CN105948702A - Porcelain plate blank powder and preparation technology thereof - Google Patents
Porcelain plate blank powder and preparation technology thereof Download PDFInfo
- Publication number
- CN105948702A CN105948702A CN201610323681.4A CN201610323681A CN105948702A CN 105948702 A CN105948702 A CN 105948702A CN 201610323681 A CN201610323681 A CN 201610323681A CN 105948702 A CN105948702 A CN 105948702A
- Authority
- CN
- China
- Prior art keywords
- porcelain plate
- base substrate
- plate base
- substrate powder
- compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses porcelain plate blank powder. The porcelain plate blank powder is prepared from components in percentage by weight as follows: 45%-60% of potassium-sodium feldspar, 5%-12% of hard high-alumina clay, 30%-45% of kaolin, 1%-2% of talc and 4%-8% of bentonite, and the weight percentage sum of the components is 100%. The porcelain plate blank powder adopts simple composition and can be applied to a dry process for preparation of a porcelain plate blank with the thickness of 2 cm, and the prepared porcelain plate blank has high strength and low water absorption. The invention further discloses a preparation technology of the porcelain plate blank powder. The preparation technology is simple, the energy consumption is low and small amount of wastewater and waste gas is produced.
Description
Technical field
The present invention relates to building tile technical field, particularly relate to a kind of porcelain plate base substrate powder and preparation technology thereof.
Background technology
Method prepared by ceramic wall and floor bricks powder can be divided into dry method powder process and the big class of wet-milling powder process two.Wet processing be by
Raw material adds water in ball mill and grinds to form the mud requiring fineness, then carries out being spray-dried powder process or being pressed by mud
Filter, beat powder after drying.It has the advantages such as operation is simple, yield is big, good, the uniform moisture of mobility of particle, but tail gas contains greatly
Amount dust, if do not processed, can cause serious atmospheric pollution, and energy consumption is the biggest.Dry process is directly to be ground to by raw material carefully
Powder, then to fine powder pelletize, has the advantage that energy consumption is low, economize on water.During producing, if poorly sealed, will result in
Substantial amounts of dust pollution, if but seal good, then the pollution that produces can seldom, and especially contaminated wastewater can be seldom.
Owing to dry method powder process method has the advantage of energy-saving and emission-reduction, it is a trend of architectural ceramic industry for a long time.But at present
Domestic due to process equipment with the problem of raw material standard, dry method powder process only limits the internal wall brick being applied to small dimension, and high intensity,
The source of the blank of the 2cm thickness porcelain plate of low water absorption is still wet processing, and energy consumption is high, the waste water and gas meeting produced in pulverizing process
Environment is caused serious pollution.Additionally, the formula of 2cm thickness porcelain plate blank in existing wet powder-making method directly can not be converted it is
Dry method powder process, because the formula of existing 2cm thickness porcelain plate blank includes highly plastic clay, and the moisture of highly plastic clay is higher
(about 30%), it is difficult to utilize dry method powder process method to carry out drying and crushing.Further, highly plastic clay is a kind of non-renewable money
Source.
Summary of the invention
In order to overcome the deficiencies in the prior art, first purpose of the present invention is to provide a kind of porcelain plate base substrate powder, should
Porcelain plate base substrate powder composition is simple, can be used for the porcelain plate base substrate that dry process is thick to prepare 2cm, and the porcelain plate blank strength prepared
Height, water absorption rate are low.
First purpose of the present invention can realize by the following technical solutions:
A kind of porcelain plate base substrate powder, it is characterised in that include following components by weight percentage:
The percentage by weight sum of above-mentioned each component is 100%.
Wherein, hard high-alumina clay is the one in fire clay, and fire clay refers to a kind of refractoriness > deposition of 1580 DEG C
Type clay, mainly by kaolinite or kaolinite illite class mineral composition, and often containing a small amount of diaspore, quartz, goethitum, sharp
Titanium ore etc..General Al2O3Content > 30%, and corresponding Fe2O3、CaO、MgO、K2O、Na2The content of O is relatively low.Work as Al2O3Content exceedes
When 45%, can be described as high-alumina clay or bauxite.
