CN105862052A - 一种不锈钢喷洗剂及其制备方法 - Google Patents
一种不锈钢喷洗剂及其制备方法 Download PDFInfo
- Publication number
- CN105862052A CN105862052A CN201610384972.4A CN201610384972A CN105862052A CN 105862052 A CN105862052 A CN 105862052A CN 201610384972 A CN201610384972 A CN 201610384972A CN 105862052 A CN105862052 A CN 105862052A
- Authority
- CN
- China
- Prior art keywords
- sodium
- parts
- agent
- raw material
- rustless steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种不锈钢喷洗剂及其制备方法，所述不锈钢喷洗剂的原料包括氢氧化钠、三聚磷酸钠、偏硅酸钠、碳酸钠、苯甲酸钠、木塑硫酸钠、葡萄糖酸钠、磷酸钠、芳香石脑油、三甲基硅油、直链烷基磺酸、乙二醇单丁醚、二丙二醇单丁醚、辛基酚聚氧乙烯醚、异丙醇、工业酒精、乙醇胺、水、污垢分散剂、有机硅消泡剂、防锈成膜剂、pH缓冲剂、长效抗腐败剂和低泡表面活性剂。本发明清洗能力强，抗硬水，使用时不受温度和PH限制能迅速清除金属表面的污垢，不产生油印、水痕和变色等不良现象；产品溶水性强，泡沫低且消泡快，便于高压喷射清洗，不含有毒物质，安全无害，对环境无污染。
Description
技术领域
本发明涉及不锈钢清洗技术领域，具体是一种不锈钢喷洗剂及其制备方法。
背景技术
不锈钢储运罐用于储运原油、稠油及重油等，通常要求把储运罐中的原油、稠油、重油排到输油管道系统之后，必须将罐体内表面清洗干净，目前的清洗方法是分别清洗大罐内腔和外表面。内腔清洗工艺是将煤油装入专用槽体中，通过高压泵接入一种可安装于大罐上端圆孔下面的高压喷射机进行清洗，清洗后的残留液从大罐下端下口排放，进入废水处理系统；大罐外表面清洗工艺是人工用抹布蘸香蕉水擦拭整体表面。煤油及香蕉水均极其易燃，现场操作容易发生火灾，严重危害人身及财产安全；另外，人工擦洗费时费力，不仅劳动强度高，而且清洗效率低。
发明内容
本发明的目的在于提供一种成本低、清洁能力强的不锈钢喷洗剂及其制备方法，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：
一种不锈钢喷洗剂，按照重量份的原料包括：氢氧化钠20-40份、三聚磷酸钠3-5份、偏硅酸钠8-10份、碳酸钠6-8份、苯甲酸钠3-5份、木塑硫酸钠0.5-1份、葡萄糖酸钠1-3份、磷酸钠6-8份、芳香石脑油8-10份、三甲基硅油2-4份、直链烷基磺酸6-8份、乙二醇单丁醚0.5-1.5份、二丙二醇单丁醚0.5-1.5份、辛基酚聚氧乙烯醚0.3-0.5份、异丙醇6-10份、工业酒精10-15份、乙醇胺1-2份、水30-50份、污垢分散剂0.1-0.5份、有机硅消泡剂0.1-0.5份、防锈成膜剂1-3份、pH缓冲剂1-3份、长效抗腐败剂2-4份、低泡表面活性剂0.3-0.7份。
