CN105949775A - Printing clay and production method thereof - Google Patents
Printing clay and production method thereof Download PDFInfo
- Publication number
- CN105949775A CN105949775A CN201610357068.4A CN201610357068A CN105949775A CN 105949775 A CN105949775 A CN 105949775A CN 201610357068 A CN201610357068 A CN 201610357068A CN 105949775 A CN105949775 A CN 105949775A
- Authority
- CN
- China
- Prior art keywords
- parts
- minutes
- silicon dioxide
- silicone oil
- oleic acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides printing clay, which is characterized by being prepared from the following ingredients in parts by weight: 50 to 80 parts of silicon dioxide, 1 to 20 parts of silicone oil, 1 to 5 parts of boracic acid and 1 to 15 parts of oleic acid. The invention provides a production method of the printing clay. The production method comprises the following steps of (1) the silicone oil and the boracic acid are heated to be 100 to 120 DEG C and are then stirred and mixed for 10 to 20 minutes; (2) the oleic acid and the silicon dioxide are added into a mixture obtained in the first step, and the stirring is performed for 10 to 20 minutes; (3) the temperature is lowered to 80 to 100 DEG C, pigment is added, the mixture is stirred for 15 to 20 minutes for uniform mixing, and a finished product is obtained. The common powdery, light-weight and floppy silicon dioxide in the nature is used as a base material; the silicone oil, the boracic acid and the oleic acid are used as bonding agents; floppy light-weight color clay is manufactured under a certain process condition. Water does not need to be added in raw materials for regulation, so that the printing clay cannot become dry in the use process and can be conveniently and repeatedly used.
Description
Technical field
The present invention relates to color mud and the technical field of production method, particularly to printing mud and production method.
Background technology
Printing mud of the prior art generally uses water to add polyvinyl alcohol or resin, add various gently
Matter filler and adjuvant are to form the color mud of lightweight.Resin type coloured silk mud needs to control the wet of color mud with moisture content
Profit and plasticity, along with the evaporation of moisture content during being at play, color mud can gradually become dry hardening, needs
Again add moisture content just can reuse, in-convenience in use.
Summary of the invention
It is an object of the invention to provide a kind of lightweight, nontoxic, will not become dry, printing easy to use
Mud and production method.
According to an aspect of the invention, it is provided printing mud, it is characterised in that include with weight portion
The following components of meter: silicon dioxide 50~80 parts, silicone oil 1~20 parts, boric acid 1~5 parts, oleic acid 1~
15 parts.
In some embodiments, print mud drum and include following components in parts by weight: silicon dioxide 60~
70 parts, silicone oil 5~10 parts, boric acid 3~4 parts, oleic acid 5~10 parts.
In some embodiments, print mud and also include pigment 1~8 parts.
According to an aspect of the invention, it is provided print the production method of mud, comprise the steps:
1) stirring mixing 10~20 minutes after silicone oil and boric acid being heated to 100~120 DEG C;
2) oleic acid and silicon dioxide are added step 1) in the mixture of gained, stir 10~20 minutes;
3) reduction temperature is to 80~100 DEG C, adds pigment, stirs 15~20 minutes mix homogeneously,
To finished product.
Thus, powder common during the present invention uses nature, light weight, soft silicon dioxide are made
For base material, and use silicone oil (C6H18OSi2), boric acid (H3BO3) and oleic acid (C18H34O2) conduct
Binding agent, produces the color mud of soft lightweight under certain process conditions.Without the tune that adds water in raw material
Joint, therefore, in use will not become dry, can conveniently reuse.
Detailed description of the invention
Below in conjunction with detailed description of the invention, invention is described in further detail.
Embodiment 1
Print mud, the following components including in parts by weight: silicon dioxide 50 parts, silicone oil 10 parts,
Boric acid 1 part, oleic acid 5 parts.
