CN105923027A - Safety measure appliance vehicle - Google Patents
Safety measure appliance vehicle Download PDFInfo
- Publication number
- CN105923027A CN105923027A CN201610376688.2A CN201610376688A CN105923027A CN 105923027 A CN105923027 A CN 105923027A CN 201610376688 A CN201610376688 A CN 201610376688A CN 105923027 A CN105923027 A CN 105923027A
- Authority
- CN
- China
- Prior art keywords
- parcel tray
- side plate
- melamine resin
- connecting rod
- side plates
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A safety measure appliance vehicle comprises a base. Four universal wheels are mounted at the four corners of the bottom of the base correspondingly. A fixing frame, two first side plates, two parallel second side plates and a first storage box are mounted on the base. The two first side plates are located between the two second side plates. A third storage box is mounted on one side of the upper portion of the fixing frame and located on the upper portions of the two second side plates. One second side plate is connected with the fixing frame, and a supporting seat is mounted on the side portion of the other second side plate. A second storage box is mounted on the upper portion of the supporting seat and located above the first storage box. One side of one second side plate is hinged to one end of one first connecting rod, and one side of the other second side plate is hinged to one end of the other first connecting rod. The other ends of the first connecting rods are hinge to one ends of second connecting rods. According to the safety measure appliance vehicle, the first side plates can be spread through the connecting rods; a fixing device can be used for fixing the first side plates after the first side plates are retracted. The safety measure appliance vehicle further has the advantages of being concise and compact in structure, low in manufacturing cost and easy and convenient to use.
Description
Technical field
The present invention relates to a kind of apparatus car, specifically a kind of safety measure apparatus car.
Background technology
At present, the safety appliance room in master control building when taking security tool, is needed to move in the tricycle master control building,
Need personnel's manual handling to come and go, take a substantial amount of time, and due to security tool such as rope buckle etc. in handling process
Structure is different, situation about being mutually wound around often occurs, and needs the consuming regular hour to process, just can be continuing with.
The design of existing safety measure apparatus bassinet structure is unreasonable, it is impossible to taking of convenient and safe instrument.
Summary of the invention
It is an object of the invention to provide a kind of safety measure apparatus car, it is possible to solve the problems referred to above.
The present invention for achieving the above object, is achieved through the following technical solutions: a kind of safety measure apparatus car, including base
Seat, the corner, bottom of pedestal is respectively mounted a universal wheel, mounting and fixing support on pedestal, two the first side plates, two parallel set
The second side plate put and the first parcel tray, two the first side plates are between two the second side plates, and the side, top of fixed mount is pacified
Filling the 3rd parcel tray, the 3rd parcel tray is positioned at the top of two the second side plates, and second side plate is connected with fixed mount, another
Second side plate sidepiece is installed and is supported seat, and the second parcel tray is installed on the top supporting seat, and the second parcel tray is positioned on the first parcel tray
Side, the both sides of two the second side plates are respectively articulated with one end of a head rod, the other end hinged second of head rod
One end of connecting rod, the other end of the second connecting rod is hinged with one end of the first corresponding side plate, the other end of the first side plate with
Pedestal is hinged, and the both sides of the 3rd parcel tray and the first side plate are respectively mounted fixing device.
