CN105936737A - Multifunctional PVC pipe for electric power construction - Google Patents

Multifunctional PVC pipe for electric power construction Download PDF

Info

Publication number
CN105936737A
CN105936737A CN201610521701.9A CN201610521701A CN105936737A CN 105936737 A CN105936737 A CN 105936737A CN 201610521701 A CN201610521701 A CN 201610521701A CN 105936737 A CN105936737 A CN 105936737A
Authority
CN
China
Prior art keywords
parts
powder
resin
pvc
power construction
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610521701.9A
Other languages
Chinese (zh)
Inventor
王义金
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610521701.9A priority Critical patent/CN105936737A/en
Publication of CN105936737A publication Critical patent/CN105936737A/en
Pending legal-status Critical Current

Abstract

The invention relates to a multifunctional PVC pipe for electric power construction. The PVC pipe is composed of the following components: phenolic resin, diisopropanolamine, dicumyl peroxide, iodopropynyl butyl carbamate, cinnamaldehyde, isothiazolinone, tea polyphenol, sodium diacetate, montmorillonite powder, triazine resin, phenothiazine, zirconium silicate powder, linseed alkyd resin, polybutylene terephthalate, acrylamide, PVC resin powder, zinc phosphate, polyacrylic acid, titanium dioxide, cylindrin, arabinogalactan, propyl paraben, copper pyrithione, melamine cyanurate, vancomycin, cyclohexanone, lumisterin, zirconium dioxide powder, silicon carbide powder, kaolin, and linseed oil. The ingredients mentioned above are mixed together to form a novel composite toughened and enhanced system, the performance indexes such as toughness, rigidity, elastic modulus, and the like, are good; the anti-aging performance and using property of product are largely improved, and the anti-corrosion effect is good.

Description

A kind of multifunction power construction PVC
Technical field
The present invention relates to a kind of multifunction power construction PVC, belong to technical field of electric power construction.
Background technology
During power construction is installed, it is often necessary to use multiple tubing, in order to electric wire or other power products utilize tubing to pacify Dress, plays protection and beauty function, and general tubing uses, and poor effect affects its service life, the most more Defencive function, it is necessary to use suitable method improve.
Summary of the invention
It is an object of the invention to provide a kind of multifunction power construction PVC, in order to be better achieved multi-functional The defencive function of power construction PVC.
To achieve these goals, technical scheme is as follows.
A kind of multifunction power construction PVC, is made up of the component of following mass fraction: phenolic resin 16～20 Part, diisopropanolamine (DIPA) 18～22 parts, cumyl peroxide 14～18 parts, iodo propinyl ammonia butyl formate 12～16 Part, cinnamic aldehyde 18～22 parts, isothiazolone 14～18 parts, tea polyphenols 12～16 parts, sodium diacetate 18～22 parts, Montmorillonite powder 14～18 parts, cyanate resin 12～16 parts, phenothiazine 18～22 parts, zirconium English powder 14～18 parts, Caulis et Folium Lini Oil alkyd resin 14～18 parts, polybutylene terephthalate (PBT) 12～16 parts, acrylamide 18～22 parts, PVC Resin-oatmeal 14～18 parts, zinc phosphate 12～16 parts, polyacrylic acid 18～22 parts, titanium dioxide 14～18 parts, Cylindrin 12～16 parts, arabinogalactan 18～22 parts, propylparaben 14～18 parts, copper pyrithione 12～16 parts, Melamine cyanurate 18～22 parts, vancomycin 14～18 parts, Ketohexamethylene 14～18 parts, lumisterol 14～18 Part, Zirconium dioxide powder 14～18 parts, silicon carbide powder 14～18 parts, Kaolin 14～18 parts, oleum lini 14～ 18 parts.
