CN105886833A - 一种耐腐蚀铬黄铜合金 - Google Patents
一种耐腐蚀铬黄铜合金 Download PDFInfo
- Publication number
- CN105886833A CN105886833A CN201610309460.1A CN201610309460A CN105886833A CN 105886833 A CN105886833 A CN 105886833A CN 201610309460 A CN201610309460 A CN 201610309460A CN 105886833 A CN105886833 A CN 105886833A
- Authority
- CN
- China
- Prior art keywords
- corrosion
- chromium
- brass alloy
- brass
- zinc
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种耐腐蚀铬黄铜合金，其化学组成为：铜62‑64.2wt％、铬2.2‑3.2wt％、镍0.1‑0.2wt％、镉0.001‑0.004wt％、钽0.006‑0.009wt％、钨0.05‑0.08wt％、钇0.05‑0.08wt％、铱0.05‑0.08wt％、硼0.002‑0.003wt％、碲0.002‑0.006wt％、钒0.008‑0.01wt％、铁0.01‑0.02wt％、钼0.03‑0.08wt％、铪0.03‑0.08wt％、稼0.14‑0.18wt％、钬0.03‑0.08wt％、锇0.03‑0.08wt％，余量为锌和不可避免的杂质，其中不可避免的杂质的含量不超过0.3wt％。本发明黄铜合金耐海水腐蚀，不会因原电池反应而离子丢失造成黄铜腐蚀，韧性好，抗冲击性强，抗电磁干扰性能优越，而且能耐酸雾的侵蚀，在潮湿环境中不会生成铜绿。
Description
技术领域
本发明涉及金属材料技术领域，具体涉及一种耐腐蚀铬黄铜合金。
背景技术
黄铜以锌作主要添加元素的铜合金，具有美观的黄色，统称黄铜。铜锌二元合金称普通黄铜或称简单黄铜。三元以上的黄铜称特殊黄铜或称复杂黄铜。含锌低於36％的黄铜合金由固溶体组成，具有良好的冷加工性能，如含锌30％的黄铜常用来制作弹壳，俗称弹壳黄铜或七三黄铜。含锌在36～42％之间的黄铜合金由和固溶体组成，其中最常用的是含锌40％的六四黄铜。为了改善普通黄铜的性能，常添加其他元素，如铝﹑镍﹑锰﹑锡﹑硅﹑铅等。铝能提高黄铜的强度﹑硬度和耐蚀性，但使塑性降低，适合作海轮冷凝管及其他耐蚀零件。锡能提高黄铜的强度和对海水的耐腐性，故称海军黄铜，用作船舶热工设备和螺旋桨等。铅能改善黄铜的切削性能；这种易切削黄铜常用作钟表零件。黄铜铸件常用来制作阀门和管道配件等。船舶常用的消防栓防爆月牙扳手，就是黄铜加铝铸造而成。
目前的黄铜合金种类多，但其品质或环保性能有时不一定能满足要求，例如，铅黄铜以其优异的耐腐蚀性能，易切削性能和成型性能而广泛应用在各个领域，但是铅极易从基体材料中脱落，而且在加工过程中以及产品废弃后，铅都会通过各种途径进入人体造成危害。
发明内容
本发明所要解决的技术问题在于提供一种耐腐蚀铬黄铜合金。
本发明所要解决的技术问题采用以下技术方案来实现：
一种耐腐蚀铬黄铜合金，其化学组成为：铜62-64.2wt％、铬2.2-3.2wt％、镍0.1-0.2wt％、镉0.001-0.004wt％、钽0.006-0.009wt％、钨0.05-0.08wt％、钇0.05-0.08wt％、铱0.05-0.08wt％、硼0.002-0.003wt％、碲0.002-0.006wt％、钒0.008-0.01wt％、铁0.01-0.02wt％、钼0.03-0.08wt％、铪0.03-0.08wt％、稼0.14-0.18wt％、钬0.03-0.08wt％、锇0.03-0.08wt％，余量为锌和不可避免的杂质，其中不可避免的杂质的含量不超过0.3wt％。
