CN105924050A - Oil-proof mortar and preparation method thereof - Google Patents
Oil-proof mortar and preparation method thereof Download PDFInfo
- Publication number
- CN105924050A CN105924050A CN201610394981.1A CN201610394981A CN105924050A CN 105924050 A CN105924050 A CN 105924050A CN 201610394981 A CN201610394981 A CN 201610394981A CN 105924050 A CN105924050 A CN 105924050A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- resistance
- cement
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses oil-proof mortar and a preparation method thereof. The oil-proof mortar comprises the following components in parts by mass: 240 to 520 parts of cement, 250 to 650 parts of quartzose sand, 30 to 70 parts of a compound compacting agent, 70 to 130 parts of superfine slag powder, 10 to 16 parts of redispersible latex powder, 1 to 3 parts of a macromolecular polymer, 1 to 5 parts of an early strength agent and 1 to 3 parts of a thixotropic agent. Compared with an existing similar product and technology, the oil-proof mortar is resistant to penetration of various kinds of oil, high in construction performance, strong in adhesive force with a substrate and free of hollowing and cracking. Oil-proof concrete can be prepared by adding 20 to 30 percent of dry and compact 5 to 35mm-grade assistant stones to the product.
Description
Technical field
The invention belongs to building material technical field, relate to a kind of resistance to oil sand slurry and preparation method thereof.
Background technology
There are the following problems for common resistance to oil sand slurry: 1, seepage-resistant grade is low, causes it can not stop all kinds of oil completely
Fat permeates, and causes concrete destruction;2 and substrate concrete cohesive force poor, easily cause the most resistance to oil-sand of hollowing
Pulp layer comes off;3, workability is not good enough;4, poor water retention property, easily there is dry shrinkage and cracking in mortar surface.
Summary of the invention
Low in order to solve like product seepage-resistant grade;All kinds of fat migration basic units damage;Workability is poor;
Low with basic unit cohesive force, hollowing problems of crack easily occurs.The invention provides a kind of resistance to oil sand slurry and preparation thereof
Method.
The purpose of the present invention is achieved through the following technical solutions: a kind of resistance to oil sand slurry, component and mass fraction are such as
Under: cement 240~520 parts, quartziferous graded sand 250~650 parts, compounding compacting agent 30~70 parts,
Slag micropowder 70~130 parts, redispersable latex powder 10~16 parts, high molecular polymer 1~3 parts, early
Strong agent 1~5 parts, thixotropic agent 1~3 parts.
Preferably, described cement is 42.5 grades of superfine cements, and described slag micropowder is S95 or higher level, institute
State redispersable latex powder for Germany's importDescribed high molecular polymer is hydroxypropyl
Methylcellulose (HPMC), described early strength agent is calcium formate, and described thixotropic agent is import 602 type dry-mixed mortar
Special thixotropic agent.
Preferably, cement 280 parts, quartziferous graded sand 550 parts, compounding compacting agent 50 parts, S95 and
Higher level slag micropowder 100 parts, redispersable latex powder 13 parts, high molecular polymer 2 parts, early strength agent 3
Part, thixotropic agent 2 parts.
Preferably, cement 300 parts, quartziferous graded sand 550 parts, compounding compacting agent 50 parts, S95 and
Higher level slag micropowder 80 parts, redispersable latex powder 13 parts, high molecular polymer 2 parts, early strength agent 3
Part, thixotropic agent 2 parts.
Preferably, cement 300 parts, quartziferous graded sand 550 parts, compounding compacting agent 50 parts, S95 and
Higher level slag micropowder 82 parts, redispersable latex powder 10 parts, high molecular polymer 3 parts, early strength agent 3
Part, thixotropic agent 2 parts.
Preferably, cement 290 parts, quartziferous graded sand 550 parts, compounding compacting agent 50 parts, S95 and
Higher level slag micropowder 90 parts, redispersable latex powder 12 parts, high molecular polymer 3 parts, early strength agent 3
Part, thixotropic agent 2 parts.