And Kaolin is a kind of clay based on kaolinite race clay mineral and clay rock.According to its quality, plasticity
It is divided into three types with the mass fraction of chiltern: (1) hard kaoline: matter is hard, without plasticity, pulverizes tool plasticity after fine grinding;
(2) soft kaolin: matter is soft, plasticity is relatively strong, chiltern mass fraction < 50%;(3) sandy kaoline: matter is soft, plasticity is relatively
Weak, chiltern mass fraction > 50%.Guangxi white clay is a kind of soft kaolin, and it has, and plasticity is good, good fluidity and associativity
Good feature.
Preferably, described Kaolin includes sandy kaoline and soft kaolin;The weight percent of described sandy kaoline
Than the 10-15% for described porcelain plate base substrate powder;The percentage by weight of described soft kaolin is described porcelain plate base substrate powder
20-30%.
Preferably, described soft kaolin includes that Guangxi white clay, the percentage by weight of described Guangxi white clay are described porcelain plate
The 10-15% of base substrate powder.
Preferably, described potassium albite includes the potassium albite from three different sources, be designated as respectively potassium albite A,
Potassium albite B and potassium albite C;The percentage by weight of described potassium albite A is the 15-20% of described porcelain plate base substrate powder;Institute
State the 15-20% that percentage by weight is described porcelain plate base substrate powder of potassium albite B;The percentage by weight of described potassium albite C
15-20% for described porcelain plate base substrate powder.
Potassium albite is a kind of flux class raw material in ceramic tile blank.Potassium albite A, potassium albite B and potassium albite C are
3 kinds of compositions are suitable, but the potassium albite that the place of production is different.Potassium albite A can originate from Yantai, Shandong, and potassium albite B can originate from
Laiwu in Shandong province, and potassium albite C can originate from Linyi, Shandong.
Further object is that the preparation technology providing a kind of porcelain plate base substrate powder, this preparation technology is simple,
Less energy consumption, the waste water and gas of generation is few, energy-conserving and environment-protective.
Another object of the present invention can realize by the following technical solutions:
The preparation technology of a kind of porcelain plate base substrate powder, comprises the following steps:
1) raw material crushes;Crushing each component in formula respectively, obtaining broken fineness is that 12 purposes first crush
Material;
2) it is dried for the first time;Respectively described first broken material being dried process, obtaining water content is 6-8% second
Broken material;
3) dispensing;Weigh described second broken material, mix homogeneously by formula ratio respectively, obtain the first compound;
4) fine grinding;Described first compound is carried out fine grinding process, and obtaining fineness is 325 purpose the second compounds;
5) humidification pelletize: described second compound is put into humidifying prilling machine, and adds the Organic adhesive that concentration is 2%
Aqueous solution, it is 40-100 purpose the 3rd compound that pelletize obtains fineness;
6) second time is dried;Described 3rd compound is dried process, and obtaining water content is 7-8% the 4th mixing
Material;
7) sieve;Described 4th compound crosses 40-100 mesh sieve, obtains described porcelain plate base substrate powder.
Preferably, also include step 8), old 24 hours of described porcelain plate base substrate powder.
Preferably, also including that selecting crude drugs with winnower remove impurity processes, described selecting crude drugs with winnower remove impurity processes and is arranged on step 4) and step 5) between.
Preferably, step 5) in, described 3rd compound water content is 10-12%, bulk density is 0.95g/cm3。
Preferably, step 5) in, described Organic adhesive is carboxymethyl cellulose;The addition of described Organic adhesive is
The 5-6% of described porcelain plate base substrate powder.
Preferably, step 6) in, use multilamellar vibrations fluidized bed dryer that described 3rd compound is dried process.
Compared to existing technology, the beneficial effects of the present invention is:
(1) porcelain plate base substrate powder provided by the present invention, each Component Source in formula is easy to get, and high without moisture content
Fat clay raw material (moisture content is more than 30%), it is to avoid be not suitable for the drawback of dry grinding equipment.This porcelain plate base substrate powder is permissible
Take the porcelain plate that dry preparation process is thick to produce 2cm, compressing after dry body strength reach 1.5MPa.And in prior art
For preparing the porcelain plate base substrate powder of porcelain plate thick for 2cm, its formula includes the fat clay raw material of high-moisture percentage, can only be with wet
Prepared by method technique.
(2) porcelain plate base substrate powder provided by the present invention, potassium albite ratio in formula is high, uses simultaneously and originates from 3
The potassium albite of individual different sources is conducive to improving the stability of product.
