CN1058744A - A kind of method of utilizing the unsaturated polyester resin craft articles - Google Patents
A kind of method of utilizing the unsaturated polyester resin craft articles Download PDFInfo
- Publication number
- CN1058744A CN1058744A CN 90109087 CN90109087A CN1058744A CN 1058744 A CN1058744 A CN 1058744A CN 90109087 CN90109087 CN 90109087 CN 90109087 A CN90109087 A CN 90109087A CN 1058744 A CN1058744 A CN 1058744A
- Authority
- CN
- China
- Prior art keywords
- polyester resin
- unsaturated polyester
- submodule
- blue
- lacquer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Utilize the method for unsaturated polyester resin craft articles, be on master mold, to make two-half die, bonding one-tenth one submodule of two-half die, submodule is that the fiber article are stuck with paste with unsaturated polyester resin, is coated with several layers of unsaturated polyester resin again and solidifies, haircuts then wires inlay, point blue coloring rolls thereon and waters unsaturated polyester resin, carries out mechanical polishing after the drying, spray one deck carboxylic ester varnish at last, to increase the brightness of artistic face.
Description
The present invention relates to a kind of method of utilizing the resin craft articles, the particularly manufacture method of imitation cloisonne process product.
The artistic effect of cloisonne enamel is simple and honest serious, and pattern line is meticulous clear, be the traditional workmanship of China, but their manufacturing process is loaded down with trivial details, the raw material costliness.
The purpose of this invention is to provide a kind of method of utilizing unsaturated polyester resin manufacturing process product, it has the different of essence with traditional cloisonne technology, and the handicraft that utilizes cheap raw material to produce has the artistic effect of cloisonne enamel.
The present invention is achieved in that according to the external form of handicraft and makes master mold, two half modules of system on master mold, two half module binding agent adhesion submodules in aggregates, submodule is that the multi-layer fiber article stick into unsaturated polyester resin, the last several layers of unsaturated polyester resin of the outer curing of submodule, the haircuts that wires inlay then accounts for blue paintedly, and then carrying out the surface again on submodule waters lid, rolling is watered several all over unsaturated polyester resin, mechanical polishing is carried out in dry rear surface, sprays the blue or green lacquer of one deck alkyd glue fat at last, dry.
Advantage of the present invention is that technology is simple, and is easily manufactured, and the prices of raw and semifnished materials of use are cheap, and the manufacturing process product have the artistic effect of cloisonne enamel.Sparkling and crystal-clear, elegant, beautiful in colour, acid and alkali-resistance, humidity have stronger viewing and admiring and use value.
The invention will be further described below in conjunction with embodiment.
1, system master mold.According to the handicraft shape of required manufacturing, choose moulding, model can be wooden, also can be steel, or other material with certain rigidity gets final product.
2, system submodule.On master mold, be coated with earlier one deck releasing agent, shear glass fabric by the master mold shape, stick with paste layer of glass cloth, be coated with one deck 103 unsaturated polyester resins, vary in size, stick with paste 10-14 layer glass fabric according to moulding, make two half modules, deviate from master mold then, two half son's moulds are sticked together, make a complete submodule.
3, solidify.After treating the submodule drying, on submodule, be coated with 4-8 layer unsaturated polyester resin, for quickening the drying time of resin, can add 3% initator and the promoter of 0.5-1% in the solidification process, quicken cold curing, when adding initator and promoter, should add initator earlier, after stirring, adds by initator promoter again, and definitely can not two kinds of addings simultaneously.
4, wire inlay, point is blue painted.Pinched gold-plated silk according to pattern with hand, spun gold has been sticked on the submodel with white glue with vinyl, by the requirement of the different color and lusters of pattern, various required glaze on the point.For strengthening glaze and submodel adhesive strength, in the dissolving glaze, add 10% white glue with vinyl, stir even back and use.
5, lid is watered on the surface.With the submodule airing after painted, roll and water 3-4 all over unsaturated polyester resin in the surface.For accelerating the hardening time of resin, also can add initator and promoter, the amount of the amount of adding during with curing is identical.
6, surperficial mechanical polishing.The product that is cured carries out surface grinding, at first with file with the uneven filing of product surface, again with the polishing of 450 rev/mins sanding machine, the husky cloth of the brown diamond spar of second usefulness rotates and polishes, and adds water mill light with waterproof abrasive paper at last.
7, surface spray light.Spray light with air compressor, to increase the brightness of handicraft surface.Material spray is that alkyd glue fat green grass or young crops is coated with lacquer with 1: 1 ether dissolution, and dry with the primary drying chamber at 80 ℃ the spray back, spray optical thickness 0.2mm.
Unsaturated polyester resin, glass fabric, releasing agent, initator, the promoter that this method is used is Changzhou No.253 Buiding Material Factory and produces.
Claims (8)
1, a kind of method of utilizing the unsaturated polyester resin craft articles, be two half modules of system on master mold, two half module bonding agent adhesion submodules in aggregates, it is characterized in that submodule is that the multi-layer fiber article solidify with unsaturated polyester resin, the haircuts that wires inlay then, point is blue painted, then carries out the surface again and water lid and roll and water unsaturated polyester resin several times on submodule, mechanical polishing is carried out in dry rear surface, sprays the blue or green lacquer of one deck alkyd glue fat, drying at last.
2, method according to claim 1 is characterized in that haircuts will wire inlay with white glue with vinyl to be bonded on the submodule.
3, method according to claim 1, the fiber article that it is characterized in that making submodule are glass fabrics.
4, according to claim 1 and 3 described methods, the glass fabric that it is characterized in that making submodule is the 10-14 layer.
5, method according to claim 1 is characterized in that rolling when watering unsaturated polyester resin at solidification process with on submodule, adds 3% initator and 0.5-1% promoter in unsaturated polyester resin.
6, method according to claim 1 or 5 is characterized in that lacquer 4-8 layer unsaturated polyester resin in the submodule solidification process.
7, method according to claim 1 or 5 is characterized in that watering to roll when covering on the submodule surface watering unsaturated polyester resin 3 or 4 times.
8, method according to claim 1, when it is characterized in that the surface spray is bright, alkyd glue fat is blue or green to be coated with lacquer with 1: 1 ether dissolution.