In order to realize the purpose of the present invention further, it is also possible to by the following technical solutions: described fixing device is by fixing
Pipe, retainer ring, fixed plate, through hole, gripper shoe, connecting rod and counterweight are constituted, and fixing pipe is arranged on the end of the first side plate, support
Plate is arranged on the both sides of the 3rd parcel tray, and gripper shoe is vertically offered through hole, installs connecting rod in through hole, the upper end peace of connecting rod
Dress fixed plate, the top installation retainer ring of fixed plate, the lower end installation counterweight of connecting rod, connecting rod can coordinate with fixing pipe;Institute
State and push rod is set on fixed mount;Described 3rd parcel tray is several, and several 3rd parcel trays are arranged side by side;Described pedestal, first
Coating puigging on side plate, the second side plate, the first parcel tray, the second parcel tray and the 3rd parcel tray, puigging is by a kind of sound insulation
Material is made, a kind of deadener, in parts by weight, is made up of following raw material: modified melamine resin foam 50 ~ 60 parts, vitreous
Microballon 5 ~ 10 parts, perlite 5 ~ 10 parts, ceramics 5 ~ 10 parts, Tissuemat E 1 ~ 3 part, quartz sand 10 ~ 20 parts, mica powder 1 ~ 5 part
With aluminium oxide 2 ~ 5 parts;
Described modified melamine resin foam is prepared by following steps:
Tripolycyanamide, polyformaldehyde, aniline and furfural are added in reactor and obtains mixed liquor, in reactor, add hydroxide
The pH value of sodium regulation mixed liquor to 8 ~ 9, after mixed liquor be warming up to 75 ~ 85 DEG C react 45 ~ 75 minutes, continue to add in reactor
Enter Polyethylene Glycol, the temperature of reactor is warming up to 90 ~ 100 DEG C, cool down after reacting 30 ~ 60 minutes, obtain modified melamine resin;
The weight ratio of described tripolycyanamide, polyformaldehyde, aniline, furfural and Polyethylene Glycol is 1:4 ~ 8:2 ~ 4:0.5 ~ 1:0.2 ~ 0.5;
To stepAdding emulsifying agent in gained modified melamine resin, foaming agent and firming agent, under 1500 ~ 2000r/min
Stir 5 ~ 10 minutes, foamed solidification 1 hour in the baking oven of 70 ~ 80 DEG C, then baking oven is warming up to 100 ~ 110 DEG C of solidifications 1 ~ 2
Hour, obtain modified melamine resin foam;Described emulsifying agent is dodecyl sodium sulfate;Described foaming agent is normal hexane;Described
Firming agent is acrylic acid;The mass ratio of described modified melamine resin, emulsifying agent, foaming agent and firming agent be 1:0.1 ~ 0.3:0.2 ~
0.4:0.1~0.3。
It is an advantage of the current invention that: the structure of the first parcel tray, the second parcel tray and the 3rd parcel tray is designed by the present invention
It is optimized, makes security tool classification layered putting, facilitate user of service to take.The universal wheel of the present invention can convenient and safe be arranged
Use tool car to move.First side plate of the present invention can fold, and when needs handbarrow, the first side plate can launch, and increases peace
The storage space of full measure apparatus car, after handbarrow completes, the first side plate can be packed up, and constitutes closing with the second side plate
Box body, in order to save the parking space of safety measure apparatus car.The connecting rod of the present invention can make the first side plate launch.This
First side plate can be fixed after the first side plate is packed up by bright fixing device.The present invention also has compact, manufacture simple for structure
Advantage with low cost and easy to use.
Accompanying drawing explanation
Fig. 1 is the structural representation of the present invention;Fig. 2 is the another kind of state diagram of Fig. 1;Fig. 3 is the left view structural representation of Fig. 1
Figure;Fig. 4 is the plan structure schematic diagram of Fig. 1;Fig. 5 is I structure for amplifying schematic diagram of Fig. 1.
Mark explanation: 1 push rod 2 universal wheel 3 pedestal 4 first parcel tray 5 second parcel tray 6 supports seat 7 the 3rd storage
Thing box 8 first side plate 9 head rod 10 fixed mount 11 retainer ring 12 fixed plate 13 through hole 14 gripper shoe 15 connects
Bar 16 counterweight 17 fixes pipe 18 second side plate 19 second connecting rod.
Detailed description of the invention
Safety measure apparatus car, as it is shown in figure 1, include pedestal 3, the corner, bottom of pedestal 3 is respectively mounted a universal wheel
2, the second side plate 18 and the first parcel tray 4 that on pedestal 3,10, two the first side plates 8, two of mounting and fixing support be arranged in parallel, two
Individual first side plate 8 is between two the second side plates 18, and the 3rd parcel tray 7, the 3rd storing are installed in the side, top of fixed mount 10
Box 7 is positioned at the top of two the second side plates 18, and second side plate 18 is connected with fixed mount 10, another the second side plate 18 sidepiece
Installing and support seat 6, the second parcel tray 5 is installed on the top supporting seat 6, and the second parcel tray 5 is positioned at above the first parcel tray 4, two
The both sides of the second side plate 18 are respectively articulated with one end of a head rod 9, and the other end hinged second of head rod 9 connects
One end of bar 19, the other end of the second connecting rod 19 is hinged with one end of the first corresponding side plate 8, the other end of the first side plate 8
Hinged with pedestal 3, the both sides of the 3rd parcel tray 7 and the first side plate 8 are respectively mounted fixing device.This structure by the first parcel tray,
The structure design of the second parcel tray and the 3rd parcel tray is optimized, and makes security tool classification layered putting, facilitates user of service
Take.The universal wheel of the present invention can move with convenient and safe measure apparatus car.First side plate of the present invention can fold, and works as needs
During handbarrow, the first side plate can launch, and increases the storage space of safety measure apparatus car, after handbarrow completes, first
Side plate can be packed up, and constitutes, with the second side plate, the box body closed, in order to save the parking space of safety measure apparatus car.This
Bright connecting rod can make the first side plate launch.The fixing device of the present invention can be solid by the first side plate after the first side plate is packed up
Fixed.The present invention also has advantage compact, cheap for manufacturing cost and easy to use simple for structure.