The preparation method of a kind of resistance to oil sand slurry, comprises the steps:
1), cement, quartziferous graded sand importing equipment are imported respective pre-homogenizing storehouse and carries out pre-homogenizing;
2), control to carry out continuous batching by computer according to part by weight;
3), compound stirring at low speed 35 minutes in forced stirrer of preparing, then moderate-speed mixer 46 points
Clock;
4) dry mash, mixed imports finished product homogenizing storehouse;
5), electronic measurement is packed automatically;
6), finished product warehouse-in.
The operation principle of the present invention and process prescription:
1, selecting superfine cement and slag micropowder as Binder Materials, its total surface area is much larger than the summary table of aggregate
Area, studying and putting into practice the most fully proves, " total surface area of adhesive material is more than the total surface area of aggregate,
I.e. can be made into oil-proof concrete ", this is the basis that resistance to oil sand slurry stops all kinds of fat migration.And, slag is micro-
Powder also has the function of filling fine pore and capillary tube concurrently.
2, the introducing of compounding compacting agent, introduces alunite [aluminum potassium sulfate KAl (SO in this resistance to oil sand slurry4)2]、
Formation entringite (C is reacted with hydrolysis product of cement3A·3CaSO4·32H2O), wet mortar is by crystallographic expansion
Stress effect, on the one hand compensate for shrinking, eliminates crackle and make again Behavior of Hardened Cement Paste more they tend to densification.Research and practice
Prove: the pore of ferric hydroxide gel blocking hydration and hardening body, it is possible to stop the infiltration of each quasi-grease;Add
Various gels, are more than 280 μ apertures in hydrated calcium silicate gel (C-S-H) further fill concrete
Harmful hole, mortar watertightness, impermeability are improved.
3, the interpolation of redispersable latex powder, hardened mortar pore structure forms the continuous thin film closed, and (what is called has
Machine inorganic crosslinking structure) so that the corrosion resistance of mortar hydration and hardening body is greatly strengthened, and mixes with basic unit
The cohesive force of solidifying soil strengthens at double, improves corrosion resistance and the durability of resistance to oil sand slurry.
4, early strength agent calcium formate makes this hydration and hardening of resistance to oil sand slurry process accelerate.
5, this resistance to oil sand slurry selects quartziferous graded sand as aggregate, meets closestpacking principle so that
Hydration and hardening body is more densely cross-linked.
6, thixotropic agent and water-retaining admixture (HPMC) so that this resistance to oil sand slurry workability and cracking resistance
It is greatly improved.
7, electronic computer controls lower factorial praluction, and proportioning is precisely consistent, and quality is the neatest.
The medicine have the advantages that compared with existing like product and technology, this resistance to oil sand slurry resists each quasi-grease
Infiltration, has good workability, and strong with basic unit cohesive force, hollowing does not ftractures.This product adds 20%~30%
It is dried 5~35mm closely knit grating stones, can be made into oil-proof concrete.It addition, have the further advantage that
1, this resistance to oil sand slurry have employed compounding compacting agent, and anti-all kinds of fat migration performances are remarkable.
2, this resistance to oil sand slurry have employed Germany's import redispersable latex powderModification,
Organic material and the cross-linked structure of inorganic material is formed after mortar hardening, the most more densely cross-linked, more impervious.
3, this resistance to oil sand slurry is high with basic unit cohesive force, and workability is excellent, not hollowing, do not ftracture.
4, this resistance to oil sand slurry interpolation 20%~30% is dried closely knit 5~35mm grating stone, can make
Become oil-proof concrete.The premixing large-scale production of this resistance to oil sand slurry factory, product quality is the most stable.
Detailed description of the invention
The present invention is described further in conjunction with the embodiments.
A kind of resistance to oil sand slurry, component and mass fraction are as follows: cement 240~520 parts, quartziferous graded sand
250~650 parts, compounding compacting agent 30~70 parts, slag micropowder 70~130 parts, redispersable latex powder
10~16 parts, high molecular polymer 1~3 parts, early strength agent 1~5 parts, thixotropic agent 1~3 parts.
