CN105884195A - Spotted glass vase and preparation technology thereof - Google Patents
Spotted glass vase and preparation technology thereof Download PDFInfo
- Publication number
- CN105884195A CN105884195A CN201610240589.1A CN201610240589A CN105884195A CN 105884195 A CN105884195 A CN 105884195A CN 201610240589 A CN201610240589 A CN 201610240589A CN 105884195 A CN105884195 A CN 105884195A
- Authority
- CN
- China
- Prior art keywords
- glass
- flower pot
- dry
- water
- tumbling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A spotted glass vase is characterized by being prepared from components by weight as follows: 195.6 g of waste glass, 1.5 g of talc, 5 g of loess, 1 g of amber, 5 g of wood fibers, 3 g of seaweed mud, 0.2 g of zinc-magnesium powder, 6 g of expanded perlite, 5 g of vermiculite, 23.6 g of calcite, 15.4 g of borax, 20 g of soda ash, 6.6 g of sodium nitrate, 1.3 g of potassium carbonate, 4.6 g of barium carbonate, 25 g of bone meal, 8 g of natural ocean jasper, 8 g of hauynite, 5 g of Huanglong mountain green mud, 5 g of sepiolite and 5 g of wood-plastic powder. The waste glass is taken as the main material, the problem of difficulty in waste glass recovery is solved, and the prepared glass vase is smooth in surface, bright and beautiful in color, spotted and high in strength through special preparation from the raw materials.
Description
Technical field
The present invention relates to technical field of living goods, be specifically related to glass flower pot and the system thereof of a kind of band speckle
Standby technique.
Background technology
The institutes of department such as glass is built widely because of the performance of its uniqueness, chemical industry, equipment, daily life
Use, along with development and the development of other industry, building, door/window glass of automobile, the glass of building industry
The various glass such as container, electrical type glass and vial are widely used in a large number in national economy so that useless
Abandon glass substantial increase.On the other hand, unprecedented in Chinese large-sized infrastructure scale, natural aggregate is day by day
Shortage, therefore under the situation that discarded glass discharge capacity increases the most day by day, scrap glass is substituted sky by research
So gather materials to come the thought of concrete batching, meet the macro-economic strategy of sustainable development.
Summary of the invention
The technical problem to be solved is to provide a kind of color natural, composition stable performance, band
The glass flower pot of speckle and preparation technology thereof.
The technical problem to be solved realizes by the following technical solutions:
The glass flower pot of a kind of band speckle, is made up of the component of following weight: discarded glass 195.6g, cunning
Stone powder 1.5g, loess 5g, succinum 1g, wood fibre 5g, algae clay 3g, zinc-magnesium powder 0.2g, expansion treasure
Pearl rock 6g, Vermiculitum 5g, calcite 23.6g, Borax 15.4g, soda 20g, sodium nitrate 6.6g, potassium carbonate
1.3g, brium carbonate 4.6g, bone meal 25g, natural marine stone 8g, hauynite 8g, this mountain green mud 5g, Hai Pao
Stone 5g, wood molding powder 5g；
The preparation technology of the glass flower pot of a kind of band speckle, comprises the technical steps that,
(1) collect discarded glass, classify according to different colours and quality, use Water spray mode pair
Same class discarded glass carries out cleaning showers, washes away surface blot；The most again discarded glass is ground into
Granular, send into cold wind drying plant, at temperature 50-55 DEG C, cold air drying 30-35 minute, makes glass
Grain dry tack free is without moisture；Water after spray uses through precipitation flocculation Posterior circle；
(2) glass particle after cold air drying is sent into vacuum tumbler and carry out tumbling process, every during tumbling
Every 5-8 minute evacuation once, exhaust tumbling 5-10 minute, then vacuum pumping after vacuum every time, so follow
Ring 2-4 time, makes the impurity of glass surface start to decompose；
(3) glass particle after tumbling is taken out, put in water and soak 1.5-2 hour, then drag for filter screen
Go out to drain the water, soak water and return first spray operation use；Process owing to have passed through tumbling, glass
The foreign material on grain surface and oil stain are easy to fill to be washed off；
(4) glass particle after spray is drained away the water, send in drying plant and carry out drying and processing, dry
Dry temperature controls at 55-60 DEG C, to glass particle surface without moisture；
(5) will dry after glass particle put in nylon ball grinder add Pulvis Talci, loess, succinum,
Wood fibre, algae clay, zinc-magnesium powder, expanded perlite, Vermiculitum, calcite, Borax, soda, nitre