Further, above-mentioned multifunction power construction PVC, it is made up of the component of following mass fraction: phenolic aldehyde tree 16 parts of fat, diisopropanolamine (DIPA) 18 parts, cumyl peroxide 14 parts, iodo propinyl ammonia butyl formate 12 parts, meat Cinnamic aldehyde 18 parts, isothiazolone 14 parts, tea polyphenols 12 parts, sodium diacetate 18 parts, montmorillonite powder 14 parts, triazine Resin 12 parts, phenothiazine 18 parts, 14 parts of zirconium English powder, oleum lini alkyd resin 14 parts, polybutylene terephthalate Ester 12 parts, acrylamide 18 parts, PVC resin powder 14 parts, zinc phosphate 12 parts, polyacrylic acid 18 parts, titanium dioxide 14 parts, Cylindrin 12 parts, arabinogalactan 18 parts, propylparaben 14 parts, copper pyrithione 12 parts, three Poly cyanamid cyanurate 18 parts, vancomycin 14 parts, Ketohexamethylene 14 parts, lumisterol 14 parts, Zirconium dioxide powder 14 Part, silicon carbide powder 14 parts, Kaolin 14 parts, oleum lini 14 parts.
Further, above-mentioned multifunction power construction PVC, it is made up of the component of following mass fraction: phenolic aldehyde tree 18 parts of fat, diisopropanolamine (DIPA) 20 parts, cumyl peroxide 16 parts, iodo propinyl ammonia butyl formate 14 parts, meat Cinnamic aldehyde 20 parts, isothiazolone 16 parts, tea polyphenols 14 parts, sodium diacetate 20 parts, montmorillonite powder 16 parts, triazine Resin 14 parts, phenothiazine 20 parts, 16 parts of zirconium English powder, oleum lini alkyd resin 16 parts, polybutylene terephthalate Ester 14 parts, acrylamide 20 parts, PVC resin powder 16 parts, zinc phosphate 14 parts, polyacrylic acid 20 parts, titanium dioxide 16 parts, Cylindrin 14 parts, arabinogalactan 20 parts, propylparaben 16 parts, copper pyrithione 14 parts, three Poly cyanamid cyanurate 20 parts, vancomycin 16 parts, Ketohexamethylene 16 parts, lumisterol 16 parts, Zirconium dioxide powder 16 Part, silicon carbide powder 16 parts, Kaolin 16 parts, oleum lini 16 parts.
Further, above-mentioned multifunction power construction PVC, it is made up of the component of following mass fraction: phenolic aldehyde tree 20 parts of fat, diisopropanolamine (DIPA) 22 parts, cumyl peroxide 18 parts, iodo propinyl ammonia butyl formate 16 parts, meat Cinnamic aldehyde 22 parts, isothiazolone 18 parts, tea polyphenols 16 parts, sodium diacetate 22 parts, montmorillonite powder 18 parts, triazine Resin 16 parts, phenothiazine 22 parts, 18 parts of zirconium English powder, oleum lini alkyd resin 18 parts, polybutylene terephthalate Ester 16 parts, acrylamide 22 parts, PVC resin powder 18 parts, zinc phosphate 16 parts, polyacrylic acid 22 parts, titanium dioxide 18 parts, Cylindrin 16 parts, arabinogalactan 22 parts, propylparaben 18 parts, copper pyrithione 16 parts, three Poly cyanamid cyanurate 22 parts, vancomycin 18 parts, Ketohexamethylene 18 parts, lumisterol 18 parts, Zirconium dioxide powder 18 Part, silicon carbide powder 18 parts, Kaolin 18 parts, oleum lini 18 parts.