Described fixing device can be made up of various structures, and preferred fixing device is by fixing pipe 17, retainer ring 11, fixing
Plate 12, through hole 13, gripper shoe 14, connecting rod 15 and counterweight 16 are constituted, and fixing pipe 17 is arranged on the end of the first side plate 8, support
Plate 14 is arranged on the both sides of the 3rd parcel tray 7, and gripper shoe 14 is vertically offered through hole 13, installs connecting rod 15, even in through hole 13
The upper end mounting plate 12 of extension bar 15, the top installation retainer ring 11 of fixed plate 12, the lower end installation counterweight 16 of connecting rod 15,
Connecting rod 15 can coordinate with fixing pipe 17.The connecting rod 15 of the present invention can coordinate with fixing pipe 17 after the first side plate 8 is packed up,
The first side plate 8 is avoided to launch under gravity.The counterweight 16 of the present invention can increase the inertia of connecting rod 15, prevents connecting rod
15 depart from fixing pipe 17 when vibration.Connecting rod 15 can be played position-limiting action by the fixed plate 12 of the present invention, the present invention's
Retainer ring 11 can facilitate user to pull connecting rod 15.Fixing device can also be made up of buckle, the first side plate 8 and the 3rd storage
The buckle that can cooperate it is respectively provided with, so that the first side plate 8 and the 3rd parcel tray 7 can mutually be locked on thing box 7.This
Plant respective outer side edges tight, but cost is high, difficult in maintenance, it is easily damaged.
Move for convenience of the present invention, described fixed mount 10 arranges push rod 1.This structure can provide hands for staff
The support that portion has an effect, facilitates staff to push the present invention and moves.
Described 3rd parcel tray 7 is several, and several 3rd parcel trays 7 are arranged side by side.This structure can be segmented further
Instrument in each the 3rd parcel tray 7, conveniently stores classifiedly different instrument.
During for avoiding the present invention to move, Tool Room mutually collides the sound sent and disturbs residents, described pedestal the 3, first side plate 8,
Coating puigging on two side plate the 18, first parcel tray the 4, second parcel trays 5 and the 3rd parcel tray 7, puigging is by a kind of sound insulation material
Material is made, a kind of deadener, in parts by weight, is made up of following raw material: modified melamine resin foam 50 ~ 60 parts, vitreous is micro-
5 ~ 10 parts of pearl, perlite 5 ~ 10 parts, ceramics 5 ~ 10 parts, Tissuemat E 1 ~ 3 part, quartz sand 10 ~ 20 parts, mica powder 1 ~ 5 part and
Aluminium oxide 2 ~ 5 parts;
Described modified melamine resin foam is prepared by following steps:
Tripolycyanamide, polyformaldehyde, aniline and furfural are added in reactor and obtains mixed liquor, in reactor, add hydroxide
The pH value of sodium regulation mixed liquor to 8 ~ 9, after mixed liquor be warming up to 75 ~ 85 DEG C react 45 ~ 75 minutes, continue to add in reactor
Enter Polyethylene Glycol, the temperature of reactor is warming up to 90 ~ 100 DEG C, cool down after reacting 30 ~ 60 minutes, obtain modified melamine resin;
The weight ratio of described tripolycyanamide, polyformaldehyde, aniline, furfural and Polyethylene Glycol is 1:4 ~ 8:2 ~ 4:0.5 ~ 1:0.2 ~ 0.5;
To stepAdding emulsifying agent in gained modified melamine resin, foaming agent and firming agent, under 1500 ~ 2000r/min
Stir 5 ~ 10 minutes, foamed solidification 1 hour in the baking oven of 70 ~ 80 DEG C, then baking oven is warming up to 100 ~ 110 DEG C of solidifications 1 ~ 2
Hour, obtain modified melamine resin foam;Described emulsifying agent is dodecyl sodium sulfate;Described foaming agent is normal hexane;Described
Firming agent is acrylic acid;The mass ratio of described modified melamine resin, emulsifying agent, foaming agent and firming agent be 1:0.1 ~ 0.3:0.2 ~