一种耐腐蚀铬黄铜合金，优选地，其化学组成为：铜63.1wt％、铬2.7wt％、镍0.1wt％、镉0.002wt％、钽0.008wt％、钨0.06wt％、钇0.06wt％、铱0.06wt％、硼0.002wt％、碲0.004wt％、钒0.009wt％、铁0.01wt％、钼0.05wt％、铪0.05wt％、稼0.16wt％、钬0.03-0.08wt％、锇0.03-0.08wt％，余量为锌和不可避免的杂质，其中不可避免的杂质的含量不超过0.3wt％。
本发明的有益效果是：本发明黄铜合金耐海水腐蚀，不会因原电池反应而离子丢失造成黄铜腐蚀，韧性好，抗冲击性强，抗电磁干扰性能优越，而且能耐酸雾的侵蚀，在潮湿环境中不会生成铜绿。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
实施例1
一种耐腐蚀铬黄铜合金，其化学组成为：铜63.1wt％、铬2.7wt％、镍0.1wt％、镉0.002wt％、钽0.008wt％、钨0.06wt％、钇0.06wt％、铱0.06wt％、硼0.002wt％、碲0.004wt％、钒0.009wt％、铁0.01wt％、钼0.05wt％、铪0.05wt％、稼0.16wt％、钬0.03-0.08wt％、锇0.03-0.08wt％，余量为锌和不可避免的杂质，其中不可避免的杂质的含量不超过0.3wt％。
实施例2
一种耐腐蚀铬黄铜合金，其化学组成为：铜62wt％、铬2.2wt％、镍0.1wt％、镉0.001wt％、钽0.006wt％、钨0.05wt％、钇0.05wt％、铱0.05wt％、硼0.002wt％、碲0.002wt％、钒0.008wt％、铁0.01wt％、钼0.03wt％、铪0.03wt％、稼0.14wt％、钬0.03wt％、锇0.03wt％，余量为锌和不可避免的杂质，其中不可避免的杂质的含量不超过0.3wt％。
实施例3
一种耐腐蚀铬黄铜合金，其化学组成为：铜64.2wt％、铬3.2wt％、镍0.2wt％、镉0.004wt％、钽0.009wt％、钨0.08wt％、钇0.08wt％、铱0.08wt％、硼0.003wt％、碲0.006wt％、钒0.01wt％、铁0.02wt％、钼0.08wt％、铪0.08wt％、稼0.18wt％、钬0.08wt％、锇0.08wt％，余量为锌和不可避免的杂质，其中不可避免的杂质的含量不超过0.3wt％。
试验
使用本发明实施例1的黄铜合金做实验，将其放置在相对湿度为60％，氧气浓度为30％的试验环境中6个月，其表面无任何变化，没有铜铝生成，将其放置在海水中，其表面无腐蚀斑点。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (2)
1.一种耐腐蚀铬黄铜合金，其特征在于，其化学组成为：铜62-64.2wt％、铬2.2-3.2wt％、镍0.1-0.2wt％、镉0.001-0.004wt％、钽0.006-0.009wt％、钨0.05-0.08wt％、钇0.05-0.08wt％、铱0.05-0.08wt％、硼0.002-0.003wt％、碲0.002-0.006wt％、钒0.008-0.01wt％、铁0.01-0.02wt％、钼0.03-0.08wt％、铪0.03-0.08wt％、稼0.14-0.18wt％、钬0.03-0.08wt％、锇0.03-0.08wt％，余量为锌和不可避免的杂质，其中不可避免的杂质的含量不超过0.3wt％。
2.如权利要求1所述的一种耐腐蚀铬黄铜合金，其特征在于，其化学组成为：铜63.1wt％、铬2.7wt％、镍0.1wt％、镉0.002wt％、钽0.008wt％、钨0.06wt％、钇0.06wt％、铱0.06wt％、硼0.002wt％、碲0.004wt％、钒0.009wt％、铁0.01wt％、钼0.05wt％、铪0.05wt％、稼0.16wt％、钬0.03-0.08wt％、锇0.03-0.08wt％，余量为锌和不可避免的杂质，其中不可避免的杂质的含量不超过0.3wt％。