Further, above-mentioned multifunction power construction PVC preparation method step is as follows:
(1) by the phenolic resin of described mass fraction, diisopropanolamine (DIPA), cumyl peroxide, iodo propinyl ammonia Butyl formate, cinnamic aldehyde, isothiazolone, phenothiazine, zirconium English powder, oleum lini alkyd resin, poly terephthalic acid fourth Diol ester, acrylamide, PVC resin powder, zinc phosphate, propylparaben, copper pyrithione, melamine cyanurate Salt, vancomycin, Ketohexamethylene, lumisterol, Zirconium dioxide powder, silicon carbide powder, Kaolin, oleum lini are mixed Closing, ultrasonic high speed dispersion, ultrasonic frequency is 20～40KHz, rate of dispersion 5000～5400r/min, jitter time It is 30～60min；
(2) adding the tea polyphenols of described mass fraction, sodium diacetate, montmorillonite powder, cyanate resin, ultrasonic high speed is divided Dissipating, ultrasonic frequency is 20～35KHz, rate of dispersion 4800～5200r/min, and jitter time is 30～50min；
(3) polyacrylic acid of described mass fraction, titanium dioxide, Cylindrin, arabinogalactan are added, ultrasonic height Speed dispersion, ultrasonic frequency is 20～30KHz, rate of dispersion 4600～4800r/min, and jitter time is 20～40min； Mixture is prepared after mix homogeneously；Add mixture to again and double screw extruder carries out melting mixing, obtain further Desired mixt；
(4) being extruded in an extruder by the mixture that step (3) obtains, it is thus achieved that finished product, wherein, extrusion condition is: Barrel temperature: 184 ± 2 DEG C, merging core temperature: 176 ± 2 DEG C, head temperature: 190 ± 5 DEG C, traction: 0.6～0.9m/min, Engine speed: 25～30 revs/min.
This beneficial effect of the invention is: the present invention relates to a kind of multifunction power construction PVC, by following group Be grouped into: phenolic resin, diisopropanolamine (DIPA), cumyl peroxide, iodo propinyl ammonia butyl formate, cinnamic aldehyde, Isothiazolone, tea polyphenols, sodium diacetate, montmorillonite powder, cyanate resin, phenothiazine, zirconium English powder, oleum lini alkyd Resin, polybutylene terephthalate (PBT), acrylamide, PVC resin powder, zinc phosphate, polyacrylic acid, titanium dioxide, Cylindrin, arabinogalactan, propylparaben, copper pyrithione, melamine cyanurate, vancomycin, Ketohexamethylene, lumisterol, Zirconium dioxide powder, silicon carbide powder, Kaolin, oleum lini.The multiple dispensing of the present invention is mutual Mixing, forms novel composite toughening and strengthens system, and toughness, rigidity, elastic modelling quantity performance indications are preferable, are greatly improved The ageing resistace of product and serviceability, have preferable anticorrosion effect.The present invention has preferable combination property, Using effect is good.Product of the present invention has the most corrosion-resistant, fire protection flame retarding, anti-mildew, anti-microbial property.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is described, in order to be better understood from the present invention.
Embodiment 1
Multifunction power construction PVC in the present embodiment, is made up of the component of following mass fraction: phenolic aldehyde tree 16 parts of fat, diisopropanolamine (DIPA) 18 parts, cumyl peroxide 14 parts, iodo propinyl ammonia butyl formate 12 parts, meat Cinnamic aldehyde 18 parts, isothiazolone 14 parts, tea polyphenols 12 parts, sodium diacetate 18 parts, montmorillonite powder 14 parts, triazine Resin 12 parts, phenothiazine 18 parts, 14 parts of zirconium English powder, oleum lini alkyd resin 14 parts, polybutylene terephthalate Ester 12 parts, acrylamide 18 parts, PVC resin powder 14 parts, zinc phosphate 12 parts, polyacrylic acid 18 parts, titanium dioxide 14 parts, Cylindrin 12 parts, arabinogalactan 18 parts, propylparaben 14 parts, copper pyrithione 12 parts, three Poly cyanamid cyanurate 18 parts, vancomycin 14 parts, Ketohexamethylene 14 parts, lumisterol 14 parts, Zirconium dioxide powder 14 Part, silicon carbide powder 14 parts, Kaolin 14 parts, oleum lini 14 parts.