作为本发明进一步的方案：所述不锈钢喷洗剂，按照重量份的原料包括：氢氧化钠25-35份、三聚磷酸钠3.5-4.5份、偏硅酸钠8.5-9.5份、碳酸钠6.5-7.5份、苯甲酸钠3.5-4.5份、木塑硫酸钠0.6-0.9份、葡萄糖酸钠1.5-2.5份、磷酸钠6.5-7.5份、芳香石脑油8.5-9.5份、三甲基硅油2.5-3.5份、直链烷基磺酸6.5-7.5份、乙二醇单丁醚0.8-1.2份、二丙二醇单丁醚0.8-1.2份、辛基酚聚氧乙烯醚0.35-0.45份、异丙醇7-9份、工业酒精11-14份、乙醇胺1.2-1.8份、水35-45份、污垢分散剂0.2-0.4份、有机硅消泡剂0.2-0.4份、防锈成膜剂1.5-2.5份、pH缓冲剂1.5-2.5份、长效抗腐败剂2.5-3.5份、低泡表面活性剂0.4-0.6份。
作为本发明进一步的方案：所述不锈钢喷洗剂，按照重量份的原料包括：氢氧化钠30份、三聚磷酸钠4份、偏硅酸钠9份、碳酸钠7份、苯甲酸钠4份、木塑硫酸钠0.8份、葡萄糖酸钠2份、磷酸钠7份、芳香石脑油9份、三甲基硅油3份、直链烷基磺酸7份、乙二醇单丁醚1份、二丙二醇单丁醚1份、辛基酚聚氧乙烯醚0.4份、异丙醇8份、工业酒精12份、乙醇胺1.5份、水40份、污垢分散剂0.3份、有机硅消泡剂0.3份、防锈成膜剂2份、pH缓冲剂2份、长效抗腐败剂3份、低泡表面活性剂0.5份。
作为本发明进一步的方案：所述防锈成膜剂由十二烯基丁二酸二甲酯和石油磺酸钙组成，十二烯基丁二酸二甲酯和石油磺酸钙的含量为1:1。
作为本发明进一步的方案：所述PH缓冲剂由硼砂、邻苯二甲酸氢钾和酸纳组成，所述硼砂、邻苯二甲酸氢钾、磷酸纳的含量比为1∶0.5∶1。
作为本发明再进一步的方案：所述效抗腐败剂由富马酸二苄酯和富马酸二乙酯组成，富马酸二苄酯和富马酸二乙酯的含量比为1:1。
所述不锈钢喷洗剂的制备方法，具体步骤如下：
（1）按照重量份称取各原料；
（2）先将水加温至70-90℃，再加入到不锈钢反应釜中，开动搅拌器，控制转速为60-80r/min；
（3）向反不锈钢应釜中加入防锈成膜剂、pH缓冲剂和长效抗腐败剂，搅拌3-5min；
（4）再依次向不锈钢反应釜中加入氢氧化钠、三聚磷酸钠、偏硅酸钠、碳酸钠、苯甲酸钠、木塑硫酸钠、葡萄糖酸钠、磷酸钠、芳香石脑油、三甲基硅油、直链烷基磺酸、乙二醇单丁醚、二丙二醇单丁醚、辛基酚聚氧乙烯醚、异丙醇、工业酒精、乙醇胺、水、污垢分散剂、有机硅消泡剂、低泡表面活性剂，每加入一种原料搅拌均匀1-3min，原料全部加入后继续搅拌至溶液呈浅黄色透明状液体得到喷洗剂成品。
与现有技术相比，本发明的有益效果是：
本发明清洗能力强，抗硬水，使用时不受温度和PH限制能迅速清除金属表面的污垢，不产生油印、水痕和变色等不良现象；产品溶水性强，泡沫低且消泡快，便于高压喷射清洗，不含有毒物质，安全无害，对环境无污染。
具体实施方式
下面结合具体实施方式对本专利的技术方案作进一步详细地说明。
实施例1
一种不锈钢喷洗剂，按照重量份的原料包括：氢氧化钠20份、三聚磷酸钠3份、偏硅酸钠8份、碳酸钠6份、苯甲酸钠3份、木塑硫酸钠0.5份、葡萄糖酸钠1份、磷酸钠6份、芳香石脑油8份、三甲基硅油2份、直链烷基磺酸6份、乙二醇单丁醚0.5份、二丙二醇单丁醚0.5份、辛基酚聚氧乙烯醚0.3份、异丙醇6份、工业酒精10份、乙醇胺1份、水30份、污垢分散剂0.1份、有机硅消泡剂0.1份、防锈成膜剂1份、pH缓冲剂1份、长效抗腐败剂2份、低泡表面活性剂0.3份。