0.4:0.1~0.3.Owing to security tool is generally made from a metal, when colliding each other, sound is very big, at pedestal 3, first
A kind of deadener of coating on side plate the 8, second side plate the 18, first parcel tray the 4, second parcel tray 5 and the 3rd parcel tray 7, it is possible to
Effectively noise reduction, it is to avoid disturb residents.This deadener soundproof effect is good, and density is little, and intensity is high, easy and other Material cladding, changes
Existing deadener weight and closely knit feature, easy construction, add its range, and the deadener of the present invention is by changing
Property melamine resin foam and additive composition, modified melamine resin is owing to having porous, loose structure, and the present invention remains interpolation
Agent can be filled to cavernous structure, it is thus possible to the isolation of noise propagated in air, cut off and separate;This material changes owing to using
Property melamine resin foam, sound can be absorbed by the porous loose structure of this foam itself as sound-absorbing material, again can be bright
The aobvious density reducing existing deadener, expands the range of existing deadener;Prepared by the deadener of the present invention
Method step is few, and the requirement to equipment is few, and technique the most easily operates and is capable of large-scale production.
Below in conjunction with specific embodiment, the deadener of the present invention is further described.
Embodiment 1
A kind of deadener, it is characterised in that: in parts by weight, it is made up of following raw material: modified melamine resin foam 50kg, glass
Change microballon 5kg, perlite 5kg, ceramics 5kg, Tissuemat E 1kg, quartz sand 10kg, mica powder 1kg and aluminium oxide 2kg;
Described modified melamine resin foam is prepared by following steps:
50kg tripolycyanamide, 200kg polyformaldehyde, 100kg aniline and 25kg furfural are added in reactor and obtains mixed liquor, to
Reactor adds the pH value of sodium hydroxide regulation mixed liquor to 8, after mixed liquor be warming up to 75 DEG C react 45 minutes, continue to
Reactor adds 10kg Polyethylene Glycol, the temperature of reactor is warming up to 90 DEG C, cool down after reacting 30 minutes, obtain modified close
Polyimide resin;
To 100kg stepAddition 10kg emulsifying agent in gained modified melamine resin, 20kg foaming agent and 10kg firming agent,
Stir 5 minutes under 1500r/min, foamed solidification 1 hour in the baking oven of 70 DEG C, then baking oven is warming up to 100 DEG C of solidifications 1 little
Time;Described emulsifying agent is dodecyl sodium sulfate;Described foaming agent is normal hexane;Described firming agent is acrylic acid.
Embodiment 2
A kind of deadener, in parts by weight, is made up of following raw material: modified melamine resin foam 60kg, glass bead 10kg,
Perlite 10kg, ceramics 10kg, Tissuemat E 3kg, quartz sand 20kg, mica powder 5kg and aluminium oxide 5kg;
Described modified melamine resin foam is prepared by following steps:
60kg tripolycyanamide, 480kg polyformaldehyde, 240kg aniline and 60kg furfural are added in reactor and obtains mixed liquor, to
Reactor adds the pH value of sodium hydroxide regulation mixed liquor to 9, after mixed liquor be warming up to 85 DEG C react 75 minutes, continue to
Reactor adds 30kg Polyethylene Glycol, the temperature of reactor is warming up to 100 DEG C, cool down after reacting 60 minutes, obtain modification
Melamine resin;
To 100kg stepAddition 30kg emulsifying agent in gained modified melamine resin, 40kg foaming agent and 30kg firming agent,
Stir 10 minutes under 2000r/min, foamed solidification 1 hour in the baking oven of 80 DEG C, then baking oven is warming up to 110 DEG C of solidifications 2
Hour;Obtain modified melamine resin foam;Described emulsifying agent is dodecyl sodium sulfate;Described foaming agent is normal hexane;Described
Firming agent is acrylic acid.