Above-mentioned multifunction power construction PVC preparation method step is as follows:
(1) by the phenolic resin of described mass fraction, diisopropanolamine (DIPA), cumyl peroxide, iodo propinyl ammonia Butyl formate, cinnamic aldehyde, isothiazolone, phenothiazine, zirconium English powder, oleum lini alkyd resin, poly terephthalic acid fourth Diol ester, acrylamide, PVC resin powder, zinc phosphate, propylparaben, copper pyrithione, melamine cyanurate Salt, vancomycin, Ketohexamethylene, lumisterol, Zirconium dioxide powder, silicon carbide powder, Kaolin, oleum lini are mixed Closing, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 5400r/min, and jitter time is 60min；
(2) adding the tea polyphenols of described mass fraction, sodium diacetate, montmorillonite powder, cyanate resin, ultrasonic high speed is divided Dissipating, ultrasonic frequency is 20kHz, rate of dispersion about 5200r/min, and jitter time is 50min；
(3) polyacrylic acid of described mass fraction, titanium dioxide, Cylindrin, arabinogalactan are added, ultrasonic height Speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 4800r/min, and jitter time is 40min；Mixing is all Mixture is prepared after even；Add mixture to again and double screw extruder carries out melting mixing, obtain required mixed further Compound；
(4) being extruded in an extruder by the mixture that step (3) obtains, it is thus achieved that finished product, wherein, extrusion condition is: Barrel temperature: 184 ± 2 DEG C, merging core temperature: 176 ± 2 DEG C, head temperature: 190 ± 5 DEG C, traction: 0.6～0.9m/min, Engine speed: 25～30 revs/min.
Embodiment 2
Multifunction power construction PVC in the present embodiment, is made up of the component of following mass fraction: phenolic resin 18 parts, diisopropanolamine (DIPA) 20 parts, cumyl peroxide 16 parts, iodo propinyl ammonia butyl formate 14 parts, Cortex Cinnamomi 20 parts of aldehyde, isothiazolone 16 parts, tea polyphenols 14 parts, sodium diacetate 20 parts, montmorillonite powder 16 parts, triazine tree 14 parts of fat, phenothiazine 20 parts, 16 parts of zirconium English powder, oleum lini alkyd resin 16 parts, polybutylene terephthalate (PBT) 14 parts, acrylamide 20 parts, PVC resin powder 16 parts, zinc phosphate 14 parts, polyacrylic acid 20 parts, titanium dioxide 16 Part, Cylindrin 14 parts, arabinogalactan 20 parts, propylparaben 16 parts, copper pyrithione 14 parts, trimerization Cyanamide cyanurate 20 parts, vancomycin 16 parts, Ketohexamethylene 16 parts, lumisterol 16 parts, Zirconium dioxide powder 16 Part, silicon carbide powder 16 parts, Kaolin 16 parts, oleum lini 16 parts.
Above-mentioned multifunction power construction PVC preparation method step is as follows:
(1) by the phenolic resin of described mass fraction, diisopropanolamine (DIPA), cumyl peroxide, iodo propinyl ammonia Butyl formate, cinnamic aldehyde, isothiazolone, phenothiazine, zirconium English powder, oleum lini alkyd resin, poly terephthalic acid fourth Diol ester, acrylamide, PVC resin powder, zinc phosphate, propylparaben, copper pyrithione, melamine cyanurate Salt, vancomycin, Ketohexamethylene, lumisterol, Zirconium dioxide powder, silicon carbide powder, Kaolin, oleum lini are mixed Closing, ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion about 5200r/min, and jitter time is 45min；
(2) adding the tea polyphenols of described mass fraction, sodium diacetate, montmorillonite powder, cyanate resin, ultrasonic high speed is divided Dissipating, ultrasonic frequency is 27kHz, rate of dispersion about 5000r/min, and jitter time is 40min；
(3) polyacrylic acid of described mass fraction, titanium dioxide, Cylindrin, arabinogalactan are added, ultrasonic height Speed dispersion, ultrasonic frequency is 25kHz, rate of dispersion about 4700r/min, and jitter time is 30min；Mixing is all Mixture is prepared after even；Add mixture to again and double screw extruder carries out melting mixing, obtain required mixed further Compound；
(4) being extruded in an extruder by the mixture that step (3) obtains, it is thus achieved that finished product, wherein, extrusion condition is: Barrel temperature: 184 ± 2 DEG C, merging core temperature: 176 ± 2 DEG C, head temperature: 190 ± 5 DEG C, traction: 0.6～0.9m/min, Engine speed: 25～30 revs/min.