所述不锈钢喷洗剂的制备方法，具体步骤如下：
（1）按照重量份称取各原料；
（2）先将水加温至70℃，再加入到不锈钢反应釜中，开动搅拌器，控制转速为60r/min；
（3）向反不锈钢应釜中加入防锈成膜剂、pH缓冲剂和长效抗腐败剂，搅拌3min；
（4）再依次向不锈钢反应釜中加入氢氧化钠、三聚磷酸钠、偏硅酸钠、碳酸钠、苯甲酸钠、木塑硫酸钠、葡萄糖酸钠、磷酸钠、芳香石脑油、三甲基硅油、直链烷基磺酸、乙二醇单丁醚、二丙二醇单丁醚、辛基酚聚氧乙烯醚、异丙醇、工业酒精、乙醇胺、水、污垢分散剂、有机硅消泡剂、低泡表面活性剂，每加入一种原料搅拌均匀1min，原料全部加入后继续搅拌至溶液呈浅黄色透明状液体得到喷洗剂成品。
实施例2
一种不锈钢喷洗剂，按照重量份的原料包括：氢氧化钠25份、三聚磷酸钠3.5份、偏硅酸钠8.5份、碳酸钠6.5份、苯甲酸钠3.5份、木塑硫酸钠0.6份、葡萄糖酸钠1.5份、磷酸钠6.5份、芳香石脑油8.5份、三甲基硅油2.5份、直链烷基磺酸6.5份、乙二醇单丁醚0.8份、二丙二醇单丁醚0.8份、辛基酚聚氧乙烯醚0.35份、异丙醇7份、工业酒精11份、乙醇胺1.2份、水35份、污垢分散剂0.2份、有机硅消泡剂0.2份、防锈成膜剂1.5份、pH缓冲剂1.5份、长效抗腐败剂2.5份、低泡表面活性剂0.4份。
所述不锈钢喷洗剂的制备方法，具体步骤如下：
（1）按照重量份称取各原料；
（2）先将水加温至75℃，再加入到不锈钢反应釜中，开动搅拌器，控制转速为65r/min；
（3）向反不锈钢应釜中加入防锈成膜剂、pH缓冲剂和长效抗腐败剂，搅拌3.5min；
（4）再依次向不锈钢反应釜中加入氢氧化钠、三聚磷酸钠、偏硅酸钠、碳酸钠、苯甲酸钠、木塑硫酸钠、葡萄糖酸钠、磷酸钠、芳香石脑油、三甲基硅油、直链烷基磺酸、乙二醇单丁醚、二丙二醇单丁醚、辛基酚聚氧乙烯醚、异丙醇、工业酒精、乙醇胺、水、污垢分散剂、有机硅消泡剂、低泡表面活性剂，每加入一种原料搅拌均匀1.5min，原料全部加入后继续搅拌至溶液呈浅黄色透明状液体得到喷洗剂成品。
实施例3
一种不锈钢喷洗剂，按照重量份的原料包括：氢氧化钠30份、三聚磷酸钠4份、偏硅酸钠9份、碳酸钠7份、苯甲酸钠4份、木塑硫酸钠0.8份、葡萄糖酸钠2份、磷酸钠7份、芳香石脑油9份、三甲基硅油3份、直链烷基磺酸7份、乙二醇单丁醚1份、二丙二醇单丁醚1份、辛基酚聚氧乙烯醚0.4份、异丙醇8份、工业酒精12份、乙醇胺1.5份、水40份、污垢分散剂0.3份、有机硅消泡剂0.3份、防锈成膜剂2份、pH缓冲剂2份、长效抗腐败剂3份、低泡表面活性剂0.5份。
所述不锈钢喷洗剂的制备方法，具体步骤如下：
（1）按照重量份称取各原料；
（2）先将水加温至80℃，再加入到不锈钢反应釜中，开动搅拌器，控制转速为70r/min；
（3）向反不锈钢应釜中加入防锈成膜剂、pH缓冲剂和长效抗腐败剂，搅拌4min；
（4）再依次向不锈钢反应釜中加入氢氧化钠、三聚磷酸钠、偏硅酸钠、碳酸钠、苯甲酸钠、木塑硫酸钠、葡萄糖酸钠、磷酸钠、芳香石脑油、三甲基硅油、直链烷基磺酸、乙二醇单丁醚、二丙二醇单丁醚、辛基酚聚氧乙烯醚、异丙醇、工业酒精、乙醇胺、水、污垢分散剂、有机硅消泡剂、低泡表面活性剂，每加入一种原料搅拌均匀2min，原料全部加入后继续搅拌至溶液呈浅黄色透明状液体得到喷洗剂成品。
实施例4
