CN105948599A - Curbstone and manufacturing method thereof - Google Patents
Curbstone and manufacturing method thereof Download PDFInfo
- Publication number
- CN105948599A CN105948599A CN201610477355.9A CN201610477355A CN105948599A CN 105948599 A CN105948599 A CN 105948599A CN 201610477355 A CN201610477355 A CN 201610477355A CN 105948599 A CN105948599 A CN 105948599A
- Authority
- CN
- China
- Prior art keywords
- parts
- cement
- road side
- side stone
- sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a curbstone and a manufacturing method thereof, relating to the field of construction materials. The curbstone comprises the following components in parts by mass: 5-10 parts of chromatic pigment, 1-3 parts of aid, 3-5 parts of reinforcer, 15-20 parts of cement, 10-15 parts of coarse sand, 10-15 parts of fine sand, 5-10 parts of mineral slag, 15-20 parts of coal ash, 5-8 parts of glass, 6 parts of ceramic and 15-20 parts of clay. The curbstone provided by the technical scheme of the invention saves the raw materials, is easy for processing and convenient to use, can perform the function of warning, and has the characteristics of favorable decorative property, favorable strength, favorable wear resistance, low weathering tendency, long service life, uniform and beautiful color and the like.
Description
Technical field
The present invention relates to building materials field, be specifically related to a kind of road side stone and manufacture method thereof.
Background technology
Road side stone is divided into: lithotome and concreting, and lithotome road side stone is attractive in appearance, cost is high, is suitable for various urban roads and residential quarters, public building internal passageway.Mainly having five Flos Nelumbinis, its yield is big, and the main place of production is in Shandong Rizhao, Baiyun District, Guangzhou City Jian Ji cement products factory, and sunshine, aberration was little, is suitable for various large-scale road pavements.The features such as kerbstone has the physical characteristics such as alkaline-resisting, acidproof, wear-resisting, has elegant in appearance, durable in use.
Traditional road side stone building stones use homogeneous natural fiber crops stone machine cut to process, the intensity of stone material must be qualified, require its uniform color, surface flawless, corner angle are complete, and outward appearance is consistent, without obvious speckle, aberration, it is not allow for air slaking phenomenon, to causing many restrictions in the selection of material.
Patent No. CN 103030339 A relates to a kind of formula producing flat stone, road side stone, floor tile, it is made up of the raw material of following weight proportioning and method: building waste 50-60 part, color pigment 5-10 part, auxiliary agent, reinforcing agent 5-10 part, cement, sandstone 20-30 part, building waste in this proportioning is pulverized by pulverizer, again each group of material is mixed in blender and is stirred, it is then placed in the mould of required form compacting, after product maintenance 48 hours, can the demoulding use.
Although technique scheme has expanded the material choice of road side stone, but its road side stone intensity produced and rub proofness are inadequate, and easy-weathering, and service life is shorter, accordingly, it would be desirable to design a kind of road side stone that can solve the problem that problem above and manufacture method thereof.
Summary of the invention
Problem to be solved by this invention is to provide a kind of road side stone and manufacture method thereof.
The purpose of the present invention can be achieved through the following technical solutions:
A kind of road side stone, by mass percentage, described road side stone includes color pigment 5-10 part, auxiliary agent 1-3 part, reinforcing agent 3-5 part, cement 15-20 part, coarse sand 10-15 part, fine sand 10-15 part, slag 5-10 part, coal ash 15-20 part, glass 5-8 part, pottery 6 parts, clay 15-20 part.
Preferably, by mass percentage, described road side stone includes color pigment 8 parts, auxiliary agent 2 parts, reinforcing agent 4 parts, cement 18 parts, coarse sand 13 parts, fine sand 13 parts, 8 parts of slag, coal ash 18 parts, 6 parts of glass, pottery 6 parts, clay 18 parts.