Embodiment 3
Multifunction power construction PVC in the present embodiment, is made up of the component of following mass fraction: phenolic aldehyde tree 20 parts of fat, diisopropanolamine (DIPA) 22 parts, cumyl peroxide 18 parts, iodo propinyl ammonia butyl formate 16 parts, meat Cinnamic aldehyde 22 parts, isothiazolone 18 parts, tea polyphenols 16 parts, sodium diacetate 22 parts, montmorillonite powder 18 parts, triazine Resin 16 parts, phenothiazine 22 parts, 18 parts of zirconium English powder, oleum lini alkyd resin 18 parts, polybutylene terephthalate Ester 16 parts, acrylamide 22 parts, PVC resin powder 18 parts, zinc phosphate 16 parts, polyacrylic acid 22 parts, titanium dioxide 18 parts, Cylindrin 16 parts, arabinogalactan 22 parts, propylparaben 18 parts, copper pyrithione 16 parts, three Poly cyanamid cyanurate 22 parts, vancomycin 18 parts, Ketohexamethylene 18 parts, lumisterol 18 parts, Zirconium dioxide powder 18 Part, silicon carbide powder 18 parts, Kaolin 18 parts, oleum lini 18 parts.
Above-mentioned multifunction power construction PVC preparation method step is as follows:
(1) by the phenolic resin of described mass fraction, diisopropanolamine (DIPA), cumyl peroxide, iodo propinyl ammonia Butyl formate, cinnamic aldehyde, isothiazolone, phenothiazine, zirconium English powder, oleum lini alkyd resin, poly terephthalic acid fourth Diol ester, acrylamide, PVC resin powder, zinc phosphate, propylparaben, copper pyrithione, melamine cyanurate Salt, vancomycin, Ketohexamethylene, lumisterol, Zirconium dioxide powder, silicon carbide powder, Kaolin, oleum lini are mixed Closing, ultrasonic high speed dispersion, ultrasonic frequency is 40kHz, rate of dispersion 5000r/min, and jitter time is 30min；(2) Add the tea polyphenols of described mass fraction, sodium diacetate, montmorillonite powder, cyanate resin, ultrasonic high speed dispersion, ultrasound wave Frequency is 35kHz, rate of dispersion 4800r/min, and jitter time is 30min；(3) poly-the third of described mass fraction is added Olefin(e) acid, titanium dioxide, Cylindrin, arabinogalactan, ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, dispersion About speed 4600r/min, jitter time is 20min；Mixture is prepared after mix homogeneously；Add mixture to again Double screw extruder carries out melting mixing, obtains desired mixt further；(4) mixing that step (3) is obtained Thing is extruded in an extruder, it is thus achieved that finished product, and wherein, extrusion condition is: barrel temperature: 184 ± 2 DEG C, merging core temperature: 176 ± 2 DEG C, head temperature: 190 ± 5 DEG C, traction: 0.6～0.9m/min, engine speed: 25～30 revs/min.
Above-described embodiment 1, embodiment 2 and the tubing obtained by embodiment 3 are carried out performance measurement, and with certain commercially available pipe As a control group, as shown in Table 1 and Table 2, embodiment of the present invention product shows more excellent property to measured performance to material Energy.
