CN105968920A - Damp-proof emulsion paint preparation method - Google Patents
Damp-proof emulsion paint preparation method Download PDFInfo
- Publication number
- CN105968920A CN105968920A CN201610358317.1A CN201610358317A CN105968920A CN 105968920 A CN105968920 A CN 105968920A CN 201610358317 A CN201610358317 A CN 201610358317A CN 105968920 A CN105968920 A CN 105968920A
- Authority
- CN
- China
- Prior art keywords
- parts
- emulsion paint
- kilograms
- deionized water
- defoamer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a damp-proof emulsion paint preparation method, and relates to the technical field of chemical industry. The damp-proof emulsion paint preparation method comprises the following steps that 1, two thirds by weight of deionized water, one third by weight of defoaming agent, a dispersing agent, bentonite, titanium dioxide and ground calcium carbonate are added into a stirring machine, and stirring is conducted at the rotating speed of 2,000 revolutions/minute for 35 min; 2, AMP95, a coalescing agent, propylene glycol, preservative and the deforming agent left in the first step are added into the stirring machine in the first step, and stirring is conducted at the rotating speed of 800 revolutions/minute for 12 min to 20 min; 3, vinyl acetate, superabsorbent resin and deionized water left in the first step are added into the stirring machine in the second step, stirring is conducted at the rotating speed of 800 revolutions/minute for 30 min, and damp-proof emulsion paint is obtained. According to the damp-proof emulsion paint preparation method, the problem that existing emulsion paint is poor in damp-proof function can be solved.
Description
Technical field
The present invention relates to chemical technology field, the preparation method of a kind of moistureproof emulsion paint for wall.
Background technology
Raising along with people's quality of life, house decoration increasingly obtains the attention of people, emulsion paint is indispensable material in house decoration, existing emulsion paint moisture-proof function is poor, between the March to April that south China especially Guangxi is annual, wet weather is constantly, air humidity is big, the globule or the flowing water of cohesion often occur on the family brush wall of emulsion paint, not only cause the most pleasant Damage by Short Circuit also resulting in household electrical appliance and the household supplies of human body, the mouldy damage of furniture, therefore provide a kind of nontoxic, strong and environment protection damp-proof the emulsion paint of caking ability is the problem that those skilled in the art need solution badly.
Summary of the invention
The technical problem to be solved is to provide a kind of moistureproof emulsion paint preparation method, and it can solve the problem that existing emulsion paint moisture-proof function is poor.
In order to solve the problems referred to above, the technical scheme is that this moistureproof emulsion paint preparation method, use the raw material of following weight portion to make:
Vinyl acetate 80 parts～130 parts, High hydrophilous resin 2.5 parts～5 parts, bentonite 25 parts～50 parts, titanium dioxide 25 parts～50 parts, triple superphosphate 30 parts～65 parts, AMP95 0.7 part～1.5 parts, dispersant 2.5 parts～5.4 parts, defoamer 0.5 part～1.5 parts, coalescents 8 parts～10 parts, propylene glycol 2 parts～5 parts, preservative 0.5 part～1 part, deionized water 230 parts～270 parts；
Comprise the steps:
A. the deionized water of 2/3rds weight portions, the defoamer of 1/3rd weight portions, dispersant, bentonite, titanium dioxide and triple superphosphate are added in blender, stir 35 minutes with the rotating speeds of 2000 revs/min；
B. in the blender of step A, add the remaining defoamer of AMP95, coalescents, propylene glycol, preservative and step A, then stir 12 minutes～20 minutes with the rotating speed of 800 revs/min；
C. in the blender of step B, add the remaining deionized water of vinyl acetate, High hydrophilous resin and step A, then stir 30 minutes with the rotating speed of 800 revs/min；Obtain.
In technique scheme, more specifically scheme is it may also is that vinyl acetate 90 parts～120 parts, High hydrophilous resin 3 parts～4.5 parts, bentonite 30 parts～40 parts, titanium dioxide 30 parts～40 parts, triple superphosphate 40 parts～55 parts, AMP950.9 part～1.2 parts, dispersant 3 parts～5 parts, defoamer 0.8 part～1.1 parts, coalescents 8.5 parts～9.5 parts, propylene glycol 3 parts～4.5 parts, preservative 0.7 part～0.9 part, deionized water 240 parts～260 parts.