Example one
A kind of resistance to oil sand slurry and manufacturing technology thereof, this oil resistant slurry component and mass fraction are as follows: cement 280
Part, quartziferous graded sand 550 parts, compounding compacting agent 50 parts, S95 and higher level slag micropowder 100 parts,
Redispersable latex powder 13 parts, high molecular polymer 2 parts, early strength agent 3 parts, thixotropic agent 2 parts.Wherein institute
Stating cement is 42.5 grades of superfine cements, and described quartziferous graded sand is the artificial sand meeting closestpacking principle
(modulus of fineness < 2.5), described compounding compacting agent is that hydrated ferric oxide. and expansion component are compounding to be obtained.Described slag
Micropowder is S95 or higher level, and described redispersable latex powder is for being Germany's importInstitute
Stating high molecular polymer is hydroxypropyl methyl cellulose (HPMC), and described early strength agent is calcium formate, described thixotroping
Agent is the import 602 special thixotropic agent of type dry-mixed mortar.
The manufacture method of above-mentioned resistance to oil sand slurry is as follows:
1), cement, quartziferous graded sand importing equipment are imported respective pre-homogenizing storehouse and carries out pre-homogenizing;
2), control to carry out continuous batching by computer according to above-mentioned part by weight;
3), compound stirring at low speed 3-5 minute in HZ-20 type forced stirrer of preparing, then middling speed stirs
Mix 4-6 minute;
4) dry mash, mixed imports finished product homogenizing storehouse;
5), electronic measurement is packed automatically;
6), finished product warehouse-in.
Implementation result: Product checking the results are shown in Table 1
Example two
A kind of resistance to oil sand slurry and manufacturing technology thereof, this oil resistant slurry component and mass fraction are as follows: cement 300
Part, quartziferous graded sand 550 parts, compounding compacting agent 50 parts, S95 and higher level slag micropowder 80 parts,
Redispersable latex powder 13 parts, high molecular polymer 2 parts, early strength agent 3 parts, thixotropic agent 2 parts.Wherein institute
Stating cement is 42.5 grades of superfine cements, and described quartziferous graded sand is the artificial sand meeting closestpacking principle
(modulus of fineness < 2.5), described compounding compacting agent is that hydrated ferric oxide. and expansion component are compounding to be obtained.Described slag
Micropowder is S95 or higher level, and described redispersable latex powder is for being Germany's importInstitute
Stating high molecular polymer is hydroxypropyl methyl cellulose (HPMC), and described early strength agent is calcium formate, described thixotroping
Agent is the import 602 special thixotropic agent of type dry-mixed mortar.
The manufacture method of above-mentioned resistance to oil sand slurry is with example one.
Implementation result: Product checking the results are shown in Table 1
Example three
A kind of resistance to oil sand slurry and manufacturing technology thereof, this oil resistant slurry component and mass fraction are as follows: cement 300
Part, quartziferous graded sand 550 parts, compounding compacting agent 50 parts, S95 and higher level slag micropowder 82 parts,
Redispersable latex powder 10 parts, high molecular polymer 3 parts, early strength agent 3 parts, thixotropic agent 2 parts.Wherein institute
Stating cement is 42.5 grades of superfine cements, and described quartziferous graded sand is the artificial sand meeting closestpacking principle
(modulus of fineness < 2.5), described compounding compacting agent is that hydrated ferric oxide. and expansion component are compounding to be obtained.Described slag
Micropowder is S95 or higher level, and described redispersable latex powder is for being Germany's importInstitute
Stating high molecular polymer is hydroxypropyl methyl cellulose (HPMC), and described early strength agent is calcium formate, described thixotroping
Agent is the import 602 special thixotropic agent of type dry-mixed mortar.
The manufacture method of above-mentioned resistance to oil sand slurry is with example one.