(3) porcelain plate base substrate powder provided by the present invention, using of hard high-alumina clay ensures that porcelain plate base substrate has enough
Aluminum content so that base substrate will not deform in the high temperature stage of burning till, base substrate has enough toughness and intensity simultaneously.
(4) porcelain plate base substrate powder provided by the present invention, Kaolin uses two classes in formula, and a class is soft, a class sand
Matter, two use time similar, i.e. can obtain certain powder particles intensity, ensure that raw material moisture content is low simultaneously, and beneficially dry method is thin
The technological requirement of mill.
(5) porcelain plate base substrate powder provided by the present invention, bentonite accounts for 4-8% in formula, and consumption is reasonable, improves base
, there is base substrate deliquescing in dry body strength after body formed, it is to avoid consumption too much causes the base substrate to burn till link at high temperature, and finished product deforms
Defect.
(6) preparation technology of porcelain plate base substrate powder provided by the present invention, be humidified granulation process, generally uses water smoke
Changing, atomized water mixes agglomerating with powder fine powder, becomes granule.But such powder particles is in later stage course of conveying, intensity meeting
Gradually reducing along with moisture content reduces, granule becomes scattered, and segmentation increases, and brings impact to later stage base substrate is compressing.Therefore make at humidification
Grain link, concentration is the aqueous solution binding agent as fine powder of 2% carboxymethyl cellulose so that it is atomization, obtains having certain
The powder particles of intensity, ultimately facilitates molding.The carboxymethyl cellulose aqueous solution of excessive concentrations is unfavorable for atomization.
(7) preparation technology of porcelain plate base substrate powder provided by the present invention, the fineness of dry method fine grinding link controls final shadow
Ringing the product intensity that later stage high temperature burns till, control 325 mesh screen residue 1-2%, the intensity of its product intensity and wet powder-making is suitable.
Detailed description of the invention
Below, in conjunction with detailed description of the invention, the present invention is described further:
A kind of porcelain plate base substrate powder, including following components by weight percentage:
The percentage by weight sum of above-mentioned each component is 100%.
Wherein, Kaolin includes sandy kaoline and soft kaolin;The percentage by weight of described sandy kaoline is institute
State the 10-15% of porcelain plate base substrate powder;The percentage by weight of described soft kaolin is the 20-of described porcelain plate base substrate powder
30%;Described soft kaolin includes that Guangxi white clay, the percentage by weight of described Guangxi white clay are described porcelain plate base substrate powder
10-15%.
According to above-mentioned formula, obtaining the porcelain plate base substrate powder of embodiment 1-3, its concrete formula see table 1 respectively.Existing
The formula of the porcelain plate base substrate powder of technology wet processing is shown in Table the record of 1 comparative example 1.
Table 1 embodiment 1-3 and the formula table of comparative example 1 porcelain plate base substrate powder
Wherein, 1. potassium albite A originates from Yantai, Shandong, and potassium albite B originates from Laiwu in Shandong province, and potassium albite C originates from mountain
Linyi, east.
2. soft kaolin A is Guangxi white clay, and soft kaolin B is the soft kaolin of non-Guangxi white clay class.
Embodiment 1
The record of the proportioning of each component of embodiment 1 and each component such as table 1.
The preparation technology of a kind of porcelain plate base substrate powder, comprises the following steps:
1) raw material crushes;Respectively each component in formula is carried out carse, medium and small broken with jaw crusher, obtain broken thin
Degree is 12 purpose the first broken materials;
2) it is dried for the first time;Respectively described first broken material being dried process, it is 6% the second broken for obtaining water content
Particle;
3) dispensing;Weigh described second broken material, mix homogeneously by formula ratio respectively, obtain the first compound;Weigh institute
When stating the second broken material, various raw materials use electronic belt continuous weighting;
4) fine grinding;Described first compound carrying out fine grinding and selecting crude drugs with winnower processes, obtaining fineness is that 325 purposes second mix
Material;
5) humidification pelletize: described second compound is put into humidifying prilling machine, and adds the carboxymethyl cellulose that concentration is 2%
Element aqueous solution, addition is the 5% of described porcelain plate base substrate powder;It is that 40 mesh, water content are 12%, pile up that pelletize obtains fineness
Density is 0.95g/cm3The 3rd compound;
6) second time is dried;Use multilamellar vibrations fluidized bed dryer that described 3rd compound is dried process,
It is 7% the 4th compound to water content;
7) sieve;Described 4th compound crosses 70 mesh sieves, obtains described porcelain plate base substrate powder;
8) described porcelain plate base substrate powder is entered storage silo by belt-conveying, old 24 hours.