Table 1
Performance measurement Embodiment 1 Embodiment 2 Embodiment 3 Matched group
Yield strength (MPa) 40 42 41 25
Tensile modulus of elasticity (MPa) 2775 2848 2675 1354
The modulus of elasticity in static bending (GPa) 2.6 2.9 2.5 1.5
Comprcssive strength (MPa) 115 122 118 42
Longitudinal extension rate (%) 1.8 1.9 1.7 9.9
Tracheid shape properties (μm) 90 82 89 151
Heat conductivity λ (W/m k) 0.15 0.16 0.13 0.11
Table 2
As seen from Table 2, product of the present invention has the most corrosion-resistant, fire protection flame retarding, anti-mildew, anti-microbial property.
The above is the preferred embodiment of the present invention, it is noted that come for those skilled in the art Saying, under the premise without departing from the principles of the invention, it is also possible to make some improvements and modifications, these improvements and modifications also regard For protection scope of the present invention.

Claims (5)

  1. null1. a multifunction power construction PVC，It is characterized in that: be made up of the component of following mass fraction: phenolic resin 16～20 parts、Diisopropanolamine (DIPA) 18～22 parts、Cumyl peroxide 14～18 parts、Iodo propinyl ammonia butyl formate 12～16 parts、Cinnamic aldehyde 18～22 parts、Isothiazolone 14～18 parts、Tea polyphenols 12～16 parts、Sodium diacetate 18～22 parts、Montmorillonite powder 14～18 parts、Cyanate resin 12～16 parts、Phenothiazine 18～22 parts、Zirconium English powder 14～18 parts、Oleum lini alkyd resin 14～18 parts、Polybutylene terephthalate (PBT) 12～16 parts、Acrylamide 18～22 parts、PVC resin powder 14～18 parts、Zinc phosphate 12～16 parts、Polyacrylic acid 18～22 parts、Titanium dioxide 14～18 parts、Cylindrin 12～16 parts、Arabinogalactan 18～22 parts、Propylparaben 14～18 parts、Copper pyrithione 12～16 parts、Melamine cyanurate 18～22 parts、Vancomycin 14～18 parts、Ketohexamethylene 14～18 parts、Lumisterol 14～18 parts、Zirconium dioxide powder 14～18 parts、Silicon carbide powder 14～18 parts、Kaolin 14～18 parts、Oleum lini 14～18 parts.
  2. nullMultifunction power construction PVC the most according to claim 1，It is characterized in that: described multifunction power construction PVC is made up of the component of following mass fraction: 16 parts of phenolic resin、Diisopropanolamine (DIPA) 18 parts、Cumyl peroxide 14 parts、Iodo propinyl ammonia butyl formate 12 parts、Cinnamic aldehyde 18 parts、Isothiazolone 14 parts、Tea polyphenols 12 parts、Sodium diacetate 18 parts、Montmorillonite powder 14 parts、Cyanate resin 12 parts、Phenothiazine 18 parts、14 parts of zirconium English powder、Oleum lini alkyd resin 14 parts、Polybutylene terephthalate (PBT) 12 parts、Acrylamide 18 parts、PVC resin powder 14 parts、Zinc phosphate 12 parts、Polyacrylic acid 18 parts、Titanium dioxide 14 parts、Cylindrin 12 parts、Arabinogalactan 18 parts、Propylparaben 14 parts、Copper pyrithione 12 parts、Melamine cyanurate 18 parts、Vancomycin 14 parts、Ketohexamethylene 14 parts、Lumisterol 14 parts、Zirconium dioxide powder 14 parts、Silicon carbide powder 14 parts、Kaolin 14 parts、Oleum lini 14 parts.
  3. null3. according to the multifunction power construction PVC described in claim 1 to 2，It is characterized in that: described multifunction power construction PVC is made up of the component of following mass fraction: 18 parts of phenolic resin、Diisopropanolamine (DIPA) 20 parts、Cumyl peroxide 16 parts、Iodo propinyl ammonia butyl formate 14 parts、Cinnamic aldehyde 20 parts、Isothiazolone 16 parts、Tea polyphenols 14 parts、Sodium diacetate 20 parts、Montmorillonite powder 16 parts、Cyanate resin 14 parts、Phenothiazine 20 parts、16 parts of zirconium English powder、Oleum lini alkyd resin 16 parts、Polybutylene terephthalate (PBT) 14 parts、Acrylamide 20 parts、PVC resin powder 16 parts、Zinc phosphate 14 parts、Polyacrylic acid 20 parts、Titanium dioxide 16 parts、Cylindrin 14 parts、Arabinogalactan 20 parts、Propylparaben 16 parts、Copper pyrithione 14 parts、Melamine cyanurate 20 parts、Vancomycin 16 parts、Ketohexamethylene 16 parts、Lumisterol 16 parts、Zirconium dioxide powder 16 parts、Silicon carbide powder 16 parts、Kaolin 16 parts、Oleum lini 16 parts.
