CN105949706A - Insulated cable sheath formula and preparation method thereof - Google Patents
Insulated cable sheath formula and preparation method thereof Download PDFInfo
- Publication number
- CN105949706A CN105949706A CN201610327729.9A CN201610327729A CN105949706A CN 105949706 A CN105949706 A CN 105949706A CN 201610327729 A CN201610327729 A CN 201610327729A CN 105949706 A CN105949706 A CN 105949706A
- Authority
- CN
- China
- Prior art keywords
- parts
- formaldehyde resin
- insulated cable
- mixture
- cresol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an insulated cable sheath formula. The formula comprises raw materials in parts by weight as follows: 6-20 parts of phenol-formaldehyde resin powder, 1-7 parts of a lubricant, 2-8 parts of white carbon black, 4-20 parts of cresol-formaldehyde resin, 3-13 parts of an antioxidant, 4-20 parts of ethylene propylene diene monomer rubber, 3-9 parts of an inorganic flame retardant, 4-12 parts of dioctyl sebacate and 5-15 parts of calcium carbonate. The insulated cable sheath formula has the advantages of reasonable material selection, good anti-corrosion effect, good insulation performance and the like.
Description
Technical field
The present invention relates to field of cables, particularly relate to a kind of insulated cable jacket formula and preparation method thereof.
Background technology
At present, along with socioeconomic development, electric wire consumption increases rapidly, the most continuous to the prescription of cable
Improving, such as in aviation, the cable of the use field such as electric power, boats and ships in, to the creep-resistant property of cable, bending property, conduction
Requirement in terms of rate and insulating properties is the highest, if the incomplete words that cable possesses, can affect in these fields
Work and benefit.
Summary of the invention
In order to overcome the defect of above-mentioned prior art, it is an object of the invention to provide a kind of insulated cable jacket formula and
Preparation method.
The present invention takes techniques below scheme to realize: a kind of insulated cable jacket formula, by following according to weight
The raw material composition of part: phenol-formaldehyde resin powder 6-20 part, lubricant 1-7 part, white carbon 2-8 part, cresol-formaldehyde resin 4-20 part is anti-
Oxidant 3-13 part, ethylene propylene diene rubber 4-20 part, inorganic combustion inhibitor 3-9 part, SA dioctyl ester 4-12 part, calcium carbonate 5-15
Part.
Above-mentioned a kind of insulated cable jacket formula, is made up of according to the raw material of weight portion following: phenol-formaldehyde resin powder 6-18
Part, lubricant 1-5 part, white carbon 2-6 part, cresol-formaldehyde resin 4-18 part, antioxidant 3-10 part, ethylene propylene diene rubber 4-
18 parts, inorganic combustion inhibitor 3-7 part, SA dioctyl ester 4-10 part, calcium carbonate 5-12 part.
Above-mentioned a kind of insulated cable jacket formula, is made up of according to the raw material of weight portion following: phenol-formaldehyde resin powder 13 parts,
Lubricant 4 parts, white carbon 5 parts, cresol-formaldehyde resin 12 parts, antioxidant 8 parts, ethylene propylene diene rubber 12 parts, inorganic combustion inhibitor
6 parts, SA dioctyl ester 8 parts, calcium carbonate 10 parts.
Above-mentioned a kind of insulated cable jacket formula and preparation method thereof, comprises the steps of:
(1) raw material is weighed according to the weight portion in claim 3, by phenol-formaldehyde resin powder, cresol-formaldehyde resin, ethylene-propylene-diene monomer
Glue, SA dioctyl ester and calcium carbonate are put into and are carried out sufficient stir process in batch mixer, make material mix homogeneously, are mixed
Thing A;
(2) lubricant, white carbon, antioxidant and inorganic combustion inhibitor are dried stir process at a temperature of 80 DEG C, go
Except the moisture contained in raw material, and make raw material be sufficiently mixed, obtain mixture B;
(3) mixture A and mixture B is placed in drying device again it is dried process, stirred by agitating device
Mix process, make mixture A and mixture B carry out mixing and pelletize process by screw extruder, obtain finished product C.
The method have the advantages that in sum the present invention have material select rationally, anticorrosion ability good and
The advantages such as good insulation preformance, the cable using this formula to make can effectively play the effect of insulation, make the use of cable more
Add conveniently.
Detailed description of the invention
A kind of insulated cable jacket formula, is made up of according to the raw material of weight portion following: phenol-formaldehyde resin powder 6-20 part, lubrication
Agent 1-7 part, white carbon 2-8 part, cresol-formaldehyde resin 4-20 part, antioxidant 3-13 part, ethylene propylene diene rubber 4-20 part, nothing
Machine fire retardant 3-9 part, SA dioctyl ester 4-12 part, calcium carbonate 5-15 part.