Porcelain plate prepared by the porcelain plate base substrate powder utilizing embodiment 1 to obtain, and the key performance data of porcelain plate are shown in Table 2.
Embodiment 2
The record of the proportioning of each component of embodiment 2 and each component such as table 1.
The preparation technology of a kind of porcelain plate base substrate powder, comprises the following steps:
1) raw material crushes;Respectively each component in formula is carried out carse, medium and small broken with dry grinding equipment, obtain broken fineness
It is 12 purpose the first broken materials;
2) it is dried for the first time;Respectively described first broken material being dried process, it is 7% the second broken for obtaining water content
Particle;
3) dispensing;Weigh described second broken material, mix homogeneously by formula ratio respectively, obtain the first compound;Weigh institute
When stating the second broken material, various raw materials use electronic belt continuous weighting;
4) fine grinding;Described first compound carrying out fine grinding and selecting crude drugs with winnower processes, obtaining fineness is that 325 purposes second mix
Material;
5) humidification pelletize: described second compound is put into humidifying prilling machine, and adds the carboxymethyl cellulose that concentration is 2%
Element aqueous solution, addition is the 6% of described porcelain plate base substrate powder;It is that 80 mesh, water content are 11%, pile up that pelletize obtains fineness
Density is 0.95g/cm3The 3rd compound;
6) second time is dried;Use multilamellar vibrations fluidized bed dryer that described 3rd compound is dried process,
It is 8% the 4th compound to water content;
7) sieve;Described 4th compound crosses 90 mesh sieves, obtains described porcelain plate base substrate powder;
8) described porcelain plate base substrate powder is entered storage silo by belt-conveying, old 24 hours.
Porcelain plate prepared by the porcelain plate base substrate powder utilizing embodiment 2 to obtain, and the key performance data of porcelain plate are shown in Table 2.
Embodiment 3
The record of the proportioning of each component of embodiment 3 and each component such as table 1.
The preparation technology of a kind of porcelain plate base substrate powder, comprises the following steps:
1) raw material crushes;Respectively each component in formula is carried out carse, medium and small broken with jaw crusher, obtain broken thin
Degree is 12 purpose the first broken materials;
2) it is dried for the first time;Respectively described first broken material being dried process, it is 8% the second broken for obtaining water content
Particle;
3) dispensing;Weigh described second broken material, mix homogeneously by formula ratio respectively, obtain the first compound;Weigh institute
When stating the second broken material, various raw materials use electronic belt continuous weighting;
4) fine grinding;Described first compound carrying out fine grinding and selecting crude drugs with winnower processes, obtaining fineness is that 325 purposes second mix
Material;
5) humidification pelletize: described second compound is put into humidifying prilling machine, and adds the carboxymethyl cellulose that concentration is 2%
Element aqueous solution, addition is the 5.5% of described porcelain plate base substrate powder;Pelletize obtain fineness be 60 mesh, water content be 10%, heap
Long-pending density is 0.95g/cm3The 3rd compound;
6) third time is dried;Use multilamellar vibrations fluidized bed dryer that described 3rd compound is dried process,
It is 7% the 4th compound to water content;
7) sieve;Described 4th compound crosses 100 mesh sieves, obtains described porcelain plate base substrate powder;
8) described porcelain plate base substrate powder is entered storage silo by belt-conveying, old 24 hours.
Porcelain plate prepared by the porcelain plate base substrate powder utilizing embodiment 3 to obtain, and the key performance data of porcelain plate are shown in Table 2.
Comparative example 1
The record of the proportioning of each component of comparative example 1 and each component such as table 1.
Existing wet processing is used to obtain the porcelain plate base substrate powder of embodiment 1.
Porcelain plate prepared by the porcelain plate base substrate powder utilizing comparative example 1 to obtain, and the key performance data of porcelain plate are shown in Table 2.