Further: vinyl acetate 110 parts, High hydrophilous resin 4 parts, bentonite 35 parts, titanium dioxide 35 parts, triple superphosphate 50 parts, AMP951 part, dispersant 4 parts, defoamer 1 part, coalescents 9 parts, propylene glycol 4 parts, preservative 1 part, deionized water 250 parts.
Owing to using technique scheme, there is advantages that
1, owing to adding bentonite as inserts, can enrich paint film, increase covering power, give emulsion paint and be difficult to precipitation and good brushability, it also has stronger hygroscopicity and a cementability, not only natural environmental-protective and improve hygroscopicity and the cementability of emulsion paint；
2, owing to adding High hydrophilous resin, play the moisture absorption effect of space air, make room in wet weather keep being dried, not only make that human body sensory is pleasant also protects household electrical appliance and household supplies, being dried of furniture.
Detailed description of the invention
By embodiment, the present invention is described in further detail below:
Embodiment 1:
This moistureproof emulsion paint preparation method, uses the raw material of following weight to make:
Vinyl acetate 80 kilograms, High hydrophilous resin 2.5 kilograms, bentonite 25 kilograms, titanium dioxide 25 kilograms, triple superphosphate 30 kilograms, AMP95 0.7 kilogram, dispersant 2.5 kilograms, defoamer 0.5 kilogram, coalescents 8 kilograms, propylene glycol 2 kilograms, preservative 0.5 kilogram, deionized water 230 kilograms；
Comprise the steps:
A. 153 kilograms of deionized waters, 0.15 kilogram of defoamer, dispersant, bentonite, titanium dioxide and triple superphosphate are added in blender, stir 35 minutes with the rotating speeds of 2000 revs/min；
B. in the blender of step A, add AMP95, coalescents, propylene glycol, preservative and remaining defoamer, then stir 12 minutes with the rotating speed of 800 revs/min；
C. in the blender of step B, add the remaining deionized water of vinyl acetate, High hydrophilous resin and step A, again stir 30 minutes with the rotating speed of 800 revs/min；Obtain.
Embodiment 2:
This moistureproof emulsion paint preparation method, uses the raw material of following weight to make:
Vinyl acetate 130 kilograms, High hydrophilous resin 5 kilograms, bentonite 50 kilograms, titanium dioxide 50 kilograms, triple superphosphate 65 kilograms, AMP95 1.5 kilograms, dispersant 5.4 kilograms, defoamer 1.5 kilograms, coalescents 10 kilograms, propylene glycol 5 kilograms, preservative 1 kilogram, deionized water 270 kilograms；
Comprise the steps:
A. 180 kilograms of deionized waters, 0.5 kilogram of defoamer, dispersant, bentonite, titanium dioxide and triple superphosphate are added in blender, stir 35 minutes with the rotating speeds of 2000 revs/min；
B. in the blender of step A, add AMP95, coalescents, propylene glycol, preservative and the remaining defoamer of step A, then stir 20 minutes with the rotating speed of 800 revs/min；
C. in the blender of step B, add the remaining deionized water of vinyl acetate, High hydrophilous resin and step A, again stir 30 minutes with the rotating speed of 800 revs/min；Obtain.
Embodiment 3:
This moistureproof emulsion paint preparation method, uses the raw material of following weight to make:
Vinyl acetate 90 kilograms, High hydrophilous resin 3 kilograms, bentonite 30 kilograms, titanium dioxide 30 kilograms, triple superphosphate 40 kilograms, AMP950.9 kilogram, dispersant 3 kilograms, defoamer 0.8 kilogram, coalescents 8.5 kilograms, propylene glycol 3 kilograms, preservative 0.7 kilogram, deionized water 240 kilograms；
Comprise the steps:
A. 160 kilograms of deionized waters, 0.27 kilogram of defoamer, dispersant, bentonite, titanium dioxide and triple superphosphate are added in blender, stir 35 minutes with the rotating speeds of 2000 revs/min；
B. in the blender of step A, add AMP95, coalescents, propylene glycol, preservative and the remaining defoamer of step A, then stir 12 minutes with the rotating speed of 800 revs/min；
C. in the blender of step B, add the remaining deionized water of vinyl acetate, High hydrophilous resin and step A, again stir 30 minutes with the rotating speed of 800 revs/min；Obtain.