Embodiment 3
A kind of deadener, in parts by weight, is made up of following raw material: modified melamine resin foam 52kg, glass bead 6kg,
Perlite 6kg, ceramics 7kg, Tissuemat E 2kg, quartz sand 14kg, mica powder 4kg and aluminium oxide 4kg;
Described modified melamine resin foam is prepared by following steps:
50kg tripolycyanamide, 300kg polyformaldehyde, 150kg aniline and 40kg furfural are added in reactor and obtains mixed liquor, to
Reactor adds the pH value of sodium hydroxide regulation mixed liquor to 8.5, after mixed liquor be warming up to 78 DEG C react 60 minutes, continue
In reactor, add 20kg Polyethylene Glycol, the temperature of reactor is warming up to 92 DEG C, cool down after reacting 45 minutes, obtain modification
Melamine resin;
To 100kg stepAddition 15kg emulsifying agent in gained modified melamine resin, 25kg foaming agent and 15kg firming agent,
Stir 6 minutes under 1800r/min, foamed solidification 1 hour in the baking oven of 78 DEG C, then baking oven is warming up to 108 DEG C of solidifications 1.5
Hour, obtain modified melamine resin foam;Described emulsifying agent is dodecyl sodium sulfate;Described foaming agent is normal hexane;Described
Firming agent is acrylic acid.
Embodiment 4
A kind of deadener, in parts by weight, is made up of following raw material: modified melamine resin foam 54kg, glass bead 8kg,
Perlite 6kg, ceramics 6kg, Tissuemat E 2kg, quartz sand 18kg, mica powder 2kg and aluminium oxide 4kg;
Described modified melamine resin foam is prepared by following steps:
50kg tripolycyanamide, 300kg polyformaldehyde, 150kg aniline and 40kg furfural are added in reactor and obtains mixed liquor, to
Reactor adds the pH value of sodium hydroxide regulation mixed liquor to 8, after mixed liquor be warming up to 80 DEG C react 60 minutes, continue to
Reactor adds 15kg Polyethylene Glycol, the temperature of reactor is warming up to 95 DEG C, cool down after reacting 45 minutes, obtain modified close
Polyimide resin;
To 100kg stepAddition 20kg emulsifying agent in gained modified melamine resin, 30kg foaming agent and 20kg firming agent,
Stir 6 minutes under 1600r/min, foamed solidification 1 hour in the baking oven of 75 DEG C, then baking oven is warming up to 105 DEG C of solidifications 2 little
Time obtain modified melamine resin;Described emulsifying agent is dodecyl sodium sulfate;Described foaming agent is normal hexane;Described firming agent is
Acrylic acid.
Embodiment 5
The preparation method of the deadener described in embodiment 1, comprises the following steps:
50kg tripolycyanamide, 200kg polyformaldehyde, 100kg aniline and 25kg furfural are added in reactor and obtains mixed liquor, to
Reactor adds the pH value of sodium hydroxide regulation mixed liquor to 8, after mixed liquor be warming up to 75 DEG C react 45 minutes, continue to
Reactor adds 10kg Polyethylene Glycol, the temperature of reactor is warming up to 90 DEG C, cool down after reacting 30 minutes, obtain modified close
Polyimide resin;
To 100kg stepAddition 10kg emulsifying agent in gained modified melamine resin, 20kg foaming agent and 10kg firming agent,
Stir 5 minutes under 1500r/min, foamed solidification 1 hour in the baking oven of 70 DEG C, then baking oven is warming up to 100 DEG C of solidifications 1 little
Time;Described emulsifying agent is dodecyl sodium sulfate;Described foaming agent is normal hexane;Described firming agent is acrylic acid;
In parts by weight, by stepGained modified melamine resin foam 50kg, glass bead 5kg, perlite 5kg, pottery
Powder 5kg, Tissuemat E 1kg, quartz sand 10kg, mica powder 1kg and aluminium oxide 2kg mix homogeneously, obtain deadener.