Print the production method of mud, comprise the steps:
1) after silicone oil and boric acid being heated to 120 DEG C, stirring mixing obtains mixture in 10 minutes;
2) oleic acid and silicon dioxide are added step 1) in the mixture of gained, stir 15 minutes;
3) reduction temperature is to 100 DEG C, adds pigment, stirs 15 minutes mix homogeneously, obtain finished product.
Embodiment 2
Print mud, the following components including in parts by weight: silicon dioxide 60 parts, silicone oil 1 part, boron
Acid 3 parts, oleic acid 15 parts and pigment.
Print the production method of mud, comprise the steps:
1) after silicone oil and boric acid being heated to 110 DEG C, stirring mixing obtains mixture in 15 minutes;
2) oleic acid and silicon dioxide are added step 1) in the mixture of gained, stir 20 minutes;
3) reduction temperature is to 80 DEG C, adds pigment, stirs 20 minutes mix homogeneously, obtain finished product.
Embodiment 3
Print mud, the following components including in parts by weight: silicon dioxide 80 parts, silicone oil 20 parts,
Boric acid 5 parts, oleic acid 10 parts.
Print the production method of mud, comprise the steps:
1) after silicone oil and boric acid being heated to 100 DEG C, stirring mixing obtains mixture in 20 minutes;
2) oleic acid and silicon dioxide are added step 1) in the mixture of gained, stir 15 minutes;
3) reduction temperature is to 90 DEG C, adds pigment, stirs 20 minutes mix homogeneously, obtain finished product.
Embodiment 4
Print mud, the following components including in parts by weight: silicon dioxide 70 parts, silicone oil 5 parts, boron
Acid 4 parts, oleic acid 1 part.
Print the production method of mud, comprise the steps:
1) after silicone oil and boric acid being heated to 120 DEG C, stirring mixing obtains mixture in 10 minutes;
2) oleic acid and silicon dioxide are added step 1) in the mixture of gained, stir 10 minutes;
3) reduction temperature is to 90 DEG C, adds pigment, stirs 15 minutes mix homogeneously, obtain finished product.
Embodiment 5
Print mud, the following components including in parts by weight: silicon dioxide 60 parts, silicone oil 8 parts, boron
Acid 3 parts, oleic acid 8 parts.
Print the production method of mud, comprise the steps:
1) after silicone oil and boric acid being heated to 110 DEG C, stirring mixing obtains mixture in 15 minutes;
2) oleic acid and silicon dioxide are added step 1) in the mixture of gained, stir 15 minutes;
3) reduction temperature is to 100 DEG C, adds pigment, stirs 18 minutes mix homogeneously, obtain finished product.
The color mud that the formula of the present invention and technique produce, quality is slim and graceful, soft, and feel is smooth, makes
It is difficult to during with become dry firmly, can conveniently reuse.
Above-described is only some embodiments of the present invention.For those of ordinary skill in the art
For, without departing from the concept of the premise of the invention, it is also possible to make some deformation and improvement,
These broadly fall into the protection domain of invention.
Claims (4)
1. print mud, it is characterised in that include following components in parts by weight: silicon dioxide 50~
80 parts, silicone oil 1~20 parts, boric acid 1~5 parts, oleic acid 1~15 parts.
Printing mud the most according to claim 1, it is characterised in that include in parts by weight with
Lower component: silicon dioxide 60~70 parts, silicone oil 5~10 parts, boric acid 3~4 parts, oleic acid 5~10
Part.
Printing mud the most according to claim 1 and 2, it is characterised in that also include pigment 1~8
Part.
The production method of printing mud the most according to claim 3, it is characterised in that include as follows
Step:
1) after silicone oil and boric acid being heated to 100~120 DEG C, stirring mixing is mixed for 10~20 minutes
Thing;
2) oleic acid and silicon dioxide are added step 1) in the mixture of gained, stir 10~20 minutes;
3) reduction temperature is to 80~100 DEG C, adds pigment, stirs 15~20 minutes mix homogeneously,
To finished product.