一种不锈钢喷洗剂，按照重量份的原料包括：氢氧化钠35份、三聚磷酸钠4.5份、偏硅酸钠9.5份、碳酸钠7.5份、苯甲酸钠4.5份、木塑硫酸钠0.9份、葡萄糖酸钠2.5份、磷酸钠7.5份、芳香石脑油9.5份、三甲基硅油3.5份、直链烷基磺酸7.5份、乙二醇单丁醚1.2份、二丙二醇单丁醚1.2份、辛基酚聚氧乙烯醚0.45份、异丙醇9份、工业酒精14份、乙醇胺1.8份、水45份、污垢分散剂0.4份、有机硅消泡剂0.4份、防锈成膜剂2.5份、pH缓冲剂2.5份、长效抗腐败剂3.5份、低泡表面活性剂0.6份。
所述不锈钢喷洗剂的制备方法，具体步骤如下：
（1）按照重量份称取各原料；
（2）先将水加温至85℃，再加入到不锈钢反应釜中，开动搅拌器，控制转速为75r/min；
（3）向反不锈钢应釜中加入防锈成膜剂、pH缓冲剂和长效抗腐败剂，搅拌4.5min；
（4）再依次向不锈钢反应釜中加入氢氧化钠、三聚磷酸钠、偏硅酸钠、碳酸钠、苯甲酸钠、木塑硫酸钠、葡萄糖酸钠、磷酸钠、芳香石脑油、三甲基硅油、直链烷基磺酸、乙二醇单丁醚、二丙二醇单丁醚、辛基酚聚氧乙烯醚、异丙醇、工业酒精、乙醇胺、水、污垢分散剂、有机硅消泡剂、低泡表面活性剂，每加入一种原料搅拌均匀2.5min，原料全部加入后继续搅拌至溶液呈浅黄色透明状液体得到喷洗剂成品。
实施例5
一种不锈钢喷洗剂，按照重量份的原料包括：氢氧化钠40份、三聚磷酸钠5份、偏硅酸钠10份、碳酸钠8份、苯甲酸钠5份、木塑硫酸钠1份、葡萄糖酸钠3份、磷酸钠8份、芳香石脑油10份、三甲基硅油4份、直链烷基磺酸8份、乙二醇单丁醚1.5份、二丙二醇单丁醚1.5份、辛基酚聚氧乙烯醚0.5份、异丙醇10份、工业酒精15份、乙醇胺2份、水50份、污垢分散剂0.5份、有机硅消泡剂0.5份、防锈成膜剂3份、pH缓冲剂3份、长效抗腐败剂4份、低泡表面活性剂0.7份。
所述不锈钢喷洗剂的制备方法，具体步骤如下：
（1）按照重量份称取各原料；
（2）先将水加温至90℃，再加入到不锈钢反应釜中，开动搅拌器，控制转速为80r/min；
（3）向反不锈钢应釜中加入防锈成膜剂、pH缓冲剂和长效抗腐败剂，搅拌5min；
（4）再依次向不锈钢反应釜中加入氢氧化钠、三聚磷酸钠、偏硅酸钠、碳酸钠、苯甲酸钠、木塑硫酸钠、葡萄糖酸钠、磷酸钠、芳香石脑油、三甲基硅油、直链烷基磺酸、乙二醇单丁醚、二丙二醇单丁醚、辛基酚聚氧乙烯醚、异丙醇、工业酒精、乙醇胺、水、污垢分散剂、有机硅消泡剂、低泡表面活性剂，每加入一种原料搅拌均匀3min，原料全部加入后继续搅拌至溶液呈浅黄色透明状液体得到喷洗剂成品。
所述防锈成膜剂由十二烯基丁二酸二甲酯和石油磺酸钙组成，十二烯基丁二酸二甲酯和石油磺酸钙的含量为1:1；所述PH缓冲剂由硼砂、邻苯二甲酸氢钾和酸纳组成，所述硼砂、邻苯二甲酸氢钾、磷酸纳的含量比为1∶0.5∶1；所述效抗腐败剂由富马酸二苄酯和富马酸二乙酯组成，富马酸二苄酯和富马酸二乙酯的含量比为1:1。
本发明清洗能力强，抗硬水，使用时不受温度和PH限制能迅速清除金属表面的污垢，不产生油印、水痕和变色等不良现象；产品溶水性强，泡沫低且消泡快，便于高压喷射清洗，不含有毒物质，安全无害，对环境无污染。
上面对本专利的较佳实施方式作了详细说明，但是本专利并不限于上述实施方式，在本领域的普通技术人员所具备的知识范围内，还可以在不脱离本专利宗旨的前提下作出各种变化。
Claims (7)