Acid sodium, potassium carbonate, brium carbonate, bone meal, natural marine stone, hauynite, this mountain green mud, meerschaum and
Wood molding powder, continuous ball milling 4-6 hour, it is stand-by that collection obtains mixed powder；
(6) feed the mixture into dehydrator, dry at 60 DEG C, be then fed into smelting furnace, make whole material
Carry out fusing mix homogeneously, obtain mother solution；
(7) mother solution is sent into forming machine, make the glass flower pot of the specification that varies in size, then by sparkling
Bottle sends into annealing kiln with conveyer after being naturally cooling to 600 DEG C of hardening, anneals complete；
(8) glass flower pot after annealing is sent into tempering case, first glass flower pot is heated to 750-900 DEG C,
Stop heating, send into cold wind, after rapidly glass flower pot being cooled to room temperature, tempering from all directions immediately
Terminate, glass flower pot is taken out from tempering case, obtains finished product.
The invention has the beneficial effects as follows: the present invention uses discarded glass as major ingredient, solves discarded glass and returns
The problem receiving difficulty, by the formulated to raw material, the glass flower pot mass color of preparation is sliding, beautiful in colour,
Spottiness, intensity is good, and compared with traditional handicraft, required time of the present invention is short, and energy consumption is low, goods texture
Good, nonhazardous material residual.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and effect and be readily apparent from
Solve, below in conjunction with specific embodiment, the present invention is expanded on further.
Embodiment 1
The glass flower pot of a kind of band speckle, is made up of the component of following weight: discarded glass 195.6g, cunning
Stone powder 1.5g, loess 5g, succinum 1g, wood fibre 5g, algae clay 3g, zinc-magnesium powder 0.2g, expansion treasure
Pearl rock 6g, Vermiculitum 5g, calcite 23.6g, Borax 15.4g, soda 20g, sodium nitrate 6.6g, potassium carbonate
1.3g, brium carbonate 4.6g, bone meal 25g, natural marine stone 8g, hauynite 8g, this mountain green mud 5g, Hai Pao
Stone 5g, wood molding powder 5g；
The preparation technology of the glass flower pot of a kind of band speckle, comprises the technical steps that,
(1) collect discarded glass, classify according to different colours and quality, use Water spray mode pair
Same class discarded glass carries out cleaning showers, washes away surface blot；The most again discarded glass is ground into
Granular, send into cold wind drying plant, at temperature 50-55 DEG C, cold air drying 30-35 minute, makes glass
Grain dry tack free is without moisture；Water after spray uses through precipitation flocculation Posterior circle；
(2) glass particle after cold air drying is sent into vacuum tumbler and carry out tumbling process, every during tumbling
Every 5-8 minute evacuation once, exhaust tumbling 5-10 minute, then vacuum pumping after vacuum every time, so follow
Ring 2-4 time, makes the impurity of glass surface start to decompose；
(3) glass particle after tumbling is taken out, put in water and soak 1.5-2 hour, then drag for filter screen
Go out to drain the water, soak water and return first spray operation use；Process owing to have passed through tumbling, glass
The foreign material on grain surface and oil stain are easy to fill to be washed off；
(4) glass particle after spray is drained away the water, send in drying plant and carry out drying and processing, dry
Dry temperature controls at 55-60 DEG C, to glass particle surface without moisture；
(5) will dry after glass particle put in nylon ball grinder add Pulvis Talci, loess, succinum,
Wood fibre, algae clay, zinc-magnesium powder, expanded perlite, Vermiculitum, calcite, Borax, soda, nitre
Acid sodium, potassium carbonate, brium carbonate, bone meal, natural marine stone, hauynite, this mountain green mud, meerschaum and
Wood molding powder, continuous ball milling 4-6 hour, it is stand-by that collection obtains mixed powder；
(6) feed the mixture into dehydrator, dry at 60 DEG C, be then fed into smelting furnace, make whole material
Carry out fusing mix homogeneously, obtain mother solution；
(7) mother solution is sent into forming machine, make the glass flower pot of the specification that varies in size, then by sparkling
Bottle sends into annealing kiln with conveyer after being naturally cooling to 600 DEG C of hardening, anneals complete；
(8) glass flower pot after annealing is sent into tempering case, first glass flower pot is heated to 750-900 DEG C,
Stop heating, send into cold wind, after rapidly glass flower pot being cooled to room temperature, tempering from all directions immediately
Terminate, glass flower pot is taken out from tempering case, obtains finished product.