Implementation result: Product checking the results are shown in Table 1
Example four
A kind of resistance to oil sand slurry and manufacturing technology thereof, this oil resistant slurry component and mass fraction are as follows: cement 290
Part, quartziferous graded sand 550 parts, compounding compacting agent 50 parts, S95 and higher level slag micropowder 90 parts,
Redispersable latex powder 12 parts, high molecular polymer 3 parts, early strength agent 3 parts, thixotropic agent 2 parts.Wherein institute
Stating cement is 42.5 grades of superfine cements, and described quartziferous graded sand is the artificial sand meeting closestpacking principle
(modulus of fineness < 2.5), described compounding compacting agent is that hydrated ferric oxide. and expansion component are compounding to be obtained.Described slag
Micropowder is S95 or higher level, and described redispersable latex powder is for being Germany's importInstitute
Stating high molecular polymer is hydroxypropyl methyl cellulose (HPMC), and described early strength agent is calcium formate, described thixotroping
Agent is the import 602 special thixotropic agent of type dry-mixed mortar.
The manufacture method of above-mentioned resistance to oil sand slurry is with example one.
Implementation result: Product checking the results are shown in Table 1
It is preferable to carry out Product checking result table 1
The foregoing is only four kinds of specific embodiments of the present invention, but embodiments of the invention are not limited to
This, any those skilled in the art is in the field of the invention, and change or the modification made all are contained
Within protection scope of the present invention.
Claims (7)
1. a resistance to oil sand slurry, it is characterised in that component and mass fraction are as follows: cement 240~520 parts, stone
English matter graded sand 250~650 parts, compounding compacting agent 30~70 parts, slag micropowder 70~130 parts,
Redispersable latex powder 10~16 parts, high molecular polymer 1~3 parts, early strength agent 1~5 parts, thixotroping
Agent 1~3 parts.
Resistance to oil sand slurry the most according to claim 1, it is characterised in that described cement is 42.5 grades of superfine cements,
Described slag micropowder is S95 or higher level, and described redispersable latex powder is Germany's import5010, described high molecular polymer is hydroxypropyl methyl cellulose (HPMC), and described morning is strong
Agent is calcium formate, and described thixotropic agent is the import 602 special thixotropic agent of type dry-mixed mortar.
Resistance to oil sand slurry the most according to claim 1 and 2, it is characterised in that cement 280 parts, quartz quality and grade
Join 550 parts of sand, compounding compacting agent 50 parts, S95 and higher level slag micropowder 100 parts, redispersible
Latex powder 13 parts, high molecular polymer 2 parts, early strength agent 3 parts, thixotropic agent 2 parts.
Resistance to oil sand slurry the most according to claim 1 and 2, it is characterised in that cement 300 parts, quartz quality and grade
Join 550 parts of sand, compounding compacting agent 50 parts, S95 and higher level slag micropowder 80 parts, redispersible breast
Rubber powder 13 parts, high molecular polymer 2 parts, early strength agent 3 parts, thixotropic agent 2 parts.
Resistance to oil sand slurry the most according to claim 1 and 2, it is characterised in that cement 300 parts, quartz quality and grade
Join 550 parts of sand, compounding compacting agent 50 parts, S95 and higher level slag micropowder 82 parts, redispersible breast
Rubber powder 10 parts, high molecular polymer 3 parts, early strength agent 3 parts, thixotropic agent 2 parts.
Resistance to oil sand slurry the most according to claim 1 and 2, it is characterised in that cement 290 parts, quartz quality and grade
Join 550 parts of sand, compounding compacting agent 50 parts, S95 and higher level slag micropowder 90 parts, redispersible breast
Rubber powder 12 parts, high molecular polymer 3 parts, early strength agent 3 parts, thixotropic agent 2 parts.
7. the preparation method of the resistance to oil sand slurry as described in claim 1-6 any one, it is characterised in that include
Following steps:
1), cement, quartziferous graded sand importing equipment are imported respective pre-homogenizing storehouse and carries out pre-homogenizing;
2), control to carry out continuous batching by computer according to part by weight;
3), compound stirring at low speed 3-5 minute in forced stirrer of preparing, then moderate-speed mixer 4-6 divides
Clock;
4) dry mash, mixed imports finished product homogenizing storehouse;
5), electronic measurement is packed automatically;
6), finished product warehouse-in.