CN1033072C - Glass fibre reinforced plastics stature and making method thereof - Google Patents
Glass fibre reinforced plastics stature and making method thereof Download PDFInfo
- Publication number
- CN1033072C CN1033072C CN 93102911 CN93102911A CN1033072C CN 1033072 C CN1033072 C CN 1033072C CN 93102911 CN93102911 CN 93102911 CN 93102911 A CN93102911 A CN 93102911A CN 1033072 C CN1033072 C CN 1033072C
- Authority
- CN
- China
- Prior art keywords
- statue
- resin
- reinforced plastics
- inserted sheet
- mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a statue and a manufacturing method thereof. The statue is manufactured by using glass fiber reinforced plastics as materials. The manufacturing process is completed by the procedures: (1), manufacturing skeleton; (2), molding clay image; (3), dividing mould; (4), buckling mould; (5), unloading mould; (6), pasting the glass fiber reinforced plastics; (7), trimming and seaming; (8), stoning, shaping and surfacing; (9), processing gel coat on the surface, etc. The present invention adopts the glass fiber reinforced plastics as raw materials to manufacture the statue and buddha statue, so the statue has light weight, little damage and no weathering in outdoor storage, so the present invention is particularly suitable for manufacturing large sculpture such as large buddha statue; the present invention also has the advantages of easy transportation, vivid manufactured statue, etc.
Description
The present invention relates to a kind of manufacture method of glass fibre reinforced plastics stature.
The used raw material of present existing sculpture, particularly figure of buddha goods is mud, wood, stone or gypsum etc. normally, and its shortcoming is that finished product is difficult for carrying for clay sculpture and woodcarving, damages easily, deposits weathering easily for a long time outdoor; Though stone carving is more firm, outdoor depositing has great advantage, and random, space spans is restricted, and carrying also has great difficulty with being connected, and gypsum sculpture is easily pulverized, the uncomfortable drying large-scale sculpture of making.
The objective of the invention is to provide a kind of body light, not fragile, the outdoor not easy-weathering of depositing is suitable for making the glass fibre reinforced plastics stature and the manufacture method thereof of the easy carrying of large-scale sculpture.
The object of the present invention is achieved like this, and this invention is that fiberglass is used to make statue as material.This manufacturing process pastes, repairs steps such as stitching, rubbed finish polishing, surperficial gel coat processing and finish by system skeleton, plasticine picture, branch mould, buckling die, mould unloading, fiberglass.Its minute, mold process was to treat that clay sculpture does the inserted sheet of back to a certain degree making with thin iron and insert the mud image surface, and the mud image surface is divided into can independent respectively some of being easy to again make up, and will can not leave the space in end to end centre when inserted sheet inserts; Its buckling die is that plaster of paris water furnishing pasty state is applied to the surface that is divided into some mud picture with inserted sheet then rapidly with unloading mold process, can add an amount of fiber crops, and its thickness is being not less than 3cm, extracts inserted sheet and unload each piece gypsum after gypsum is stablized 30 minutes; Its fiber glass resin be with resin, curing agent, promoter, silica flour by 10: 1: 1: 1 proportioning is made.
The present invention since adopt fiberglass be raw material make statue and figure of buddha institute so that the statue body gently, not fragile, the outdoor not easy-weathering of depositing, particularly be suitable for making large-scale sculpture, (as the big figure of buddha) advantages such as it also has the carrying of being easy to simultaneously, and the statue of making is vivid true to nature.
Accompanying drawings embodiment.
Fig. 1 is the manufacturing process flow diagram of glass fibre reinforced plastics stature.
Describe concrete manufacture process of the present invention in detail below in conjunction with accompanying drawing, the present invention by system skeleton 1, plasticine as 2, divide that mould 3, buckling die 4, mould unloading 5, fiberglass paste 6, finishing sews up 7, rubbed finish polishing 8, surperficial gel coat are handled steps such as 9 and finished.One, use the reinforcing bar welded framework to determine the basic configuration of sculpture goods according to the size of statue, use the sculpture clay plastotype, and the overall image of moulding the mud extraction picture, require smooth, be rich in expressive force, details is given prominence to, and after the mud original text is done to a certain degree the inserted sheet made from thin iron is inserted the mud image surface, the mud image surface is divided into some that can independently be easy to again make up respectively, inserted sheet is end to end, and space (this process is for dividing mould) can not be left in the centre.Two, plaster of paris water is in harmonious proportion, until becoming pasty state, be applied to the chamotte mould surface then rapidly, this process can cooperate to play the effect of firm bulk with fiber crops, its thickness is decided on actual conditions, generally should be not less than 3cm (this process is a buckling die), treat gypsum stablize certain intensity was arranged in 30 minutes after, can extract inserted sheet, and unload each piece gypsum, note keeping the globality (this process is a mould unloading) of plaster block, to carry out suitable trimming and necessary being connected to the cream mould afterwards, connection work is still carried out under fiber crops auxiliary with gypsum and water, and available in case of necessity timber and steel wire etc. are coated with wax polish and releasing agent at last on gypsum mold.Three, resin, curing agent, promoter, silica flour 10: 1: 1: 1 proportioning, and be equipped with suitable color, make fiber glass resin, by needed color fiber glass resin is coated onto on the plaster cast, general thickness is that 3mm gets final product, and the glass wool cloth that soaked in fiber glass resin is stuck with paste on the plaster cast that scribbles a resin.Thickness is decided on the size of sculpture goods, treats that fiber glass resin dries the fertile gypsum in back fully and smashes and slough.Four, the GRP mold that makes is sewed up under the cooperation of glass wool cloth with resin by the position at its place, will be after the stitching with the angle grinding machine in the suture finishing moulding of polishing, then statue is carried out comprehensive polishing, undesirable as the brightness of glass fibre reinforced plastics stature work surface, can carry out gel coat on the surface handles, make the surface brighter, so just finished its whole technical process.
Claims (1)
1, a kind of manufacture method of glass fibre reinforced plastics stature, may further comprise the steps: (1) system skeleton, (2) plasticine picture, (3) divide mould, (4) buckling die, (5) mould unloading, (6) fiberglass pastes, (7) finishing is sewed up, (8) rubbed finish polishing, (9) surperficial gel coat is handled, described minute mold process is to treat that the inserted sheet made from thin iron after clay sculpture is done to a certain degree inserts the mud image surface, the mud image surface is divided into some that can independently be easy to again make up respectively, it is end to end when inserted sheet inserts, the space can not be left in the centre, described buckling die is plaster of paris water furnishing pasty state with unloading mold process, be applied to the surface that is divided into some mud pictures with inserted sheet then rapidly, add an amount of fiber crops, its thickness is not less than 3cm, after gypsum is stablized 30 minutes, extract inserted sheet and unload each piece gypsum, be coated with wax polish and releasing agent thereon, the described fiberglass process of pasting is according to required color fiber glass resin to be coated onto on the plaster cast, thickness is 3mm, then the glass wool cloth that soaked in fiber glass resin is stuck with paste on the plaster cast that scribbles a resin, thickness is decided on the size of sculpture goods, treat that fiber glass resin dries back gypsum is smashed fully and sloughs, fiber glass resin is to use resin, curing agent, promoter, silica flour was by 10: 1: 1: 1 proportioning is made, at last GRP mold is sewed up under the cooperation of glass wool cloth with resin, handled through rubbed finish polishing and surperficial gel coat again after the stitching.