Preferably, the modulus of fineness of described fine sand is at 2.3-2.6, the clay content 1% of fine sand, described coarse sand is inertia sand, and the particle diameter fineness of coarse sand is at below 0.5mm, and described strength of cement grade is not less than 32.5, normal consistency water requirement≤27% of cement, the presetting period of cement >=45min, the final setting time≤6.5h of cement, the specific surface area >=3000cm of cement2/ g, 80um square hole screen screen over-size≤10% of cement, the 3d comprcssive strength >=12.0Mpa of cement, 28d comprcssive strength >=the 32.5Mpa of cement, the Fast Anti of cement tears intensity >=5.5Mpa open, and the 3d of cement is anti-tears intensity >=2.5 open, and the 28d of cement is anti-tears intensity >=5.5 open.
Preferably, described reinforcing agent uses concrete intensifier, and described auxiliary agent uses ethylene-vinyl acetate copolymer.
Preferably, described color pigment is grouped into by the one-tenth of following parts by weight: pigment 3-5 part, white cement 8-10 part, quartz sand 3-5 part.
A kind of manufacture method of road side stone, described preparation method specifically includes following steps:
A. raw material weighs: weigh color pigment 5-10 part, auxiliary agent 1-3 part, reinforcing agent 3-5 part, cement 15-20 part, coarse sand 10-15 part, fine sand 10-15 part, slag 5-10 part, coal ash 15-20 part, glass 5-8 part, pottery 6 parts, clay 15-20 part by mass percentage；
B. raw material pulverizing: be sequentially added in pulverizer by raw material and pulverize, grinding time is 1-3min；
C. mixing: material pulverizing completed adds water and stirs mixing, and mixing time is 5-10min；
D. compacting: mixed raw material rolling is kneaded into uniform mud bar, puts into road side stone mould and suppress；
E. maintenance: product is carried out maintenance, curing time is 24-48h；
F. the demoulding: the demoulding i.e. can get finished product.
Using technical scheme, save raw material, be prone to processing, easy to use, can play warning and the feature such as good decorative property, meanwhile, the road side stone intensity produced and anti-wear performance are good, not easy-weathering, and service life is long, and uniform in color, attractive in appearance.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below in conjunction with detailed description of the invention, the present invention is expanded on further.
Embodiment
1
:
A kind of road side stone, by mass percentage, described road side stone includes color pigment 5 parts, auxiliary agent 1 part, reinforcing agent 3 parts, cement 15 parts, coarse sand 10 parts, fine sand 10 parts, 5 parts of slag, coal ash 15 parts, 5 parts of glass, pottery 6 parts, clay 15 parts.
Wherein, the modulus of fineness of described fine sand is 2.5, the clay content 1% of fine sand, described coarse sand is inertia sand, and the particle diameter fineness of coarse sand is at 0.5mm, described strength of cement grade 32.5, the normal consistency water requirement 27% of cement, the presetting period 45min of cement, the final setting time 6.5h of cement, specific surface area 3000cm of cement2/ g, the 80um square hole screen screen over-size 10% of cement, 3d comprcssive strength 12.0Mpa of cement, 28d comprcssive strength 32.5Mpa of cement, the Fast Anti of cement tears intensity 5.5Mpa open, and the 3d of cement is anti-tears intensity 2.5 open, and the 28d of cement is anti-tears intensity 5.5 open.
Wherein, described reinforcing agent uses concrete intensifier, and described auxiliary agent uses ethylene-vinyl acetate copolymer.
Wherein, described color pigment is grouped into by the one-tenth of following parts by weight: pigment 3 parts, white cement 8 parts, quartz sand 3 parts.
A kind of manufacture method of road side stone, described preparation method specifically includes following steps:
A. raw material weighs: weigh color pigment 5 parts, auxiliary agent 1 part, reinforcing agent 3 parts, cement 15 parts, coarse sand 10 parts, fine sand 10 parts, 5 parts of slag, coal ash 15 parts, 5 parts of glass, pottery 6 parts, clay 15 parts by mass percentage；
B. raw material pulverizing: be sequentially added in pulverizer by raw material and pulverize, grinding time is 2min；
C. mixing: material pulverizing completed adds water and stirs mixing, and mixing time is 8min；
D. compacting: mixed raw material rolling is kneaded into uniform mud bar, puts into road side stone mould and suppress；
E. maintenance: product is carried out maintenance, curing time is 36h；
F. the demoulding: the demoulding i.e. can get finished product.
Embodiment
2
:
A kind of road side stone, by mass percentage, described road side stone includes color pigment 10 parts, auxiliary agent 3 parts, reinforcing agent 5 parts, cement 20 parts, coarse sand 15 parts, fine sand 15 parts, 10 parts of slag, coal ash 20 parts, 8 parts of glass, pottery 6 parts, clay 20 parts.