Embodiment 6
The preparation method of the deadener described in embodiment 2, comprises the following steps:
60kg tripolycyanamide, 480kg polyformaldehyde, 240kg aniline and 60kg furfural are added in reactor and obtains mixed liquor, to
Reactor adds the pH value of sodium hydroxide regulation mixed liquor to 9, after mixed liquor be warming up to 85 DEG C react 75 minutes, continue to
Reactor adds 30kg Polyethylene Glycol, the temperature of reactor is warming up to 100 DEG C, cool down after reacting 60 minutes, obtain modification
Melamine resin;
To 100kg stepAddition 30kg emulsifying agent in gained modified melamine resin, 40kg foaming agent and 30kg firming agent,
Stir 10 minutes under 2000r/min, foamed solidification 1 hour in the baking oven of 80 DEG C, then baking oven is warming up to 110 DEG C of solidifications 2
Hour;Obtain modified melamine resin foam;Described emulsifying agent is dodecyl sodium sulfate;Described foaming agent is normal hexane;Described
Firming agent is acrylic acid;
In parts by weight, by stepGained modified melamine resin foam 60kg, glass bead 10kg, perlite 10kg, pottery
Porcelain powder 10kg, Tissuemat E 3kg, quartz sand 20kg, mica powder 5kg and aluminium oxide 5kg mix homogeneously, obtain deadener.
Embodiment 7
The preparation method of the deadener described in embodiment 3, comprises the following steps:
50kg tripolycyanamide, 300kg polyformaldehyde, 150kg aniline and 40kg furfural are added in reactor and obtains mixed liquor, to
Reactor adds the pH value of sodium hydroxide regulation mixed liquor to 8.5, after mixed liquor be warming up to 78 DEG C react 60 minutes, continue
In reactor, add 20kg Polyethylene Glycol, the temperature of reactor is warming up to 92 DEG C, cool down after reacting 45 minutes, obtain modification
Melamine resin;
To 100kg stepAddition 15kg emulsifying agent in gained modified melamine resin, 25kg foaming agent and 15kg firming agent,
Stir 6 minutes under 1800r/min, foamed solidification 1 hour in the baking oven of 78 DEG C, then baking oven is warming up to 108 DEG C of solidifications 1.5
Hour, obtain modified melamine resin foam;Described emulsifying agent is dodecyl sodium sulfate;Described foaming agent is normal hexane;Described
Firming agent is acrylic acid;
In parts by weight, by stepGained modified melamine resin foam 52kg, glass bead 6kg, perlite 6kg, pottery
Powder 7kg, Tissuemat E 2kg, quartz sand 14kg, mica powder 4kg and aluminium oxide 4kg mix homogeneously, obtain deadener;Described
Perlite is through following pretreatment: at 1100 DEG C, roasting perlite makes its volumetric expansion 11 times.
Embodiment 8
The preparation method of the deadener described in embodiment 4, comprises the following steps:
50kg tripolycyanamide, 300kg polyformaldehyde, 150kg aniline and 40kg furfural are added in reactor and obtains mixed liquor, to
Reactor adds the pH value of sodium hydroxide regulation mixed liquor to 8, after mixed liquor be warming up to 80 DEG C react 60 minutes, continue to
Reactor adds 15kg Polyethylene Glycol, the temperature of reactor is warming up to 95 DEG C, cool down after reacting 45 minutes, obtain modified close
Polyimide resin;
To 100kg stepAddition 20kg emulsifying agent in gained modified melamine resin, 30kg foaming agent and 20kg firming agent,
Stir 6 minutes under 1600r/min, foamed solidification 1 hour in the baking oven of 75 DEG C, then baking oven is warming up to 105 DEG C of solidifications 2 little
Time obtain modified melamine resin;Described emulsifying agent is dodecyl sodium sulfate;Described foaming agent is normal hexane;Described firming agent is
Acrylic acid;
In parts by weight, by stepGained modified melamine resin foam 54kg, glass bead 8kg, perlite 6kg, pottery
Powder 6kg, Tissuemat E 2kg, quartz sand 18kg, mica powder 2kg and aluminium oxide 4kg mix homogeneously, obtain deadener.
Technical scheme is not restricted in the range of embodiment of the present invention.The most detailed description of the present invention
Technology contents be known technology.
