CN105860850A - 一种防霉涂料 - Google Patents
一种防霉涂料 Download PDFInfo
- Publication number
- CN105860850A CN105860850A CN201610337531.9A CN201610337531A CN105860850A CN 105860850 A CN105860850 A CN 105860850A CN 201610337531 A CN201610337531 A CN 201610337531A CN 105860850 A CN105860850 A CN 105860850A
- Authority
- CN
- China
- Prior art keywords
- parts
- mould
- resistant paint
- water
- mildew resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种防霉涂料,包括纯丙烯酸树脂、白竹炭粉、纳米钛、杀菌剂、乙基硅橡胶、防霉剂、弹性乳液、水,各组分的质量份数为:纯丙烯酸树脂13‑16、白竹炭粉7‑12、纳米钛5‑10、杀菌剂4‑8、乙基硅橡胶6‑9、防霉剂8‑15、弹性乳液20‑25、水7‑16。本发明具有更高效的防霉技术,有效吸收潮湿空气中的水分,防止墙面发霉,一扫霉味带来的沉闷气息透气防潮,提供最佳的墙面效果,特别适合于墙面翻新及室内装修。
Description
技术领域
本发明涉及一种涂料制备技术领域,具体地讲,本发明涉及一种防霉涂料。
背景技术
传统的涂料多以石油工业的下游产品为主要原料,是由高分子物质和配料组成的混合物,随着人们健康意识的不断提高,人们对所使用的涂料产品的要求也越来越高。
现实生活中,温度、湿度、霉菌孢子是发霉的三个必备条件,而人体觉得舒服的温度也是霉菌生长的温度,这是改变不了的。霉菌的发生不仅影响物体表面的美观,在深层生长的霉菌还会冲破漆膜造成开裂和剥落,导致物体受损 ;并且增生的霉菌还会威胁到动物和人类的健康。因此,涂料的防霉已引起足够的重视。
发明内容
针对现有技术中存在的上述不足,本发明所要解决的技术问题是提供一种保养效果好的防霉涂料。
本发明解决其技术问题所采用的技术方案是:提供一种防霉涂料,包括纯丙烯酸树脂、白竹炭粉、纳米钛、杀菌剂、乙基硅橡胶、防霉剂、弹性乳液、水,各组分的质量份数为:纯丙烯酸树脂13-16、白竹炭粉7-12、纳米钛5-10、杀菌剂4-8、乙基硅橡胶6-9、防霉剂8-15、弹性乳液20-25、水7-16。
作为优选,所述的防霉涂料,其特征在于:所述防霉涂料各组分的质量份数为:纯丙烯酸树脂15、白竹炭粉7、纳米钛5、杀菌剂5、乙基硅橡胶7、防霉剂13、弹性乳液25、水15。
作为优选,所述的防霉涂料,其特征在于:所述纳米钛的粒径≤120nm。
作为优选,所述的防霉涂料,其特征在于:所述水为去离子水。
作为优选,所述的防霉涂料具体制备步骤:将所述质量份数的各组分混合均匀,置于容器中,微波加热反应后得到粗产物;然后在上述粗产物中加入水充分搅拌即可。
本发明得到的一种防霉涂料,具有更高效的防霉技术,有效吸收潮湿空气中的水分,防止墙面发霉,一扫霉味带来的沉闷气息透气防潮,提供最佳的墙面效果,特别适合于墙面翻新及室内装修。
具体实施方式
本发明提供的一种防霉涂料,包括纯丙烯酸树脂、白竹炭粉、纳米钛、杀菌剂、乙基硅橡胶、防霉剂、弹性乳液、水,各组分的质量份数为:纯丙烯酸树脂13-16、白竹炭粉7-12、纳米钛5-10、杀菌剂4-8、乙基硅橡胶6-9、防霉剂8-15、弹性乳液20-25、水7-16。
作为优选,所述的防霉涂料,其特征在于:所述防霉涂料各组分的质量份数为:纯丙烯酸树脂15、白竹炭粉7、纳米钛5、杀菌剂5、乙基硅橡胶7、防霉剂13、弹性乳液25、水15。
作为优选,所述的防霉涂料,其特征在于:所述纳米钛的粒径≤120nm。
作为优选,所述的防霉涂料,其特征在于:所述水为去离子水。
作为优选,所述的防霉涂料具体制备步骤:将所述质量份数的各组分混合均匀,置于容器中,微波加热反应后得到粗产物;然后在上述粗产物中加入水充分搅拌即可。
以上所述,仅是对本发明的较佳实施例而已,并非对本发明做其他形式的限制,任何熟悉本专业的技术人员可能利用上述揭示的技术内容加以变更或改型为同等变化的等效实施例。凡是未脱离本发明方案内容,依据本发明的技术实质对以上实施例所做的任何简单修改、等同变化与改型,均落在本发明的保护范围内。
Claims (5)
1.一种防霉涂料,其特征在于:包括纯丙烯酸树脂、白竹炭粉、纳米钛、杀菌剂、乙基硅橡胶、防霉剂、弹性乳液、水,各组分的质量份数为:纯丙烯酸树脂13-16、白竹炭粉7-12、纳米钛5-10、杀菌剂4-8、乙基硅橡胶6-9、防霉剂8-15、弹性乳液20-25、水7-16。
2.根据权利要求1所述的防霉涂料,其特征在于:所述防霉涂料各组分的质量份数为:纯丙烯酸树脂15、白竹炭粉7、纳米钛5、杀菌剂5、乙基硅橡胶7、防霉剂13、弹性乳液25、水15。
3.根据权利要求1-2所述的防霉涂料,其特征在于:所述纳米钛的粒径≤120nm。
4.根据权利要求1-2所述的防霉涂料,其特征在于:所述水为去离子水。
5.根据权利要求1-2所述的防霉涂料,其特征在于具体制备步骤:将所述质量份数的各组分混合均匀,置于容器中,微波加热反应后得到粗产物;然后在上述粗产物中加入水充分搅拌即可。