for being attached to coating surface is removed, because leading without adding any promotor again
Wanting curing mode is spontaneous curing, and in order to save curing time, the methods of heated-air drying or induction heating, coating also can be used
After solidification, coating is not in picking and crack phenomenon.
Coating high temperature resistant principle prepared by the present invention are as follows: when temperature reaches 900 DEG C, organic coating starts slowly burned
Fall, but Fe starts slowly to melt softening, it at this time can be the Al powder and Al in coating2O3Powder is fixed on roll or capstan winch surface, rises
To heat-insulated effect；Alloying reaction occurs for Al powder and Ti in coating, forms TiAl3Alloy-layer, this layer of substance is very fine and close,
The substances such as body titanium and extraneous (steel) ferro element can be completely cut off, bonding reaction occurs, have the function that titanium-steel bonding occurs for prevention and treatment.
The temperature that the anti-titanium of high temperature resistant-steel bonding coating uses is not particularly limited, but molten due to inorganic agent of the invention
Agent is water, guarantees the temperature condition that water does not freeze and vaporizes, uses at normal temperature.
A kind of anti-titanium of high temperature resistant of the present invention-steel bonds coating, is painted on rolling capstan winch surface online, can consolidate rapidly
Change, form self-drying type coating, which can guarantee titanium tube under 900 DEG C of high temperature, and surface does not occur bonding with steel surface and generates
TiFe phase can be effectively reduced production cost and improve productivity effect, more main raising Product Precision size and surface quality；This
The corresponding coating process technology provided with good economic efficiency, social benefit and wide popularization and application foreground are provided.
A specific embodiment of the invention is further described below with reference to embodiment, is not therefore limited the present invention
System is among the embodiment described range.
Embodiment 1
Aqueous anti-stick coating is prepared according to each raw material in table 1 and its weight proportion:
The raw material and its proportion of the aqueous anti-stick coating of table 1
Wherein, K1~K4 is experimental group, and D1~D2 is control group, and a blank control group D3 is separately arranged and (does not apply coating
Direct Rolling), and wherein Watery film-fomer is epoxy resin (solid content 50%)；Curing agent is SiO2, dispersing agent is poly- second
Enol.Aqueous anti-stick coating pH value prepared by the present invention is 7.5~9.5；Solid content is 85~90%.
Preparation method are as follows: at normal temperatures and pressures, by Watery film-fomer, Al powder, talcum powder, Al2O3Powder is added to container
In, it is stirred continuously in adition process, is stirring evenly and then adding into curing agent, dispersing agent and water, stirs evenly, to solution in uniformly steady
Fixed phase is to get aqueous anti-stick coating.
Aqueous anti-stick coating prepared by above-mentioned each group is by the way of pneumatic spraying, airless spraying or manual brushing
It carries out after being coated in steel equipment surface, roller surface or capstan winch surface, spontaneously dries at room temperature, solidifies 10~15min,
Obtain the film layer with a thickness of 0.2~0.4mm.Titanium tube rolling is carried out at 900 DEG C.The titanium tube surface quality obtained after rolling is good
Good, titanium tube and roll, capstan winch etc. are not adhered, and specific comparative situation is as follows:
The aqueous anti-stick coating of table 2 and control group test performance
From Table 2, it can be seen that using the coating coating equipment of embodiment K1~K4, the titanium tube surface matter that is obtained after rolling
Amount is good, and titanium tube and roll, capstan winch etc. hardly bond.It is not coated by the roll or strand of any coating (i.e. blank control group D3)
Disk, the titanium tube obtained after rolling, titanium tube surface defect is serious, and equipment also has a degree of viscous titanium, ability after needing to polish
It continues to use.Using the coating coating equipment of D1 and D2, the titanium tube surface defect rate after rolling is still higher, cannot prevent well
Only titanium steel bonds.
10,000 tons of production capacities are produced in design per year, are calculated with 1.5 tons of each titanium ingot (semifinished product), to be produced 6300 or so titaniums every year
There is titanium steel bonding 5mm~20mm depth calculation with each titanium ingot in billet, and each titanium ingot will machine away 100~200 kilograms, with
80000 yuan/ton of titanium ingot calculating, each titanium ingot lose between 8000~16000 yuan because gluing titanium cutting tip, meanwhile, also to spend
Take a large amount of human and material resources to be cut, it is additional to increase production cost and production time, and use this technology, will for titanium tube and
A large amount of production cost is saved in the production of other titanium alloy products, in terms of in each titanium ingot operation of rolling using 2~5kg of coating
It calculates, every coating price is calculated by 200,000/ton, and the new returns of this technology are seen below shown in formula:
The output of the annual titanium ingot of W-: being calculated with 10,000 tons, about produces 6300 titanium ingots every year；
The each titanium ingot of A- is because gluing titanium-steel layer problem cutting amount: pressing 50Kg calculating/titanium ingot；
The cost of P1- titanium ingot: 80 yuan/Kg；
W1- sprays the consumption of high temperature resistant anti-stick coating, 3Kg/ ingot；
P2- high temperature resistant anti-stick coating price per ton: it is calculated by 200 yuan/Kg；
The new returns that Y- uses this technology to generate every year:
Then:
Y=(P1 × A-W1 × P2) × W
=(4000-600) × 6300
=2142 (ten thousand yuan)
As it can be seen that coating provided by the invention is with good economic efficiency, social benefit and wide popularization and application foreground.
Claims (10)
1. aqueous anti-stick coating, it is characterised in that: be made of following parts by weight ingredient: 50~150 parts of Watery film-fomer, Al powder
400~450 parts, Al2O3350~400 parts of powder, 10~50 parts of talcum powder, 1~2 part of curing agent, 0.5~1 part of dispersing agent, water 1~5
Part；Wherein, the aqueous anti-stick coating is coated in steel equipment surface, roller surface or capstan winch surface.
2. aqueous anti-stick coating according to claim 1, it is characterised in that: the Watery film-fomer is epoxy resin, water
Property polyurethane paint, Aqueous acrylic latex's paint, at least one of Water-borne alkyd coating.
3. aqueous anti-stick coating according to claim 1 or claim 2, it is characterised in that: the curing agent is SiO2, waterglass,
Al2(HPO4)3At least one of；The dispersing agent is at least one of polyvinyl alcohol, hydrolyzed maleic anhydride, barium stearate.
4. aqueous anti-stick coating according to claim 3, it is characterised in that: the curing agent is SiO2；The dispersing agent is
Polyvinyl alcohol.
5. aqueous anti-stick coating according to claim 1 or claim 2, it is characterised in that: the pH value of the aqueous anti-stick coating
It is 7.5~9.5；Solid content is 85~90%.
6. aqueous anti-stick coating according to claim 5, it is characterised in that: solid content 87%.
7. application of any one of the claim 1~6 aqueous anti-stick coating in titanium tube rolling.
8. applying according to claim 7, it is characterised in that: at room temperature, aqueous anti-stick coating is set coated in steel
Standby surface, roller surface or capstan winch surface, form the film layer of 0.2~0.4mm thickness.
9. applying according to claim 8, it is characterised in that: form the film layer of 0.3mm thickness.
10. applying according to claim 7, it is characterised in that: using the side of pneumatic spraying, airless spraying or manual brushing
Formula is coated.