Wherein, the modulus of fineness of described fine sand is 2.5, the clay content 1% of fine sand, described coarse sand is inertia sand, and the particle diameter fineness of coarse sand is at 0.5mm, described strength of cement grade 32.5, the normal consistency water requirement 27% of cement, the presetting period 45min of cement, the final setting time 6.5h of cement, specific surface area 3000cm of cement2/ g, the 80um square hole screen screen over-size 10% of cement, 3d comprcssive strength 12.0Mpa of cement, 28d comprcssive strength 32.5Mpa of cement, the Fast Anti of cement tears intensity 5.5Mpa open, and the 3d of cement is anti-tears intensity 2.5 open, and the 28d of cement is anti-tears intensity 5.5 open.
Wherein, described reinforcing agent uses concrete intensifier, and described auxiliary agent uses ethylene-vinyl acetate copolymer.
Wherein, described color pigment is grouped into by the one-tenth of following parts by weight: pigment 5 parts, white cement 10 parts, quartz sand 5 parts.
A kind of manufacture method of road side stone, described preparation method specifically includes following steps:
A. raw material weighs: weigh color pigment 10 parts, auxiliary agent 3 parts, reinforcing agent 5 parts, cement 20 parts, coarse sand 15 parts, fine sand 15 parts, 10 parts of slag, coal ash 20 parts, 8 parts of glass, pottery 6 parts, clay 20 parts by mass percentage；
B. raw material pulverizing: be sequentially added in pulverizer by raw material and pulverize, grinding time is 2min；
C. mixing: material pulverizing completed adds water and stirs mixing, and mixing time is 8min；
D. compacting: mixed raw material rolling is kneaded into uniform mud bar, puts into road side stone mould and suppress；
E. maintenance: product is carried out maintenance, curing time is 36h；
F. the demoulding: the demoulding i.e. can get finished product.
Embodiment
3
:
A kind of road side stone, by mass percentage, described road side stone includes color pigment 8 parts, auxiliary agent 2 parts, reinforcing agent 4 parts, cement 18 parts, coarse sand 13 parts, fine sand 13 parts, 8 parts of slag, coal ash 18 parts, 6 parts of glass, pottery 6 parts, clay 18 parts.
Wherein, the modulus of fineness of described fine sand is 2.5, the clay content 1% of fine sand, described coarse sand is inertia sand, and the particle diameter fineness of coarse sand is at below 0.5mm, described strength of cement grade 32.5, the normal consistency water requirement 27% of cement, the presetting period 45min of cement, the final setting time 6.5h of cement, specific surface area 3000cm of cement2/ g, the 80um square hole screen screen over-size 10% of cement, 3d comprcssive strength 12.0Mpa of cement, 28d comprcssive strength 32.5Mpa of cement, the Fast Anti of cement tears intensity 5.5Mpa open, and the 3d of cement is anti-tears intensity 2.5 open, and the 28d of cement is anti-tears intensity 5.5 open.
Wherein, described reinforcing agent uses concrete intensifier, and described auxiliary agent uses ethylene-vinyl acetate copolymer.
Wherein, described color pigment is grouped into by the one-tenth of following parts by weight: pigment 4 parts, white cement 9 parts, quartz sand 4 parts.
