CN105964898A - 一种粉煤灰铸造涂料 - Google Patents

一种粉煤灰铸造涂料 Download PDF

Info

Publication number
CN105964898A
CN105964898A CN201610549599.3A CN201610549599A CN105964898A CN 105964898 A CN105964898 A CN 105964898A CN 201610549599 A CN201610549599 A CN 201610549599A CN 105964898 A CN105964898 A CN 105964898A
Authority
CN
China
Prior art keywords
fly ash
coating
foundry coating
resin
foundry
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610549599.3A
Other languages
English (en)
Inventor
李水金
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610549599.3A priority Critical patent/CN105964898A/zh
Publication of CN105964898A publication Critical patent/CN105964898A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种粉煤灰铸造涂料，由粉煤灰，高铝矾土，锆英粉，树脂，助剂，酒精等组分混合制备而成。本发明的粉煤灰铸造涂料，经科学选材，使用了粉煤灰，高铝矾土，锆英粉为骨料，配以膨润土，羧甲基纤维素醚，淀粉醚等为悬浮剂，酚醛树脂为粘结剂，制备了性能优良的铸造涂料，同时还添加了一定量的可分散乳胶粉，有效地改善了涂料的铸造性能以及悬浮性，而且提高了涂层的抗剥落能力，保证了粉煤灰铸造涂料各项性能指标优异。

Description

一种粉煤灰铸造涂料
技术领域
本发明涉及涂料领域，具体涉及一种粉煤灰铸造涂料。
背景技术
铸造涂料是在铸件和铸型中间起阻挡隔离作用，达到防粘砂目的。消失模铸造又称实行铸造，是将与铸件尺寸形状相似的石蜡或泡沫模型粘结组合成模型簇，涂刷涂料并烘干后，埋在石英砂中震动造型，在负压下浇注，使模型气化，液体金属占据模型位置，凝固冷却后形成铸件的铸造方法。消失模铸造涂料的性能将直接影响铸件的外在和内在质量，涂料在消失模的浇注过程中要起到排气、支撑、保温和吸附泡沫液态残留物的作用，其中，良好的液态吸附性是消失模涂料较重要的一种性能，涂料具备该性能才能保证泡沫的残渣不会残留到铸件的内部和外表，从而保证铸件的质量。现有的消失模铸造涂料在一定程度上均存在具透气性、悬浮性，高温抗裂性差的问题，直接影响了铸件的质量。
发明内容
本发明目的在于，提供一种粉煤灰铸造涂料，本发明所采用的技术方案是：
一种粉煤灰铸造涂料，其特征在于，由以下组分按重量百分比混合制备而成：
粉煤灰 20-30份
高铝矾土 25-35份
锆英粉 10-20份
树脂 2-5份
助剂 2-8份
酒精 20-35份。
优选地，所述的树脂是酚醛树脂。
优选地，所述的助剂包括有机膨润土，羧甲基纤维素醚，淀粉醚，可再分散乳胶粉，消泡剂，聚乙烯醇缩丁醛。
本发明相对于现有技术的有益效果是：本发明的粉煤灰铸造涂料，经科学选材，使用了粉煤灰，高铝矾土，锆英粉为骨料，配以膨润土，羧甲基纤维素醚，淀粉醚等为悬浮剂，酚醛树脂为粘结剂，制备了性能优良的铸造涂料，同时还添加了一定量的可分散乳胶粉，有效地改善了涂料的铸造性能以及悬浮性，而且提高了涂层的抗剥落能力，保证了粉煤灰铸造涂料各项性能指标优异。
具体实施方式
以下将结合实施例对本发明的构思及产生的技术效果进行清楚、完整地描述，以充分地理解本发明的目的、特征和效果。显然，所描述的实施例只是本发明的一部分实施例，而不是全部实施例，基于本发明的实施例，本领域的技术人员在不付出创造性劳动的前提下所获得的其他实施例，均属于本发明保护的范围。
实施例1：一种粉煤灰铸造涂料，由以下组分按重量百分比混合制备而成：
粉煤灰 25份
高铝矾土 28份
锆英粉 16份
树脂 4份
助剂 5份
酒精 22份。
实施例2：一种粉煤灰铸造涂料，由以下组分按重量百分比混合制备而成：
粉煤灰 28份
高铝矾土 26份
锆英粉 12份
酚醛树脂 3份
有机膨润土 2份
羧甲基纤维素醚 0.3份
淀粉醚 0.2份
可再分散乳胶粉 0.5份
消泡剂 0.5份
聚乙烯醇缩丁醛 0.5份
酒精 27份。
以上对本发明的较佳实施方式进行了具体说明，但本发明创造并不限于所述实施例，熟悉本领域的技术人员在不违背本发明精神的前提下还可作出种种的等同变型或替换，这些等同的变型或替换均包含在本申请权利要求所限定的范围内。

Claims (3)

1.一种粉煤灰铸造涂料，其特征在于，由以下组分按重量百分比混合制备而成：
粉煤灰 20-30份
高铝矾土 25-35份
锆英粉 10-20份
树脂 2-5份
助剂 2-8份
酒精 20-35份。
2.根据权利要求1所述的粉煤灰铸造涂料，其特征在于，所述的树脂是酚醛树脂。
3.根据权利要求1所述的粉煤灰铸造涂料，其特征在于，所述的助剂包括有机膨润土，羧甲基纤维素醚，淀粉醚，可再分散乳胶粉，消泡剂，聚乙烯醇缩丁醛。
CN201610549599.3A 2016-07-13 2016-07-13 一种粉煤灰铸造涂料 Pending CN105964898A (zh)