1.一种不锈钢喷洗剂，其特征在于，按照重量份的原料包括：氢氧化钠20-40份、三聚磷酸钠3-5份、偏硅酸钠8-10份、碳酸钠6-8份、苯甲酸钠3-5份、木塑硫酸钠0.5-1份、葡萄糖酸钠1-3份、磷酸钠6-8份、芳香石脑油8-10份、三甲基硅油2-4份、直链烷基磺酸6-8份、乙二醇单丁醚0.5-1.5份、二丙二醇单丁醚0.5-1.5份、辛基酚聚氧乙烯醚0.3-0.5份、异丙醇6-10份、工业酒精10-15份、乙醇胺1-2份、水30-50份、污垢分散剂0.1-0.5份、有机硅消泡剂0.1-0.5份、防锈成膜剂1-3份、pH缓冲剂1-3份、长效抗腐败剂2-4份、低泡表面活性剂0.3-0.7份。
2.根据权利要求1所述的不锈钢喷洗剂，其特征在于，按照重量份的原料包括：氢氧化钠25-35份、三聚磷酸钠3.5-4.5份、偏硅酸钠8.5-9.5份、碳酸钠6.5-7.5份、苯甲酸钠3.5-4.5份、木塑硫酸钠0.6-0.9份、葡萄糖酸钠1.5-2.5份、磷酸钠6.5-7.5份、芳香石脑油8.5-9.5份、三甲基硅油2.5-3.5份、直链烷基磺酸6.5-7.5份、乙二醇单丁醚0.8-1.2份、二丙二醇单丁醚0.8-1.2份、辛基酚聚氧乙烯醚0.35-0.45份、异丙醇7-9份、工业酒精11-14份、乙醇胺1.2-1.8份、水35-45份、污垢分散剂0.2-0.4份、有机硅消泡剂0.2-0.4份、防锈成膜剂1.5-2.5份、pH缓冲剂1.5-2.5份、长效抗腐败剂2.5-3.5份、低泡表面活性剂0.4-0.6份。
3.根据权利要求1所述的不锈钢喷洗剂，其特征在于，按照重量份的原料包括：氢氧化钠30份、三聚磷酸钠4份、偏硅酸钠9份、碳酸钠7份、苯甲酸钠4份、木塑硫酸钠0.8份、葡萄糖酸钠2份、磷酸钠7份、芳香石脑油9份、三甲基硅油3份、直链烷基磺酸7份、乙二醇单丁醚1份、二丙二醇单丁醚1份、辛基酚聚氧乙烯醚0.4份、异丙醇8份、工业酒精12份、乙醇胺1.5份、水40份、污垢分散剂0.3份、有机硅消泡剂0.3份、防锈成膜剂2份、pH缓冲剂2份、长效抗腐败剂3份、低泡表面活性剂0.5份。
4.根据权利要求1-3任一所述的不锈钢喷洗剂，其特征在于，所述防锈成膜剂由十二烯基丁二酸二甲酯和石油磺酸钙组成，十二烯基丁二酸二甲酯和石油磺酸钙的含量为1:1。
5.根据权利要求1-3任一所述的不锈钢喷洗剂，其特征在于，所述PH缓冲剂由硼砂、邻苯二甲酸氢钾和酸纳组成，所述硼砂、邻苯二甲酸氢钾、磷酸纳的含量比为1∶0.5∶1。
6.根据权利要求1-3任一所述的不锈钢喷洗剂，其特征在于，述效抗腐败剂由富马酸二苄酯和富马酸二乙酯组成，富马酸二苄酯和富马酸二乙酯的含量比为1:1。
7.一种如权利要求1-3任一所述的不锈钢喷洗剂的制备方法，其特征在于，具体步骤如下：
（1）按照重量份称取各原料；
（2）先将水加温至70-90℃，再加入到不锈钢反应釜中，开动搅拌器，控制转速为60-80r/min；
（3）向反不锈钢应釜中加入防锈成膜剂、pH缓冲剂和长效抗腐败剂，搅拌3-5min；
（4）再依次向不锈钢反应釜中加入氢氧化钠、三聚磷酸钠、偏硅酸钠、碳酸钠、苯甲酸钠、木塑硫酸钠、葡萄糖酸钠、磷酸钠、芳香石脑油、三甲基硅油、直链烷基磺酸、乙二醇单丁醚、二丙二醇单丁醚、辛基酚聚氧乙烯醚、异丙醇、工业酒精、乙醇胺、水、污垢分散剂、有机硅消泡剂、低泡表面活性剂，每加入一种原料搅拌均匀1-3min，原料全部加入后继续搅拌至溶液呈浅黄色透明状液体得到喷洗剂成。