A kind of manufacture method of road side stone, described preparation method specifically includes following steps:
A. raw material weighs: weigh color pigment 8 parts, auxiliary agent 2 parts, reinforcing agent 4 parts, cement 18 parts, coarse sand 13 parts, fine sand 13 parts, 8 parts of slag, coal ash 18 parts, 6 parts of glass, pottery 6 parts, clay 18 parts by mass percentage；
B. raw material pulverizing: be sequentially added in pulverizer by raw material and pulverize, grinding time is 1min；
C. mixing: material pulverizing completed adds water and stirs mixing, and mixing time is 8min；
D. compacting: mixed raw material rolling is kneaded into uniform mud bar, puts into road side stone mould and suppress；
E. maintenance: product is carried out maintenance, curing time is 48h；
F. the demoulding: the demoulding i.e. can get finished product.
Based on above-mentioned, use technical scheme, save raw material, be prone to processing, easy to use, can play the features such as warning and good decorative property, meanwhile, the road side stone intensity produced and anti-wear performance are good, not easy-weathering, service life is long, and uniform in color, attractive in appearance.
Obviously the present invention implements and is not subject to the restrictions described above; if the improvement of the various unsubstantialities that the method design that have employed the present invention is carried out with technical scheme; or the most improved design by the present invention and technical scheme directly apply to other occasion, all within protection scope of the present invention.
Claims (6)
1. a road side stone, it is characterized in that, by mass percentage, described road side stone includes color pigment 5-10 part, auxiliary agent 1-3 part, reinforcing agent 3-5 part, cement 15-20 part, coarse sand 10-15 part, fine sand 10-15 part, slag 5-10 part, coal ash 15-20 part, glass 5-8 part, pottery 6 parts, clay 15-20 part.
A kind of road side stone the most according to claim 1, it is characterized in that: by mass percentage, described road side stone includes color pigment 8 parts, auxiliary agent 2 parts, reinforcing agent 4 parts, cement 18 parts, coarse sand 13 parts, fine sand 13 parts, 8 parts of slag, coal ash 18 parts, 6 parts of glass, pottery 6 parts, clay 18 parts.
A kind of road side stone the most according to claim 1, it is characterized in that: the modulus of fineness of described fine sand is at 2.3-2.6, the clay content 1% of fine sand, described coarse sand is inertia sand, and the particle diameter fineness of coarse sand is at below 0.5mm, and described strength of cement grade is not less than 32.5, normal consistency water requirement≤27% of cement, the presetting period of cement >=45min, the final setting time≤6.5h of cement, the specific surface area >=3000cm of cement2/ g, 80um square hole screen screen over-size≤10% of cement, the 3d comprcssive strength >=12.0Mpa of cement, 28d comprcssive strength >=the 32.5Mpa of cement, the Fast Anti of cement tears intensity >=5.5Mpa open, and the 3d of cement is anti-tears intensity >=2.5 open, and the 28d of cement is anti-tears intensity >=5.5 open.
A kind of road side stone the most according to claim 1, it is characterised in that: described reinforcing agent uses concrete intensifier, and described auxiliary agent uses ethylene-vinyl acetate copolymer.
A kind of road side stone the most according to claim 1, it is characterised in that: described color pigment is grouped into by the one-tenth of following parts by weight: pigment 3-5 part, white cement 8-10 part, quartz sand 3-5 part.
6. the method for the road side stone described in a manufacturing claims 1-5 any one, it is characterised in that described preparation method specifically includes following steps:
A. raw material weighs: weigh color pigment 5-10 part, auxiliary agent 1-3 part, reinforcing agent 3-5 part, cement 15-20 part, coarse sand 10-15 part, fine sand 10-15 part, slag 5-10 part, coal ash 15-20 part, glass 5-8 part, pottery 6 parts, clay 15-20 part by mass percentage；
B. raw material pulverizing: be sequentially added in pulverizer by raw material and pulverize, grinding time is 1-3min；
C. mixing: material pulverizing completed adds water and stirs mixing, and mixing time is 5-10min；
D. compacting: mixed raw material rolling is kneaded into uniform mud bar, puts into road side stone mould and suppress；
E. maintenance: product is carried out maintenance, curing time is 24-48h；
F. the demoulding: the demoulding i.e. can get finished product.