CN106554651A - A kind of moistureproof powder of lacquer putty for use on - Google Patents
A kind of moistureproof powder of lacquer putty for use on Download PDFInfo
- Publication number
- CN106554651A CN106554651A CN201510619954.5A CN201510619954A CN106554651A CN 106554651 A CN106554651 A CN 106554651A CN 201510619954 A CN201510619954 A CN 201510619954A CN 106554651 A CN106554651 A CN 106554651A
- Authority
- CN
- China
- Prior art keywords
- parts
- lacquer putty
- powder
- moistureproof
- moistureproof powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of powder of lacquer putty for use on, specifically a kind of for indoor moistureproof powder of lacquer putty for use on, belong to building material technical field.A kind of moistureproof powder of lacquer putty for use on, is made using the raw material of following weight portion：White cement：15-25 parts；Palygorskite clay：6-14 parts；Bagasse fibre：3-8 parts；Hydroxypropyl methyl cellulose：0.5-1 parts；High hydrophilous resin：4-8 parts；Bentonite：2-4 parts；Na-alginate：2-4 parts；Sodium chloride：0.5-1 parts；Ultramarine 0.6-0.9 parts.The moistureproof powder of lacquer putty for use on of the present invention, has the advantages that highly versatile, low cost, intensity height, water-tolerant, whiteness are high.
Description
Technical field
The present invention relates to a kind of powder of lacquer putty for use on, specifically a kind of for indoor moistureproof powder of lacquer putty for use on, belong to building material technical field.
Background technology
With the raising of people's quality of life, house decoration increasingly obtains the attention of people, powder of lacquer putty for use on is indispensable material in house decoration, using the raw materials such as Calcium Carbonate, Pulvis Talci, PVOH glue to make existing powder of lacquer putty for use on more, bad adhesion, it is important that moistureproof poor, easily go mouldy after time length, not only cause the not pleasant short circuit for also resulting in household electrical appliance of human body to burn out and household supplies, the mouldy damage of furniture.
The content of the invention
It is an object of the invention to solve the deficiency that existing nursing agent is unable to waterproof, there is provided a kind of caking property is strong, the powder of lacquer putty for use on that moisture effect is good.
A kind of moistureproof powder of lacquer putty for use on of the present invention is achieved through the following technical solutions：
A kind of moistureproof powder of lacquer putty for use on, is made using the raw material of following weight portion：
White cement：15-25 parts；Palygorskite clay：6-14 parts；Bagasse fibre：3-8 parts；Hydroxypropyl methyl cellulose：0.5-1 part；High hydrophilous resin：4-8 parts；Bentonite：2-4 parts；Na-alginate：2-4 parts；Sodium chloride：0.5-1 parts；Ultramarine 0.6-0.9 parts.
Preferably, white cement：18-22 parts；Palygorskite clay：8-12 parts；Bagasse fibre：5-7 parts；Hydroxypropyl methyl cellulose：0.6-0.8 parts；High hydrophilous resin：5-7 parts；Bentonite：2.5-3.5 parts；Na-alginate：2.5-3.5 parts；Sodium chloride：0.5-1 parts；Ultramarine 0.6-0.9 parts.
Further：White cement：20 parts；Palygorskite clay：10 parts；Bagasse fibre：6 parts；Hydroxypropyl methyl cellulose：0.7 part；High hydrophilous resin：6 parts；Bentonite：3 parts；Na-alginate：3 parts；Sodium chloride：08 part；0.75 part of ultramarine.
The moistureproof powder of lacquer putty for use on of the present invention, has the advantages that highly versatile, low cost, intensity height, water-tolerant, whiteness are high.
Specific embodiment
Form by the following examples, the above of the present invention is described in further detail again, but this scope for being interpreted as above-mentioned theme of the invention should not be only limitted to Examples below, all technologies realized based on the above of the present invention belong to the scope of the present invention.
Embodiment 1：A kind of moistureproof powder of lacquer putty for use on, is made using the raw material of following weight portion：
White cement：20 parts；Palygorskite clay：10 parts；Bagasse fibre：6 parts；Hydroxypropyl methyl cellulose：0.7 part；High hydrophilous resin：6 parts；Bentonite：3 parts；Na-alginate：3 parts；Sodium chloride：08 part；0.75 part of ultramarine.
Embodiment 2：A kind of moistureproof powder of lacquer putty for use on, is made using the raw material of following weight portion：
White cement：15 parts；Palygorskite clay：6 parts；Bagasse fibre：3 parts；Hydroxypropyl methyl cellulose：0.5
Part；High hydrophilous resin：4 parts；Bentonite：2 parts；Na-alginate：2
Part；Sodium chloride：0.5 part；0.6 part of ultramarine.
Embodiment 3：A kind of moistureproof powder of lacquer putty for use on, is made using the raw material of following weight portion：
White cement：25 parts；Palygorskite clay：14 parts；Bagasse fibre：8 parts；Hydroxypropyl methyl cellulose：1 part；High hydrophilous resin：8 parts；Bentonite：4 parts；Na-alginate：4 parts；Sodium chloride：1 part；0.9 part of ultramarine.
Claims (3)
1. a kind of moistureproof powder of lacquer putty for use on,
It is characterized in that：Made using the raw material of following weight portion：
White cement：15-25 parts；Palygorskite clay：6-14 parts；Bagasse fibre：3-8 parts；Hydroxypropyl methyl cellulose：0.5-1 part；High hydrophilous resin：4-8 parts；Bentonite：2-4 parts；Na-alginate：2-4 parts；Sodium chloride：0.5-1 parts；Ultramarine 0.6-0.9 parts.
2. a kind of moistureproof powder of lacquer putty for use on according to claim 1, it is characterised in that：Made using the raw material of following weight portion：White cement：18-22 parts；Palygorskite clay：8-12 parts；Bagasse fibre：5-7 parts；Hydroxypropyl methyl cellulose：0.6-0.8 parts；High hydrophilous resin：5-7 parts；Bentonite：2.5-3.5 parts；Na-alginate：2.5-3.5 parts；Sodium chloride：0.5-1 parts；Ultramarine 0.6-0.9 parts.
3. a kind of moistureproof powder of lacquer putty for use on according to claim 1 or claim 2, it is characterised in that：Made using the raw material of following weight portion：White cement：20 parts；Palygorskite clay：10 parts；Bagasse fibre：6 parts；Hydroxypropyl methyl cellulose：0.7 part；High hydrophilous resin：6 parts；Bentonite：3 parts；Na-alginate：3 parts；Sodium chloride：08 part；0.75 part of ultramarine.