Table 2 embodiment 1-3 and the performance inventory table of comparative example 1 porcelain plate
Can obtain from the data of table 2, by adjusting the formula of wet processing porcelain plate powder body, and take suitable dry process system
Standby porcelain plate, its end properties of the product obtained is suitable with the properties of product of wet processing, porcelain plate base the most provided by the present invention
Body powder is applicable to prepare thick porcelain plate blank (the porcelain plate blank that such as 2cm is thick) with dry process, and dry preparation process energy consumption is low,
The waste water and waste liquid produced is few, energy-conserving and environment-protective, not only conforms with the policy requirements that national energy-saving reduces discharging, and also has reality to enterprise
Interests.Additionally, the properties of powder made by preparation technology provided by the present invention is through the test of lab scale pilot scale, fully meet
The big needs produced.
It will be apparent to those skilled in the art that can technical scheme as described above and design, make other various
Corresponding change and deformation, and all these change and deformation all should belong to the protection domain of the claims in the present invention
Within.
Claims (10)
1. a porcelain plate base substrate powder, it is characterised in that include following components by weight percentage:
Potassium albite 45-60%;Hard high-alumina clay 5-12%;
Kaolin 30-45%;Talcum 1-2%;
Bentonite 4-8%;
The percentage by weight sum of above-mentioned each component is 100%.
Porcelain plate base substrate powder the most according to claim 1, it is characterised in that described Kaolin includes sandy kaoline and soft
Matter Kaolin;The percentage by weight of described sandy kaoline is the 10-15% of described porcelain plate base substrate powder;Described soft kaolin
The 20-30% that percentage by weight is described porcelain plate base substrate powder.
Porcelain plate base substrate powder the most according to claim 1, it is characterised in that described soft kaolin includes Guangxi white clay,
The percentage by weight of described Guangxi white clay is the 10-15% of described porcelain plate base substrate powder.
Porcelain plate base substrate powder the most according to claim 1, it is characterised in that described potassium albite includes from three differences
The potassium albite in the place of production, is designated as potassium albite A, potassium albite B and potassium albite C respectively;The weight percent of described potassium albite A
Than the 15-20% for described porcelain plate base substrate powder;The percentage by weight of described potassium albite B is described porcelain plate base substrate powder
15-20%;The percentage by weight of described potassium albite C is the 15-20% of described porcelain plate base substrate powder.
5. the preparation technology of a porcelain plate base substrate powder as claimed in claim 1, it is characterised in that comprise the following steps:
1) raw material crushes;Crushing each component in formula respectively, obtaining broken fineness is 12 purpose the first broken materials;
2) it is dried for the first time;Respectively described first broken material being dried process, obtaining water content is that 6-8% second crushes
Material;
3) dispensing;Weigh described second broken material, mix homogeneously by formula ratio respectively, obtain the first compound;
4) fine grinding;Described first compound is carried out fine grinding process, and obtaining fineness is 325 purpose the second compounds;
5) humidification pelletize: described second compound is put into humidifying prilling machine, and it is water-soluble to add the Organic adhesive that concentration is 2%
Liquid, it is 40-100 purpose the 3rd compound that pelletize obtains fineness;
6) second time is dried;Described 3rd compound is dried process, and obtaining water content is 7-8% the 4th compound;
7) sieve;Described 4th compound crosses 40-100 mesh sieve, obtains described porcelain plate base substrate powder.
The preparation technology of porcelain plate base substrate powder the most according to claim 5, it is characterised in that also include step 8), institute
State porcelain plate base substrate powder old 24 hours.
The preparation technology of porcelain plate base substrate powder the most according to claim 5, it is characterised in that also include at selecting crude drugs with winnower remove impurity
Reason, described selecting crude drugs with winnower remove impurity processes and is arranged on step 4) and step 5) between.
The preparation technology of porcelain plate base substrate powder the most according to claim 5, it is characterised in that step 5) in, the described 3rd
Compound water content is 10-12%, bulk density is 0.95g/cm3。
The preparation technology of porcelain plate base substrate powder the most according to claim 5, it is characterised in that step 5) in, described organic
Adhesive is carboxymethyl cellulose;The addition of described Organic adhesive is the 5-6% of described porcelain plate base substrate powder.
The preparation technology of porcelain plate base substrate powder the most according to claim 5, it is characterised in that step 6) in, use multilamellar
Vibrations fluidized bed dryer is dried process to described 3rd compound.