  4. null4. according to the multifunction power construction PVC described in claims 1 to 3，It is characterized in that: described multifunction power construction PVC is made up of the component of following mass fraction: 20 parts of phenolic resin、Diisopropanolamine (DIPA) 22 parts、Cumyl peroxide 18 parts、Iodo propinyl ammonia butyl formate 16 parts、Cinnamic aldehyde 22 parts、Isothiazolone 18 parts、Tea polyphenols 16 parts、Sodium diacetate 22 parts、Montmorillonite powder 18 parts、Cyanate resin 16 parts、Phenothiazine 22 parts、18 parts of zirconium English powder、Oleum lini alkyd resin 18 parts、Polybutylene terephthalate (PBT) 16 parts、Acrylamide 22 parts、PVC resin powder 18 parts、Zinc phosphate 16 parts、Polyacrylic acid 22 parts、Titanium dioxide 18 parts、Cylindrin 16 parts、Arabinogalactan 22 parts、Propylparaben 18 parts、Copper pyrithione 16 parts、Melamine cyanurate 22 parts、Vancomycin 18 parts、Ketohexamethylene 18 parts、Lumisterol 18 parts、Zirconium dioxide powder 18 parts、Silicon carbide powder 18 parts、Kaolin 18 parts、Oleum lini 18 parts.
  5. Multifunction power construction PVC the most according to claim 1, it is characterised in that: described multifunction power construction PVC preparation method step is as follows:
    (1) by the phenolic resin of described mass fraction, diisopropanolamine (DIPA), cumyl peroxide, iodo propinyl ammonia butyl formate, cinnamic aldehyde, isothiazolone, phenothiazine, zirconium English powder, oleum lini alkyd resin, polybutylene terephthalate (PBT), acrylamide, PVC resin powder, zinc phosphate, propylparaben, copper pyrithione, melamine cyanurate, vancomycin, Ketohexamethylene, lumisterol, Zirconium dioxide powder, silicon carbide powder, Kaolin, oleum lini is mixed, ultrasonic high speed dispersion, ultrasonic frequency is 20～40KHz, rate of dispersion is about 5000～5400r/min, jitter time is 30～about 60min；
    (2) adding the tea polyphenols of described mass fraction, sodium diacetate, montmorillonite powder, cyanate resin, ultrasonic high speed dispersion, ultrasonic frequency is 20～35KHz, and rate of dispersion is about 4800～5200r/min, and jitter time is about 30～50min；
    (3) adding the polyacrylic acid of described mass fraction, titanium dioxide, Cylindrin, arabinogalactan, ultrasonic high speed dispersion, ultrasonic frequency is 20～30KHz, and rate of dispersion is about 4600～4800r/min, and jitter time is 20～about 40min；Mixture is prepared after mix homogeneously；Add mixture to again and double screw extruder carries out melting mixing, obtain desired mixt further；
    (4) mixture that step (3) obtains is extruded in an extruder, it is thus achieved that finished product, wherein, extrusion condition is: barrel temperature: 184 ± 2 DEG C, merging core temperature: 176 ± 2 DEG C, head temperature: 190 ± 5 DEG C, traction: 0.6～0.9m/min, engine speed: 25～30 revs/min.
CN201610521701.9A 2016-06-29 2016-06-29 Multifunctional PVC pipe for electric power construction Pending CN105936737A (en)