Embodiment 4
This moistureproof emulsion paint preparation method, uses the raw material of following weight to make:
Vinyl acetate 120 kg, High hydrophilous resin 4.5 kilograms, bentonite 40 kilograms, titanium dioxide 40 kilograms, triple superphosphate 55 kilograms, AMP951.2 kilogram, dispersant 5 kilograms, defoamer 1.1 kilograms, coalescents 9.5 kilograms, propylene glycol 4.5 kilograms, preservative 0.9 kilogram, deionized water 260 kilograms；
Comprise the steps:
A. by 173 kilograms of deionized waters, 0.36 kilogram of defoamer, dispersant, bentonite, titanium dioxide, triple superphosphate adds in blender, stirs 35 minutes with the rotating speeds of 2000 revs/min；
B. in the blender of step A, add AMP95, coalescents, propylene glycol, preservative and the remaining defoamer of step A, then stir 18 minutes with the rotating speed of 800 revs/min；
C. in the blender of step B, add the remaining deionized water of vinyl acetate, High hydrophilous resin and step A, again stir 30 minutes with the rotating speed of 800 revs/min；Obtain.
Embodiment 5
This moistureproof emulsion paint preparation method, uses the raw material of following weight to make:
Vinyl acetate 110 kilograms, High hydrophilous resin 4 kilograms, bentonite 35 kilograms, titanium dioxide 35 kilograms, triple superphosphate 50 kilograms, AMP951 kilogram, dispersant 4 kilograms, defoamer 1 kilogram, coalescents 9 kilograms, propylene glycol 4 kilograms, preservative 1 kilogram, deionized water 250 kilograms；
Comprise the steps:
A. 167 kilograms of deionized waters, 0.3 kilogram of defoamer, dispersant, bentonite, titanium dioxide and triple superphosphate are added in blender, stir 35 minutes with the rotating speeds of 2000 revs/min；
B. in the blender of step A, add AMP95, coalescents, propylene glycol, preservative and the remaining defoamer of step A, then stir 15 minutes with the rotating speed of 800 revs/min；
C. in the blender of step B, add the remaining deionized water of vinyl acetate, High hydrophilous resin and step A, again stir 30 minutes with the rotating speed of 800 revs/min；Obtain.
Claims (3)
1. a moistureproof emulsion paint preparation method, it is characterised in that: use the raw material of following weight portion to make:
Vinyl acetate 80 parts～130 parts, High hydrophilous resin 2.5 parts～5 parts, bentonite 25 parts～50 parts, titanium dioxide 25 parts～50 parts, triple superphosphate 30 parts～65 parts, AMP95 0.7 part～1.5 parts, dispersant 2.5 parts～5.4 parts, defoamer 0.5 part～1.5 parts,
Coalescents 8 parts～10 parts, propylene glycol 2 parts～5 parts, preservative 0.5 part～1 part, deionized water 230 parts～270 parts；
Comprise the steps:
A. the deionized water of 2/3rds weight portions, the defoamer of 1/3rd weight portions, dispersant, bentonite, titanium dioxide and triple superphosphate are added in blender, stir 35 minutes with the rotating speeds of 2000 revs/min；
B. in the blender of step A, add the remaining defoamer of AMP95, coalescents, propylene glycol, preservative and step A, then stir 12 minutes～20 minutes with the rotating speed of 800 revs/min；
C. in the blender of step B, add the remaining deionized water of vinyl acetate, High hydrophilous resin and step A, then stir 30 minutes with the rotating speed of 800 revs/min；Obtain.
Moistureproof emulsion paint preparation method the most according to claim 1, it is characterised in that: use the raw material of following weight portion to make:
Vinyl acetate 90 parts～120 parts, High hydrophilous resin 3 parts～4.5 parts, bentonite 30 parts～40 parts, titanium dioxide 30 parts～40 parts, triple superphosphate 40 parts～55 parts, AMP950.9 part～1.2 parts, dispersant 3 parts～5 parts, defoamer 0.8 part～1.1 parts,
Coalescents 8.5 parts～9.5 parts,
Propylene glycol 3 parts～4.5 parts, preservative 0.7 part～0.9 part, deionized water 240 parts～260 parts.
Moistureproof emulsion paint preparation method the most according to claim 1 and 2, it is characterised in that: use the raw material of following weight portion to make:
Vinyl acetate 110 parts, High hydrophilous resin 4 parts, bentonite 35 parts, titanium dioxide 35 parts, triple superphosphate 50 parts, AMP951 part, dispersant 4 parts,
Defoamer 1 part,
Coalescents 9 parts,
Propylene glycol 4 parts, preservative 1 part, deionized water 250 parts.