Above-mentioned a kind of insulated cable jacket formula, is made up of according to the raw material of weight portion following: phenol-formaldehyde resin powder 6-18
Part, lubricant 1-5 part, white carbon 2-6 part, cresol-formaldehyde resin 4-18 part, antioxidant 3-10 part, ethylene propylene diene rubber 4-
18 parts, inorganic combustion inhibitor 3-7 part, SA dioctyl ester 4-10 part, calcium carbonate 5-12 part.
Above-mentioned a kind of insulated cable jacket formula, is made up of according to the raw material of weight portion following: phenol-formaldehyde resin powder 13 parts,
Lubricant 4 parts, white carbon 5 parts, cresol-formaldehyde resin 12 parts, antioxidant 8 parts, ethylene propylene diene rubber 12 parts, inorganic combustion inhibitor
6 parts, SA dioctyl ester 8 parts, calcium carbonate 10 parts.
Above-mentioned a kind of insulated cable jacket formula and preparation method thereof, comprises the steps of:
(1) raw material is weighed according to the weight portion in claim 3, by phenol-formaldehyde resin powder, cresol-formaldehyde resin, ethylene-propylene-diene monomer
Glue, SA dioctyl ester and calcium carbonate are put into and are carried out sufficient stir process in batch mixer, make material mix homogeneously, are mixed
Thing A;
(2) lubricant, white carbon, antioxidant and inorganic combustion inhibitor are dried stir process at a temperature of 80 DEG C, go
Except the moisture contained in raw material, and make raw material be sufficiently mixed, obtain mixture B;
(3) mixture A and mixture B is placed in drying device again it is dried process, stirred by agitating device
Mix process, make mixture A and mixture B carry out mixing and pelletize process by screw extruder, obtain finished product C.
The present invention has that material selects rationally, anticorrosion ability is good and the advantage such as good insulation preformance, uses this formula to make
Cable can effectively play the effect of insulation, the use making cable is convenient.
The above is embodiments of the invention, therefore all according to the structure described in the present patent application scope, feature and principle institute
The equivalence change done or modification, in the range of being all included in present patent application.
Claims (4)
1. an insulated cable jacket formula, it is characterised in that be made up of according to the raw material of weight portion following: phenol-formaldehyde resin powder 6-
20 parts, lubricant 1-7 part, white carbon 2-8 part, cresol-formaldehyde resin 4-20 part, antioxidant 3-13 part, ethylene propylene diene rubber
4-20 part, inorganic combustion inhibitor 3-9 part, SA dioctyl ester 4-12 part, calcium carbonate 5-15 part.
A kind of insulated cable jacket formula the most according to claim 1, it is characterised in that by following former according to weight portion
Material composition: phenol-formaldehyde resin powder 6-18 part, lubricant 1-5 part, white carbon 2-6 part, cresol-formaldehyde resin 4-18 part, antioxidant
3-10 part, ethylene propylene diene rubber 4-18 part, inorganic combustion inhibitor 3-7 part, SA dioctyl ester 4-10 part, calcium carbonate 5-12 part.
A kind of insulated cable jacket formula the most according to claim 1, it is characterised in that by following former according to weight portion
Material composition: phenol-formaldehyde resin powder 13 parts, lubricant 4 parts, white carbon 5 parts, cresol-formaldehyde resin 12 parts, antioxidant 8 parts, ternary
12 parts of EP rubbers, inorganic combustion inhibitor 6 parts, SA dioctyl ester 8 parts, calcium carbonate 10 parts.
4. a kind of insulated cable jacket formula as described in claim 1-3 and preparation method thereof, it is characterised in that by with
Lower step forms:
(1) raw material is weighed according to the weight portion in claim 3, by phenol-formaldehyde resin powder, cresol-formaldehyde resin, ethylene-propylene-diene monomer
Glue, SA dioctyl ester and calcium carbonate are put into and are carried out sufficient stir process in batch mixer, make material mix homogeneously, are mixed
Thing A;
(2) lubricant, white carbon, antioxidant and inorganic combustion inhibitor are dried stir process at a temperature of 80 DEG C, go
Except the moisture contained in raw material, and make raw material be sufficiently mixed, obtain mixture B;
(3) mixture A and mixture B is placed in drying device again it is dried process, stirred by agitating device
Mix process, make mixture A and mixture B carry out mixing and pelletize process by screw extruder, obtain finished product C.