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.One's own profession
Skilled person will appreciate that of industry, the present invention is not restricted to the described embodiments, above-described embodiment and explanation
The principle that the present invention is simply described described in book, without departing from the spirit and scope of the present invention,
The present invention also has various changes and modifications, and these changes and improvements both fall within claimed invention model
In enclosing.Claimed scope is defined by appending claims and equivalent thereof.
Claims (1)
1. the glass flower pot of a band speckle, it is characterised in that be made up of the component of following weight: waste and old
Glass 195.6g, Pulvis Talci 1.5g, loess 5g, succinum 1g, wood fibre 5g, algae clay 3g, zinc-magnesium
Powder 0.2g, expanded perlite 6g, Vermiculitum 5g, calcite 23.6g, Borax 15.4g, soda 20g, nitric acid
Sodium 6.6g, potassium carbonate 1.3g, brium carbonate 4.6g, bone meal 25g, natural marine stone 8g, hauynite 8g, basis
Mountain green mud 5g, meerschaum 5g, wood molding powder 5g；
The preparation technology of above-mentioned glass flower pot is as follows:
(1) collect discarded glass, classify according to different colours and quality, use Water spray mode pair
Same class discarded glass carries out cleaning showers, washes away surface blot；The most again discarded glass is ground into
Granular, send into cold wind drying plant, at temperature 50-55 DEG C, cold air drying 30-35 minute, makes glass
Grain dry tack free is without moisture；
(2) glass particle after cold air drying is sent into vacuum tumbler and carry out tumbling process, every during tumbling
Every 5-8 minute evacuation once, exhaust tumbling 5-10 minute, then vacuum pumping after vacuum every time, so follow
Ring 2-4 time, makes the impurity of glass surface start to decompose；
(3) glass particle after tumbling is taken out, put in water and soak 1.5-2 hour, then drag for filter screen
Go out to drain the water, soak water and return first spray operation use；
(4) glass particle after spray is drained away the water, send in drying plant and carry out drying and processing, dry
Dry temperature controls at 55-60 DEG C, to glass particle surface without moisture；
(5) will dry after glass particle put in nylon ball grinder add Pulvis Talci, loess, succinum,
Wood fibre, algae clay, zinc-magnesium powder, expanded perlite, Vermiculitum, calcite, Borax, soda, nitre
Acid sodium, potassium carbonate, brium carbonate, bone meal, natural marine stone, hauynite, this mountain green mud, meerschaum and
Wood molding powder, continuous ball milling 4-6 hour, it is stand-by that collection obtains mixed powder；
(6) feed the mixture into dehydrator, dry at 60 DEG C, be then fed into smelting furnace, make whole material
Carry out fusing mix homogeneously, obtain mother solution；
(7) mother solution is sent into forming machine, make the glass flower pot of the specification that varies in size, then by sparkling
Bottle sends into annealing kiln with conveyer after being naturally cooling to 600 DEG C of hardening, anneals complete；
(8) glass flower pot after annealing is sent into tempering case, first glass flower pot is heated to 750-900 DEG C,
Stop heating, send into cold wind, after rapidly glass flower pot being cooled to room temperature, tempering from all directions immediately
Terminate, glass flower pot is taken out from tempering case, obtains finished product.