Claims (5)
1. safety measure apparatus car, it is characterised in that: include pedestal (3), the corner, bottom of pedestal (3) be respectively mounted one universal
Wheel (2), the upper mounting and fixing support (10) of pedestal (3), two the first side plates (8), two the second side plates (18) be arrangeding in parallel and the
One parcel tray (4), two the first side plates (8) are positioned between two the second side plates (18), and the side, top of fixed mount (10) is installed
3rd parcel tray (7), the 3rd parcel tray (7) is positioned at the top of two the second side plates (18), and second side plate (18) is with fixing
Frame (10) connects, and another the second side plate (18) sidepiece is installed and supported seat (6), and the second parcel tray is installed on the top supporting seat (6)
(5), the second parcel tray (5) is positioned at the first parcel tray (4) top, and the both sides of two the second side plates (18) are respectively articulated with one first
One end of connecting rod (9), one end of hinged second connecting rod of the other end (19) of head rod (9), the second connecting rod (19)
The other end hinged with one end of corresponding the first side plate (8), the other end of the first side plate (8) is hinged with pedestal (3), the 3rd storage
The both sides of thing box (7) and the first side plate (8) are respectively mounted fixing device.
Safety measure apparatus car the most according to claim 1, it is characterised in that: described fixing device by fix pipe (17),
Retainer ring (11), fixed plate (12), through hole (13), gripper shoe (14), connecting rod (15) and counterweight (16) are constituted, fixing pipe (17)
Being arranged on the end of the first side plate (8), gripper shoe (14) is arranged on the both sides of the 3rd parcel tray (7), and gripper shoe (14) is upper vertically
Offer through hole (13), connecting rod (15), the upper end mounting plate (12) of connecting rod (15), fixed plate are installed in through hole (13)
(12) retainer ring (11) is installed on top, and counterweight (16) is installed in the lower end of connecting rod (15), and connecting rod (15) can be with fixing pipe
(17) coordinate.
Safety measure apparatus car the most according to claim 1, it is characterised in that: described fixed mount arranges push rod on (10)
(1)。
Safety measure apparatus car the most according to claim 1, it is characterised in that: described 3rd parcel tray (7) is several, number
Individual 3rd parcel tray (7) is arranged side by side.
Safety measure apparatus car the most according to claim 1, it is characterised in that: described pedestal (3), the first side plate (8),
Coating puigging on two side plates (18), the first parcel tray (4), the second parcel tray (5) and the 3rd parcel tray (7), puigging is by one
Plant deadener to make, a kind of deadener, in parts by weight, be made up of following raw material: modified melamine resin foam 50 ~ 60
Part, glass bead 5 ~ 10 parts, perlite 5 ~ 10 parts, ceramics 5 ~ 10 parts, Tissuemat E 1 ~ 3 part, quartz sand 10 ~ 20 parts, Muscovitum
1 ~ 5 part of powder and aluminium oxide 2 ~ 5 parts;
Described modified melamine resin foam is prepared by following steps:
Tripolycyanamide, polyformaldehyde, aniline and furfural are added in reactor and obtains mixed liquor, in reactor, add hydroxide
The pH value of sodium regulation mixed liquor to 8 ~ 9, after mixed liquor be warming up to 75 ~ 85 DEG C react 45 ~ 75 minutes, continue to add in reactor
Enter Polyethylene Glycol, the temperature of reactor is warming up to 90 ~ 100 DEG C, cool down after reacting 30 ~ 60 minutes, obtain modified melamine resin;
The weight ratio of described tripolycyanamide, polyformaldehyde, aniline, furfural and Polyethylene Glycol is 1:4 ~ 8:2 ~ 4:0.5 ~ 1:0.2 ~ 0.5;
To stepGained modified melamine resin adds emulsifying agent, foaming agent and firming agent, stirs under 1500 ~ 2000r/min
Mix 5 ~ 10 minutes, foamed solidification 1 hour in the baking oven of 70 ~ 80 DEG C, then baking oven is warming up to 100 ~ 110 DEG C of solidifications 1 ~ 2 little
Time, obtain modified melamine resin foam;Described emulsifying agent is dodecyl sodium sulfate;Described foaming agent is normal hexane;Described solid
Agent is acrylic acid;The mass ratio of described modified melamine resin, emulsifying agent, foaming agent and firming agent be 1:0.1 ~ 0.3:0.2 ~
0.4:0.1~0.3。